CN107857518A - A kind of environmental protection and energy saving brick and its production method - Google Patents
A kind of environmental protection and energy saving brick and its production method Download PDFInfo
- Publication number
- CN107857518A CN107857518A CN201711134474.5A CN201711134474A CN107857518A CN 107857518 A CN107857518 A CN 107857518A CN 201711134474 A CN201711134474 A CN 201711134474A CN 107857518 A CN107857518 A CN 107857518A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- environmental protection
- mesh
- energy saving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection and energy saving brick and its production method, belong to building material technical field.It is made up of the raw material of following parts by weight:8~16 parts of 10~20 parts of spoil powder, 8~20 parts of river sand, 10~20 parts of building waste, 10~18 parts of zirconia powder, 10~20 parts of andalusite powder, 8~18 parts of Kaolin Tailings powder and attapulgite.The environmental protection and energy saving brick compression strength of the present invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids second of pollution to environment.
Description
Technical field
The present invention relates to building material technical field, specifically, is to provide a kind of environmental protection and energy saving brick and its production method.
Background technology
Traditional burned brick is mainly using clay as raw material.But with the continuous development of building trade, the demand of brick is progressively
Increase, existing clay resource can not meet the needs of brickmaking again, continuous reinforcement of the China for environmental protection in addition.Cause
This research and development is a kind of to replace clay, the environmental protection and energy saving brick with superior performance to become urgent problem using other raw materials.
The content of the invention
An object of the present invention, it is to provide a kind of environmental protection and energy saving brick.The environmental protection and energy saving brick compression strength of the present invention is high, anti-
Folding endurance is good, cost is low, has effectively saved resource, avoids second of pollution to environment.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:A kind of environmental protection and energy saving brick, by following parts by weight
Raw material is made:10~20 parts of spoil powder, 8~20 parts of river sand, 10~20 parts of building waste, 10~18 parts of zirconia powder, andalusite
8~16 parts of 10~20 parts of powder, 8~18 parts of kaolin soil mine tailing and attapulgite.
The environmental protection and energy saving brick compression strength of the present invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids
Second of pollution to environment.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight:15 parts of spoil powder, 14 parts of river sand, 15 parts of building waste, oxidation
12 parts of 14 parts of zirconium powder, 15 parts of andalusite powder, 13 parts of kaolin soil mine tailing and attapulgite.
Further, the particle diameter of the spoil powder is 40~60 mesh, and the particle diameter of the building waste is 40~60 mesh, the oxygen
The particle diameter for changing zirconium powder is 40~60 mesh, and the particle diameter of the andalusite powder is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is
40~60 mesh.
The second object of the present invention, it is to provide the production method of above-mentioned environmental protection and energy saving brick.The production method of the present invention is simple,
Wide market, it is adapted to large-scale promotion.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:A kind of production method of environmental protection and energy saving brick, including such as
Lower processing step:Take the raw material of following parts by weight:10~20 parts of spoil powder, 8~20 parts of river sand, 10~20 parts of building waste,
8~16 parts of 10~18 parts of zirconia powder, 10~20 parts of andalusite powder, 8~18 parts of kaolin soil mine tailing and attapulgite, mixing
After uniformly, it is sufficiently stirred digestion 3~8 hours, is then pressed into type, finally the steam pressure under the conditions of 180~190 DEG C, 1~1.2MPa
Maintenance, that is, obtain the environmental protection and energy saving brick.
The production method of the present invention is simple, wide market, is adapted to large-scale promotion.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the parts by weight of the raw material are:15 parts of spoil powder, 14 parts of river sand, 15 parts of building waste, zirconia powder
12 parts of 14 parts, 15 parts of andalusite powder, 13 parts of kaolin soil mine tailing and attapulgite.
Further, the particle diameter of the spoil powder is 40~60 mesh, and the particle diameter of the building waste is 40~60 mesh, the oxygen
The particle diameter for changing zirconium powder is 40~60 mesh, and the particle diameter of the andalusite powder is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is
40~60 mesh.
The beneficial effects of the invention are as follows:
(1) environmental protection and energy saving brick compression strength of the invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids
Second of pollution to environment.
(2) production method of the invention is simple, wide market, is adapted to large-scale production.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
Embodiment 1:
The environmental protection and energy saving brick of the present embodiment, is made up of the raw material of following weight:Spoil powder 10kg, river sand 20kg, building rubbish
Rubbish 10kg, zirconia powder 18kg, andalusite powder 10kg, kaolin soil mine tailing 18kg and attapulgite 8kg, wherein, the cash
The particle diameter of stone flour is 40~60 mesh, and the particle diameter of the building waste is 40~60 mesh, and the particle diameter of the zirconia powder is 40~60
Mesh, the particle diameter of the andalusite powder is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The production method of above-mentioned environmental protection and energy saving brick, is comprised the technical steps that:Take the raw material of following weight:Spoil powder
10kg, river sand 20kg, building waste 10kg, zirconia powder 18kg, andalusite powder 10kg, kaolin soil mine tailing 18kg and bumps
Rod soil 8kg, after being well mixed, digestion 3 hours is sufficiently stirred, is then pressed into type, finally the steam pressure under the conditions of 180 DEG C, 1MPa
Maintenance, that is, obtain the environmental protection and energy saving brick.
