CN107641420A - 一种开关柜喷涂防霉底漆的制备方法 - Google Patents

一种开关柜喷涂防霉底漆的制备方法 Download PDF

Info

Publication number
CN107641420A
CN107641420A CN201710879999.5A CN201710879999A CN107641420A CN 107641420 A CN107641420 A CN 107641420A CN 201710879999 A CN201710879999 A CN 201710879999A CN 107641420 A CN107641420 A CN 107641420A
Authority
CN
China
Prior art keywords
parts
switch cubicle
preparation
spraying
modified epoxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710879999.5A
Other languages
English (en)
Inventor
刘立忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangshan Haiwei Technology Co Ltd
Original Assignee
Jiangshan Haiwei Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangshan Haiwei Technology Co Ltd filed Critical Jiangshan Haiwei Technology Co Ltd
Priority to CN201710879999.5A priority Critical patent/CN107641420A/zh
Publication of CN107641420A publication Critical patent/CN107641420A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种开关柜喷涂防霉底漆的制备方法，按重量份，在搅拌釜中加入防霉改性环氧树脂100份、聚氨酯丙烯酸酯5‑15份、环氧丙烯酸酯5‑15份、双（2,4‑二叔丁基苯基）季戊四醇二亚磷酸酯5‑10份、1‑羟基环己基苯基甲酮1‑4份、白油10‑18份、邻苯二甲酸二异壬酯5‑15份、搅拌0.5‑2.5h，即得到开关柜喷涂防霉底漆。

Description

一种开关柜喷涂防霉底漆的制备方法
技术领域
本发明涉及一种油漆的制备方法，尤其是一种开关柜喷涂防霉底漆的制备方法。
背景技术
开关柜（switch cabinet）是一种电气设备，控制各种设备的开与关。开关柜外线先进入柜内主控开关，然后进入分控开关，各分路按其需要设置。如仪表，自控，电动机磁力开关，各种交流接触器等，有的还设高压室与低压室开关柜，设有高压母线，如发电厂等，有的还设有为保主要设备的低周减载。开关柜内的部件主要有断路器、隔离开关、负荷开关、操作机构、互感器以及各种保护装置等。开关柜的分类方法很多，如通过断路器安装方式可以分为移开式开关柜和固定式开关柜；或按照柜体结构的不同，可分为敞开式开关柜、金属封闭开关柜、和金属封闭铠装式开关柜；根据电压等级不同又可分为高压开关柜，中压开关柜和低压开关柜等。
CN104004450A公开了一种开关柜喷涂底漆，其特征在于，由下列重量份的原料制备制成：聚氨酯丙烯酸酯40-45、环氧丙烯酸酯23-28、钛白粉3-4、疏水二氧化硅2-3、氰尿酸锌2-3、氧化锌3-4、明矾粉2-3、异丙基硫杂蒽酮1-2、安息香双甲醚3-4、甲基丙烯酸甲酯1-2、乙二醇乙醚醋酸酯3-5、双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯8-10、乙酸乙酯7-9、分散助剂3-4；分散助剂提高了光学性能，使油漆分散均匀，并且维持了油漆的稳定性；防流挂，涂膜丰富，附着力强，能够快速固化，大大提高了工作效率。
CN106085225A涉及一种开关柜用防护漆，所述防护漆按重量份计，由以下组分组成：脂肪醇醚硫酸钠2-4份，羟基乙酸1-3份，凹凸棒土0.5-0.7份，氢氧化钾0.8-1.0份，硫酸钡1-2份，己基癸醇1-3份和环氧硅树脂11-15份。
CN103555138A涉及一种开关柜喷涂漆，由下列重量份的原料制成：E-12环氧树脂55-60、氨基树脂30-35、聚酯树脂（EL-1000H）20-24、乙撑双硬脂酸酰胺2-3、硫基乙酸异辛酯2-3、聚乙烯醇缩丁醛3-4、双(二辛氧基焦磷酸酯基)乙撑钛酸酯2-3、氢氧化镁6-8、二氧化钛4-5、氧化锌1-2、碳酸钙10-12、乙酸乙酯15-18、助剂4-5；本发明助剂提高了光学性能，使油漆分散均匀，并且维持了油漆的稳定性、提高成膜效果。
现有的开关柜耐热防腐漆，在湿度较大的，容易滋生霉菌的环境下，容易产生霉菌，生成霉斑。
发明内容
本发明的目的是：提供一种开关柜喷涂防霉底漆的制备方法，其特征在于以下步骤：
步骤1.防霉改性环氧树脂的制备
按重量份计，在反应釜中加入环氧树脂，四甲基胍乳酸盐，4,5-二氯-2-正辛基-3-异噻唑啉酮，三氟甲烷磺酸镝，升温至60-78℃，反应4-8h，得到防霉改性环氧树脂。
步骤2.开关柜喷涂防霉底漆的制备方法
按重量份计，在搅拌釜中加入步骤1所制得的防霉改性环氧树脂100份、聚氨酯丙烯酸酯5-15份、环氧丙烯酸酯5-15份、双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯5-10份、1-羟基环己基苯基甲酮1-4份、白油10-18份、邻苯二甲酸二异壬酯5-15份、搅拌0.5-2.5h，即得到开关柜喷涂防霉底漆。
所述的防霉改性环氧树脂，其原料质量用量比为环氧树脂：四甲基胍乳酸盐：4,5-二氯-2-正辛基-3-异噻唑啉酮：三氟甲烷磺酸镝=100：0.2-1：0.5-1.5:0.5-2。
所述的环氧树脂，四甲基胍乳酸盐，4,5-二氯-2-正辛基-3-异噻唑啉酮，三氟甲烷磺酸镝，聚氨酯丙烯酸酯，环氧丙烯酸酯、双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯、1-羟基环己基苯基甲酮、白油、邻苯二甲酸二异壬酯均为市售产品。
本发明的产品具有以下有益效果：
本发明所生产的开关柜喷涂防霉底漆，其主要材料树脂交联程度大，不易老化，产品的力学性能良好，同时对于霉菌等细菌有着长久且强效的杀菌效果。
具体实施方式
以下实例仅仅是进一步说明本发明，并不是限制本发明保护的范围。
实施例1
步骤1.防霉改性环氧树脂的制备
按重量份计，在反应釜中加入环氧树脂，四甲基胍乳酸盐，4,5-二氯-2-正辛基-3-异噻唑啉酮，三氟甲烷磺酸镝，升温至68℃，反应6h，得到防霉改性环氧树脂。
步骤2.开关柜喷涂防霉底漆的制备方法
按重量份计，在搅拌釜中加入步骤1所制得的防霉改性环氧树脂100份、聚氨酯丙烯酸酯11份、环氧丙烯酸酯13份、双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯7份、1-羟基环己基苯基甲酮2份、白油15份、邻苯二甲酸二异壬酯9份、搅拌1h，即得到开关柜喷涂防霉底漆。
所述的防霉改性环氧树脂，其原料质量用量比为环氧树脂：四甲基胍乳酸盐：4,5-二氯-2-正辛基-3-异噻唑啉酮：三氟甲烷磺酸镝=100：0.5：1:1。
实施例2
步骤1.防霉改性环氧树脂的制备
按重量份计，在反应釜中加入环氧树脂，四甲基胍乳酸盐，4,5-二氯-2-正辛基-3-异噻唑啉酮，三氟甲烷磺酸镝，升温至60℃，反应8h，得到防霉改性环氧树脂。
步骤2.开关柜喷涂防霉底漆的制备方法
按重量份计，在搅拌釜中加入步骤1所制得的防霉改性环氧树脂100份、聚氨酯丙烯酸酯5份、环氧丙烯酸酯5份、双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯5份、1-羟基环己基苯基甲酮1份、白油10份、邻苯二甲酸二异壬酯5份、搅拌0.5h，即得到开关柜喷涂防霉底漆。
所述的防霉改性环氧树脂，其原料质量用量比为环氧树脂：四甲基胍乳酸盐：4,5-二氯-2-正辛基-3-异噻唑啉酮：三氟甲烷磺酸镝=100：0.2：0.5:0.5。
实施例3
步骤1.防霉改性环氧树脂的制备
按重量份计，在反应釜中加入环氧树脂，四甲基胍乳酸盐，4,5-二氯-2-正辛基-3-异噻唑啉酮，三氟甲烷磺酸镝，升温至78℃，反应4h，得到防霉改性环氧树脂。
步骤2.开关柜喷涂防霉底漆的制备方法
按重量份计，在搅拌釜中加入步骤1所制得的防霉改性环氧树脂100份、聚氨酯丙烯酸酯15份、环氧丙烯酸酯15份、双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯10份、1-羟基环己基苯基甲酮4份、白油18份、邻苯二甲酸二异壬酯15份、搅拌2.5h，即得到开关柜喷涂防霉底漆。
所述的防霉改性环氧树脂，其原料质量用量比为环氧树脂：四甲基胍乳酸盐：4,5-二氯-2-正辛基-3-异噻唑啉酮：三氟甲烷磺酸镝=100：1：1.5:2。
对比例1
步骤1不加入四甲基胍乳酸盐，其他条件同实施例1。
对比例2
步骤1不加入4,5-二氯-2-正辛基-3-异噻唑啉酮，其他条件同实施例1。
对比例3
步骤1不加入三氟甲烷磺酸镝，其他条件同实施例1。
对比例4
步骤2不加入双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯，其他条件同实施例1。
对比例5
步骤1取消，环氧树脂不改性，其他条件同实施例1。
实施例4
分别将实施例1-3与对比例1-4所生产出的开关柜喷涂防霉底漆，参照标准QBT2591-2003提供的方法检验其抗霉菌能力和两个月以后的抗霉菌能力。见表1。
表1：不同工艺生产出的开关柜喷涂防霉底漆的抗霉菌性能。

