CN107762366A - 隔音防火门 - Google Patents

隔音防火门 Download PDF

Info

Publication number
CN107762366A
CN107762366A CN201711085185.0A CN201711085185A CN107762366A CN 107762366 A CN107762366 A CN 107762366A CN 201711085185 A CN201711085185 A CN 201711085185A CN 107762366 A CN107762366 A CN 107762366A
Authority
CN
China
Prior art keywords
parts
puigging
intermediate layer
fire door
insulated fire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711085185.0A
Other languages
English (en)
Inventor
刘晓东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711085185.0A priority Critical patent/CN107762366A/zh
Publication of CN107762366A publication Critical patent/CN107762366A/zh
Pending legal-status Critical Current

Abstract

一种隔音防火门，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层；所述隔音层包括以下重量份的原料：柱晶松脂0.3‑0.5份，粘接剂1‑3份，丙烯酸树脂0.6‑1.0份，硫氰钠钴0.1‑0.3份，聚甲基丙烯酸甲酯10‑15份，甲基纤维素0.6‑1.2份，玻璃纤维0.1‑0.4份，纳米硫酸钡0.2‑0.4份，蜜蜡石粉0.4‑0.6份。本发明提供的隔音防火门通过在门芯外表面涂覆隔音层、中间层、防火层，提高了门的隔音防火性能，同时表面光泽度高，中间层有效的解决了隔音层和防火层界面不兼容问题；本发明隔音防火门长期使用坚固不变形，寿命长。

