CN107822924A - A kind of magnetic nail polish - Google Patents
A kind of magnetic nail polish Download PDFInfo
- Publication number
- CN107822924A CN107822924A CN201711267961.9A CN201711267961A CN107822924A CN 107822924 A CN107822924 A CN 107822924A CN 201711267961 A CN201711267961 A CN 201711267961A CN 107822924 A CN107822924 A CN 107822924A
- Authority
- CN
- China
- Prior art keywords
- parts
- copolymer
- nail polish
- mixture
- magnetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of magnetic nail polish, the component and its ratio of weight and number are：20 30 parts of butyl acetate, 10 20 parts of ethyl acetate, 5 10 parts of nitrocellulose, 5 10 parts of denatured ethyl alcohol, 25 parts of tributyl 2-acetylcitrate, 25 parts of isopropanol, 25 parts of oronain hectorite draws in 25 parts of tricresyl phosphate phenol ester, 25 parts of Sucrose acetoisobutyrate, department, 13 parts of mica, 13 parts of silica, 0.2 0.4 parts of iron oxide, 48 parts of natural pigment, 10 20 parts of copolymer A, 10 parts of copolymer B5,35 parts of magnetic, 35 parts of cornstarch.The magnetic nail polish adhesive ability of the present invention is good, is not easy to scrape damage and drops, environment protection health, and makeup effect is good.
Description
Technical field
The invention belongs to cosmetic field, more particularly, to a kind of magnetic nail polish.
Background technology
Magnetic nail polish is a kind of cosmetics, is widely used in finger nail or toenail, and various colors are gorgeous, is had concurrently attractive in appearance
And protective effect.
The composition of common magnetic nail polish is typically made up of two classes, and one kind is solid state component, mainly pigment, flash of light material
Deng；One kind is the solvent composition of liquid, and what is mainly used has acetone, ethyl acetate, phthalic acid ester, formaldehyde etc..
Harm of the current magnetic nail polish not only to human body is big, and adhesive ability is poor, through often scraping after smearing
Situation about dropping is damaged, and then have impact on makeup effect, the pattern that current nail polish is formed after smearing in addition is single, and Micron Technology's degree is poor.
The content of the invention
The present invention is for overcome the deficiencies in the prior art, there is provided a kind of adhesive ability is good, is not easy to scrape damage and drops, ring health care
Health, the good magnetic nail polish of makeup effect.
To achieve these goals, the present invention uses following technical scheme：A kind of magnetic nail polish, it is characterised in that：Institute
State component and its ratio of weight and number is：Butyl acetate 20-30 parts, ethyl acetate 10-20 parts, nitrocellulose 5-10 parts, it is denatured second
Alcohol 5-10 parts, tributyl 2-acetylcitrate 2-5 parts, isopropanol 2-5 parts, tricresyl phosphate phenol ester 2-5 parts, Sucrose acetoisobutyrate
2-5 parts, department's drawing oronain hectorite 2-5 parts, mica 1-3 parts, silica 1-3 parts, iron oxide 0.2-0.4 parts, natural pigment 4-8 parts,
Copolymer A 10-20 parts, copolymer B5-10 parts, magnetic 3-5 parts, cornstarch 3-5 parts.
Harm of each raw material to human body is small in magnetic nail polish prepared by the present invention, health environment-friendly, can be reached between each raw material
To a synergistic function so that the magnetic nail polish adhesive ability prepared is good, is not easy to scrape damage and drops, makeup effect
It is good, additionally by magnetic is added in the feed, after this product is applied on nail, magnetic sheet is disposed close to nail
Opening position, the decorative pattern of texture identical with magnetic sheet can be just showed in nail polish, there can be difference thereby using nail polish
Pattern effect so that the nail more Micron Technology after smearing.
Further, the copolymer A is adipic acid/neopentyl glycol/trimellitic acid anhydride copolymer, and copolymer B is propylene
Acid, the copolymer of methacrylic acid stearoylketene ester.
