CN102552071A - Environment-friendly water-based fingernail paint - Google Patents
Environment-friendly water-based fingernail paint Download PDFInfo
- Publication number
- CN102552071A CN102552071A CN201110445457XA CN201110445457A CN102552071A CN 102552071 A CN102552071 A CN 102552071A CN 201110445457X A CN201110445457X A CN 201110445457XA CN 201110445457 A CN201110445457 A CN 201110445457A CN 102552071 A CN102552071 A CN 102552071A
- Authority
- CN
- China
- Prior art keywords
- add
- water
- minutes
- fingernail
- rev
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment friendly water-based fingernail paint, which comprises the following components by weight percentage: 10-20% of deionized water, 50-70% of water-based acrylic emulsion, 6-8% of ethanol, 1-2% of thickener, 2-4% of texanol film forming adjuvant, 0.005-0.015% of defoamer, 0.2-0.3% of dimethylethanolamine, 0.02-0.04% of leveling agent, 2-4% of non-resin water-based transparent color paste, 4-7% of pearl-luster pigment and 4-6% of propylene glycol. The main raw material of the fingernail paint adopts the nanometer thermoplastic water-based acrylic resin, so that the adhesive force of paint film is good, and the main raw material of the formula belongs to the water-based system, so that the fingernail paint is dried rapidly after being painted on a fingernail, the cleaning and makeup removal operation are simple, no toxic organic solvents exist in the formula, no harm is caused to the fingernail during painting, and further, no pungent odors and gases are generated.
Description
Technical field
The present invention relates to a kind of nail varuish, be specifically related to a kind of environment-friendly water-based nail varuish.
Background technology
Nail varuish is called nial polish again, and nial polish is coated on the fingernail, can make henna gorgeous moistening, and colour-fast for a long time, receives people and likes.At present; The raw material of nial polish such as acetone, ethyl acetate etc. mostly have certain bio-toxicity, and they are inflammable and explosive, and generation makes us dazzling dizzy penetrating odor when volatilization; (their volume of volatilization back will expand 1,000 times) stained in generation to room air; Under long-term situation about sucking, mucosa there is strong and stimulating, also might produce harm to nervous system.
In addition; For guaranteeing the manicure effect; Performance to nail varuish has higher requirements, and nail varuish must have strong adhesion, fast-drying easy is coated with and characteristics such as cleaning easily, and the material that can satisfy the essential performance of nail varuish at present is less; Nail varuish on the market mostly is made up of modified resin, plasticizer, nitrocellulose, cosolvent; The organic solvents volatile, excitatory such as lipids, ketone, benzene class that use in the nail varuish are to reduce the injury that nail varuish produces human body more, need to seek a kind of performance meet instructions for use, environment-friendly type the aqueous nail varuish.
Summary of the invention
The objective of the invention is to overcome the deficiency of above-mentioned prior art, a kind of strong adhesion, easy removing, toxicity circlet water-retaining property nail varuish are provided.
The technical scheme that the present invention adopted is following:
A kind of environment-friendly water-based nail varuish comprises the component of following weight percentage ratio: deionized water 10～20; (50～80 nanometer particle size) aqueous acrylic emulsion 50～70; Ethanol 6～8; Alkali association thickener 1～2; Alcohol ester 12 coalescents 2～4; Non-silicone mineral oil is defoamer 0.005～0.015; Dimethylethanolamine (PH regulator) 0.2～0.3; Levelling agent (BYK346) 0.02～0.04; No resin aqueous transparent color mill base 2～4; Pearl essence 4～7; Propylene glycol 4～6.
The preferred version of a kind of environment-friendly water-based nail varuish of the present invention is (component is weight percentage): deionized water 15; (50～80 nanometer particle size) aqueous acrylic emulsion 60; Ethanol 6.9; Alkali association thickener 1.49; Alcohol ester 12 coalescents 2.33; Non-silicone mineral oil is defoamer 0.01; Dimethylethanolamine (PH regulator) 0.24; Levelling agent (BYK346) 0.03; No resin aqueous transparent color mill base 3; Pearl essence 6; Propylene glycol 5.
A kind of environment-friendly water-based nail varuish of the present invention, formulated as follows:
(1) base material preparation
In the container of high speed dispersor is housed, add deionized water, under the stirring of 300 rev/mins of rotating speeds, add the alkali association thickener; Stirred 2 minutes, the high speed dispersor rotating speed is transferred to 600 rev/mins, slowly adds dimethylethanolamine in the container; Stirred 10 minutes, and got base material;
(2) varnish preparation
In the container of high speed dispersor is housed, add the nano-scale water acrylic emulsion, under the stirring of 300 rev/mins of rotating speeds, add ethanol; Stirred 5 minutes; Slowly add alcohol ester 12 coalescents again, adjustment rotating speed to 400 rev/min adds the base material that step (1) makes; Stirred 10 minutes, and got varnish;
(3) metallic finishe preparation
In the container of high speed dispersor is housed, add no resin aqueous transparent color mill base, the rotating speed of adjustment high speed dispersor is 400 rev/mins, adds propylene glycol; Stir after 5 minutes, add pearl essence, stir after 7 minutes, add the varnish that step (2) makes; Stir after 10 minutes; Add levelling agent more successively and non-silicone mineral oil is defoamer, the rotating speed of adjustment high speed dispersor is 350 rev/mins, stirs and promptly obtains said nail varuish after 15 minutes.
