CN107601971A - A kind of rub resistance automotive coatings and its preparation technology - Google Patents
A kind of rub resistance automotive coatings and its preparation technology Download PDFInfo
- Publication number
- CN107601971A CN107601971A CN201710971767.2A CN201710971767A CN107601971A CN 107601971 A CN107601971 A CN 107601971A CN 201710971767 A CN201710971767 A CN 201710971767A CN 107601971 A CN107601971 A CN 107601971A
- Authority
- CN
- China
- Prior art keywords
- parts
- automotive coatings
- added
- mixing
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of rub resistance automotive coatings and its preparation technology, automotive coatings component includes 20 40 parts of diatomite, 10 20 parts of expanded perlite, 5 15 parts of toughener, 4 10 parts of wood fibre, 39 parts of methylcellulose, 28 parts of nano titanium oxide, 10 20 parts of zirconia ceramics powder, 3 12 parts of titanium diboride, 4 10 parts of tungsten carbide powder, 29 parts of castor oil polyoxyethylene ether in parts by weight, preparation technology of the present invention is simple, obtained coating rub resistance, corrosion resistant, high-temperature resistant result are good, improve the performance of automobile.
Description
Technical field
The present invention relates to automotive coatings preparing technical field, specially a kind of rub resistance automotive coatings and its preparation technology.
Background technology
Automotive coatings are that coating once applies resulting solid-state continuous film, are the insulation in order to protect, the purpose of decoration,
The plastic sheet being coated on the matrixes such as metal, fabric, plastics.Coating can be gaseous state, liquid, solid-state, generally according to needs
The matrix of spraying determines the species and state of coating.Automotive coatings of the prior art are wear-resisting, corrosion resistant performance is poor.
The content of the invention
It is an object of the invention to provide a kind of rub resistance automotive coatings and its preparation technology, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides following technical scheme:A kind of rub resistance automotive coatings, automotive coatings component
Include diatomite 20-40 parts, expanded perlite 10-20 parts, toughener 5-15 parts, wood fibre 4-10 parts, first in parts by weight
Base cellulose 3-9 parts, nano titanium oxide 2-8 parts, zirconia ceramics powder 10-20 parts, titanium diboride 3-12 parts, tungsten carbide powder 4-
10 parts, castor oil polyoxyethylene ether 2-9 parts.
Preferably, the preferable composition proportion of automotive coatings component includes 30 parts of diatomite, 15 parts of expanded perlite, toughener
10 parts, 7 parts of wood fibre, 6 parts of methylcellulose, 5 parts of nano titanium oxide, 15 parts of zirconia ceramics powder, 8 parts of titanium diboride,
7 parts of tungsten carbide powder, 5 parts of castor oil polyoxyethylene ether.
Preferably, its preparation technology comprises the following steps:
A, by wood fibre, methylcellulose, nano titanium oxide, zirconia ceramics powder, titanium diboride, tungsten carbide powder, castor-oil plant
Stirring at low speed in stirred tank is added after oily APEO mixing, speed is 100 revs/min, time 30min, obtains mixture
A;
B, the stirring of stirred tank high speed is added after mixing diatomite, expanded perlite, toughener, mixing is added in whipping process
Thing A, stir speed (S.S.) are 3000 revs/min, mixing time 20min, obtain mixture B;
C, mixture B is added in kneading machine and be kneaded, temperature is 80 DEG C, time 40min, is cooled to room temperature afterwards, that is, obtains
Automotive coatings.
Compared with prior art, the beneficial effects of the invention are as follows:Preparation technology of the present invention is simple, obtained coating antifriction
Wiping, corrosion resistant, high-temperature resistant result are good, improve the performance of automobile;Wherein, the present invention in add zirconia ceramics powder, two
Titanium boride, tungsten carbide powder can improve the corrosion resistant and compressive property of coating, be effectively protected auto parts and components;That adds is wooden
Fiber, methylcellulose, it is possible to increase the toughness of coating;In addition, the preparation technology that the present invention uses is simple to operate, cost of manufacture
It is low, it can prevent material from caking phenomenon occur, influence performance.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
The present invention provides following technical scheme:A kind of rub resistance automotive coatings, automotive coatings component include in parts by weight
Diatomite 20-40 parts, expanded perlite 10-20 parts, toughener 5-15 parts, wood fibre 4-10 parts, methylcellulose 3-9 parts,
Nano titanium oxide 2-8 parts, zirconia ceramics powder 10-20 parts, titanium diboride 3-12 parts, tungsten carbide powder 4-10 parts, castor oil gather
Oxygen vinethene 2-9 parts.
