CN107761393A - A kind of flame-retardant coating fabric and its preparation technology - Google Patents
A kind of flame-retardant coating fabric and its preparation technology Download PDFInfo
- Publication number
- CN107761393A CN107761393A CN201711157282.6A CN201711157282A CN107761393A CN 107761393 A CN107761393 A CN 107761393A CN 201711157282 A CN201711157282 A CN 201711157282A CN 107761393 A CN107761393 A CN 107761393A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating fabric
- preparation technology
- flame
- tpe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of flame-retardant coating fabric and its preparation technology, coating fabric component includes 30 50 parts of polyurethane resin, 10 20 parts of antimony oxide, 770 8 14 parts of light stabilizer, 10 20 parts of thermoplastic elastomer (TPE), 5 16 parts of aqueous acrylic emulsion, 39 parts of tributoxyethyl phosphate, 4 12 parts of hydroxyethyl cellulose, 5 10 parts of flake asbestos, 3 10 parts of silane coupler in parts by weight, preparation technology of the present invention is simple, and obtained coating fabric has the advantages of excellent fire-retardant, heat-insulated, radiation proof.
Description
Technical field
The present invention relates to coating fabric preparing technical field, specially a kind of flame-retardant coating fabric and its preparation technology.
Background technology
Coating fabric is a kind of fabric handled through special process.It is exactly to utilize solvent or water by required coating adhesive
Grain(There are PU glue, A/C glue, PVC, PE glue)Etc. being dissolved into salivation shape, then by a kind of (cylinder, scraper or roller in a manner of certain)
Even is coated on cloth(There are the base materials such as cotton, terylene, polyamide fibre), then pass through the set of oven temperature again, make in web surface
Form one layer of uniform covering sizing material, windproof so as to reach waterproof, the function such as ventilative;Current coating fabric preparation technology answers
It is miscellaneous, and obtained fabric bad mechanical property.
The content of the invention
It is an object of the invention to provide a kind of flame-retardant coating fabric and its preparation technology, to solve in above-mentioned background technology
The problem of proposition.
To achieve the above object, the present invention provides following technical scheme:A kind of flame-retardant coating fabric, coating fabric component are pressed
Parts by weight include polyurethane resin 30-50 parts, antimony oxide 10-20 parts, the 8-14 parts of light stabilizer 770, thermoplastic elastic
Body 10-20 parts, aqueous acrylic emulsion 5-16 parts, tributoxyethyl phosphate 3-9 parts, hydroxyethyl cellulose 4-12 parts, asbestos
Powder 5-10 parts, silane coupler 3-10 parts.
Preferably, the preferable composition proportion of coating fabric component is steady including 40 parts of polyurethane resin, three 2 15 parts of oxidations, light
Determine 770 11 parts of agent, 15 parts of thermoplastic elastomer (TPE), 12 parts of aqueous acrylic emulsion, 6 parts of tributoxyethyl phosphate, ethoxy fibre
8 parts of dimension element, 8 parts of flake asbestos, 7 parts of silane coupler.
Preferably, its preparation technology comprises the following steps:
A, after aqueous acrylic emulsion, tributoxyethyl phosphate, hydroxyethyl cellulose, flake asbestos, silane coupler being mixed
The stirring of stirred tank high speed is added, stir speed (S.S.) is 3000 revs/min, mixing time 20min, obtains mixture A;
B, antimony oxide, light stabilizer 770, thermoplastic elastomer (TPE) are sequentially added in mixture A, low speed is carried out after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, time 10min, obtains mixture B;
C, polyurethane resin is finally added in mixture B, adds in kneading machine and is kneaded after mixing, melting temperature is 120 DEG C, when
Between be 30min, that is, obtain coating fabric.
Compared with prior art, the beneficial effects of the invention are as follows:Preparation technology of the present invention is simple, obtained coating fabric tool
There is the advantages of excellent fire-retardant, heat-insulated, radiation proof;Wherein, thermoplastic elastomer (TPE), the aqueous acrylamide yogurt added in the present invention
Liquid, it is possible to increase the toughness of fabric, improve its compression strength;Hydroxyethyl cellulose, the flake asbestos of addition, it is possible to increase coating
The anti-uv-ray of fabric.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
The present invention provides following technical scheme:A kind of flame-retardant coating fabric, coating fabric component include poly- in parts by weight
It is urethane resin 30-50 parts, antimony oxide 10-20 parts, the 8-14 parts of light stabilizer 770, thermoplastic elastomer (TPE) 10-20 parts, water-based
Acrylic emulsion 5-16 parts, tributoxyethyl phosphate 3-9 parts, hydroxyethyl cellulose 4-12 parts, flake asbestos 5-10 parts, silane are even
Join agent 3-10 parts.