Present invention also offers a kind of preparation method for preparing above-mentioned magnetic nail polish：Comprise the following steps：
S1：Butyl acetate, ethyl acetate, nitrocellulose and copolymer A are mixed and uniform stirring obtains mixture A；
S2：By denatured ethyl alcohol, tributyl 2-acetylcitrate, isopropanol, tricresyl phosphate phenol ester, Sucrose acetoisobutyrate and
Copolymer B mixing and uniform stirring acquisition mixture B；
S3：Draw oronain hectorite, mica, silica, cornstarch, iron oxide and natural pigment to be ground department, grind
Mixture C is obtained to 1200 mesh sieves are crossed；
S4：Mixture C is added in mixture A simultaneously heating stirring simultaneously, adds mixture B uniform stirrings afterwards；
S5：Magnetic and uniform stirring are added in the mixture that S4 steps obtain, is cooled to tinning after room temperature.
Each composition substantially uniformity of magnetic nail polish that this preparation method prepares mixes, and COLOR COMPOSITION THROUGH DISTRIBUTION is uniform,
Adhesive ability is good.
Further, temperature setting is 35-40 DEG C when being stirred in the S1 steps, and mixing time is 40-60 minutes, stirring
After the completion of be cooled to 20-25 DEG C；Temperature setting is 35-40 DEG C during stirring, and mixing time is that 40-60 minutes ensure that each component energy
It is enough to dissolve mutually completely together.
Further, temperature setting is 30-40 DEG C when being stirred in the S2 steps, and mixing time is 40-60 minutes；Ensure
Each component can dissolve mutually together completely.
Further, heating stirring temperature is 30-40 DEG C in the S4 steps, and mixing time is 40-60 minutes.
In summary, magnetic nail polish adhesive ability of the invention is good, is not easy to scrape damage and drops, environment protection health, makeup effect
Fruit is good.
Embodiment
In order that those skilled in the art are better understood from the present invention program, to the technical scheme in the embodiment of the present invention
Carry out clear, complete description.
Embodiment 1
A kind of magnetic nail polish, the component and its ratio of weight and number are：20 parts of butyl acetate, 10 parts of ethyl acetate, nitre
5 parts of chemical fibre dimension, 5 parts of denatured ethyl alcohol, 2 parts of tributyl 2-acetylcitrate, 2 parts of isopropanol, 2 parts of tricresyl phosphate phenol ester, Sucrose Acetate
2 parts of oronain hectorite, 1 part of mica, 1 part of silica, 0.2 part of iron oxide, 4 parts of natural pigment, copolymer draw in sour 2 parts of sucrose ester, department
A10 parts, copolymer B5 parts, 3 parts of jade of magnetic, 3 parts of rice starch.
Specifically, the copolymer A is adipic acid/neopentyl glycol/trimellitic acid anhydride copolymer, copolymer B be acrylic acid,
The copolymer of methacrylic acid stearoylketene ester.
Described magnetic nail polish is prepared by above-mentioned raw materials proportioning, is comprised the following steps：
S1：Butyl acetate, ethyl acetate, nitrocellulose and copolymer A are mixed and uniform stirring obtains mixture A；
S2：By denatured ethyl alcohol, tributyl 2-acetylcitrate, isopropanol, tricresyl phosphate phenol ester, Sucrose acetoisobutyrate and
Copolymer B mixing and uniform stirring acquisition mixture B；
S3：Draw oronain hectorite, mica, silica, cornstarch, iron oxide and natural pigment to be ground department, grind
Mixture C is obtained to 1200 mesh sieves are crossed；
S4：Mixture C is added in mixture A simultaneously heating stirring simultaneously, adds mixture B uniform stirrings afterwards；
S5：Magnetic and uniform stirring are added in the mixture that S4 steps obtain, is cooled to tinning after room temperature.
Specifically, temperature setting is 35 DEG C when being stirred in the S1 steps, mixing time is 40 minutes, is dropped after the completion of stirring
Temperature is to 20 DEG C.
Specifically, temperature setting is 30 DEG C when being stirred in the S2 steps, mixing time is 40 minutes.
Specifically, heating stirring temperature is 30 DEG C in the S4 steps, mixing time is 40 minutes.
