CN103751036A - UV (Ultraviolet) nail phototherapy gel and preparation method thereof - Google Patents
UV (Ultraviolet) nail phototherapy gel and preparation method thereof Download PDFInfo
- Publication number
- CN103751036A CN103751036A CN201410016652.4A CN201410016652A CN103751036A CN 103751036 A CN103751036 A CN 103751036A CN 201410016652 A CN201410016652 A CN 201410016652A CN 103751036 A CN103751036 A CN 103751036A
- Authority
- CN
- China
- Prior art keywords
- fingernail
- phototherapy
- high speed
- phototherapy glue
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an UV (Ultraviolet) nail phototherapy gel and a preparation method thereof. According to the formula, the phototherapy gel comprises the following components in percentage by mass: 40 to 50% of single functional monomer, 40 to 50% of aliphatic polyurethane acrylic resin, 8 to 11% of photoinitiator, 0.2 to 0.4% of flatting agent, and 0.1 to 0.2% of defoaming agent. The UV nail phototherapy gel shows an outstanding brightening effect with a coating, and also has the characteristics of being environmentally-friendly, convenient to coat, high in transparence, high in glossiness, natural, lightweight, high in toughness, no pungent smell, difficult to yellow and break, long in holding time, etc.
Description
Technical field
The present invention relates to a kind of UV glue coating, particularly a kind of UV fingernail phototherapy glue and preparation method thereof.
Background technology
In common nial polish, contain a large amount of chemical solvents as toluene, ethyl acetate and ethanol, phthalic acid ester, formaldehyde etc., produce many harm to health, and cover with paint, lacquer, colour wash, etc. after dry easily drop, abnormal smells from the patient is large, glossiness conservation degree is low.
Publication number is that the Chinese patent application of CN103479537 discloses a kind of flash of light nial polish, and its formula contains following component: 20 grams, acetone, 15 grams of ethyl acetate, 75 grams of phthalic acid esters, 10 grams of tonyreds, 5 grams, formaldehyde, 25 grams of flashlight powders.Although this nial polish has flash effect, wherein contain formaldehyde etc., health is had to certain harm.
Summary of the invention
The object of the invention is to make up the deficiencies in the prior art, a kind of UV fingernail phototherapy glue is provided, it films this phototherapy glue and has excellent brightness effect, also has environmental protection simultaneously, covers with paint, lacquer, colour wash, etc. the features such as convenient, transparency is high, glossiness good, naturally light and handy, good toughness, nonirritant taste, inhibited from yellowing, the retention time is grown.
The technical scheme that the present invention reaches its object employing is as follows: a kind of UV fingernail phototherapy glue, and its formula comprises each component of following mass percent:
Described monofunctional monomer is one or more the mixture in acryloyl morpholine (be called for short ACMO), hydroxyethyl methylacrylate (being called for short HEMA), 3.3.5-trimethyl cyclohexyl acrylate (being called for short TMCHA).Wherein, acryloyl morpholine (be called for short ACMO) can adopt the product of Japanese Xing Ren Co., Ltd., hydroxyethyl methylacrylate (being called for short HEMA) can adopt the product of MIT, and 3.3.5-trimethyl cyclohexyl acrylate (being called for short TMCHA) can adopt the EM2104 of Changxing, Taiwan company.The monomer that the present invention adopts all adopts the high curing rate monomer in the middle of simple function, wherein acryloyl morpholine is a kind of thermostability functional monomer of superior performance, zest to skin is very little, because its steam pressure is very low, so produce hardly any penetrating odor.ACMO also has the features such as low viscosity and fast setting and low cubical contraction.The zest of the adhesive force that hydroxyethyl methylacrylate has had and low skin, 3.3.5-trimethyl cyclohexyl acrylate (be called for short TMCHA) has high adhesion force high response and low cure shrinkage, can improve the internal stress that reduces coating in curing rate in system.Also can be to the effects such as hardness, adhesive force are provided of filming in the diluting effect that above monomer can play when coordinating or using in formula system of the present invention separately and fast curing rate.