Description

隔音防火门
技术领域
本发明涉及家具技术领域，具体涉及一种隔音防火门。
背景技术
智能家居(英文：smart home,home automation)是以住宅为平台，利用综合布线技术、网络通信技术、安全防范技术、自动控制技术、音视频技术将家居生活有关的设施集成，构建高效的住宅设施与家庭日程事务的管理系统，提升家居安全性、便利性、舒适性、艺术性，并实现环保节能的居住环境。
门作为智能家居的组成部分，不在仅仅停留在防盗、美观的功能上，需要满足更多的功能才能与智能家居匹配。
发明内容
本发明为解决上述问题，提供一种隔音防火门。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种隔音防火门，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层。
所述隔音层包括以下重量份的原料：
柱晶松脂0.3-0.5份，粘接剂1-3份，丙烯酸树脂0.6-1.0份，硫氰钠钴0.1-0.3份，聚甲基丙烯酸甲酯10-15份，甲基纤维素0.6-1.2份，玻璃纤维0.1-0.4份，纳米硫酸钡0.2-0.4份，蜜蜡石粉0.4-0.6份。
所述粘接剂为活性树脂粘接剂。
所述中间层包括以下重量份的原料：
核桃油2-3份，蜂蜡0.5-1.0份，降香叶提取物0.8-1.2份，丙烯腈-苯乙烯树脂20-25份，珠光粉0.4-0.6份，纳米二氧化硅0.5-0.8份，表面活性剂1.2-1.5份，液晶聚合物0.3-0.7份，二氧化钛0.4-0.8份，氧化锌0.5-0.7份。
所述表面活性剂为偶联剂型表面活性剂。
所述偶联剂型表面活性剂为硅烷类、钛酸酯类、锆铝酸盐类中的一种或几种。
所述防火层包括以下重量份的原料：
纳米二氧化硅0.2-0.6份，聚异丁烯0.6-0.8份，刚玉粉0.5-0.7份，有机硅树脂10-12份，聚硅氧烷0.2-0.8份，石英粉1.2-1.6份。
所述隔音层、中间层、防火层厚度比为2:1：1～2。
所述隔音层、中间层、防火层厚度分别为0.2mm、0.1mm、0.2mm。
本发明的有益效果为：本发明提供的隔音防火门通过在门芯外表面涂覆隔音层、中间层、防火层，提高了门的隔音防火性能，同时表面光泽度高，中间层有效的解决了隔音层和防火层界面不兼容问题；本发明隔音防火门长期使用坚固不变形，寿命长。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合实施例，进一步阐述本发明。
实施例1
一种隔音防火门，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层。
所述隔音层包括以下重量份的原料：
柱晶松脂0.3份，粘接剂1份，丙烯酸树脂0.6份，硫氰钠钴0.1份，聚甲基丙烯酸甲酯10份，甲基纤维素0.6份，玻璃纤维0.1份，纳米硫酸钡0.2份，蜜蜡石粉0.4份。
所述粘接剂为活性树脂粘接剂。
所述中间层包括以下重量份的原料：
核桃油2份，蜂蜡0.5份，降香叶提取物0.8份，丙烯腈-苯乙烯树脂20份，珠光粉0.4份，纳米二氧化硅0.5份，表面活性剂1.2份，液晶聚合物0.3份，二氧化钛0.4份，氧化锌0.5份。
所述表面活性剂为偶联剂型表面活性剂。
所述偶联剂型表面活性剂为硅烷类、钛酸酯类、锆铝酸盐类中的一种或几种。
所述防火层包括以下重量份的原料：
纳米二氧化硅0.2份，聚异丁烯0.6份，刚玉粉0.5份，有机硅树脂10份，聚硅氧烷0.2份，石英粉1.2份。
所述隔音层、中间层、防火层厚度比为2:1：1～2。
所述隔音层、中间层、防火层厚度分别为0.2mm、0.1mm、0.2mm。
实施例2
一种隔音防火门，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层。
所述隔音层包括以下重量份的原料：
柱晶松脂0.4份，粘接剂2份，丙烯酸树脂0.8份，硫氰钠钴0.2份，聚甲基丙烯酸甲酯13份，甲基纤维素0.9份，玻璃纤维0.3份，纳米硫酸钡0.3份，蜜蜡石粉0.5份。
所述粘接剂为活性树脂粘接剂。
所述中间层包括以下重量份的原料：
核桃油2份，蜂蜡0.5份，降香叶提取物0.8份，丙烯腈-苯乙烯树脂20份，珠光粉0.4份，纳米二氧化硅0.5份，表面活性剂1.2份，液晶聚合物0.3份，二氧化钛0.4份，氧化锌0.5份。
所述表面活性剂为偶联剂型表面活性剂。
所述偶联剂型表面活性剂为硅烷类、钛酸酯类、锆铝酸盐类中的一种或几种。
所述防火层包括以下重量份的原料：
纳米二氧化硅0.2份，聚异丁烯0.6份，刚玉粉0.5份，有机硅树脂10份，聚硅氧烷0.2份，石英粉1.2份。
所述隔音层、中间层、防火层厚度比为2:1：1～2。
所述隔音层、中间层、防火层厚度分别为0.2mm、0.1mm、0.2mm。
实施例3
一种隔音防火门，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层。
所述隔音层包括以下重量份的原料：
柱晶松脂0.5份，粘接剂3份，丙烯酸树脂1.0份，硫氰钠钴0.3份，聚甲基丙烯酸甲酯15份，甲基纤维素1.2份，玻璃纤维0.4份，纳米硫酸钡0.4份，蜜蜡石粉0.6份。
所述粘接剂为活性树脂粘接剂。
所述中间层包括以下重量份的原料：
核桃油2份，蜂蜡0.5份，降香叶提取物0.8份，丙烯腈-苯乙烯树脂20份，珠光粉0.4份，纳米二氧化硅0.5份，表面活性剂1.2份，液晶聚合物0.3份，二氧化钛0.4份，氧化锌0.5份。
所述表面活性剂为偶联剂型表面活性剂。
所述偶联剂型表面活性剂为硅烷类、钛酸酯类、锆铝酸盐类中的一种或几种。
所述防火层包括以下重量份的原料：
纳米二氧化硅0.2份，聚异丁烯0.6份，刚玉粉0.5份，有机硅树脂10份，聚硅氧烷0.2份，石英粉1.2份。
所述隔音层、中间层、防火层厚度比为2:1：1～2。
所述隔音层、中间层、防火层厚度分别为0.2mm、0.1mm、0.2mm。
实施例4
一种隔音防火门，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层。
所述隔音层包括以下重量份的原料：
柱晶松脂0.4份，粘接剂2份，丙烯酸树脂0.8份，硫氰钠钴0.2份，聚甲基丙烯酸甲酯13份，甲基纤维素0.9份，玻璃纤维0.3份，纳米硫酸钡0.3份，蜜蜡石粉0.5份。
所述粘接剂为活性树脂粘接剂。
所述中间层包括以下重量份的原料：
核桃油3份，蜂蜡1.0份，降香叶提取物1.2份，丙烯腈-苯乙烯树脂25份，珠光粉0.6份，纳米二氧化硅0.8份，表面活性剂1.5份，液晶聚合物0.7份，二氧化钛0.8份，氧化锌0.7份。
所述表面活性剂为偶联剂型表面活性剂。
所述偶联剂型表面活性剂为硅烷类、钛酸酯类、锆铝酸盐类中的一种或几种。
所述防火层包括以下重量份的原料：
纳米二氧化硅0.2份，聚异丁烯0.6份，刚玉粉0.5份，有机硅树脂10份，聚硅氧烷0.2份，石英粉1.2份。
所述隔音层、中间层、防火层厚度比为2:1：1～2。
所述隔音层、中间层、防火层厚度分别为0.2mm、0.1mm、0.2mm。
实施例5
一种隔音防火门，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层。
所述隔音层包括以下重量份的原料：
柱晶松脂0.4份，粘接剂2份，丙烯酸树脂0.8份，硫氰钠钴0.2份，聚甲基丙烯酸甲酯13份，甲基纤维素0.9份，玻璃纤维0.3份，纳米硫酸钡0.3份，蜜蜡石粉0.5份。
所述粘接剂为活性树脂粘接剂。
所述中间层包括以下重量份的原料：
核桃油2份，蜂蜡0.5份，降香叶提取物0.8份，丙烯腈-苯乙烯树脂20份，珠光粉0.4份，纳米二氧化硅0.5份，表面活性剂1.2份，液晶聚合物0.3份，二氧化钛0.4份，氧化锌0.5份。
所述表面活性剂为偶联剂型表面活性剂。
所述偶联剂型表面活性剂为硅烷类、钛酸酯类、锆铝酸盐类中的一种或几种。
所述防火层包括以下重量份的原料：
纳米二氧化硅0.6份，聚异丁烯0.8份，刚玉粉0.7份，有机硅树脂12份，聚硅氧烷0.8份，石英粉1.6份。
所述隔音层、中间层、防火层厚度比为2:1：1～2。
所述隔音层、中间层、防火层厚度分别为0.2mm、0.1mm、0.2mm。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的仅为本发明的优选例，并不用来限制本发明，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (8)