Embodiment 2
A kind of magnetic nail polish, the component and its ratio of weight and number are：25 parts of butyl acetate, 15 parts of ethyl acetate, nitre
6 parts of chemical fibre dimension, 7 parts of denatured ethyl alcohol, 4 parts of tributyl 2-acetylcitrate, 3 parts of isopropanol, 3 parts of tricresyl phosphate phenol ester, Sucrose Acetate
4 parts of oronain hectorite, 2 parts of mica, 2 parts of silica, 0.3 part of iron oxide, 6 parts of natural pigment, copolymer draw in sour 4 parts of sucrose ester, department
A15 parts, copolymer B7 parts, 4 parts of magnetic, 3 parts of cornstarch.
Specifically, the copolymer A is adipic acid/neopentyl glycol/trimellitic acid anhydride copolymer, copolymer B be acrylic acid,
The copolymer of methacrylic acid stearoylketene ester.
Specifically, the preparation method and embodiment 1 are identical
Embodiment 3
A kind of magnetic nail polish, the component and its ratio of weight and number are：30 parts of butyl acetate, 20 parts of ethyl acetate, nitre
Chemical fibre ties up 10 parts, and 10 parts of denatured ethyl alcohol, 5 parts of tributyl 2-acetylcitrate, 5 parts of isopropanol, 5 parts of tricresyl phosphate phenol ester, acetic acid is different
5 parts of oronain hectorite, 3 parts of mica, 3 parts of silica, 0.4 part of iron oxide, 8 parts of natural pigment, copolymerization are drawn by 5 parts of butyric acid sucrose ester, department
Thing A20 parts, copolymer B10 parts, 5 parts of magnetic, 5 parts of cornstarch.
Specifically, the copolymer A is adipic acid/neopentyl glycol/trimellitic acid anhydride copolymer, copolymer B be acrylic acid,
The copolymer of methacrylic acid stearoylketene ester.
Described magnetic nail polish is prepared by above-mentioned raw materials proportioning, is comprised the following steps：
S1：Butyl acetate, ethyl acetate, nitrocellulose and copolymer A are mixed and uniform stirring obtains mixture A；
S2：By denatured ethyl alcohol, tributyl 2-acetylcitrate, isopropanol, tricresyl phosphate phenol ester, Sucrose acetoisobutyrate and
Copolymer B mixing and uniform stirring acquisition mixture B；
S3：Draw oronain hectorite, mica, silica, cornstarch, iron oxide and natural pigment to be ground department, grind
Mixture C is obtained to 1200 mesh sieves are crossed；
S4：Mixture C is added in mixture A simultaneously heating stirring simultaneously, adds mixture B uniform stirrings afterwards；
S5：Magnetic and uniform stirring are added in the mixture that S4 steps obtain, is cooled to tinning after room temperature.
Specifically, temperature setting is 35-40 DEG C when being stirred in the S1 steps, mixing time is 40-60 minutes, has been stirred
20-25 DEG C is cooled to after.
Specifically, temperature setting is 30-40 DEG C when being stirred in the S2 steps, mixing time is 40-60 minutes.
Specifically, heating stirring temperature is 30-40 DEG C in the S4 steps, mixing time is 40-60 minutes.
Comparative example 1
A kind of magnetic nail polish, the component and its ratio of weight and number are：20 parts of butyl acetate, 10 parts of ethyl acetate, nitre
5 parts of chemical fibre dimension, 5 parts of denatured ethyl alcohol, 2 parts of tributyl 2-acetylcitrate, 2 parts of isopropanol, 2 parts of tricresyl phosphate phenol ester, Sucrose Acetate
2 parts of oronain hectorite, 1 part of mica, 1 part of silica, 0.2 part of iron oxide, 4 parts of natural pigment, copolymer draw in sour 2 parts of sucrose ester, department
A10 parts, copolymer B5 parts,.
The copolymer A is adipic acid/neopentyl glycol/trimellitic acid anhydride copolymer, and copolymer B is acrylic acid, methyl-prop
The copolymer of olefin(e) acid stearoylketene ester.
Specific preparation method and embodiment 1 are identical.