Embodiment one:
Automotive coatings component includes 20 parts of diatomite, 10 parts of expanded perlite, 5 parts of toughener, wood fibre 4 in parts by weight
Part, 3 parts of methylcellulose, 2 parts of nano titanium oxide, 10 parts of zirconia ceramics powder, 3 parts of titanium diboride, 4 parts of tungsten carbide powder, castor
2 parts of sesame oil APEO.
The preparation technology of the present embodiment comprises the following steps:
A, by wood fibre, methylcellulose, nano titanium oxide, zirconia ceramics powder, titanium diboride, tungsten carbide powder, castor-oil plant
Stirring at low speed in stirred tank is added after oily APEO mixing, speed is 100 revs/min, time 30min, obtains mixture
A;
B, the stirring of stirred tank high speed is added after mixing diatomite, expanded perlite, toughener, mixing is added in whipping process
Thing A, stir speed (S.S.) are 3000 revs/min, mixing time 20min, obtain mixture B;
C, mixture B is added in kneading machine and be kneaded, temperature is 80 DEG C, time 40min, is cooled to room temperature afterwards, that is, obtains
Automotive coatings.
Embodiment two:
Automotive coatings component includes 40 parts of diatomite, 20 parts of expanded perlite, 15 parts of toughener, wood fibre 10 in parts by weight
Part, 9 parts of methylcellulose, 8 parts of nano titanium oxide, 20 parts of zirconia ceramics powder, 12 parts of titanium diboride, 10 parts of tungsten carbide powder,
9 parts of castor oil polyoxyethylene ether.
The preparation technology of the present embodiment comprises the following steps:
A, by wood fibre, methylcellulose, nano titanium oxide, zirconia ceramics powder, titanium diboride, tungsten carbide powder, castor-oil plant
Stirring at low speed in stirred tank is added after oily APEO mixing, speed is 100 revs/min, time 30min, obtains mixture
A;
B, the stirring of stirred tank high speed is added after mixing diatomite, expanded perlite, toughener, mixing is added in whipping process
Thing A, stir speed (S.S.) are 3000 revs/min, mixing time 20min, obtain mixture B;
C, mixture B is added in kneading machine and be kneaded, temperature is 80 DEG C, time 40min, is cooled to room temperature afterwards, that is, obtains
Automotive coatings.
Embodiment three:
Automotive coatings component includes 25 parts of diatomite, 12 parts of expanded perlite, 7 parts of toughener, wood fibre 5 in parts by weight
Part, 4 parts of methylcellulose, 3 parts of nano titanium oxide, 12 parts of zirconia ceramics powder, 5 parts of titanium diboride, 5 parts of tungsten carbide powder, castor
3 parts of sesame oil APEO.
The preparation technology of the present embodiment comprises the following steps:
A, by wood fibre, methylcellulose, nano titanium oxide, zirconia ceramics powder, titanium diboride, tungsten carbide powder, castor-oil plant
Stirring at low speed in stirred tank is added after oily APEO mixing, speed is 100 revs/min, time 30min, obtains mixture
A;
B, the stirring of stirred tank high speed is added after mixing diatomite, expanded perlite, toughener, mixing is added in whipping process
Thing A, stir speed (S.S.) are 3000 revs/min, mixing time 20min, obtain mixture B;
C, mixture B is added in kneading machine and be kneaded, temperature is 80 DEG C, time 40min, is cooled to room temperature afterwards, that is, obtains
Automotive coatings.
Example IV:
Automotive coatings component includes 35 parts of diatomite, 18 parts of expanded perlite, 14 parts of toughener, wood fibre 9 in parts by weight
Part, 8 parts of methylcellulose, 7 parts of nano titanium oxide, 16 parts of zirconia ceramics powder, 10 parts of titanium diboride, 9 parts of tungsten carbide powder, castor
8 parts of sesame oil APEO.