1.一种隔音防火门，其特征在于，包括由实木制成的门芯，涂覆在门芯外表面的隔音层，涂覆在隔音层上的中间层，涂覆在中间层上的防火层；
所述隔音层包括以下重量份的原料：
柱晶松脂0.3-0.5份，粘接剂1-3份，丙烯酸树脂0.6-1.0份，硫氰钠钴0.1-0.3份，聚甲基丙烯酸甲酯10-15份，甲基纤维素0.6-1.2份，玻璃纤维0.1-0.4份，纳米硫酸钡0.2-0.4份，蜜蜡石粉0.4-0.6份。
2.如权利要求1所述的隔音防火门，其特征在于，所述粘接剂为活性树脂粘接剂。
3.如权利要求1所述的隔音防火门，其特征在于，所述中间层包括以下重量份的原料：
核桃油2-3份，蜂蜡0.5-1.0份，降香叶提取物0.8-1.2份，丙烯腈-苯乙烯树脂20-25份，珠光粉0.4-0.6份，纳米二氧化硅0.5-0.8份，表面活性剂1.2-1.5份，液晶聚合物0.3-0.7份，二氧化钛0.4-0.8份，氧化锌0.5-0.7份。
4.如权利要求3所述的隔音防火门，其特征在于，所述表面活性剂为偶联剂型表面活性剂。
5.如权利要求4所述的隔音防火门，其特征在于，所述偶联剂型表面活性剂为硅烷类、钛酸酯类、锆铝酸盐类中的一种或几种。
6.如权利要求1所述的隔音防火门，其特征在于，所述防火层包括以下重量份的原料：
纳米二氧化硅0.2-0.6份，聚异丁烯0.6-0.8份，刚玉粉0.5-0.7份，有机硅树脂10-12份，聚硅氧烷0.2-0.8份，石英粉1.2-1.6份。
7.如权利要求1至6任一所述的隔音防火门，其特征在于，所述隔音层、中间层、防火层厚度比为2:1：1～2。
8.如权利要求7所述的隔音防火门，其特征在于，所述隔音层、中间层、防火层厚度分别为0.2mm、0.1mm、0.2mm。
CN201711085185.0A 2017-11-07 2017-11-07 隔音防火门 Pending CN107762366A (zh)