Comparative example 2
A kind of magnetic nail polish, the component and its ratio of weight and number are：20 parts of butyl acetate, 10 parts of ethyl acetate, nitre
5 parts of chemical fibre dimension, 5 parts of denatured ethyl alcohol, 2 parts of tributyl 2-acetylcitrate, 2 parts of isopropanol, 2 parts of tricresyl phosphate phenol ester, Sucrose Acetate
Sour sucrose ester 2-5 parts, 2 parts of department's drawing oronain hectorite, 1 part of mica, 1 part of silica, 0.2 part of iron oxide, natural pigment 4-8 parts, altogether
Polymers A10 parts, copolymer B5 parts, 3 parts of magnetic, 3 parts of cornstarch.
The copolymer A is adipic acid/neopentyl glycol/trimellitic acid anhydride copolymer, and copolymer B is acrylic acid, methyl-prop
The copolymer of olefin(e) acid stearoylketene ester.
Described magnetic nail polish is prepared by above-mentioned raw materials proportioning, is comprised the following steps：
S1：Butyl acetate, ethyl acetate, nitrocellulose and copolymer A are mixed and uniform stirring obtains mixture A；
S2：By denatured ethyl alcohol, tributyl 2-acetylcitrate, isopropanol, tricresyl phosphate phenol ester, Sucrose acetoisobutyrate and
Copolymer B mixing and uniform stirring acquisition mixture B；
S3：Draw oronain hectorite, mica, silica, cornstarch, iron oxide and natural pigment to be ground department, grind
Mixture C is obtained to 1200 mesh sieves are crossed；
S4：Mixture C is added in mixture A simultaneously heating stirring simultaneously, adds mixture B uniform stirrings afterwards；
S5：Magnetic and uniform stirring are added in the mixture that S4 steps obtain, is cooled to tinning after room temperature.
Specifically, temperature setting is 35 DEG C when being stirred in the S1 steps, mixing time is 40 minutes.
Specifically, temperature setting is 30 DEG C when being stirred in the S2 steps, mixing time is 40 minutes.
Specifically, heating stirring temperature is 30 DEG C in the S4 steps, mixing time is 40 minutes.
Comparative example 3
A kind of magnetic nail polish, the component and its ratio of weight and number are：20 parts of butyl acetate, 10 parts of ethyl acetate, nitre
5 parts of chemical fibre dimension, 5 parts of denatured ethyl alcohol, 2 parts of tributyl 2-acetylcitrate, 2 parts of isopropanol, 2 parts of tricresyl phosphate phenol ester, Sucrose Acetate
2 parts of oronain hectorite, 1 part of mica, 1 part of silica, 0.2 part of iron oxide, 4 parts of natural pigment, copolymer draw in sour 2 parts of sucrose ester, department
A10 parts, copolymer B5 parts, 3 parts of magnetic.
The copolymer A is adipic acid/neopentyl glycol/trimellitic acid anhydride copolymer, and copolymer B is acrylic acid, methyl-prop
The copolymer of olefin(e) acid stearoylketene ester.
Described magnetic nail polish is prepared by above-mentioned raw materials proportioning, is comprised the following steps：
S1：Butyl acetate, ethyl acetate, nitrocellulose and copolymer A are mixed and uniform stirring obtains mixture A；
S2：By denatured ethyl alcohol, tributyl 2-acetylcitrate, isopropanol, tricresyl phosphate phenol ester, Sucrose acetoisobutyrate and
Copolymer B mixing and uniform stirring acquisition mixture B；
S3：Draw oronain hectorite, mica, silica, cornstarch, iron oxide and natural pigment to be ground department, grind
Mixture C is obtained to 1200 mesh sieves are crossed；
S4：Mixture C is added in mixture A simultaneously heating stirring simultaneously, adds mixture B uniform stirrings afterwards；
S5：Magnetic and uniform stirring are added in the mixture that S4 steps obtain, is cooled to tinning after room temperature.
Specifically, temperature setting is 20 DEG C when being stirred in the S1 steps, mixing time is 30 minutes.
Specifically, temperature setting is 20 DEG C when being stirred in the S2 steps, mixing time is 40 minutes.