Described aliphatic polyurethane acrylic resin Wei Er functional group's aliphatic polyurethane acrylic resin and composite the mixing of six functional groups aliphatic polyurethane acrylic resin.In formula system of the present invention, use this composite resin, it has in low energy condition and is issued to high curing rate, and filming after solidifying has high rigidity, the feature of high tenacity, high glaze and high richness effect.In the present invention, two functional group's aliphatic polyurethane acrylic resins and six functional groups aliphatic polyurethane acrylic resin specifically can be according to mass ratio (30-40): (5-15) composite.Concrete, described aliphatic polyurethane acrylic resin can preferably adopt two functional groups that Shenzhen Sa Bisi Science and Technology Ltd. produces exempt from clean the six functional groups aliphatic polyurethane acrylic resin 6145-100 that the special-purpose specific functionality aliphatic urethane acrylate SM-582 of UV phototherapy glue and Changxing, Taiwan company produce and mix.The resistance to xanthochromia transitivity that aliphatic urethane acrylate has had, what the present invention adopted is the composite use of 2 functional groups and 6 functional groups.The SM-582 preferably adopting be a kind of two functional groups exempt to clean the special-purpose specific functionality aliphatic urethane acrylate of UV phototherapy glue, there is low-yield high curing rate, high glaze, outstanding oil resistant and weather-proof chemical resistance, outstanding wear-resisting scratch-resisting, outstanding film forming tenacity, can be in the present invention as matrix resin, supporting resin preferably adopts 6 officials' energy aliphatic polyurethane acrylic resin 6145-100 of Changxing company, it has high curing rate, high rigidity, and high tenacity, can be used as matrix resin hardness and curing rate deficiency supplementary.
Described light trigger is 1-hydroxy cyclohexyl phenylketone (184), 2,4, the mixture of 6-trimethylbenzoyl-diphenyl phosphate oxidation (TPO), diphenyl phosphine oxide (819); Specifically can be selected from the corresponding Related product of BASF AG or Beijing Ying Li scientific & technical corporation or Tianjin Jiu scientific & technical corporation.Light trigger can absorb ultraviolet energy, produces free radical, then causes coating oligomer and monomer is realized polymerization, crosslinked, makes system be cross-linked film forming.The light trigger that the present invention preferably adopts is 1-hydroxy cyclohexyl phenylketone (184), 2, 4, 6-, trimethylbenzoyl-diphenyl phosphate oxidation (TPO) and diphenyl phosphine oxide (819) mix composite forming according to the mass ratio of 1:1:0.1, 1-hydroxy cyclohexyl phenylketone (184) belongs to skin drying mould light trigger, 2, 4, 6-trimethylbenzoyl-diphenyl phosphate oxidation (TPO) and diphenyl phosphine oxide (819) belong to long wave deep layer and solidify light trigger, light trigger after composite can absorb ultraviolet wavelength between 280-450um, just in time send wavelength correspondence with phototherapy lamp, the energy-curable effect that allows fingernail phototherapy glue reach.
The dimethyl polysiloxane of described levelling agent Wei Han acrylic functional group; Specifically can adopt the BYK of Bi Ke chemical company
-UV3576.Phototherapy glue needs quick levelling effect, in formulation for coating material, add appropriate levelling agent, can improve coating flow leveling, in the present invention, levelling agent adopts polyether siloxane copolymers, the preferred dimethyl polysiloxane of Yong Han acrylic functional group, more preferably adopt BYK company containing the dimethyl polysiloxane leveling auxiliary agent BYK of acrylic functional group
-UV3576, levelling is eliminated and is coated with trace fast.
Described defoamer, for not containing organosilyl polymer-type defoamer, specifically can be selected from the BYK1794 of Bi Ke chemical company.Phototherapy glue all can produce bubble in production covering with paint process, the existence of bubble can cause the generation defect of filming, need defoamer to improve, defoamer can provide good defoaming effect, prevent the generation of paint film defect, defoamer of the present invention is not for containing organosilyl polymer-type defoamer, in formula system of the present invention, add not containing organosilyl polymer-type defoamer, in the good antifoam performance of maintenance, prepared UV fingernail phototherapy glue does not have a negative impact to ply adhesion when recoat, make the effect of UV fingernail phototherapy glue of the present invention better.