The environmental protection and energy saving brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test,
Compression strength is 13.5MPa, rupture strength 2.8Mpa.
Embodiment 2:
The environmental protection and energy saving brick of the present embodiment, is made up of the raw material of following weight:Spoil powder 15kg, river sand 14kg, building rubbish
Rubbish 15kg, zirconia powder 14kg, andalusite powder 15kg, kaolin soil mine tailing 13kg and attapulgite 12kg, wherein, the cash
The particle diameter of stone flour is 40~60 mesh, and the particle diameter of the building waste is 40~60 mesh, and the particle diameter of the zirconia powder is 40~60
Mesh, the particle diameter of the andalusite powder is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The production method of above-mentioned environmental protection and energy saving brick, is comprised the technical steps that:Take the raw material of following weight:Spoil powder
15kg, river sand 14kg, building waste 15kg, zirconia powder 14kg, andalusite powder 15kg, kaolin soil mine tailing 13kg and bumps
Rod soil 12kg, after being well mixed, digestion 5 hours is sufficiently stirred, type is then pressed into, is finally steamed under the conditions of 185 DEG C, 1.1MPa
Pressure maintenance, that is, obtain the environmental protection and energy saving brick.
The environmental protection and energy saving brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test,
Compression strength is 14.8MPa, rupture strength 4.0Mpa.
Embodiment 3:
The environmental protection and energy saving brick of the present embodiment, is made up of the raw material of following weight:Spoil powder 20kg, river sand 8kg, building waste
20kg, zirconia powder 10kg, andalusite powder 20kg, kaolin soil mine tailing 8kg and attapulgite 16kg, wherein, the useless brick
Watt particle diameter be 80~100 mesh, the particle diameter of the building waste is 40~60 mesh, and the particle diameter of the flyash is 40~60 mesh,
The particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The production method of above-mentioned environmental protection and energy saving brick, is comprised the technical steps that:Take the raw material of following weight:Spoil powder
20kg, river sand 8kg, building waste 20kg, zirconia powder 10kg, andalusite powder 20kg, kaolin soil mine tailing 8kg and concave convex rod
Native 16kg, after being well mixed, digestion 8 hours is sufficiently stirred, is then pressed into type, finally the steam pressure under the conditions of 190 DEG C, 1.2MPa
Maintenance, that is, obtain the environmental protection and energy saving brick.
The environmental protection and energy saving brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test,
Compression strength is 13.2MPa, rupture strength 3.0Mpa.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (6)
1. a kind of environmental protection and energy saving brick, it is characterised in that be made up of the raw material of following parts by weight:10~20 parts of spoil powder, river sand 8
~20 parts, 10~20 parts of building waste, 10~18 parts of zirconia powder, 10~20 parts of andalusite powder, 8~18 parts of Kaolin Tailings powder
With 8~16 parts of attapulgite.
2. a kind of environmental protection and energy saving brick according to claim 1, it is characterised in that be made up of the raw material of following parts by weight:
15 parts of spoil powder, 14 parts of river sand, 15 parts of building waste, 14 parts of zirconia powder, 15 parts of andalusite powder, 13 parts of kaolin soil mine tailing
With 12 parts of attapulgite.
A kind of 3. environmental protection and energy saving brick according to claim 1 or 2, it is characterised in that the particle diameter of the spoil powder be 40~
60 mesh, the particle diameter of the building waste is 40~60 mesh, and the particle diameter of the zirconia powder is 40~60 mesh, the andalusite powder
Particle diameter is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
4. a kind of production method of environmental protection and energy saving brick, it is characterised in that comprise the technical steps that:Take the original of following parts by weight
Material:10~20 parts of spoil powder, 8~20 parts of river sand, 10~20 parts of building waste, 10~18 parts of zirconia powder, andalusite powder 10~
8~16 parts of 20 parts, 8~18 parts of kaolin soil mine tailing and attapulgite, after being well mixed, it is sufficiently stirred digestion 3~8 hours,
Type is then pressed into, finally the steam press maintenance under the conditions of 180~190 DEG C, 1~1.2MPa, that is, obtains the environmental protection and energy saving brick.
A kind of 5. production method of environmental protection and energy saving brick according to claim 4, it is characterised in that the parts by weight of the raw material
Number is:15 parts of spoil powder, 14 parts of river sand, 15 parts of building waste, 14 parts of zirconia powder, 15 parts of andalusite powder, kaolin soil mine tailing
12 parts of 13 parts of powder and attapulgite.
6. the production method of a kind of environmental protection and energy saving brick according to claim 4 or 5, it is characterised in that the spoil powder
Particle diameter is 40~60 mesh, and the particle diameter of the building waste is 40~60 mesh, and the particle diameter of the zirconia powder is 40~60 mesh, described
The particle diameter of andalusite powder is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh.