CN107777945A - A kind of environmental protection brick and its production method - Google Patents
A kind of environmental protection brick and its production method Download PDFInfo
- Publication number
- CN107777945A CN107777945A CN201710982119.7A CN201710982119A CN107777945A CN 107777945 A CN107777945 A CN 107777945A CN 201710982119 A CN201710982119 A CN 201710982119A CN 107777945 A CN107777945 A CN 107777945A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- environmental protection
- mesh
- particle diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection brick and its production method, belong to building material technical field.It is made up of the raw material of following parts by weight：3~9 parts of 6~12 parts of clinker, 4~10 parts of river sand, 3~9 parts of building waste, 5~15 parts of colliery powder, 4~10 parts of andalusite powder, 5~9 parts of granite tailings, 8~16 parts of zirconia powder and Kaolin Tailings powder.The environmental protection brick compression strength of the present invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids second of pollution to environment.
Description
Technical field
The present invention relates to building material technical field, specifically, is to provide a kind of environmental protection brick and its production method.
Background technology
Traditional burned brick is mainly using clay as raw material.But with the continuous development of building trade, the demand of brick is progressively
Increase, existing clay resource can not meet the needs of brickmaking again, continuous reinforcement of the China for environmental protection in addition.Cause
This research and development is a kind of to replace clay, the environmental protection brick with superior performance to become urgent problem using other raw materials.
The content of the invention
An object of the present invention, it is to provide a kind of environmental protection brick.The environmental protection brick compression strength of the present invention is high, fold resistance is good,
Cost is low, has effectively saved resource, avoids second of pollution to environment.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of environmental protection brick, by the raw material of following parts by weight
It is made：6~12 parts of clinker, 4~10 parts of river sand, 3~9 parts of building waste, 5~15 parts of colliery powder, 4~10 parts of andalusite powder,
3~9 parts of 5~9 parts of granite tailings, 8~16 parts of zirconia powder and Kaolin Tailings powder.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight：9 parts of clinker, 7 parts of river sand, 6 parts of building waste, colliery powder
6 parts of 10 parts, 7 parts of andalusite powder, 7 parts of granite tailings, 12 parts of zirconia powder and Kaolin Tailings powder.
Further, the particle diameter of the clinker is 80~100 mesh, and the particle diameter of the building waste is 60~100 mesh, the coal
The particle diameter of spoil powder is 40~80 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The second object of the present invention, it is to provide the production method of above-mentioned environmental protection brick.The production method of the present invention is simple, market
Have a extensive future, be adapted to large-scale promotion.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of production method of environmental protection brick, including following work
Skill step：Take the raw material of following parts by weight：6~12 parts of clinker, 4~10 parts of river sand, 3~9 parts of building waste, colliery powder 5
3~9 parts of~15 parts, 4~10 parts of andalusite powder, 5~9 parts of granite tailings, 8~16 parts of zirconia powder and Kaolin Tailings powder,
After well mixed, it is sufficiently stirred digestion 4~8 hours, is then pressed into type, finally under the conditions of 160~180 DEG C, 1~1.6MPa
Steam press maintenance, that is, obtain the environmental protection brick.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the parts by weight of the raw material are：9 parts of clinker, 7 parts of river sand, 6 parts of building waste, 10 parts of colliery powder,
6 parts of 7 parts of andalusite powder, 7 parts of granite tailings, 12 parts of zirconia powder and Kaolin Tailings powder.
Further, the particle diameter of the clinker is 80~100 mesh, and the particle diameter of the building waste is 60~100 mesh, the coal
The particle diameter of spoil powder is 40~80 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The beneficial effects of the invention are as follows：
(1) environmental protection brick compression strength of the invention is high, fold resistance is good, cost is low, has effectively saved resource, avoids pair
Second of pollution of environment.
(2) production method of the invention is simple, wide market, is adapted to large-scale production.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
Embodiment 1：
The environmental protection brick of the present embodiment, it is made up of the raw material of following weight：Clinker 6kg, river sand 10kg, building waste 3kg, coal
Spoil powder 15kg, andalusite powder 4kg, granite tailings 9kg, zirconia powder 8kg and Kaolin Tailings powder 9kg, wherein, the stove
The particle diameter of slag is 80~100 mesh, and the particle diameter of the building waste is 60~100 mesh, and the particle diameter of the colliery powder is 40~80
Mesh, the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The production method of above-mentioned environmental protection brick, is comprised the technical steps that：Take the raw material of following weight：Clinker 6kg, river sand
10kg, building waste 3kg, colliery powder 15kg, andalusite powder 4kg, granite tailings 9kg, zirconia powder 8kg and kaolin tail
Miberal powder 9kg, wherein, the particle diameter of the clinker is 80~100 mesh, and the particle diameter of the building waste is 60~100 mesh, the bastard coal
The particle diameter of stone flour is 40~80 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh, after being well mixed, is sufficiently stirred digestion
4 hours, type is then pressed into, finally the steam press maintenance under the conditions of 160 DEG C, 1.6MPa, that is, obtain the environmental protection brick.
The environmental protection brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test, resistance to compression
Intensity is 14.2MPa, rupture strength 3.2Mpa.