Compared with prior art; Primary raw material in the present invention's prescription adopts nanoscale thermoplasticity water-borne acrylic resin, its vitrification point high (Tg45 ℃), film-forming temperature low (MFT6 ℃), and paint film adhesion is good; Fast dry when covering with paint, lacquer, colour wash, etc. fingernail; Operation is simple and easy when cleaning makeup removing, in 50 ℃～65 ℃ hot water, soaks after about 1 minute during makeup removing, uses family's alkaline soap commonly used to clean up.The primary raw material of this prescription belongs to water-based system, does not contain just like poisonous organic solvents such as acetone, ethyl acetate, xylene, banana oil in the prescription, during covering with paint fingernail is not had injury, and no toxic solvent evaporates, and does not produce penetrating odor gas.
The specific embodiment
Embodiment 1
A kind of environment-friendly water-based nail varuish of the present invention comprises the component of following weight percentage ratio: deionized water 10; (50～80 nanometer particle size) aqueous acrylic emulsion 70; Ethanol 6; Alkali association thickener 1.27; Alcohol ester 12 coalescents 2; Non-silicone mineral oil is defoamer 0.01; Dimethylethanolamine (PH regulator) 0.2; Levelling agent (BYK346) 0.02; No resin aqueous transparent color mill base 2; Pearl essence 4; Propylene glycol 4.5.
Embodiment 2
A kind of environment-friendly water-based nail varuish of the present invention comprises the component of following weight percentage ratio: deionized water 15; (50～80 nanometer particle size) aqueous acrylic emulsion 60; Ethanol 6.9; Alkali association thickener 1.49; Alcohol ester 12 coalescents 2.33; Non-silicone mineral oil is defoamer 0.01; Dimethylethanolamine (PH regulator) 0.24; Levelling agent (BYK346) 0.03; No resin aqueous transparent color mill base 3; Pearl essence 6; Propylene glycol 5.
The environment-friendly water-based nail varuish of the present invention carries out the adhesive force test according to the circle method of drawing of national standard standard GB1720-89 (79) regulation, and test result shows that adhesive force reaches 1 grade.
Embodiment 3
A kind of environment-friendly water-based nail varuish of the present invention comprises the component of following weight percentage ratio:
Deionized water 13; (50～80 nanometer particle size) aqueous acrylic emulsion 60; Ethanol 8; Alkali association thickener 1.65; Alcohol ester 12 coalescents 4; Non-silicone mineral oil is defoamer 0.01; Dimethylethanolamine (PH regulator) 0.3; Levelling agent (BYK346) 0.04; No resin aqueous transparent color mill base 3; Pearl essence 5; Propylene glycol 5.
Claims (3)
1. environment-friendly water-based nail varuish is characterized in that said nail varuish comprises the component of following weight percentage ratio:
Deionized water 10～20
Grain of rice footpath aqueous acrylic emulsion 50～70 in 50～80
Ethanol 6～8
Alkali association thickener 1～2
Alcohol ester 12 coalescents 2～4
Non-silicone mineral oil is defoamer 0.005～0.015
Dimethylethanolamine 0.2～0.3
Levelling agent 0.02～0.04
No resin aqueous transparent color mill base 2～4
Pearl essence 4～7
Propylene glycol 4～6
2. according to the described a kind of environment-friendly water-based nail varuish of claim 1, it is characterized in that said nail varuish comprises the component of following weight percentage ratio:
Deionized water 15
Grain of rice footpath aqueous acrylic emulsion 60 in 50～80
Ethanol 6.9
Alkali association thickener 1.49
Alcohol ester 12 coalescents 2.33
Non-silicone mineral oil is defoamer 0.01
Dimethylethanolamine 0.24
Levelling agent 0.03
No resin aqueous transparent color mill base 3
Pearl essence 6
Propylene glycol 5
3. according to claim 1 or 2 described a kind of environment-friendly water-based nail varuish, it is characterized in that what said nail varuish was prepared as follows:
(1) base material preparation
In the container of high speed dispersor is housed, add deionized water, under the stirring of 300 rev/mins of rotating speeds, add the alkali association thickener; Stir after 2 minutes, the high speed dispersor rotating speed is transferred to 600 rev/mins, slowly add dimethylethanolamine in the container again; Stirred 10 minutes, and obtained base material;
(2) varnish preparation
, the container of high speed dispersor adds the nano-scale water acrylic emulsion in being housed; Under the stirring of 300 rev/mins of rotating speeds, add ethanol, stirred 5 minutes, slowly add alcohol ester 12 coalescents again; Adjustment rotating speed to 400 rev/min; Add the base material that step (1) makes, stirred 10 minutes, get varnish;
(3) metallic finishe preparation
In the container of high speed dispersor is housed, add no resin aqueous transparent color mill base, the rotating speed of adjustment high speed dispersor is 400 rev/mins and adds propylene glycol, stirs after 5 minutes; Add pearl essence again; Stir and add the varnish that step (2) makes after 7 minutes, stir after 10 minutes, add levelling agent more successively and non-silicone mineral oil is defoamer; The rotating speed of adjustment high speed dispersor is 350 rev/mins, stirs and promptly obtains said nail varuish after 15 minutes.