CN107216078A - A kind of concrete road pavement brick and preparation method thereof - Google Patents
A kind of concrete road pavement brick and preparation method thereof Download PDFInfo
- Publication number
- CN107216078A CN107216078A CN201710471095.9A CN201710471095A CN107216078A CN 107216078 A CN107216078 A CN 107216078A CN 201710471095 A CN201710471095 A CN 201710471095A CN 107216078 A CN107216078 A CN 107216078A
- Authority
- CN
- China
- Prior art keywords
- parts
- road pavement
- waste
- concrete road
- stalk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of concrete road pavement brick, includes the raw material of following parts by weight:20~30 parts of cement, 8~10 parts of stone, 15~25 parts of quartz sand, 13~18 parts of building waste, 8~13 parts of stalk, 15~22 parts of water, 3~7 parts of water reducer, 5~8 parts of VAE emulsions, 15~22 parts of epoxy resin fiberglass granulated slag;Its preparation method comprises the following steps:Building waste, epoxy resin fiberglass granulated slag are pulverized and mixed, and water, water reducer, the mixing of VAE emulsions, the aqueous solution are mixed into pavior brick slurry with material stirring, and by the first low-frequency high-amplitude vibration of pavior brick slurry, the concrete road pavement brick is made in pressure head extrusion forming again.Concrete floor brick cost of the present invention is low, performance is good, and service life is long;Preparation method technique of the present invention is simple, be adapted to promote.
Description
Technical field
The invention belongs to building material technical field, and in particular to a kind of concrete road pavement brick and preparation method thereof.
Background technology
Concrete road pavement brick is with cement and gathered materials for main raw material(s) that processed, vibration is pressurizeed or other moulding process
It is made, for laying the concrete road surface of urban road pavement, city square etc. and the block of ground surface works, plate etc..But this
The raw material for planting pavior brick are very big to the stone of nature and the demand of sand, and the exploitation to natural environment is extremely relied on, this
Serious influence is brought to ecological environment;Also, due to making to gather materials using these natural stones and sand, it result in road surface
The intensity of brick is relatively low, and service life is not long, and on the larger road surface of flow of the people, the breakage rate of pavior brick is very high, and people are also frequent
The time every 1~2 year can be found, these road surfaces will lay new pavior brick again by renovating, and cause manpower and financial resources
Waste.
If but using some there is the high performance additive face brick that goes to satisfy the need to be modified, then it must can cause pavior brick
Manufacturing cost rise, and the product that pavior brick is originally dirt cheap after its terminal price rises, must can influence it to push away
Wide application.
Therefore, the Improvement requirement for the face brick that satisfies the need how is met with a kind of inexpensive improved procedure to be become at present urgently
The problem of solution.
The content of the invention
The invention provides a kind of concrete road pavement brick and preparation method thereof, the concrete floor brick cost is low, performance
Good, service life is long.
In order to solve the problem of prior art is present, adopt the following technical scheme that:
A kind of concrete road pavement brick, includes the raw material of following parts by weight:20~30 parts of cement, 8~10 parts of stone, quartz sand 15~
25 parts, 13~18 parts of building waste, 8~13 parts of stalk, 15~22 parts of water, 3~7 parts of water reducer, 5~8 parts of VAE emulsions, epoxy
15~22 parts of plexiglas fiber granulated slag.
It is preferred that, the concrete road pavement brick includes the raw material of following parts by weight:23~27 parts of cement, stone 9~10
Part, 22~24 parts of quartz sand, 14~16 parts of building waste, 10~12 parts of stalk, 19~21 parts of water, 4~6 parts of water reducer, VAE breast
6~8 parts of liquid, 18~21 parts of epoxy resin fiberglass granulated slag.
It is preferred that, the concrete road pavement brick includes the raw material of following parts by weight:24 parts of cement, 9 parts of stone, quartz sand
23 parts, 15 parts of building waste, 11 parts of stalk, 20 parts of water, 5 parts of water reducer, 7 parts of VAE emulsions, epoxy resin fiberglass granulated slag 19
Part.
It is preferred that, the building waste be waste concrete block, useless crushed stone, useless brick and tile fragment, waste mortar, waste plastics it is mixed
Compound.
It is preferred that, the waste concrete block, useless crushed stone, the mass ratio of useless brick and tile fragment, waste mortar and waste plastics are 1:
2:1:1:0.5。
It is preferred that, the stalk is the rhizome of crops, through drying, the graininess straw for crushing, shearing and being obtained after scattered
Stalk.
A kind of method for preparing the concrete road pavement brick, comprises the following steps:
(1)Building waste and epoxy resin fiberglass granulated slag are respectively placed in pulverizer and crushed, 100 mesh sieves is crossed, then mixes
Close uniform, obtained mixed material A is standby;
(2)Water is well mixed with water reducer, VAE emulsions mixed aqueous solution B is made, be divided into three parts, it is standby;
(3)Cement, quartz sand are put into mixer, stirred 10~20 minutes, a mixing water is added during stirring
Solution B, is stirring evenly and then adding into stone, mixed material A, stirs 10~20 minutes, adds a mixed aqueous solution B, and stirring is equal
Stalk, mixed aqueous solution B are added after even, stirs 40~60 minutes, obtains mixed material C;
(4)Mixed material C is placed in mould, pressure head is press-formed again for first low-frequency high-amplitude vibration, is then put in curing room and is supported
Shield 7~10 days, the demoulding, you can obtain the concrete road pavement brick.
It is preferred that, the frequency of low-frequency high-amplitude vibration is per minute to be less than 10 times, amplitude is highly more than 0.1 meter.
Compared with prior art, it has the advantages that the present invention:
Concrete floor brick cost of the present invention is low, performance is good, and service life is long;Preparation method technique of the present invention
Simply, it is adapted to promote, it is specific as follows:
(1)Concrete floor brick of the present invention, as raw material, reduces cost of material using stalk and building waste, develops
The new application of stalk and building waste, solves the problem of building waste processing is difficult, it is to avoid straw burning pollution environment
Phenomenon, reduce Environmental costs;
(2)Water reducer, VAE emulsions, stalk are added in concrete floor brick of the present invention, the concrete ground is improved
The performance of brick, adds its service life;
(3)Preparation method of the present invention is vibrated again using low-frequency high-amplitude by the way of pressure head extrusion forming so that prepare
Concrete floor brick, intensity is big, and service life is long;
(4)Preparation method of the present invention is low for equipment requirements, is adapted to promote.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
The present embodiment is related to a kind of concrete road pavement brick, includes the raw material of following parts by weight:20 parts of cement, 8 parts of stone, quartz sand
15 parts, 13 parts of building waste, 8 parts of stalk, 15 parts of water, 3 parts of water reducer, 5 parts of VAE emulsions, epoxy resin fiberglass granulated slag 15
Part.
Wherein, the building waste is waste concrete block, useless crushed stone, useless brick and tile fragment, waste mortar, the mixing of waste plastics
Thing.
Wherein, the waste concrete block, useless crushed stone, the mass ratio of useless brick and tile fragment, waste mortar and waste plastics are 1:2:
1:1:0.5。
Wherein, the stalk is the rhizome of crops, through drying, the graininess stalk for crushing, shearing and being obtained after scattered.
A kind of method for preparing the concrete road pavement brick, comprises the following steps:
(1)Building waste and epoxy resin fiberglass granulated slag are respectively placed in pulverizer and crushed, 100 mesh sieves is crossed, then mixes
Close uniform, obtained mixed material A is standby;
(2)Water is well mixed with water reducer, VAE emulsions mixed aqueous solution B is made, be divided into three parts, it is standby;
(3)Cement, quartz sand are put into mixer, stirred 10 minutes, a mixed aqueous solution is added during stirring
B, is stirring evenly and then adding into stone, mixed material A, stirs 10 minutes, adds a mixed aqueous solution B, is stirring evenly and then adding into
Stalk, mixed aqueous solution B, stir 40 minutes, obtain mixed material C;
(4)Mixed material C is placed in mould, pressure head is press-formed again for first low-frequency high-amplitude vibration, is then put in curing room and is supported
Shield 7 days, the demoulding, you can obtain the concrete road pavement brick.
Wherein, 20 times per minute of the frequency of the low-frequency high-amplitude vibration, amplitude are highly 0.2 meter.
Embodiment 2
The present embodiment is related to a kind of concrete road pavement brick, includes the raw material of following parts by weight:30 parts of cement, 10 parts of stone, quartz
25 parts of sand, 18 parts of building waste, 13 parts of stalk, 22 parts of water, 7 parts of water reducer, 8 parts of VAE emulsions, epoxy resin fiberglass granulated slag
22 parts.
Wherein, the building waste is waste concrete block, useless crushed stone, useless brick and tile fragment, waste mortar, the mixing of waste plastics
Thing.
Wherein, the waste concrete block, useless crushed stone, the mass ratio of useless brick and tile fragment, waste mortar and waste plastics are 1:2:
1:1:0.5。
Wherein, the stalk is the rhizome of crops, through drying, the graininess stalk for crushing, shearing and being obtained after scattered.
A kind of method for preparing the concrete road pavement brick, comprises the following steps:
(1)Building waste and epoxy resin fiberglass granulated slag are respectively placed in pulverizer and crushed, 100 mesh sieves is crossed, then mixes
Close uniform, obtained mixed material A is standby;
(2)Water is well mixed with water reducer, VAE emulsions mixed aqueous solution B is made, be divided into three parts, it is standby;
(3)Cement, quartz sand are put into mixer, stirred 20 minutes, a mixed aqueous solution is added during stirring
B, is stirring evenly and then adding into stone, mixed material A, stirs 20 minutes, adds a mixed aqueous solution B, is stirring evenly and then adding into
Stalk, mixed aqueous solution B, stir 60 minutes, obtain mixed material C;
(4)Mixed material C is placed in mould, pressure head is press-formed again for first low-frequency high-amplitude vibration, is then put in curing room and is supported
Shield 7~10 days, the demoulding, you can obtain the concrete road pavement brick.
Wherein, the frequency of low-frequency high-amplitude vibration be 10 times per minute, amplitude be highly 0.1 meter.
Embodiment 3
The present embodiment is related to a kind of concrete road pavement brick, includes the raw material of following parts by weight:23 parts of cement, 9 parts of stone, quartz sand
22 parts, 14 parts of building waste, 10 parts of stalk, 19 parts of water, 4 parts of water reducer, 6 parts of VAE emulsions, epoxy resin fiberglass granulated slag 18
Part.
Wherein, the building waste is waste concrete block, useless crushed stone, useless brick and tile fragment, waste mortar, the mixing of waste plastics
Thing.
Wherein, the waste concrete block, useless crushed stone, the mass ratio of useless brick and tile fragment, waste mortar and waste plastics are 1:2:
1:1:0.5。
Wherein, the stalk is the rhizome of crops, through drying, the graininess stalk for crushing, shearing and being obtained after scattered.
A kind of method for preparing the concrete road pavement brick, comprises the following steps:
(1)Building waste and epoxy resin fiberglass granulated slag are respectively placed in pulverizer and crushed, 100 mesh sieves is crossed, then mixes
Close uniform, obtained mixed material A is standby;
(2)Water is well mixed with water reducer, VAE emulsions mixed aqueous solution B is made, be divided into three parts, it is standby;
(3)Cement, quartz sand are put into mixer, stirred 15 minutes, a mixed aqueous solution is added during stirring
B, is stirring evenly and then adding into stone, mixed material A, stirs 12 minutes, adds a mixed aqueous solution B, is stirring evenly and then adding into
Stalk, mixed aqueous solution B, stir 42 minutes, obtain mixed material C;
(4)Mixed material C is placed in mould, pressure head is press-formed again for first low-frequency high-amplitude vibration, is then put in curing room and is supported
Shield 9 days, the demoulding, you can obtain the concrete road pavement brick.
Wherein, 15 times per minute of the frequency of the low-frequency high-amplitude vibration, amplitude are highly 0.15 meter.
Embodiment 4
The present embodiment is related to a kind of concrete road pavement brick, includes the raw material of following parts by weight:27 parts of cement, 10 parts of stone, quartz
24 parts of sand, 16 parts of building waste, 12 parts of stalk, 21 parts of water, 6 parts of water reducer, 8 parts of VAE emulsions, epoxy resin fiberglass granulated slag
21 parts.
Wherein, the building waste is waste concrete block, useless crushed stone, useless brick and tile fragment, waste mortar, the mixing of waste plastics
Thing.
Wherein, the waste concrete block, useless crushed stone, the mass ratio of useless brick and tile fragment, waste mortar and waste plastics are 1:2:
1:1:0.5。
Wherein, the stalk is the rhizome of crops, through drying, the graininess stalk for crushing, shearing and being obtained after scattered.
A kind of method for preparing the concrete road pavement brick, comprises the following steps:
(1)Building waste and epoxy resin fiberglass granulated slag are respectively placed in pulverizer and crushed, 100 mesh sieves is crossed, then mixes
Close uniform, obtained mixed material A is standby;
(2)Water is well mixed with water reducer, VAE emulsions mixed aqueous solution B is made, be divided into three parts, it is standby;
(3)Cement, quartz sand are put into mixer, stirred 18 minutes, a mixed aqueous solution is added during stirring
B, is stirring evenly and then adding into stone, mixed material A, stirs 15 minutes, adds a mixed aqueous solution B, is stirring evenly and then adding into
Stalk, mixed aqueous solution B, stir 50 minutes, obtain mixed material C;
(4)Mixed material C is placed in mould, pressure head is press-formed again for first low-frequency high-amplitude vibration, is then put in curing room and is supported
Shield 8 days, the demoulding, you can obtain the concrete road pavement brick.
Wherein, the frequency of low-frequency high-amplitude vibration be 30 times per minute, amplitude be highly 0.3 meter.
Embodiment 5
The present embodiment is related to a kind of concrete road pavement brick, includes the raw material of following parts by weight:24 parts of cement, 9 parts of stone, quartz sand
23 parts, 15 parts of building waste, 11 parts of stalk, 20 parts of water, 5 parts of water reducer, 7 parts of VAE emulsions, epoxy resin fiberglass granulated slag 19
Part.
Wherein, the building waste is waste concrete block, useless crushed stone, useless brick and tile fragment, waste mortar, the mixing of waste plastics
Thing.
Wherein, the waste concrete block, useless crushed stone, the mass ratio of useless brick and tile fragment, waste mortar and waste plastics are 1:2:
1:1:0.5。
Wherein, the stalk is the rhizome of crops, through drying, the graininess stalk for crushing, shearing and being obtained after scattered.
A kind of method for preparing the concrete road pavement brick, comprises the following steps:
(1)Building waste and epoxy resin fiberglass granulated slag are respectively placed in pulverizer and crushed, 100 mesh sieves is crossed, then mixes
Close uniform, obtained mixed material A is standby;
(2)Water is well mixed with water reducer, VAE emulsions mixed aqueous solution B is made, be divided into three parts, it is standby;
(3)Cement, quartz sand are put into mixer, stirred 15 minutes, a mixed aqueous solution is added during stirring
B, is stirring evenly and then adding into stone, mixed material A, stirs 18 minutes, adds a mixed aqueous solution B, is stirring evenly and then adding into
Stalk, mixed aqueous solution B, stir 55 minutes, obtain mixed material C;
(4)Mixed material C is placed in mould, pressure head is press-formed again for first low-frequency high-amplitude vibration, is then put in curing room and is supported
Shield 9 days, the demoulding, you can obtain the concrete road pavement brick.
Wherein, the frequency of low-frequency high-amplitude vibration be 30 times per minute, amplitude be highly 0.3 meter.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of concrete road pavement brick, it is characterised in that include the raw material of following parts by weight:20~30 parts of cement, stone 8~10
Part, 15~25 parts of quartz sand, 13~18 parts of building waste, 8~13 parts of stalk, 15~22 parts of water, 3~7 parts of water reducer, VAE breast
5~8 parts of liquid, 15~22 parts of epoxy resin fiberglass granulated slag.
2. concrete road pavement brick according to claim 1, it is characterised in that include the raw material of following parts by weight:Cement 23
~27 parts, 9~10 parts of stone, 22~24 parts of quartz sand, 14~16 parts of building waste, 10~12 parts of stalk, 19~21 parts of water, subtract
4~6 parts of aqua, 6~8 parts of VAE emulsions, 18~21 parts of epoxy resin fiberglass granulated slag.
3. concrete road pavement brick according to claim 1, it is characterised in that include the raw material of following parts by weight:Cement 24
Part, 9 parts of stone, 23 parts of quartz sand, 15 parts of building waste, 11 parts of stalk, 20 parts of water, 5 parts of water reducer, 7 parts of VAE emulsions, epoxy
19 parts of plexiglas fiber granulated slag.
4. concrete road pavement brick according to claim 1, it is characterised in that the building waste is waste concrete block, given up
Crushed stone, useless brick and tile fragment, waste mortar, the mixture of waste plastics.
5. concrete road pavement brick according to claim 4, it is characterised in that the waste concrete block, useless crushed stone, useless brick
The mass ratio of watt fragment, waste mortar and waste plastics is 1:2:1:1:0.5.
6. concrete road pavement brick according to claim 1, it is characterised in that the stalk is the rhizome of crops, through drying in the air
Graininess stalk that is dry, crushing, shear and obtained after scattered.
7. a kind of method for preparing any one of claim 1~6 concrete road pavement brick, it is characterised in that including following step
Suddenly:
(1)Building waste and epoxy resin fiberglass granulated slag are respectively placed in pulverizer and crushed, 100 mesh sieves is crossed, then mixes
Close uniform, obtained mixed material A is standby;
(2)Water is well mixed with water reducer, VAE emulsions mixed aqueous solution B is made, be divided into three parts, it is standby;
(3)Cement, quartz sand are put into mixer, stirred 10~20 minutes, a mixing water is added during stirring
Solution B, is stirring evenly and then adding into stone, mixed material A, stirs 10~20 minutes, adds a mixed aqueous solution B, and stirring is equal
Stalk, mixed aqueous solution B are added after even, stirs 40~60 minutes, obtains mixed material C;
(4)Mixed material C is placed in mould, pressure head is press-formed again for first low-frequency high-amplitude vibration, is then put in curing room and is supported
Shield 7~10 days, the demoulding, you can obtain the concrete road pavement brick.
8. preparation method according to claim 7, it is characterised in that the frequency of the low-frequency high-amplitude vibration is per minute to be less than
10 times, amplitude highly be more than 0.1 meter.