Embodiment 2：
The environmental protection brick of the present embodiment, it is made up of the raw material of following weight：Clinker 9kg, river sand 7kg, building waste 6kg, coal
Spoil powder 10kg, andalusite powder 7kg, granite tailings 7kg, zirconia powder 12kg and Kaolin Tailings powder 6kg, wherein, it is described
The particle diameter of clinker is 80~100 mesh, and the particle diameter of the building waste is 40~60 mesh, and the particle diameter of the colliery powder is 40~60
Mesh, the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The production method of above-mentioned environmental protection brick, is comprised the technical steps that：Take the raw material of following weight：Clinker 9kg, river sand
7kg, building waste 6kg, colliery powder 10kg, andalusite powder 7kg, granite tailings 7kg, zirconia powder 12kg and kaolin tail
Miberal powder 6kg, wherein, the particle diameter of the clinker is 80~100 mesh, and the particle diameter of the building waste is 40~60 mesh, the bastard coal
The particle diameter of stone flour is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh, after being well mixed, is sufficiently stirred digestion
4 hours, type is then pressed into, finally the steam press maintenance under the conditions of 170 DEG C, 1.3MPa, that is, obtain the environmental protection brick.
The environmental protection brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test, resistance to compression
Intensity is 14.8MPa, rupture strength 3.6Mpa.
Embodiment 3：
The environmental protection brick of the present embodiment, it is made up of the raw material of following weight：Clinker 12kg, river sand 4kg, building waste 9kg, coal
Spoil powder 5kg, andalusite powder 10kg, granite tailings 5kg, zirconia powder 16kg and Kaolin Tailings powder 3kg, wherein, it is described
The particle diameter of clinker is 80~100 mesh, and the particle diameter of the building waste is 40~60 mesh, and the particle diameter of the colliery powder is 40~60
Mesh, the particle diameter of the Kaolin Tailings powder is 40~60 mesh.
The production method of above-mentioned environmental protection brick, is comprised the technical steps that：Take the raw material of following weight：Clinker 12kg, river sand
4kg, building waste 9kg, colliery powder 5kg, andalusite powder 10kg, granite tailings 5kg, zirconia powder 16kg and kaolin tail
Miberal powder 3kg, wherein, the particle diameter of the clinker is 80~100 mesh, and the particle diameter of the building waste is 40~60 mesh, the bastard coal
The particle diameter of stone flour is 40~60 mesh, and the particle diameter of the Kaolin Tailings powder is 40~60 mesh, after being well mixed, is sufficiently stirred digestion
6 hours, type is then pressed into, finally the steam press maintenance under the conditions of 180 DEG C, 1MPa, that is, obtain the environmental protection brick.
The environmental protection brick produced according to GB11945-1999 standards to the present embodiment carries out crushing resistance and fold resistance test, resistance to compression
Intensity is 14.5MPa, rupture strength 3.3Mpa.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (6)
1. a kind of environmental protection brick, it is characterised in that be made up of the raw material of following parts by weight：6~12 parts of clinker, 4~10 parts of river sand,
3~9 parts of building waste, 5~15 parts of colliery powder, 4~10 parts of andalusite powder, 5~9 parts of granite tailings, zirconia powder 8~16
3~9 parts of part and Kaolin Tailings powder.
2. a kind of environmental protection brick according to claim 1, it is characterised in that be made up of the raw material of following parts by weight：Clinker 9
Part, 7 parts of river sand, 6 parts of building waste, 10 parts of colliery powder, 7 parts of andalusite powder, 7 parts of granite tailings, 12 parts of zirconia powder and
6 parts of Kaolin Tailings powder.
A kind of 3. environmental protection brick according to claim 1 or 2, it is characterised in that the particle diameter of the clinker is 80~100 mesh,
The particle diameter of the building waste is 60~100 mesh, and the particle diameter of the colliery powder is 40~80 mesh, the Kaolin Tailings powder
Particle diameter is 40~60 mesh.
4. a kind of production method of environmental protection brick, it is characterised in that comprise the technical steps that：Take the raw material of following parts by weight：
6~12 parts of clinker, 4~10 parts of river sand, 3~9 parts of building waste, 5~15 parts of colliery powder, 4~10 parts of andalusite powder, granite
3~9 parts of 5~9 parts of tailings, 8~16 parts of zirconia powder and Kaolin Tailings powder, after being well mixed, it is small to be sufficiently stirred digestion 4~8
When, type is then pressed into, finally the steam press maintenance under the conditions of 160~180 DEG C, 1~1.6MPa, that is, obtain the environmental protection brick.
A kind of 5. production method of environmental protection brick according to claim 4, it is characterised in that the parts by weight of the raw material
For：9 parts of clinker, 7 parts of river sand, 6 parts of building waste, 10 parts of colliery powder, 7 parts of andalusite powder, 7 parts of granite tailings, zirconium oxide
6 parts of 12 parts of powder and Kaolin Tailings powder.
6. the production method of a kind of environmental protection brick according to claim 4 or 5, it is characterised in that the particle diameter of the clinker is
80~100 mesh, the particle diameter of the building waste are 60~100 mesh, and the particle diameter of the colliery powder is 40~80 mesh, the kaolinite
The particle diameter of native mine tailing is 40~60 mesh.