CN107746218A - A kind of green brick and its production method - Google Patents
A kind of green brick and its production method Download PDFInfo
- Publication number
- CN107746218A CN107746218A CN201711134440.6A CN201711134440A CN107746218A CN 107746218 A CN107746218 A CN 107746218A CN 201711134440 A CN201711134440 A CN 201711134440A CN 107746218 A CN107746218 A CN 107746218A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- mesh
- particle diameter
- green brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of green brick and its production method, belong to building material technical field.It is made up of the raw material of following parts by weight：6~12 parts of 4~16 parts of flyash, 6~12 parts of crushed crude pearlite, 8~16 parts of shale miberal powder, 6~12 parts of silicon powder, 5~15 parts of clay, 5~15 parts of zeolite powder and silicon nitride powder.The green brick compression strength of the present invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids second of pollution to environment.
Description
Technical field
The present invention relates to building material technical field, specifically, is to provide a kind of green brick and its production method.
Background technology
Traditional burned brick is mainly using clay as raw material.But with the continuous development of building trade, the demand of brick is progressively
Increase, existing clay resource can not meet the needs of brickmaking again, continuous reinforcement of the China for environmental protection in addition.Cause
This research and development is a kind of to replace clay, the green brick with superior performance to become urgent problem using other raw materials.
The content of the invention
An object of the present invention, it is to provide a kind of green brick.The green brick compression strength of the present invention is high, anti-
Folding endurance is good, cost is low, has effectively saved resource, avoids second of pollution to environment.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of green brick, by following parts by weight
Raw material is made：4~16 parts of flyash, 6~12 parts of crushed crude pearlite, 8~16 parts of shale miberal powder, 6~12 parts of silicon powder, clay 5~
6~12 parts of 15 parts, 5~15 parts of zeolite powder and silicon nitride powder.
The green brick compression strength of the present invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids
Second of pollution to environment.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight：10 parts of flyash, 9 parts of crushed crude pearlite, 12 parts of shale miberal powder,
9 parts of 9 parts of silicon powder, 10 parts of clay, 10 parts of zeolite powder and silicon nitride powder.
Further, the particle diameter of the flyash is 50~80 mesh, and the particle diameter of the crushed crude pearlite is 50~80 mesh, described,
The particle diameter of shale miberal powder is 50~80 mesh, and the particle diameter of the silicon powder is 50~80 mesh, and the particle diameter of the zeolite powder is 50~80
Mesh, the particle diameter of the silicon nitride powder is 50~80 mesh.
The second object of the present invention, it is to provide the production method of above-mentioned green brick.The production method of the present invention is simple,
Wide market, it is adapted to large-scale promotion.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of production method of green brick, including such as
Lower processing step：Take the raw material of following parts by weight：4~16 parts of flyash, 6~12 parts of crushed crude pearlite, shale miberal powder 8~16
Part, 6~12 parts of silicon powder, 5~15 parts of clay, 5~15 parts of zeolite powder and 6~12 parts of silicon nitride powder, after being well mixed, fully stir
Mix digestion 4~8 hours, be then pressed into type, finally the steam press maintenance under the conditions of 180~190 DEG C, 1~2MPa, that is, obtain described
Green brick.
The production method of the present invention is simple, wide market, is adapted to large-scale promotion.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the parts by weight of the raw material are：10 parts of flyash, 9 parts of crushed crude pearlite, 12 parts of shale miberal powder, silicon are micro-
9 parts of 9 parts of powder, 10 parts of clay, 10 parts of zeolite powder and silicon nitride powder.
Further, the particle diameter of the flyash is 50~80 mesh, and the particle diameter of the crushed crude pearlite is 50~80 mesh, described,
The particle diameter of shale miberal powder is 50~80 mesh, and the particle diameter of the silicon powder is 50~80 mesh, and the particle diameter of the zeolite powder is 50~80
Mesh, the particle diameter of the silicon nitride powder is 50~80 mesh.
The beneficial effects of the invention are as follows：
(1) green brick compression strength of the invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids
Second of pollution to environment.
(2) production method of the invention is simple, wide market, is adapted to large-scale production.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
Embodiment 1：
The green brick of the present embodiment, is made up of the raw material of following weight：Flyash 4kg, crushed crude pearlite 12kg, shale
Miberal powder 8kg, silicon powder 12kg, clay 5kg, zeolite powder 15kg and silicon nitride powder 6kg, wherein, the particle diameter of the flyash is 50
~80 mesh, the particle diameter of the silica flour are 50~80 mesh, and the particle diameter of the cinder is 50~80 mesh, the wheat stalk powder
The particle diameter at end is 50~80 mesh, and the particle diameter of the zeolite powder is 50~80 mesh, and the particle diameter of the calcium carbide waste slag is 50~80 mesh.
The production method of above-mentioned green brick, is comprised the technical steps that：Take the raw material of following weight：Flyash 4kg,
Crushed crude pearlite 12kg, shale miberal powder 8kg, silicon powder 12kg, clay 5kg, zeolite powder 15kg and silicon nitride powder 6kg, it is well mixed
Afterwards, digestion 4 hours is sufficiently stirred, is then pressed into type, finally the steam press maintenance under the conditions of 180 DEG C, 2.0MPa, that is, is obtained described
Green brick.
