CN107603258A - 一种高耐水性能的板材 - Google Patents

一种高耐水性能的板材 Download PDF

Info

Publication number
CN107603258A
CN107603258A CN201710925398.3A CN201710925398A CN107603258A CN 107603258 A CN107603258 A CN 107603258A CN 201710925398 A CN201710925398 A CN 201710925398A CN 107603258 A CN107603258 A CN 107603258A
Authority
CN
China
Prior art keywords
parts
flaggy
water resistance
sheet material
thickness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710925398.3A
Other languages
English (en)
Inventor
姜剑波
辛世花
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhenjiang City Star Yao Intelligent Equipment Co Ltd
Original Assignee
Zhenjiang City Star Yao Intelligent Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhenjiang City Star Yao Intelligent Equipment Co Ltd filed Critical Zhenjiang City Star Yao Intelligent Equipment Co Ltd
Priority to CN201710925398.3A priority Critical patent/CN107603258A/zh
Publication of CN107603258A publication Critical patent/CN107603258A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提出了一种高耐水性能的板材，自上而下依次包括第一板层、第二板层和第三板层，第一板层的厚度为1‑2mm，第二板层的厚度为0.2‑0.5mm，第三板层的厚度为1‑2mm，第一板层、第二板层和第三板层之间涂覆环氧树脂胶并压合成型；所述第一板层、第二板层和第三板层的组成成分按重量份数计均包括：木粉35‑45份、竹粉25‑30份、PVC粉10‑18份和胶粘剂38‑50份，具有相当的强度，同时又能达到很好的耐水性能。

