CN107903524A - A kind of plastic processing toughener and its preparation process - Google Patents

A kind of plastic processing toughener and its preparation process Download PDF

Info

Publication number
CN107903524A
CN107903524A CN201711309697.0A CN201711309697A CN107903524A CN 107903524 A CN107903524 A CN 107903524A CN 201711309697 A CN201711309697 A CN 201711309697A CN 107903524 A CN107903524 A CN 107903524A
Authority
CN
China
Prior art keywords
parts
toughener
nano
preparation process
eps
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711309697.0A
Other languages
Chinese (zh)
Inventor
伊婕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711309697.0A priority Critical patent/CN107903524A/en
Publication of CN107903524A publication Critical patent/CN107903524A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of plastic processing toughener and its preparation process, toughener component includes 20 40 parts of expanded polystyrene (EPS) in parts by weight, 10 20 parts of silicon rubber, 5 10 parts of nano-titanium dioxide, 4 12 parts of nano silicon dioxide, 39 parts of white carbon, 10 20 parts of core shell structure polymer, 5 14 parts of maleic anhydride, 8 18 parts of silane coupling agent, 8 20 parts of crosslinking agent, 14 parts of antioxidant, preparation process of the present invention is simple, obtained toughener can carry out toughening modifying to plastic products, and there is environmental protection, the service life of plastic products can effectively be extended.