Second aspect present invention provides a kind of method of preparing UV fingernail phototherapy glue as described above, comprises the steps:
Step 1, takes each component by formula: monofunctional monomer 40~50%, aliphatic polyurethane acrylic resin 40~50%, light trigger 8~11%, levelling agent 0.2~0.4%, defoamer 0.1~0.2%;
Step 2, drops into monofunctional monomer, fat adoption urethane acrylate resin to disperse, in cylinder, to use high speed dispersor high speed dispersion 10~15 minutes;
Step 3, drops into levelling agent, with high speed dispersor, disperses 10~15 minutes;
Step 4, drops into light trigger, uses high speed dispersor high speed dispersion 10~15 minutes;
Step 5, drops into defoamer, with high speed dispersor, disperses 10~15 minutes, and 300 order filter-cloth filterings, make UV fingernail phototherapy glue;
Wherein, the rotating speed of the high speed dispersor of described step 2 and step 3 is 1200~1500 revs/min; The rotating speed of the high speed dispersor of step 4 and step 5 is 800~1000 revs/min.
Phototherapy glue of the present invention can be no more than 10% shades of colour environmental protection mill base and bronze and by toning, forms the UV fingernail phototherapy glue of different colours series by adding.
Technical scheme of the present invention has following beneficial effect:
Adopt formula of the present invention, in its formula system, each component compatibility is good, by each component interaction, the prepared UV fingernail phototherapy glue of working in coordination, have environmental protection, cover with paint, lacquer, colour wash, etc. and conveniently, low-yield to solidify, to have after film forming highlighted effect, good toughness, tasteless nontoxic, inhibited from yellowing, not frangibility, loss of gloss not, the feature such as do not come off, the retention time is long.
UV fingernail phototherapy glue preparation method provided by the invention has feature simply and easily, and prepared phototherapy glue is covered with paint, lacquer, colour wash, etc. after fingernail with professional manicure instrument, and under 36W phototherapy lamp, lamp, according to 2 minutes, gets final product film forming.Phototherapy glue after film forming is filmed, and to have gloss highlighted, and richness is good, and adhesive force is good, good toughness, and the features such as good weatherability also have good leveling property simultaneously, low abnormal smells from the patient, the low-yield feature such as solidify.Manicure surface-brightening after phototherapy glue of the present invention is covered with paint, lacquer, colour wash, etc., naturally lightly, good toughness, nonirritant taste, inhibited from yellowing, frangibility, retention time do not reach one month.
The specific embodiment
Below technical scheme of the present invention is described further:
Embodiment 1~4
Embodiment 1-4 is the Preparation Example of UV fingernail phototherapy glue, the formula of embodiment 1~4 (unit: kg) as shown in table 1.
Table 1
The SM-582 that two sense aliphatic polyurethane acrylic resins described in table 1 specifically can adopt Shenzhen Sa Bisi Science and Technology Ltd. to produce; The 6145-100 that six described sense aliphatic polyurethane acrylic resins specifically can adopt Changxing, Taiwan to produce).
The preparation method of the UV fingernail phototherapy glue of embodiment 1-4, all in accordance with the following steps:
Step 1, takes each component by the formula of upper table 1;
Step 2, drops into monofunctional monomer, aliphatic polyurethane acrylic resin to disperse, in cylinder, to use high speed dispersor high speed dispersion 10~15 minutes;
Step 3, drops into levelling agent, with high speed dispersor, disperses 10~15 minutes;
Step 4, drops into light trigger, with high speed dispersor, disperses high speed dispersion 10~15 minutes,
Step 5, drops into defoamer, with high speed dispersor, disperses 10~15 minutes, and 300 order filter-cloth filterings, make UV fingernail phototherapy glue.
