CN101697943A - Environment-friendly water-based nail polish - Google Patents
Environment-friendly water-based nail polish Download PDFInfo
- Publication number
- CN101697943A CN101697943A CN200910112685A CN200910112685A CN101697943A CN 101697943 A CN101697943 A CN 101697943A CN 200910112685 A CN200910112685 A CN 200910112685A CN 200910112685 A CN200910112685 A CN 200910112685A CN 101697943 A CN101697943 A CN 101697943A
- Authority
- CN
- China
- Prior art keywords
- environment
- nial polish
- water
- aqueous
- nail polish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environment-friendly water-based nail polish. The water-based nail polish is characterized by taking pure water and environment-friendly resin as main components, thus having no damage on nails, being mild to people and having the properties of environment protection, non toxicity and tastelessness.
Description
Technical field
The present invention relates to a kind of nial polish, refer more particularly to a kind of environment-friendly type aqueous nial polish.
Background technology
Traditional nial polish contains a large amount of stimulation chemical analysis, as acetone, toluene etc., this be harmful substance, easily allow your fingernail exsiccation, flavescence, become fragile,, will influence health and environmental pollution.
The principle that nial polish is attached to nail surface is earlier the fingernail top layer to be destroyed, and produces many coarse duck eyes on the surface, and nial polish infiltrates in the pothole, and under the life-time service, pigment precipitates easily, and fingernail is easily yellow, dry and cracked, and many women that like to be beautiful have sacrificed health for this reason.
In addition because nial polish must possess quick-drying, glossy, strong adhesion, water-fast, easily be coated with and characteristics such as removal easily, although the nial polish technology is along with development of science and technology obtains significant progress, owing to can satisfy simultaneously seldom as the material of the essential performance of nial polish, thereby up to the present, comprise on the market that the nial polish that international major company produces almost all is by nitrocellulose, modified resin, plasticizer, multiple mixed solvent is formed, yet can dissolve nitrocellulosic solvent generally all is some lipids, ketone, the benzene class, alcohol ethers etc. are volatile, the material of strong toxicity excitatory, popularizing along with nial polish in recent years, the rise of manicure, also more and more such as nial polish to human injury's report, nial polish become the to like to be beautiful thing of women's love-hate relationship.
Summary of the invention
The object of the invention is to overcome above-mentioned weak point of the prior art and preparation method that a kind of environment-friendly type aqueous nial polish is provided.The environment-friendly type aqueous nial polish of the present invention, as solvent, pure water, environment-friendly resin are Main Ingredients and Appearance with water, and the oiliness nial polish of abandoning tradition is the mode of Main Ingredients and Appearance with a large amount of poisonous and hazardous organic solvents, develop environmental protection, nontoxic nial polish product.
The present invention realizes in the following way: each composition quality % ratio is:
Aqueous environment protection resin 70～90
Water 4-15
Propylene glycol 2.0～8
Moistening flatting agent 0.2～1
Antiseptic 0.01～0.02
Pearlescent pigment or mill base 1～3
Thickening agent 0.5～1
Other auxiliary agent 1～2
Above-mentioned raw materials is got final product than stirring after mixing by quality % of the present invention.
In sum, the environment-friendly type aqueous nial polish of the present invention, as solvent, pure water, environment-friendly resin are Main Ingredients and Appearance with water, can not injure fingernail, to human body as mild as a dove, really embody green, environmental protection, nontoxic, tasteless performance, represented the trend of nial polish development from now on, nial polish is as a branch of cosmetics, be each women's that likes to be beautiful requirement, occupied very big a slice market share, so its market prospect is very optimistic.
The specific embodiment
The present invention realizes in the following way: each composition material quality % ratio is:
Aqueous environment protection resin 70～90
Water 4-15
Propylene glycol 2.0～8
Moistening flatting agent 0.2～1
Antiseptic 0.01～0.02
Pearlescent pigment or mill base 1～3
Thickening agent 0.5～1
Other auxiliary agent 1～2
Above-mentioned raw materials is got final product than stirring after mixing by quality % of the present invention.