Description

一种高耐水性能的板材
技术领域
本发明涉及一种板材，具体地说是一种高耐水性能的板材。
背景技术
在耐水性竹、木板材，如：建筑模板，集装箱底板，车用板材，强化 复合木地板等的生产加工技术上，国内外一直使用一些耐水性高的胶粘剂， 如：酚醛树脂，聚氨酯，三聚氰胺甲醛树脂等。这些胶粘剂在板材的加工 过程中，能与木材纤维发生交联反应，形成网状结构，从而提高了板材的 耐水性能。但使用这些胶粘剂普遍存在成本高，耗费大量石油化工资源等 问题。同时在胶粘剂合成中使用大量的苯酚，异氰酸酯，三聚氰胺等毒性 较大的化工原料，不但污染环境，而且对生产人员危害较大。因此，迫切 需要开发出成本低、污染小、强度高、耐水性好的新型胶粘剂和板材加工 技术。
发明内容
本发明针对上述问题提出了一种高耐水性能的板材，具有相当的强度，同时又能达到很好的耐水性能。
具体的技术方案如下：
一种高耐水性能的板材，自上而下依次包括第一板层、第二板层和第三板层，第一板层的厚度为1-2mm，第二板层的厚度为0.2-0.5mm，第三板层的厚度为1-2mm，第一板层、第二板层和第三板层之间涂覆环氧树脂胶并压合成型；
所述第一板层、第二板层和第三板层的组成成分按重量份数计均包括：木粉35-45份、竹粉25-30份、PVC粉10-18份和胶粘剂38-50份。
进一步的，所述胶粘剂的组成成分按重量份数计如下：
改性的脲醛树脂35-48份、氢氧化钠5-8份、乳化剂3-8份、环己酮40-55份、聚丙烯纤维10-15份、聚乙二醇二缩水甘油醚12-15份、二氧化硅3-5份、异氰酸酯1-3份、成膜助剂2-4份。
进一步的，所述改性的脲醛树脂由聚乙二醇、脲醛树脂和水按2：6：3混合制备得到。
进一步的，所述乳化剂为烷基酚聚氧乙烯醚。
进一步的，所述成膜助剂为丙二醇丁醚。
本发明的有益效果为：本发明具有相当的强度，同时又能达到很好的耐水性能。
具体实施方式
为使本发明的技术方案更加清晰明确，下面对本发明进行进一步描述，任何对本发明技术方案的技术特征进行等价替换和常规推理得出的方案均落入本发明保护范围。
实施例一
一种高耐水性能的板材，自上而下依次包括第一板层、第二板层和第三板层，第一板层的厚度为1-2mm，第二板层的厚度为0.2-0.5mm，第三板层的厚度为1-2mm，第一板层、第二板层和第三板层之间涂覆环氧树脂胶并压合成型；
所述第一板层、第二板层和第三板层的组成成分按重量份数计均包括：木粉40份、竹粉28份、PVC粉15份和胶粘剂42份。
进一步的，所述胶粘剂的组成成分按重量份数计如下：
改性的脲醛树脂40份、氢氧化钠7份、乳化剂5份、环己酮48份、聚丙烯纤维12份、聚乙二醇二缩水甘油醚13份、二氧化硅4份、异氰酸酯2份、成膜助剂3份。
进一步的，所述改性的脲醛树脂由聚乙二醇、脲醛树脂和水按2：6：3混合制备得到。
进一步的，所述乳化剂为烷基酚聚氧乙烯醚。
进一步的，所述成膜助剂为丙二醇丁醚。
实施例二
一种高耐水性能的板材，自上而下依次包括第一板层、第二板层和第三板层，第一板层的厚度为1-2mm，第二板层的厚度为0.2-0.5mm，第三板层的厚度为1-2mm，第一板层、第二板层和第三板层之间涂覆环氧树脂胶并压合成型；
所述第一板层、第二板层和第三板层的组成成分按重量份数计均包括：木粉35份、竹粉25份、PVC粉10份和胶粘剂38份。
进一步的，所述胶粘剂的组成成分按重量份数计如下：
改性的脲醛树脂35份、氢氧化钠5份、乳化剂3份、环己酮40份、聚丙烯纤维10份、聚乙二醇二缩水甘油醚12份、二氧化硅3份、异氰酸酯1份、成膜助剂2份。
进一步的，所述改性的脲醛树脂由聚乙二醇、脲醛树脂和水按2：6：3混合制备得到。
进一步的，所述乳化剂为烷基酚聚氧乙烯醚。
进一步的，所述成膜助剂为丙二醇丁醚。
实施例三
一种高耐水性能的板材，自上而下依次包括第一板层、第二板层和第三板层，第一板层的厚度为1-2mm，第二板层的厚度为0.2-0.5mm，第三板层的厚度为1-2mm，第一板层、第二板层和第三板层之间涂覆环氧树脂胶并压合成型；
所述第一板层、第二板层和第三板层的组成成分按重量份数计均包括：木粉45份、竹粉30份、PVC粉18份和胶粘剂50份。
进一步的，所述胶粘剂的组成成分按重量份数计如下：
改性的脲醛树脂48份、氢氧化钠8份、乳化剂8份、环己酮55份、聚丙烯纤维15份、聚乙二醇二缩水甘油醚15份、二氧化硅5份、异氰酸酯3份、成膜助剂4份。
进一步的，所述改性的脲醛树脂由聚乙二醇、脲醛树脂和水按2：6：3混合制备得到。
进一步的，所述乳化剂为烷基酚聚氧乙烯醚。
进一步的，所述成膜助剂为丙二醇丁醚。

Claims (5)

1.一种高耐水性能的板材，其特征为，自上而下依次包括第一板层、第二板层和第三板层，第一板层的厚度为1-2mm，第二板层的厚度为0.2-0.5mm，第三板层的厚度为1-2mm，第一板层、第二板层和第三板层之间涂覆环氧树脂胶并压合成型；
所述第一板层、第二板层和第三板层的组成成分按重量份数计均包括：木粉35-45份、竹粉25-30份、PVC粉10-18份和胶粘剂38-50份。
2.进一步的，所述胶粘剂的组成成分按重量份数计如下：
改性的脲醛树脂35-48份、氢氧化钠5-8份、乳化剂3-8份、环己酮40-55份、聚丙烯纤维10-15份、聚乙二醇二缩水甘油醚12-15份、二氧化硅3-5份、异氰酸酯1-3份、成膜助剂2-4份。
3.如权利要求1所述的一种高耐水性能的板材，其特征为，所述改性的脲醛树脂由聚乙二醇、脲醛树脂和水按2：6：3混合制备得到。
4.如权利要求1所述的一种高耐水性能的板材，其特征为，所述乳化剂为烷基酚聚氧乙烯醚。
5.如权利要求1所述的一种高耐水性能的板材，其特征为，所述成膜助剂为丙二醇丁醚。
CN201710925398.3A 2017-10-04 2017-10-04 一种高耐水性能的板材 Withdrawn CN107603258A (zh)