Wherein, the rotating speed of the high speed dispersor of described step 2 and step 3 is 1200~1500 revs/min; The rotating speed of the high speed dispersor of step 4 and step 5 is 800~1000 revs/min.
After testing, the UV fingernail phototherapy glue of embodiment 1~4 preparation, color outward appearance is that colourless transparent liquid, solid content are 98~99%, viscosity is 800~1000mpa.s (25 ℃).After embodiment 1-4 processes by color paste toning separately, all adopt following coating method to cover with paint, lacquer, colour wash, etc.: 1. with professional manicure instrument polishing fingernail, 2. with professional nail brush, evenly cover with paint, lacquer, colour wash, etc. first color UV fingernail phototherapy glue after fingernail, under 36W phototherapy lamp, lamp was according to 2 minutes, 3. with professional nail brush, evenly cover with paint, lacquer, colour wash, etc. the 2nd road color UV fingernail phototherapy glue on fingernail, under 36W phototherapy lamp, lamp was according to 2 minutes, 4. with professional nail brush, evenly cover with paint, lacquer, colour wash, etc. the colourless UV fingernail of light phototherapy glue on fingernail, under 36W phototherapy lamp, lamp, according to 2 minutes, obtains the lasting beautiful phototherapy glue of color and films.After the phototherapy glue film forming of embodiment 1-4, it is filmed and all has difficult drop-off, easily smears, and solidify drying time short, and hold period is permanent, there is no bad smell, easy fracture not, high resilience, the feature such as color is lasting beautiful.
The above, it is only preferred embodiment of the present invention, not the present invention is done to any pro forma restriction, the content that does not depart from technical solution of the present invention therefore all, according to technical spirit of the present invention, to any simple modification made for any of the above embodiments, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (8)
2. UV fingernail phototherapy glue according to claim 1, is characterized in that, monofunctional monomer is one or more the mixture in acryloyl morpholine, hydroxyethyl methylacrylate, 3.3.5-trimethyl cyclohexyl acrylate.
3. UV fingernail phototherapy glue according to claim 1, is characterized in that, described aliphatic polyurethane acrylic resin Wei Er functional group's aliphatic polyurethane acrylic resin and composite the mixing of six functional groups aliphatic polyurethane acrylic resin.
4. UV fingernail phototherapy glue according to claim 3, is characterized in that, described aliphatic polyurethane acrylic resin is the SM-582 of Shenzhen Sa Bisi Science and Technology Ltd. production and composite the mixing of 6145-100 that Changxing, Taiwan company produces.
5. UV fingernail phototherapy glue according to claim 1, is characterized in that, described light trigger is 1-hydroxy cyclohexyl phenylketone, 2,4, the mixture of 6-trimethylbenzoyl-diphenyl phosphate oxidation, diphenyl phosphine oxide.
6. UV fingernail phototherapy glue according to claim 1, is characterized in that, the dimethyl polysiloxane of described levelling agent Wei Han acrylic functional group.
7. UV fingernail phototherapy glue according to claim 1, is characterized in that, described defoamer is not for containing organosilyl polymer-type defoamer.
8. a method of preparing the UV fingernail phototherapy glue as described in claim 1-7 any one, is characterized in that, comprises the steps:
Step 1, takes each component by formula: monofunctional monomer 40~50%, aliphatic polyurethane acrylic resin 40~50%, light trigger 8~11%, levelling agent 0.2~0.4%, defoamer 0.1~0.2%;
Step 2, drops into monofunctional monomer, aliphatic polyurethane acrylic resin to disperse, in cylinder, to use high speed dispersor high speed dispersion 10~15 minutes;
Step 3, drops into levelling agent, with high speed dispersor, disperses 10~15 minutes;
Step 4, drops into light trigger, uses high speed dispersor high speed dispersion 10~15 minutes;
Step 5, drops into defoamer, with high speed dispersor, disperses 10~15 minutes, and 300 order filter-cloth filterings, make UV fingernail phototherapy glue.