Claims (3)

1.一种开关柜喷涂防霉底漆的制备方法，其特征在于包括以下步骤：
按重量份计，在搅拌釜中加入步骤1所制得的防霉改性环氧树脂100份、聚氨酯丙烯酸酯5-15份、环氧丙烯酸酯5-15份、双（2,4-二叔丁基苯基）季戊四醇二亚磷酸酯5-10份、1-羟基环己基苯基甲酮1-4份、白油10-18份、邻苯二甲酸二异壬酯5-15份、搅拌0.5-2.5h，即得到开关柜喷涂防霉底漆。
2.根据权利要求1所述的一种开关柜喷涂防霉底漆的制备方法，其特征在于：所述的防霉改性环氧树脂的制备方法为：
按重量份计，在反应釜中加入环氧树脂，四甲基胍乳酸盐，4,5-二氯-2-正辛基-3-异噻唑啉酮，三氟甲烷磺酸镝，升温至60-78℃，反应4-8h，得到防霉改性环氧树脂。
3.根据权利要求2所述的一种开关柜喷涂防霉底漆的制备方法，其特征在于：所述的防霉改性环氧树脂，其原料质量用量比为环氧树脂：四甲基胍乳酸盐：4,5-二氯-2-正辛基-3-异噻唑啉酮：三氟甲烷磺酸镝=100：0.2-1：0.5-1.5:0.5-2。
CN201710879999.5A 2017-09-26 2017-09-26 一种开关柜喷涂防霉底漆的制备方法 Pending CN107641420A (zh)