CN106609094A - Metal anticorrosive coating - Google Patents
Metal anticorrosive coating Download PDFInfo
- Publication number
- CN106609094A CN106609094A CN201510702889.2A CN201510702889A CN106609094A CN 106609094 A CN106609094 A CN 106609094A CN 201510702889 A CN201510702889 A CN 201510702889A CN 106609094 A CN106609094 A CN 106609094A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosive paint
- metal anti
- metal
- anticorrosive coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a metal anticorrosive coating. The metal anticorrosive coating comprises, by weight, 30 to 60 parts of epoxy resin, 5 to 15 parts of phenolic neoprene, 2 to 10 parts of dipropionic acid, 1 to 5 parts of chlorinated paraffin, 0.1 to 1 part of methyl cellulose, 1 to 5 parts of a coloring pigment and 5 to 15 parts of a curing agent. The metal anticorrosive coating solves the problems of the traditional coating, has strong corrosion resistance, can effectively prevent the corrosion caused by acids, alkalis and salts and reduces a cost.
Description
Technical field
The invention is related to chemical material field, more particularly to a kind of metal anti-corrosive paint.
Background technology
Metal erosion is a kind of very universal phenomenon present in nature, to people in daily life and
The harm of the hardware used in production is very big, economically huge that industrial metal erosion is caused
Big loss is difficult to the appraisal, accounts for the 15%-20% of global output of steel, it is seen then that the protection to corroding is
How important.With developing rapidly for modern industry, the anti-corrosion of metal surface is increasingly subject to each row each
The great attention of industry.Method of inhibiting corrosion has a lot, such as using plating and cathodic protection, causes discharge
Pollution, is unfavorable for environmental conservation；Also using corrosion resisting alloy, though antisepsises are played, engineering
Cost is big.
The content of the invention
To solve above-mentioned technical problem, the technical solution used in the present invention is：
A kind of metal anti-corrosive paint, in terms of parts by weight, including following component：Epoxy resin 30～60
Part, 5～15 parts of phenolic aldehyde neoprene, 2～10 parts of dimerization propanoic acid, 1～5 part of chlorinated paraffin, Methyl cellulose
0.1～1 part of element, 1～5 part of coloring pigment, 5～15 parts of firming agent.
Further, the metal anti-corrosive paint, in terms of parts by weight, including following component：Epoxy resin
40 parts, 8 parts of phenolic aldehyde neoprene, 6 parts of dimerization propanoic acid, 3 parts of chlorinated paraffin, 0.3 part of methylcellulose,
3 parts of coloring pigment, 10 parts of firming agent.
Further, the firming agent is phenolic resin or Corvic.
Further, the coloring pigment is titanium dioxide or iron oxide blue.
The present invention has the advantages and positive effects that：The metal anti-corrosive paint of the present invention, compensate for tradition
The deficiency of coating, anticorrosive property are strong, can effectively anti-antacid, alkali, the corrosion of salt, reduce cost.
Specific embodiment
The present invention is further detailed below by specific embodiment.
Embodiment 1
Metal anti-corrosive paint, in terms of parts by weight, including following component：40 parts of epoxy resin, phenolic aldehyde
8 parts of neoprene, 6 parts of dimerization propanoic acid, 3 parts of chlorinated paraffin, 1 part of methylcellulose, 3 parts of coloring pigment,
10 parts of firming agent, the firming agent are phenolic resin or Corvic, and the coloring pigment is titanium
White lead or iron oxide blue.
Embodiment 2
Metal anti-corrosive paint, in terms of parts by weight, including following component：30 parts of epoxy resin, phenolic aldehyde
15 parts of neoprene, 2 parts of dimerization propanoic acid, 1 part of chlorinated paraffin, 0.1 part of methylcellulose, coloring pigment 5
Part, 5 parts of firming agent, the firming agent are phenolic resin or Corvic, and the coloring pigment is
Titanium dioxide or iron oxide blue.
Embodiment 3
Metal anti-corrosive paint, in terms of parts by weight, including following component：60 parts of epoxy resin, phenolic aldehyde
5 parts of neoprene, 10 parts of dimerization propanoic acid, 5 parts of chlorinated paraffin, 0.1 part of methylcellulose, coloring pigment 1
Part, 15 parts of firming agent, the firming agent are phenolic resin or Corvic, the coloring pigment
For titanium dioxide or iron oxide blue.
Above one embodiment of the present of invention is described in detail, but the content has been only the present invention's
Preferred embodiment, it is impossible to be considered as limiting practical range of the invention.It is all according to the present patent application scope
The impartial change made and improvement etc., still all should belong within the patent covering scope of the present invention.
Claims (4)
1. a kind of metal anti-corrosive paint, it is characterised in that：The metal anti-corrosive paint, in terms of parts by weight,
Including following component：30～60 parts of epoxy resin, 5～15 parts of phenolic aldehyde neoprene, dimerization propanoic acid 2～10
Part, 1～5 part of chlorinated paraffin, 0.1～1 part of methylcellulose, 1～5 part of coloring pigment, firming agent 5～
15 parts.
2. a kind of metal anti-corrosive paint according to claim 1, it is characterised in that：The metal is prevented
Rotten coating, in terms of parts by weight, including following component：40 parts of epoxy resin, 8 parts of phenolic aldehyde neoprene,
6 parts of dimerization propanoic acid, 3 parts of chlorinated paraffin, 0.3 part of methylcellulose, 3 parts of coloring pigment, firming agent
10 parts.
3. a kind of metal anti-corrosive paint according to claim 1, it is characterised in that：The firming agent
For phenolic resin or Corvic.
4. a kind of metal anti-corrosive paint according to claim 1, it is characterised in that：The coloring face
Expect for titanium dioxide or iron oxide blue.