CN106365593A - Environment-friendly brick and preparation method thereof - Google Patents
Environment-friendly brick and preparation method thereof Download PDFInfo
- Publication number
- CN106365593A CN106365593A CN201610747381.9A CN201610747381A CN106365593A CN 106365593 A CN106365593 A CN 106365593A CN 201610747381 A CN201610747381 A CN 201610747381A CN 106365593 A CN106365593 A CN 106365593A
- Authority
- CN
- China
- Prior art keywords
- parts
- particle diameter
- mesh
- environmental protection
- straw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly brick and a preparation method thereof, which belong to the technical field of building materials. The environment-friendly brick is prepared from the following raw materials in parts by weight: 10 to 20 parts of coal ash, 10 to 20 parts of river sand, 10 to 20 parts of building rubbish, 10 to 20 parts of coal gangue, 10 to 20 parts of straw and 10 to 20 parts of kaolin tail mineral powder. The environment-friendly brick provided by the invention is high in compressive strength, good in breaking resistance and low in cost, the resource is effectively saved, and the secondary pollution on the environment is avoided.
Description
Technical field
The present invention relates to building material technical field, specifically, it is that a kind of environmental protection brick and preparation method thereof is provided.
Background technology
Traditional burned brick is mainly with clay as raw material.But, with the continuous development of building trade, the demand of brick is progressively
Increase, existing clay resource can not meet the demand of brickmaking again, and China is for the continuous reinforcement of environmental conservation in addition.Cause
The environmental protection brick that this research and development is a kind of to replace clay using other raw materials, have a superior performance becomes urgent problem.
Content of the invention
An object of the present invention, is to provide a kind of environmental protection brick.The environmental protection brick comprcssive strength of the present invention is high, fold resistance is good,
Low cost, effectively saved resource, it is to avoid second pollution to environment.
The technical scheme is that a kind of environmental protection brick, by the raw material of following parts by weight
Make: 10～20 parts of flyash, 10～20 parts of fluvial sand, 10～20 parts of building waste, 10～20 parts of gangue, 10～20 parts of straw
With 10～20 parts of Kaolin Tailings powder.
The environmental protection brick comprcssive strength of the present invention is high, fold resistance is good, low cost, effectively saved resource, it is to avoid to ring
Second pollution in border.
On the basis of technique scheme, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight: 15 parts of flyash, 15 parts of fluvial sand, 15 parts of building waste, bastard coal
15 parts of stone, 15 parts of straw and 15 parts of Kaolin Tailings powder.
Further, the particle diameter of described flyash is 80～100 mesh, and the particle diameter of described building waste is 40～60 mesh, described
The particle diameter of gangue is 40～60 mesh, and the particle diameter of described straw is 0.5～1cm, the particle diameter of described Kaolin Tailings powder is 40～
60 mesh.
The second object of the present invention, is the preparation method providing above-mentioned environmental protection brick.The preparation method of the present invention is simple, market
Have a extensive future, suitable large-scale promotion.
The technical scheme is that a kind of preparation method of environmental protection brick, including following work
Skill step: take the raw material of following parts by weight: 10～20 parts of flyash, 10～20 parts of fluvial sand, 10～20 parts of building waste, bastard coal
10～20 parts of stone, 10～20 parts of straw and 10～20 parts of Kaolin Tailings powder, after mix homogeneously, are sufficiently stirred for digesting 2～6 little
When, it is then pressed into type, finally steam press maintenance under the conditions of 180～190 DEG C, 0.9～1.0mpa, that is, obtain described environmental protection brick.
The preparation method of the present invention is simple, wide market, suitable large-scale promotion.
On the basis of technique scheme, the present invention can also do following improvement.
Further, the parts by weight of described raw material are: 15 parts of flyash, 15 parts of fluvial sand, 15 parts of building waste, gangue 15
Part, 15 parts of straw and 15 parts of Kaolin Tailings powder.
Further, the particle diameter of described flyash is 80～100 mesh, and the particle diameter of described building waste is 40～60 mesh, described
The particle diameter of gangue is 40～60 mesh, and the particle diameter of described straw is 0.5～1cm, the particle diameter of described Kaolin Tailings powder is 40～
60 mesh.
The invention has the beneficial effects as follows:
(1) the environmental protection brick comprcssive strength of the present invention is high, fold resistance is good, low cost, has effectively saved resource, it is to avoid right
Second pollution of environment.
(2) preparation method of the present invention is simple, wide market, suitable large-scale production.
Specific embodiment
Below in conjunction with specific embodiment, the principle of the present invention and feature are described, example is served only for explaining this
Bright, it is not intended to limit the scope of the present invention.
Embodiment 1:
The environmental protection brick of the present embodiment, is made up of the raw material of following weight: flyash 10kg, fluvial sand 20kg, building waste
10kg, gangue 20kg, straw 10kg and Kaolin Tailings powder 20kg, wherein, the particle diameter of described flyash is 80～100 mesh,
The particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, the particle diameter of described straw is 0.5～
1cm, the particle diameter of described Kaolin Tailings powder is 40～60 mesh.