Description

A kind of plastic processing toughener and its preparation process
Technical field
The present invention relates to toughener preparing technical field, is specially a kind of plastic processing toughener and its preparation process.
Background technology
Plastics are using widely since invention, and the toughness of plastics is always people's concern, and toughener is A kind of additive in resin is added in order to reduce the brittleness after plastic hardening to improve its impact strength and elongation percentage.
Toughener can be divided into rubber toughener and thermoplastic elastomer (TPE) class toughener.Rubber toughener, mainly there is liquid Body polysulfide rubber, liquid polybutadiene rubber, nitrile rubber, EP rubbers and butadiene-styrene rubber etc..Thermoplastic elastomer (TPE), is a kind of Show at normal temperatures caoutchouc elasticity, at high temperature again can plasticizing forming synthetic material.
Current plastic processing is high with toughener cost of manufacture, and toughness reinforcing poor performance, can not effectively extend plastic products Service life.
The content of the invention
It is an object of the invention to provide a kind of plastic processing toughener and its preparation process, to solve above-mentioned background skill The problem of being proposed in art.
To achieve the above object, the present invention provides following technical solution:A kind of plastic processing toughener, toughener component Include 20-40 parts of expanded polystyrene (EPS), 10-20 parts of silicon rubber, 5-10 parts of nano-titanium dioxide, nanometer titanium dioxide in parts by weight 4-12 parts of silicon, 3-9 parts of white carbon, 10-20 parts of core shell structure polymer, 5-14 parts of maleic anhydride, 8-18 parts of silane coupling agent, friendship Join 8-20 parts of agent, 1-4 parts of antioxidant.
Preferably, the preferable composition proportion of toughener component includes 30 parts of expanded polystyrene (EPS), 15 part, nanometer two of silicon rubber It is 8 parts of titanium oxide, 8 parts of nano silicon dioxide, 6 parts of white carbon, 15 parts of core shell structure polymer, 10 parts of maleic anhydride, silane coupled 13 parts of agent, 14 parts of crosslinking agent, 3 parts of antioxidant.
Preferably, its preparation process comprises the following steps:
A, expanded polystyrene (EPS), silicon rubber, nano-titanium dioxide, nano silicon dioxide, white carbon, core shell structure polymer are mixed Stirring at low speed in stirred tank is added after conjunction, stir speed (S.S.) is 220 revs/min, and mixing time 18min, obtains mixture A;
B, maleic anhydride silane coupling agent, crosslinking agent, antioxidant are sequentially added in mixture A, adds and is kneaded after being sufficiently mixed It is kneaded in machine, melting temperature is 120 DEG C, obtains mixture B;
C, mixture B is slowly cooled to room temperature, stands 1h afterwards, that is, obtain toughener.
Compared with prior art, the beneficial effects of the invention are as follows:Preparation process of the present invention is simple, and obtained toughener can Toughening modifying is carried out to plastic products, and there is environmental protection, can effectively extend the service life of plastic products;Its In, the nano-titanium dioxide, nano silicon dioxide, the white carbon that are added in the present invention, can effectively improve the wear-resisting of toughener Performance, and then improve the wear-resisting property of plastic products;Obtained through overtesting, toughener tensile strength produced by the present invention reaches To 42MPA.
Embodiment
The technical solution in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment Only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this area Art personnel all other embodiments obtained without making creative work, belong to the model that the present invention protects Enclose.
The present invention provides following technical solution:A kind of plastic processing toughener, toughener component include in parts by weight 20-40 parts of expanded polystyrene (EPS), 10-20 parts of silicon rubber, 5-10 parts of nano-titanium dioxide, 4-12 parts of nano silicon dioxide, hard charcoal 3-9 parts black, 10-20 parts of core shell structure polymer, 5-14 parts of maleic anhydride, 8-18 parts of silane coupling agent, 8-20 parts of crosslinking agent, 1-4 parts of antioxidant.
Embodiment one:
Toughener component includes 20 parts of expanded polystyrene (EPS), 10 parts of silicon rubber, nano-titanium dioxide 5 part, nanometer in parts by weight 4 parts of silica, 3 parts of white carbon, 10 parts of core shell structure polymer, 5 parts of maleic anhydride, 8 parts of silane coupling agent, 8 parts of crosslinking agent , 1 part of antioxidant.
The preparation process of the present embodiment comprises the following steps:
A, expanded polystyrene (EPS), silicon rubber, nano-titanium dioxide, nano silicon dioxide, white carbon, core shell structure polymer are mixed Stirring at low speed in stirred tank is added after conjunction, stir speed (S.S.) is 220 revs/min, and mixing time 18min, obtains mixture A;
B, maleic anhydride silane coupling agent, crosslinking agent, antioxidant are sequentially added in mixture A, adds and is kneaded after being sufficiently mixed It is kneaded in machine, melting temperature is 120 DEG C, obtains mixture B;
C, mixture B is slowly cooled to room temperature, stands 1h afterwards, that is, obtain toughener.
Embodiment two:
Toughener component includes 40 parts of expanded polystyrene (EPS), 20 parts of silicon rubber, nano-titanium dioxide 10 part, nanometer in parts by weight 2 parts of silica 1,9 parts of white carbon, 20 parts of core shell structure polymer, 14 parts of maleic anhydride, 18 parts of silane coupling agent, crosslinking agent 20 parts, 4 parts of antioxidant.
The preparation process of the present embodiment comprises the following steps:
A, expanded polystyrene (EPS), silicon rubber, nano-titanium dioxide, nano silicon dioxide, white carbon, core shell structure polymer are mixed Stirring at low speed in stirred tank is added after conjunction, stir speed (S.S.) is 220 revs/min, and mixing time 18min, obtains mixture A;
B, maleic anhydride silane coupling agent, crosslinking agent, antioxidant are sequentially added in mixture A, adds and is kneaded after being sufficiently mixed It is kneaded in machine, melting temperature is 120 DEG C, obtains mixture B;
C, mixture B is slowly cooled to room temperature, stands 1h afterwards, that is, obtain toughener.
Embodiment three:
Toughener component includes 25 parts of expanded polystyrene (EPS), 12 parts of silicon rubber, nano-titanium dioxide 6 part, nanometer in parts by weight 6 parts of silica, 4 parts of white carbon, 12 parts of core shell structure polymer, 6 parts of maleic anhydride, 10 parts of silane coupling agent, 9 parts of crosslinking agent , 2 parts of antioxidant.
The preparation process of the present embodiment comprises the following steps:
A, expanded polystyrene (EPS), silicon rubber, nano-titanium dioxide, nano silicon dioxide, white carbon, core shell structure polymer are mixed Stirring at low speed in stirred tank is added after conjunction, stir speed (S.S.) is 220 revs/min, and mixing time 18min, obtains mixture A;
B, maleic anhydride silane coupling agent, crosslinking agent, antioxidant are sequentially added in mixture A, adds and is kneaded after being sufficiently mixed It is kneaded in machine, melting temperature is 120 DEG C, obtains mixture B;
C, mixture B is slowly cooled to room temperature, stands 1h afterwards, that is, obtain toughener.
Example IV:
Toughener component includes 38 parts of expanded polystyrene (EPS), 18 parts of silicon rubber, nano-titanium dioxide 9 part, nanometer in parts by weight 0 part of silica 1,8 parts of white carbon, 18 parts of core shell structure polymer, 12 parts of maleic anhydride, 16 parts of silane coupling agent, crosslinking agent 16 parts, 3 parts of antioxidant.
The preparation process of the present embodiment comprises the following steps:
A, expanded polystyrene (EPS), silicon rubber, nano-titanium dioxide, nano silicon dioxide, white carbon, core shell structure polymer are mixed Stirring at low speed in stirred tank is added after conjunction, stir speed (S.S.) is 220 revs/min, and mixing time 18min, obtains mixture A;
B, maleic anhydride silane coupling agent, crosslinking agent, antioxidant are sequentially added in mixture A, adds and is kneaded after being sufficiently mixed It is kneaded in machine, melting temperature is 120 DEG C, obtains mixture B;
C, mixture B is slowly cooled to room temperature, stands 1h afterwards, that is, obtain toughener.
Embodiment five:
Toughener component includes 30 parts of expanded polystyrene (EPS), 15 parts of silicon rubber, nano-titanium dioxide 8 part, nanometer in parts by weight 8 parts of silica, 6 parts of white carbon, 15 parts of core shell structure polymer, 10 parts of maleic anhydride, 13 parts of silane coupling agent, crosslinking agent 14 Part, 3 parts of antioxidant.
The preparation process of the present embodiment comprises the following steps:
A, expanded polystyrene (EPS), silicon rubber, nano-titanium dioxide, nano silicon dioxide, white carbon, core shell structure polymer are mixed Stirring at low speed in stirred tank is added after conjunction, stir speed (S.S.) is 220 revs/min, and mixing time 18min, obtains mixture A;
B, maleic anhydride silane coupling agent, crosslinking agent, antioxidant are sequentially added in mixture A, adds and is kneaded after being sufficiently mixed It is kneaded in machine, melting temperature is 120 DEG C, obtains mixture B;
C, mixture B is slowly cooled to room temperature, stands 1h afterwards, that is, obtain toughener.
Preparation process of the present invention is simple, and obtained toughener can carry out plastic products toughening modifying, and with environmental protection The advantages of, it can effectively extend the service life of plastic products;Wherein, the present invention in add nano-titanium dioxide, nanometer Silica, white carbon, can effectively improve the wear-resisting property of toughener, and then improve the wear-resisting property of plastic products; Obtained through overtesting, toughener tensile strength produced by the present invention reaches 42MPA.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of changes, modification, replace And modification, the scope of the present invention is defined by the appended.

