CN107553991A - A kind of antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming - Google Patents
A kind of antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming Download PDFInfo
- Publication number
- CN107553991A CN107553991A CN201710675451.9A CN201710675451A CN107553991A CN 107553991 A CN107553991 A CN 107553991A CN 201710675451 A CN201710675451 A CN 201710675451A CN 107553991 A CN107553991 A CN 107553991A
- Authority
- CN
- China
- Prior art keywords
- embroidery
- antifouling
- fabric
- compound
- flaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming, in turn include the following steps, weaving high intensity embroidery fabric, with fire retardant nonwoven fabric it is compound, carry out computerized embroidery, embroidery pattern side carries out nano antifouling coating treatment, with fire retardant nonwoven fabric side flame retardant type wall paper body paper carry out it is compound, pass through the compound one layer of release liners of adhesive layer in body paper side.A kind of seamless front cover production technology of the antifouling embroidery of high-strength anti-flaming involved in the present invention so that high, antifouling, the fire-retardant embroidery wall cloth of the wall paper intensity produced, and production procedure is simple, can reduce production cost.And using the structure of ultra-wide, splicing can not be had in fitment process, without brush coating, is integrally affixed on Work machine on metope, smooth and firm pasting.
Description
Technical field
The present invention relates to decorative material for wall surface, especially a kind of antifouling seamless front cover production technology of embroidery of high-strength anti-flaming.
Background technology
With the development of the society, the lifting of people's level of consumption, this luxury goods in the past of wall paper have entered into common people
Family.At present, the decorative material for internal wall species on domestic market is various, wherein the wall paper constructed using barbola work, is especially pierced
Front cover is embroidered, because ornamental gradually substitution coating strong, easy for construction turns into the first choice of people, but common wall paper surface is only coated with one layer
PVC materials, have grown that easy alice is mouldy, cracking degumming the time, and common wall paper then because making fabric using fabric, is easily deformed and dirty
Damage, service life is short, is not suitable for the big place of the flows of the people such as hotel.And wall paper is in use, oil may be stained with
The spots such as dirt, it is more difficult to clean.
And in some public places, especially hotel, also there is very high requirement, existing wall to the fire resistance of wall paper
The fire-retardant of cloth is to carry out flame-proof treatment to wall paper, fire resistance can be died down over time.
The content of the invention
It is an object of the invention to provide a kind of antifouling undoubtedly wall paper production technology of embroidering of high-strength anti-flaming, can produce strong
Degree is high, and can be fire-retardant, antifouling embroidery wall cloth.
In order to solve the above technical problems, the object of the present invention is achieved like this:A kind of high intensity involved in the present invention
Inflaming-retarding antifouling embroidery seamless wall cloth production technology, in turn includes the following steps,
Step A, high intensity embroidery fabric is weaved;
Step B, the embroidery fabric that step A is obtained is compound with fire retardant nonwoven fabric, obtains base fabric of embroidering;
Step C, to the embroidery fabric obtained by step B, computerized embroidery is carried out, obtains embroidered cloth;
Step D, to the embroidered cloth obtained by step C, nano antifouling coating treatment is carried out in the pattern side of embroidery;
Step E, the embroidered cloth fire retardant nonwoven fabric side flame retardant type wall paper body paper after step D processing is carried out compound;
Step F, in the compound one layer of release liners in body paper side;
In step A, the raw material of described embroidery fabric is to use high strength polyester filament yarn as raw material, and the thickness for fabric of embroidering is
0.2-0.25mm;The fineness of used high strength polyester filament yarn is 30-50D;The weight per square meter of described embroidery fabric is
90-200 grams.
As a further illustration of the above scheme, in step A, described embroidery fabric is made using woven or knitting
.
As a further illustration of the above scheme, in step B, described fire retardant nonwoven fabric be fire-retardant spunlace non-woven cloth or
Fire-retardant spun-bonded non-woven fabrics, weight per square meter are 60-150 grams;Described fire retardant nonwoven fabric is compound by PU glue and embroidery fabric.
As a further illustration of the above scheme, in step C, described computerized embroidery is successively as follows, successively
As follows:
Step C1, the designed pattern typing computer of embroidery computer printing is carried out according to pattern, computer printing is carried out according to pattern
Programming;
Step C2, computerized emboridering machine is embroidered:The qualified embroidery program entry computerized emboridering machine that will be completed, it is embroidered needing
Embroidered cloth fabric stretch tight on framework, open embroidery machine carry out continuously repeating embroidery.
As a further illustration of the above scheme, step D, described nano antifouling coating treatment, successively as follows:
Step D1, the embroidered cloth obtained by step C, in its embroidery pattern side, the TPU membrane progress thick with 0.1mm is compound;
Step D2, brushing nano zine oxide treatment fluid in TPU membrane, 55- is obtained after drying in TPU membrane on step D1 institutes are compound
The antifouling nano coating of 90nm thickness.
As a further illustration of the above scheme, also include:
Step G, in the compound one layer of adhesive layer in the back side of wall paper body paper, one layer of release liners is adhered to again on adhesive layer, are embroidered
Wall paper;
Step H, embroidery wall cloth is examined, storage through cutting edge clot.
