CN107814540A - 一种纤维增韧喷射混凝土 - Google Patents

一种纤维增韧喷射混凝土 Download PDF

Info

Publication number
CN107814540A
CN107814540A CN201711370570.XA CN201711370570A CN107814540A CN 107814540 A CN107814540 A CN 107814540A CN 201711370570 A CN201711370570 A CN 201711370570A CN 107814540 A CN107814540 A CN 107814540A
Authority
CN
China
Prior art keywords
water
gunite concrete
bamboo fibre
flyash
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711370570.XA
Other languages
English (en)
Inventor
闫振
李来波
芦令超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Jinan
Original Assignee
University of Jinan
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Jinan filed Critical University of Jinan
Priority to CN201711370570.XA priority Critical patent/CN107814540A/zh
Publication of CN107814540A publication Critical patent/CN107814540A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种纤维增韧喷射混凝土，它是由以下重量份的原料组成：水泥230~310、粉煤灰200~300、细骨料900~1000、粗骨料800~900、竹纤维丝50~80,减水剂6~10、黏度调节组分0.5~1.5、速凝剂12~18。该喷射混凝土加入了竹纤维丝增强了韧性，且力学性能有所改善。

Description

一种纤维增韧喷射混凝土
技术领域
本发明属于建筑材料领域，特别涉及一种纤维增韧喷射混凝土。
背景技术
喷射混凝土是一种将胶凝材料、骨料、外加剂等按一定比例拌制的混凝土拌合物送入喷射设备，借助压缩空气或其它动力输送至喷射口，高速喷至受喷面所形成的混凝土。喷射混凝土具有施工简便，施工速度快、周期短，早期强度高，无需振捣自密实等优点，在施工场地及条件有限的矿道工程，隧道工程等具有广泛的应用前景。但现有的喷射混凝土存在强度高但脆性大，韧度不够的问题，严重制约了喷射混凝土的推广应用。
发明内容
本发明目的在于提供一种纤维增韧喷射混凝土，旨在解决现有技术制备的喷射混凝土脆性大，韧度不够，应用范围受限的问题。
本发明的技术方案如下：
一种纤维增韧喷射混凝土，其特征在于，它是由以下重量份的原料组成：水泥 230~310、粉煤灰200~300、细骨料900~1000、粗骨料800~900、竹纤维丝50~80，减水剂6~10、黏度调节组分0.5~1.5、速凝剂12~18；
所述的水泥为普通硅酸盐水泥，强度等级为52.5，初凝时间30分钟，终凝时间160分钟；
所述粉煤灰为二级细灰，化学组成中二氧化硅含量为40~50%；
所述细骨料为连续级配机制砂，石粉含量为4~11%；
所述粗骨料为连续级配石灰石碎石，最大粒径为20mm；
所述纤维为竹纤维丝，长度为5~10mm；
所述减水剂为萘系高效减水剂，减水率为25~35%；
所述黏度调节组分为可再分散性乳胶粉，吸水倍率为70~85。
与现有技术相比，本发明的喷射混凝土突出优点是在混凝土中加入竹纤维丝，增强了混凝土韧性，且力学性能有所改善。
具体实施方式
下面结合具体实施例对本发明做进一步的详细说明。
实施例1
一种大掺量粉煤灰喷射混凝土，各组分重量份数如下：水泥 230、粉煤灰200、细骨料900、粗骨料800、竹纤维丝50,减水剂6、黏度调节组分0.5、速凝剂18；
所述粉煤灰为二级细灰，化学组成中二氧化硅含量为50%；
所述细骨料为连续级配机制砂，石粉含量为4%；
所述纤维为竹纤维，长度为5mm；
所述减水剂为萘系高效减水剂，减水率为30%；
所述黏度调节组分为可再分散性乳胶粉，吸水倍率为80。
实施例2
水泥 310、粉煤灰300、细骨料1000、粗骨料900、竹纤维丝80,减水剂10、黏度调节组分1.5、速凝剂12；
所述粉煤灰为二级细灰，化学组成中二氧化硅含量为50%；
所述细骨料为连续级配机制砂，石粉含量为10%；
所述纤维为竹纤维丝，长度为5~10mm；
所述减水剂为萘系高效减水剂，减水率为25%；
所述黏度调节组分为可再分散性乳胶粉，吸水倍率为70。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。

Claims (1)

1.一种纤维增韧喷射混凝土，其特征在于，它是由以下重量份的原料组成：水泥 230~310、粉煤灰200~300、细骨料900~1000、粗骨料800~900、竹纤维丝50~80,减水剂6~10、黏度调节组分0.5~1.5、速凝剂12~18；
所述的水泥为普通硅酸盐水泥，强度等级为52.5，初凝时间30分钟，终凝时间160分钟；
所述粉煤灰为二级细灰，化学组成中二氧化硅含量为40~50%；
所述细骨料为连续级配机制砂，石粉含量为4~11%；
所述粗骨料为连续级配石灰石碎石，最大粒径为20mm；
所述纤维丝为竹纤维丝，长度5~10mm；
所述减水剂为萘系高效减水剂，减水率为25~35%；
所述黏度调节组分为可再分散性乳胶粉，吸水倍率为70~85。
CN201711370570.XA 2017-12-19 2017-12-19 一种纤维增韧喷射混凝土 Pending CN107814540A (zh)