CN104559629A - Metal corrosion prevention coating - Google Patents
Metal corrosion prevention coating Download PDFInfo
- Publication number
- CN104559629A CN104559629A CN201510032048.5A CN201510032048A CN104559629A CN 104559629 A CN104559629 A CN 104559629A CN 201510032048 A CN201510032048 A CN 201510032048A CN 104559629 A CN104559629 A CN 104559629A
- Authority
- CN
- China
- Prior art keywords
- parts
- formaldehyde
- prevention coating
- corrosion prevention
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal corrosion prevention coating which comprises the following components in parts by weight: 5-15 parts of phenol resin,1-5 parts of formaldehyde, 2-6 parts of oxalic acid, 2-7 parts of dimer acid, 3-9 parts of polyketone, 5-10 parts of high-chlorinated polyethylene resin, 10-20 parts of chlorcosane, 7-15 parts of aluminum powder, 5-10 parts of titanium dioxide, 5-10 parts of epoxy resin and 10-20 parts of a curing agent. The metal corrosion prevention coating provided by the invention makes up for deficiencies of traditional coatings, has extremely good abrasion resistance and corrosion resistance, can effectively isolate corrosion of acid, alkali and salt, reduces the production costs of raw materials and expands the functions of coatings.
Description
Technical field
The invention belongs to chemical field, what be specifically related to is a kind of metal anti-corrosive paint.
Background technology
Metallic corrosion is a kind of very general phenomenon that occurring in nature exists; very large to the harm of the hardware that people use in daily life and production; at present; people adopt protective system to realize the corrosionproof protection to metal; but existing protective system preservative effect is not very good; and function singleness, do not possess the functions such as fire prevention.
Along with the develop rapidly of modern industry, the anticorrosion great attention being more and more subject to all trades and professions of metallic surface, adopting paint application anticorrosion is a kind of not only economy but also the method for actual effect, concerning industrial and mining enterprises, the metallic corrosion massive losses caused economically is difficult to estimate, account for 15% ~ 20% of global output of steel, visible, be how important to the protection of corrosion.Prevent the method for metallic corrosion a lot, as selected anti-corrosive alloy material on use material, though the preservative activity of playing, construction costs is large, is unfavorable for protection and the Sciences Economics of nonferrous metal resource; Also have and adopt plating and cathode protecting process, but cause exhaust emission, be unfavorable for environment protection.Protection practices proves, taking to paint coating protection is the most general the most most economical method, is first easy construction, wide adaptability, by the compression of device area, form size, secondly paint protection can with other safeguard procedures conbined usage, just can obtain more perfect corrosion protection system.The enterprise that China produces paint is a lot, paint various in style, but all belong to usual production, far can not adapt to the needs of China's Iron And Steel Industry and anti-corrosion of metal industry, corrosion of metal is that metal is subject to the chemistry of surrounding medium or electrochemical action and destroyed physical chemical phenomenon.
Summary of the invention
The object of the invention is to overcome the above problem that prior art exists, a kind of metal anti-corrosive paint is provided, acidproof, alkaline-resisting and the anti-rotten time is long.
For realizing above-mentioned technical purpose, reach above-mentioned technique effect, the present invention is achieved through the following technical solutions:
A kind of metal anti-corrosive paint, following component is comprised: phenolic resin 5-15 part, formaldehyde 1-5 part, oxalic acid 2-6 part in components by weight percent, dimeracid 2-7 part, many ketone 3-9 part, HCPE 5-10 part, clorafin 10-20 part, aluminium powder 7-15 part, titanium dioxide 5-10 part, epoxy resin 5-10 part, solidifying agent 10-20 part.
Preferably, following component is comprised: phenolic resin 8-12 part, formaldehyde 2-4 part, oxalic acid 3-5 part in components by weight percent, dimeracid 4-6 part, many ketone 5-8 part, HCPE 6-8 part, clorafin 14-16 part, aluminium powder 9-12 part, titanium dioxide 6-8 part, epoxy resin 6-8 part, solidifying agent 12-16 part.
Preferably, described solidifying agent is formaldehyde resin.
The invention has the beneficial effects as follows:
Protective system of the present invention, compensate for the deficiency of traditional coating, has fabulous wear resistance, erosion resistance, effectively can completely cut off the corrosion of acid, alkali, salt, reduces the cost making raw material, has enriched the function of coating.
Embodiment
Below in conjunction with embodiment, describe the present invention in detail.
Embodiment 1
A kind of metal anti-corrosive paint, comprises following component: phenolic resin 5 parts, 1 part, formaldehyde, oxalic acid 2 parts, dimeracid 2 parts, many ketone 3 parts, HCPE 5 parts, clorafin 10 parts, aluminium powder 7 parts, titanium dioxide 5 parts, epoxy resin 5 parts, formaldehyde resin 10 parts.
Embodiment 2
A kind of metal anti-corrosive paint, comprises following component: phenolic resin 10 parts, 3 parts, formaldehyde, oxalic acid 4 parts, dimeracid 5 parts, many ketone 6 parts, HCPE 7 parts, clorafin 15 parts, aluminium powder 10 parts, titanium dioxide 7 parts, epoxy resin 7 parts, formaldehyde resin 14 parts.
Embodiment 3
A kind of metal anti-corrosive paint, comprises following component: phenolic resin 15 parts, 5 parts, formaldehyde, oxalic acid 6 parts, dimeracid 7 parts, many ketone 9 parts, HCPE 10 parts, clorafin 20 parts, aluminium powder 15 parts, titanium dioxide 10 parts, epoxy resin 10 parts, 20 parts, solidifying agent.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. a metal anti-corrosive paint, is characterized in that, comprises following component in components by weight percent: phenolic resin 5-15 part, formaldehyde 1-5 part, oxalic acid 2-6 part, dimeracid 2-7 part, many ketone 3-9 part, HCPE 5-10 part, clorafin 10-20 part, aluminium powder 7-15 part, titanium dioxide 5-10 part, epoxy resin 5-10 part, solidifying agent 10-20 part.
2. metal anti-corrosive paint according to claim 1, is characterized in that, comprises following component in components by weight percent: phenolic resin 8-12 part, formaldehyde 2-4 part, oxalic acid 3-5 part, dimeracid 4-6 part, many ketone 5-8 part, HCPE 6-8 part, clorafin 14-16 part, aluminium powder 9-12 part, titanium dioxide 6-8 part, epoxy resin 6-8 part, solidifying agent 12-16 part.
3. metal anti-corrosive paint according to claim 1, is characterized in that: described solidifying agent is formaldehyde resin.