Embodiment one:
Coating fabric component in parts by weight include 30 parts of polyurethane resin, 10 parts of antimony oxide, 770 8 parts of light stabilizer,
10 parts of thermoplastic elastomer (TPE), 5 parts of aqueous acrylic emulsion, 3 parts of tributoxyethyl phosphate, 4 parts of hydroxyethyl cellulose, flake asbestos
5 parts, 3 parts of silane coupler.
The preparation technology of the present embodiment comprises the following steps:
A, after aqueous acrylic emulsion, tributoxyethyl phosphate, hydroxyethyl cellulose, flake asbestos, silane coupler being mixed
The stirring of stirred tank high speed is added, stir speed (S.S.) is 3000 revs/min, mixing time 20min, obtains mixture A;
B, antimony oxide, light stabilizer 770, thermoplastic elastomer (TPE) are sequentially added in mixture A, low speed is carried out after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, time 10min, obtains mixture B;
C, polyurethane resin is finally added in mixture B, adds in kneading machine and is kneaded after mixing, melting temperature is 120 DEG C, when
Between be 30min, that is, obtain coating fabric.
Embodiment two:
Coating fabric component in parts by weight include 50 parts of polyurethane resin, 20 parts of antimony oxide, 770 14 parts of light stabilizer,
20 parts of thermoplastic elastomer (TPE), 16 parts of aqueous acrylic emulsion, 9 parts of tributoxyethyl phosphate, 12 parts of hydroxyethyl cellulose, asbestos
10 parts of powder, 10 parts of silane coupler.
The preparation technology of the present embodiment comprises the following steps:
A, after aqueous acrylic emulsion, tributoxyethyl phosphate, hydroxyethyl cellulose, flake asbestos, silane coupler being mixed
The stirring of stirred tank high speed is added, stir speed (S.S.) is 3000 revs/min, mixing time 20min, obtains mixture A;
B, antimony oxide, light stabilizer 770, thermoplastic elastomer (TPE) are sequentially added in mixture A, low speed is carried out after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, time 10min, obtains mixture B;
C, polyurethane resin is finally added in mixture B, adds in kneading machine and is kneaded after mixing, melting temperature is 120 DEG C, when
Between be 30min, that is, obtain coating fabric.
Embodiment three:
Coating fabric component in parts by weight include 35 parts of polyurethane resin, 12 parts of antimony oxide, 770 10 parts of light stabilizer,
14 parts of thermoplastic elastomer (TPE), 7 parts of aqueous acrylic emulsion, 4 parts of tributoxyethyl phosphate, 6 parts of hydroxyethyl cellulose, flake asbestos
6 parts, 5 parts of silane coupler.
The preparation technology of the present embodiment comprises the following steps:
A, after aqueous acrylic emulsion, tributoxyethyl phosphate, hydroxyethyl cellulose, flake asbestos, silane coupler being mixed
The stirring of stirred tank high speed is added, stir speed (S.S.) is 3000 revs/min, mixing time 20min, obtains mixture A;
B, antimony oxide, light stabilizer 770, thermoplastic elastomer (TPE) are sequentially added in mixture A, low speed is carried out after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, time 10min, obtains mixture B;
C, polyurethane resin is finally added in mixture B, adds in kneading machine and is kneaded after mixing, melting temperature is 120 DEG C, when
Between be 30min, that is, obtain coating fabric.
Example IV:
Coating fabric component in parts by weight include 45 parts of polyurethane resin, 16 parts of antimony oxide, 770 12 parts of light stabilizer,
16 parts of thermoplastic elastomer (TPE), 13 parts of aqueous acrylic emulsion, 7 parts of tributoxyethyl phosphate, 10 parts of hydroxyethyl cellulose, asbestos
8 parts of powder, 7 parts of silane coupler.