Claims (3)

  1. A kind of 1. plastic processing toughener, it is characterised in that:Toughener component includes expanded polystyrene (EPS) 20- in parts by weight 40 parts, 10-20 parts of silicon rubber, 5-10 parts of nano-titanium dioxide, 4-12 parts of nano silicon dioxide, 3-9 parts of white carbon, core shell structure 10-20 parts of polymer, 5-14 parts of maleic anhydride, 8-18 parts of silane coupling agent, 8-20 parts of crosslinking agent, 1-4 parts of antioxidant.
  2. A kind of 2. plastic processing toughener according to claim 1, it is characterised in that:The preferable component of toughener component Proportioning includes 30 parts of expanded polystyrene (EPS), 15 parts of silicon rubber, 8 parts of nano-titanium dioxide, 8 parts of nano silicon dioxide, white carbon 6 Part, 15 parts of core shell structure polymer, 10 parts of maleic anhydride, 13 parts of silane coupling agent, 14 parts of crosslinking agent, 3 parts of antioxidant.
  3. 3. realize a kind of preparation process of plastic processing toughener described in claim 1, it is characterised in that:Its preparation process Comprise the following steps:
    A, expanded polystyrene (EPS), silicon rubber, nano-titanium dioxide, nano silicon dioxide, white carbon, core shell structure polymer are mixed Stirring at low speed in stirred tank is added after conjunction, stir speed (S.S.) is 220 revs/min, and mixing time 18min, obtains mixture A;
    B, maleic anhydride silane coupling agent, crosslinking agent, antioxidant are sequentially added in mixture A, adds and is kneaded after being sufficiently mixed It is kneaded in machine, melting temperature is 120 DEG C, obtains mixture B;
    C, mixture B is slowly cooled to room temperature, stands 1h afterwards, that is, obtain toughener.
CN201711309697.0A 2017-12-11 2017-12-11 A kind of plastic processing toughener and its preparation process Withdrawn CN107903524A (en)