The preparation method of above-mentioned environmental protection brick, comprises the technical steps that: takes the raw material of following weight: flyash 10kg, river
Sand 20kg, building waste 10kg, gangue 20kg, straw 10kg and Kaolin Tailings powder 20kg, wherein, the grain of described flyash
Footpath is 80～100 mesh, and the particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, described straw
The particle diameter of stalk is 0.5～1cm, and the particle diameter of described Kaolin Tailings powder is 40～60 mesh, after mix homogeneously, is sufficiently stirred for digesting 2
Hour, it is then pressed into type, finally steam press maintenance under the conditions of 180 DEG C, 1.0mpa, that is, obtain described environmental protection brick.
Crushing resistance and fold resistance test, resistance to compression are carried out according to gb11945-1999 standard to environmental protection brick manufactured in the present embodiment
Intensity is 14.5mpa, and rupture strength is 3.5mpa.
Embodiment 2:
The environmental protection brick of the present embodiment, is made up of the raw material of following weight: flyash 15kg, fluvial sand 15kg, building waste
15kg, gangue 15kg, straw 15kg and Kaolin Tailings powder 25kg, wherein, the particle diameter of described flyash is 80～100 mesh,
The particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, the particle diameter of described straw is 0.5～
1cm, the particle diameter of described Kaolin Tailings powder is 40～60 mesh.
The preparation method of above-mentioned environmental protection brick, comprises the technical steps that: takes the raw material of following weight: flyash 15kg, river
Sand 15kg, building waste 15kg, gangue 15kg, straw 15kg and Kaolin Tailings powder 25kg, wherein, the grain of described flyash
Footpath is 80～100 mesh, and the particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, described straw
The particle diameter of stalk is 0.5～1cm, and the particle diameter of described Kaolin Tailings powder is 40～60 mesh, after mix homogeneously, is sufficiently stirred for digesting 4
Hour, it is then pressed into type, finally steam press maintenance under the conditions of 185 DEG C, 1.0mpa, that is, obtain described environmental protection brick.
Crushing resistance and fold resistance test, resistance to compression are carried out according to gb11945-1999 standard to environmental protection brick manufactured in the present embodiment
Intensity is 16.0mpa, and rupture strength is 3.9mpa.
Embodiment 3:
The environmental protection brick of the present embodiment, is made up of the raw material of following weight: flyash 20kg, fluvial sand 10kg, building waste
20kg, gangue 10kg, straw 20kg and Kaolin Tailings powder 10kg, wherein, the particle diameter of described flyash is 80～100 mesh,
The particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, the particle diameter of described straw is 0.5～
1cm, the particle diameter of described Kaolin Tailings powder is 40～60 mesh.
The preparation method of above-mentioned environmental protection brick, comprises the technical steps that: takes the raw material of following weight: flyash 20kg, river
Sand 10kg, building waste 20kg, gangue 10kg, straw 20kg and Kaolin Tailings powder 10kg, wherein, the grain of described flyash
Footpath is 80～100 mesh, and the particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, described straw
The particle diameter of stalk is 0.5～1cm, and the particle diameter of described Kaolin Tailings powder is 40～60 mesh, after mix homogeneously, is sufficiently stirred for digesting 6
Hour, it is then pressed into type, finally steam press maintenance under the conditions of 190 DEG C, 0.9mpa, that is, obtain described environmental protection brick.
Crushing resistance and fold resistance test, resistance to compression are carried out according to gb11945-1999 standard to environmental protection brick manufactured in the present embodiment
Intensity is 14.1mpa, and rupture strength is 3.2mpa.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement made etc., should be included within the scope of the present invention.
Claims (6)
1. a kind of environmental protection brick is it is characterised in that be made up of the raw material of following parts by weight: 10～20 parts of flyash, fluvial sand 10～
20 parts, 10～20 parts of building waste, 10～20 parts of gangue, 10～20 parts of straw and 10～20 parts of Kaolin Tailings powder.
2. a kind of environmental protection brick according to claim 1 is it is characterised in that be made up of the raw material of following parts by weight: fine coal
15 parts of ash, 15 parts of fluvial sand, 15 parts of building waste, 15 parts of gangue, 15 parts of straw and 15 parts of Kaolin Tailings powder.
3. a kind of environmental protection brick according to claim 1 and 2 is it is characterised in that the particle diameter of described flyash is 80～100
Mesh, the particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, and the particle diameter of described straw is
0.5～1cm, the particle diameter of described Kaolin Tailings powder is 40～60 mesh.
4. a kind of preparation method of environmental protection brick is it is characterised in that comprise the technical steps that: takes the raw material of following parts by weight:
10～20 parts of flyash, 10～20 parts of fluvial sand, 10～20 parts of building waste, 10～20 parts of gangue, 10～20 parts of straw and height
Ridge 10～20 parts of mine tailing of soil, after mix homogeneously, is sufficiently stirred for digesting 2～6 hours, is then pressed into type, finally 180～
190 DEG C, steam press maintenance under the conditions of 0.9～1.0mpa, that is, obtain described environmental protection brick.
5. a kind of preparation method of environmental protection brick according to claim 4 is it is characterised in that the parts by weight of described raw material
For: 15 parts of flyash, 15 parts of fluvial sand, 15 parts of building waste, 15 parts of gangue, 15 parts of straw and 15 parts of Kaolin Tailings powder.
6. a kind of preparation method of the environmental protection brick according to claim 4 or 5 is it is characterised in that the particle diameter of described flyash
For 80～100 mesh, the particle diameter of described building waste is 40～60 mesh, and the particle diameter of described gangue is 40～60 mesh, described straw
Particle diameter be 0.5～1cm, the particle diameter of described Kaolin Tailings powder is 40～60 mesh.