The preparation technology of the present embodiment comprises the following steps:
A, after aqueous acrylic emulsion, tributoxyethyl phosphate, hydroxyethyl cellulose, flake asbestos, silane coupler being mixed
The stirring of stirred tank high speed is added, stir speed (S.S.) is 3000 revs/min, mixing time 20min, obtains mixture A;
B, antimony oxide, light stabilizer 770, thermoplastic elastomer (TPE) are sequentially added in mixture A, low speed is carried out after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, time 10min, obtains mixture B;
C, polyurethane resin is finally added in mixture B, adds in kneading machine and is kneaded after mixing, melting temperature is 120 DEG C, when
Between be 30min, that is, obtain coating fabric.
Embodiment five:
Coating fabric component includes 40 parts of polyurethane resin, three 2 15 parts of oxidations, 770 11 parts of light stabilizer, heat in parts by weight
15 parts of thermoplastic elastic, 12 parts of aqueous acrylic emulsion, 6 parts of tributoxyethyl phosphate, 8 parts of hydroxyethyl cellulose, flake asbestos 8
Part, 7 parts of silane coupler.
The preparation technology of the present embodiment comprises the following steps:
A, after aqueous acrylic emulsion, tributoxyethyl phosphate, hydroxyethyl cellulose, flake asbestos, silane coupler being mixed
The stirring of stirred tank high speed is added, stir speed (S.S.) is 3000 revs/min, mixing time 20min, obtains mixture A;
B, antimony oxide, light stabilizer 770, thermoplastic elastomer (TPE) are sequentially added in mixture A, low speed is carried out after mixing and is stirred
Mix, stir speed (S.S.) is 200 revs/min, time 10min, obtains mixture B;
C, polyurethane resin is finally added in mixture B, adds in kneading machine and is kneaded after mixing, melting temperature is 120 DEG C, when
Between be 30min, that is, obtain coating fabric.
Preparation technology of the present invention is simple, and obtained coating fabric has the advantages of excellent fire-retardant, heat-insulated, radiation proof;Its
In, the thermoplastic elastomer (TPE), the aqueous acrylic emulsion that are added in the present invention, it is possible to increase the toughness of fabric, improve its resistance to compression
Intensity;Hydroxyethyl cellulose, the flake asbestos of addition, it is possible to increase the anti-uv-ray of coating fabric.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
- A kind of 1. flame-retardant coating fabric, it is characterised in that:Coating fabric component includes polyurethane resin 30-50 in parts by weight Part, antimony oxide 10-20 parts, the 8-14 parts of light stabilizer 770, thermoplastic elastomer (TPE) 10-20 parts, aqueous acrylic emulsion 5- 16 parts, tributoxyethyl phosphate 3-9 parts, hydroxyethyl cellulose 4-12 parts, flake asbestos 5-10 parts, silane coupler 3-10 parts.
- A kind of 2. flame-retardant coating fabric according to claim 1, it is characterised in that:The preferable composition of coating fabric component is matched somebody with somebody Than including 40 parts of polyurethane resin, three 2 15 parts of oxidations, 770 11 parts of light stabilizer, 15 parts of thermoplastic elastomer (TPE), aqueous acrylamide 12 parts of yogurt liquid, 6 parts of tributoxyethyl phosphate, 8 parts of hydroxyethyl cellulose, 8 parts of flake asbestos, 7 parts of silane coupler.
- 3. realize a kind of preparation technology of flame-retardant coating fabric described in claim 1, it is characterised in that:Its preparation technology includes Following steps:A, after aqueous acrylic emulsion, tributoxyethyl phosphate, hydroxyethyl cellulose, flake asbestos, silane coupler being mixed The stirring of stirred tank high speed is added, stir speed (S.S.) is 3000 revs/min, mixing time 20min, obtains mixture A;B, antimony oxide, light stabilizer 770, thermoplastic elastomer (TPE) are sequentially added in mixture A, low speed is carried out after mixing and is stirred Mix, stir speed (S.S.) is 200 revs/min, time 10min, obtains mixture B;C, polyurethane resin is finally added in mixture B, adds in kneading machine and is kneaded after mixing, melting temperature is 120 DEG C, when Between be 30min, that is, obtain coating fabric.