The green brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test,
Compression strength is 14.2MPa, rupture strength 3.2Mpa.
Embodiment 2：
The green brick of the present embodiment, is made up of the raw material of following weight：Flyash 10kg, crushed crude pearlite 9kg, shale
Miberal powder 12kg, silicon powder 9kg, clay 10kg, zeolite powder 10kg and silicon nitride powder 9kg, wherein, the particle diameter of the flyash is 50
~80 mesh, the particle diameter of the silica flour are 50~80 mesh, and the particle diameter of the cinder is 50~80 mesh, the wheat stalk powder
The particle diameter at end is 50~80 mesh, and the particle diameter of the zeolite powder is 50~80 mesh, and the particle diameter of the calcium carbide waste slag is 50~80 mesh.
The production method of above-mentioned green brick, is comprised the technical steps that：Take the raw material of following weight：Flyash
10kg, crushed crude pearlite 9kg, shale miberal powder 12kg, silicon powder 9kg, clay 10kg, zeolite powder 10kg and silicon nitride powder 9kg, mixing
After uniformly, digestion 6 hours is sufficiently stirred, is then pressed into type, finally the steam press maintenance under the conditions of 185 DEG C, 1.5MPa, that is, obtain
The green brick.
The green brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test,
Compression strength is 15.8MPa, rupture strength 3.8Mpa.
Embodiment 3：
The green brick of the present embodiment, is made up of the raw material of following weight：Flyash 16kg, crushed crude pearlite 6kg, shale
Miberal powder 16kg, silicon powder 6kg, clay 15kg, zeolite powder 5kg and silicon nitride powder 12kg, wherein, the particle diameter of the flyash is 50
~80 mesh, the particle diameter of the silica flour are 50~80 mesh, and the particle diameter of the cinder is 50~80 mesh, the wheat stalk powder
The particle diameter at end is 50~80 mesh, and the particle diameter of the zeolite powder is 50~80 mesh, and the particle diameter of the calcium carbide waste slag is 50~80 mesh.
The production method of above-mentioned green brick, is comprised the technical steps that：Take the raw material of following weight：Flyash
16kg, crushed crude pearlite 6kg, shale miberal powder 16kg, silicon powder 6kg, clay 15kg, zeolite powder 5kg and silicon nitride powder 12kg, mixing
After uniformly, digestion 8 hours is sufficiently stirred, is then pressed into type, finally the steam press maintenance under the conditions of 190 DEG C, 1MPa, that is, obtain institute
State green brick.
The green brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test,
Compression strength is 14.6MPa, rupture strength 3.3Mpa.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (6)
1. a kind of green brick, it is characterised in that be made up of the raw material of following parts by weight：4~16 parts of flyash, perlite
6~12 parts of powder, 8~16 parts of shale miberal powder, 6~12 parts of silicon powder, 5~15 parts of clay, 5~15 parts of zeolite powder and silicon nitride powder 6
~12 parts.
2. a kind of green brick according to claim 1, it is characterised in that be made up of the raw material of following parts by weight：
10 parts of flyash, 9 parts of crushed crude pearlite, 12 parts of shale miberal powder, 9 parts of silicon powder, 10 parts of clay, 10 parts of zeolite powder and silicon nitride powder 9
Part.
A kind of 3. green brick according to claim 1 or 2, it is characterised in that the particle diameter of the flyash be 50~
80 mesh, the particle diameter of the crushed crude pearlite is 50~80 mesh, and described, shale miberal powder particle diameter is 50~80 mesh, the silicon powder
Particle diameter is 50~80 mesh, and the particle diameter of the zeolite powder is 50~80 mesh, and the particle diameter of the silicon nitride powder is 50~80 mesh.
4. a kind of production method of green brick, it is characterised in that comprise the technical steps that：Take the original of following parts by weight
Material：4~16 parts of flyash, 6~12 parts of crushed crude pearlite, 8~16 parts of shale miberal powder, 6~12 parts of silicon powder, 5~15 parts of clay, boiling
6~12 parts of 5~15 parts of stone flour and silicon nitride powder, after being well mixed, it is sufficiently stirred digestion 4~8 hours, is then pressed into type, most
The steam press maintenance under the conditions of 180~190 DEG C, 1~2MPa afterwards, that is, obtain the green brick.
A kind of 5. production method of green brick according to claim 4, it is characterised in that the parts by weight of the raw material
Number is：10 parts of flyash, 9 parts of crushed crude pearlite, 12 parts of shale miberal powder, 9 parts of silicon powder, 10 parts of clay, 10 parts of zeolite powder and nitridation
9 parts of silica flour.
6. the production method of a kind of green brick according to claim 4 or 5, it is characterised in that the flyash
Particle diameter is 50~80 mesh, and the particle diameter of the crushed crude pearlite is 50~80 mesh, and described, shale miberal powder particle diameter is 50~80 mesh, institute
The particle diameter for stating silicon powder is 50~80 mesh, and the particle diameter of the zeolite powder is 50~80 mesh, the particle diameter of the silicon nitride powder for 50~
80 mesh.