The preparation technology of the present embodiment comprises the following steps:
A, by wood fibre, methylcellulose, nano titanium oxide, zirconia ceramics powder, titanium diboride, tungsten carbide powder, castor-oil plant
Stirring at low speed in stirred tank is added after oily APEO mixing, speed is 100 revs/min, time 30min, obtains mixture
A;
B, the stirring of stirred tank high speed is added after mixing diatomite, expanded perlite, toughener, mixing is added in whipping process
Thing A, stir speed (S.S.) are 3000 revs/min, mixing time 20min, obtain mixture B;
C, mixture B is added in kneading machine and be kneaded, temperature is 80 DEG C, time 40min, is cooled to room temperature afterwards, that is, obtains
Automotive coatings.
Embodiment five:
Automotive coatings component includes 30 parts of diatomite, 15 parts of expanded perlite, 10 parts of toughener, wood fibre 7 in parts by weight
Part, 6 parts of methylcellulose, 5 parts of nano titanium oxide, 15 parts of zirconia ceramics powder, 8 parts of titanium diboride, 7 parts of tungsten carbide powder, castor
5 parts of sesame oil APEO.
The preparation technology of the present embodiment comprises the following steps:
A, by wood fibre, methylcellulose, nano titanium oxide, zirconia ceramics powder, titanium diboride, tungsten carbide powder, castor-oil plant
Stirring at low speed in stirred tank is added after oily APEO mixing, speed is 100 revs/min, time 30min, obtains mixture
A;
B, the stirring of stirred tank high speed is added after mixing diatomite, expanded perlite, toughener, mixing is added in whipping process
Thing A, stir speed (S.S.) are 3000 revs/min, mixing time 20min, obtain mixture B;
C, mixture B is added in kneading machine and be kneaded, temperature is 80 DEG C, time 40min, is cooled to room temperature afterwards, that is, obtains
Automotive coatings.
Preparation technology of the present invention is simple, and obtained coating rub resistance, corrosion resistant, high-temperature resistant result are good, improve making for automobile
Use performance;Wherein, the zirconia ceramics powder added in the present invention, titanium diboride, tungsten carbide powder can improve coating corrosion resistant and
Compressive property, it is effectively protected auto parts and components;Wood fibre, the methylcellulose of addition, it is possible to increase the toughness of coating;
In addition, the preparation technology that the present invention uses is simple to operate, it low manufacture cost, can prevent material from caking phenomenon occur, influence to make
Use performance.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
- A kind of 1. rub resistance automotive coatings, it is characterised in that:Automotive coatings component in parts by weight include diatomite 20-40 parts, Expanded perlite 10-20 parts, toughener 5-15 parts, wood fibre 4-10 parts, methylcellulose 3-9 parts, nano titanium oxide 2-8 Part, zirconia ceramics powder 10-20 parts, titanium diboride 3-12 parts, tungsten carbide powder 4-10 parts, castor oil polyoxyethylene ether 2-9 parts.
- A kind of 2. rub resistance automotive coatings according to claim 1, it is characterised in that:The preferable composition of automotive coatings component Proportioning includes 30 parts of diatomite, 15 parts of expanded perlite, 10 parts of toughener, 7 parts of wood fibre, part, nanometer two of methylcellulose 6 5 parts of titanium oxide, 15 parts of zirconia ceramics powder, 8 parts of titanium diboride, 7 parts of tungsten carbide powder, 5 parts of castor oil polyoxyethylene ether.
- 3. realize a kind of preparation technology of rub resistance automotive coatings described in claim 1, it is characterised in that:Its preparation technology bag Include following steps:A, by wood fibre, methylcellulose, nano titanium oxide, zirconia ceramics powder, titanium diboride, tungsten carbide powder, castor-oil plant Stirring at low speed in stirred tank is added after oily APEO mixing, speed is 100 revs/min, time 30min, obtains mixture A;B, the stirring of stirred tank high speed is added after mixing diatomite, expanded perlite, toughener, mixing is added in whipping process Thing A, stir speed (S.S.) are 3000 revs/min, mixing time 20min, obtain mixture B;C, mixture B is added in kneading machine and be kneaded, temperature is 80 DEG C, time 40min, is cooled to room temperature afterwards, that is, obtains Automotive coatings.