1 resin choice
Since nial polish must possess quick-drying, glossy, strong adhesion, wear-resisting, water-fast, easily be coated with and characteristics such as removal easily, guarantee its feature of environmental protection simultaneously for realizing these performances, the film forming matter of selecting a kind of excellence is the most important thing.Can reach normal temperature crosslinked, convenient brushing, transparency well then can only be designed to single-component system, and this type of waterborne film-forming thing is mainly water-borne acrylic type, dispersions of polyurethanes, aqueous NC Nitroncellulose etc.It is medium that aqueous acrylic emulsion is done speed, and to be used for fingernail more crisp but film, and need a certain amount of coalescents, is difficult for satisfying the requirement of this project feature of environmental protection; Aqueous polyurethane has performances such as excellent abrasive, pliability, adhesive force, but its solid content is low, and dried speed can't satisfy the requirement of surface drying within the nial polish number minute more slowly; Quick-drying, transparent good advantage that the aqueous NC Nitroncellulose has, but it is crisp to film, and is not suitable for independent film forming, and weatherability is relatively poor.This project is taked it is used according to certain mixed, or carries out chemical graft or hydridization, makes it have the advantage of several film forming matters concurrently.It is primary raw material that this project is selected aqueous polyurethane and aqueous nitrocellulose for use, can at room temperature crosslinked film forming, and coating promptly has performances such as excellent hardness, pliability, adhesive force, has excellent quick-drying and transparent again.The aqueous polyurethane that the present invention is selected and aqueous NC Nitroncellulose are through confirming as environment-friendly type.
2 selection of pigment
Color is an important indicator of nial polish, and because of it is a kind of high-decoration that is used for, high-quality series cosmetics product need possess and enrich gorgeous color and ornamental.Therefore contain at least a coloring agent in the nial polish dye compositions of the present invention, can use conventional coloring agent, as pearl essence material or conventional dispersible pigment color paste.Yet pearlescent pigment generally is just to add in the coating in the stage of production process, and its density is bigger in addition need not pass through milling apparatus, so pearlescent pigment very easily precipitates bad dispersibility.Need to screen, find to use a kind of anti-settling agent simultaneously and help the dispersant that pearl essence aligns, can solve the sedimentation problem of pearlescent pigment effectively by test repeatedly.Pigment is difficult to keep secular suspension and stable in base material simultaneously, causes easily to be separated, so must rely on certain amount of dispersant, the adding of thickening agent simultaneously also helps its suspension.
Because the easy property and the bad dispersibility of sinking of pearlescent pigment is pre-dispersed before interpolation, makes the pearlescent pigment slurry, as it is pre-dispersed in water, adds an amount of dispersant, and can add a certain amount of cosolvent as required, helps it and evenly suspends and arrangement.
The selection of 3 auxiliary agents
Because the life cycle of nial polish is long, decoration and instructions for use are high, so it must possess following significant performance:
(1) drying property fast;
(2) gorgeous color effect;
(3) splendid anti-heavy performance and bin stability;
(4) good gloss;
(5) nontoxic or low toxicity.
Nial polish is coated on the fingernail, must have good levelability, and wear-resisting scratch-resisting is convenient to apply, and must have certain viscosity.Above-mentioned these characteristics, the present invention needs to adjust by auxiliary agent.
With film forming matter much relations are arranged on the one hand as drying property, but the present invention simultaneously can also help by the auxiliary agent of drier and so on.Color aspect and pigment are in close relations but need to select for use some suitable dispersants to help its moistening homodisperse simultaneously even so that obtain a color development, the system that no loose colour grows dim; Anti-sinking then become the project of a need emphasis solution of nial polish with storage, the uniformity of system is very important, this can need add thickening agent and come to reduce its speed of related movement so that each component is disperseed more equably to an one good suspension system simultaneously from dispersant and two aspect collocation of anti-settling agent; We need add a certain amount of levelling, smoothly reach anti-scratch auxiliary agent so that nail polish is filmed more smooth smooth more wear-resisting in addition.
4 Performance Evaluations
(1) appearance of film: smooth smooth, special pearl effect is arranged
(2) drying time: surface drying (minute) :≤10
Do solid work (minute) :≤30
(3) gloss (%): 〉=70
Claims (1)
1. environment-friendly type aqueous nial polish, it is characterized in that: the quality % ratio of each composition of the present invention is:
Aqueous environment protection resin 70～90
Water 4-15
Propylene glycol 2.0～8
Moistening flatting agent 0.2～1
Antiseptic 0.01～0.02
Pearlescent pigment or mill base 1～3
Thickening agent 0.5～1
Other auxiliary agent 1～2
Above-mentioned raw materials is got final product than stirring after mixing by quality % of the present invention.