Specifically, heating stirring temperature is 20 DEG C in the S4 steps, mixing time is 40 minutes.
Test example
Select 200 people at random to try out embodiment 1~3, comparative example 1~3 and commercially available prod, every morning smears magnetic
Property nail polish once, it is 40 days to try out the time, finally counts trial effect, and every effect total score is 5 points, and 5 points are best result table
Show very well；4 points represent good；3 points represent general；2 points of expressions are bad；1 point of expression can not receive.It is every average mark below,
It is as shown in the table：
| Adhesive ability | Makeup effect | Scratch resistant damage effect | |
| Embodiment 1 | 4.5 | 4.6 | 4.7 |
| Embodiment 2 | 4.5 | 4.7 | 4.8 |
| Embodiment 3 | 4.7 | 4.7 | 4.8 |
| Comparative example 1 | 4.4 | 4.5 | 4.5 |
| Comparative example 2 | 4.5 | 4.4 | 4.7 |
| Comparative example 3 | 4.5 | 4.3 | 4.7 |
| Commercially available prod | 4.4 | 4.5 | 4.4 |
Knowable to embodiment 1~3, comparative example 1 and commercially available product are contrasted, magnetic nail polish of the invention has energy of attachment
Power is good, makeup effect is good, the advantages of being not easy to scrape damage, embodiment 1 and comparative example 2,3 are contrasted knowable to, pass through the system of invention
The eye shadow cream makeup effect that Preparation Method prepares is good.
Obviously, described embodiment is only the part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made
Embodiment, it should all belong to the scope of protection of the invention.
Claims (6)
- A kind of 1. magnetic nail polish, it is characterised in that：The component and its ratio of weight and number are：Butyl acetate 20-30 parts, acetic acid Ethyl ester 10-20 parts, nitrocellulose 5-10 parts, denatured ethyl alcohol 5-10 parts, tributyl 2-acetylcitrate 2-5 parts, isopropanol 2-5 parts, Oronain hectorite 2-5 parts, mica 1-3 parts, silica 1-3 draw in tricresyl phosphate phenol ester 2-5 parts, Sucrose acetoisobutyrate 2-5 parts, department Part, iron oxide 0.2-0.4 parts, natural pigment 4-8 parts, copolymer A 10-20 parts, copolymer B5-10 parts, magnetic 3-5 parts, corn Starch 3-5 parts.
- 2. magnetic nail polish according to claim 1, it is characterised in that：The copolymer A be adipic acid/neopentyl glycol/ Trimellitic acid anhydride copolymer, copolymer B are acrylic acid, the copolymer of methacrylic acid stearoylketene ester.
- A kind of 3. preparation method for preparing the magnetic nail polish described in claim 1~2 any one：It is characterized in that：Including Following steps：S1：Butyl acetate, ethyl acetate, nitrocellulose and copolymer A are mixed and uniform stirring obtains mixture A；S2：By denatured ethyl alcohol, tributyl 2-acetylcitrate, isopropanol, tricresyl phosphate phenol ester, Sucrose acetoisobutyrate and copolymerization Thing B mixing and uniform stirring acquisition mixture B；S3：Draw oronain hectorite, mica, silica, cornstarch, iron oxide and natural pigment to be ground department, be ground to 1200 mesh sieves obtain mixture C；S4：Mixture C is added in mixture A simultaneously heating stirring simultaneously, adds mixture B uniform stirrings afterwards；S5：Magnetic and uniform stirring are added in the mixture that S4 steps obtain, is cooled to tinning after room temperature.
- 4. magnetic nail polish according to claim 3, it is characterised in that：Temperature setting is when being stirred in the S1 steps 35-40 DEG C, mixing time is 40-60 minutes, and 20-25 DEG C is cooled to after the completion of stirring.
- 5. magnetic nail polish according to claim 3, it is characterised in that：Temperature setting is when being stirred in the S2 steps 30-40 DEG C, mixing time is 40-60 minutes.
- 6. magnetic nail polish according to claim 3, it is characterised in that：Heating stirring temperature is 30- in the S4 steps 40 DEG C, mixing time is 40-60 minutes.