The beneficial effects of the invention are as follows:Front cover production work that a kind of antifouling embroidery of high-strength anti-flaming involved in the present invention is seamless
Skill so that high, antifouling, the fire-retardant embroidery wall cloth of the wall paper intensity produced, and production procedure is simple, can reduce and be produced into
This.And using the structure of ultra-wide, splicing can not be had in fitment process, without brush coating, wall is integrally affixed on Work machine
On face, smooth and firm pasting.
Embodiment
The present invention is further described for specific embodiment below.
Embodiment one
The antifouling embroidery seamless wall cloth production technology of a kind of high-strength anti-flaming involved by the present embodiment, in turn includes the following steps:
Step A, high intensity embroidery fabric is weaved;It is selected in the present embodiment to be woven next obtained by woven or knitting
High intensity embroidery fabric is made, the raw material for fabric of embroidering is to use high strength polyester filament yarn as raw material, and the thickness for fabric of embroidering is
0.2mm;The fineness of used high strength polyester filament yarn is 30D;The weight per square meter of described embroidery fabric is 90 grams.
Step B, the embroidery fabric that step A is obtained is compound with fire retardant nonwoven fabric, obtains base fabric of embroidering;Described fire-retardant nonwoven
Cloth is fire-retardant spunlace non-woven cloth or fire-retardant spun-bonded non-woven fabrics, and weight per square meter is 150 grams;Described fire retardant nonwoven fabric passes through PU glue
It is compound with embroidery fabric.Selected for fire-retardant spunlace non-woven cloth in the present embodiment, used raw material is anti-flaming viscose, fineness
For 1.56dtex, length 38mm.
Anti-flaming viscose is 25-35 DEG C in temperature, and in the environment of humidity is 75%, weighed feeding equipment claims to raw material
Weight and feeding, shredding and mixing are then carried out to raw material by fiber opening equipment and mixing apparatus.Mixed raw material is led to
Cross fiber carding machine and comb networking, cross lapping machine lapping is entered after carding machine output and forms intersection paving subsequently into drafting machine
The web of net.Raw material knot spun-laced machine after networking, the water needle plate that liquid drugs injection and aperture in spun-laced machine are 0.1mm are used cooperatively,
And reinforced by being sprayed under six different pressures, whole procedure is then completed by drying machine drying machine, lapper afterwards in rolls.The
First, two spun lacing pressure are 80bar, and third and fourth road spun lacing pressure is 100bar, and the 5th spun lacing pressure is 140bar, the 6th
Road spun lacing pressure is 70bar.
Step C, to the embroidery fabric obtained by step B, computerized embroidery is carried out, obtains embroidered cloth;Computerized embroidery be successively by
Following steps, successively as follows:
Step C1, embroidery computer printing is carried out according to pattern, designed pattern typing computer, computer printing is carried out according to pattern
Programming.Required embroidery flower pattern is carried out to retouch original text design, then carries out embroidery version plate-making, first by designed pattern typing electricity
Brain, film-making is carried out according to pattern computer, and embroidered by examination, test run determines suitable embroidery program.
Step C2, computerized emboridering machine is embroidered:The qualified embroidery program entry computerized emboridering machine that will be completed, needs
Embroidered embroidered cloth fabric stretches tight on framework, opens embroidery machine and carries out continuously repeating embroidery, until whole cloth cloth is completed.
Step D, to the embroidered cloth obtained by step C, nano antifouling coating treatment is carried out in the pattern side of embroidery;Nanometer is anti-
Dirty coating treatment, successively as follows:
In its embroidery pattern side, the TPU membrane progress thick with 0.1 mm is compound.
Brushing nano zine oxide treatment fluid in TPU membrane, obtains the anti-of 55nm thickness in TPU membrane on institute is compound after drying
Dirty nano coating.
Step E, the embroidered cloth fire retardant nonwoven fabric side flame retardant type wall paper body paper after step D processing is carried out compound;First have to
EVA glued membranes are combined on the wallpaper base stock with flame retardant effect by hot pressing, then stereotyped embroidered cloth and surface recombination
The wallpaper base stock of EVA glued membranes is compound, selected EVA glued membranes for thickness between 0.01mm fusing point more than 70 DEG C, with
According to production on-site environment temperature appropriate adjustment recombination time and film thickness, the breadth of wallpaper base stock selects 2.8 meters;Wall
The surface with glue of paper body paper and the back side fitting of embroidered cloth are placed in parallel alignment selvedge and trimming, and compound, hot pressing is heated using hot press
Temperature is in the range of 90 DEG C, and hot pressing time heated compound tense between 30 seconds, and the embroidery of embroidered cloth is face-up, and heating platen is to thorn
Front heating is embroidered, the breadth of hot press heating breadth is 2.5 meters, between the length heated every time is 1 meter to 1.5 meters, passes through heat
Press uses segmented heat pressure adhesive to embroidered cloth and wallpaper base stock, and continuously compound centre is not cut out for whole process embroidered cloth and wallpaper base stock
It is disconnected.
Step F, the compound one layer of release liners of adhesive layer are passed through in body paper side.So that when pasting, release liners can be taken off, just
It can be attached on front cover, the engineering time can be saved, improve effect, and the pollution in room is reduced without using coating.
Step G, embroidery wall cloth is examined, storage through cutting edge clot.
Embodiment two
The antifouling embroidery seamless wall cloth production technology of a kind of high-strength anti-flaming involved by the present embodiment, in turn includes the following steps:
Step A, high intensity embroidery fabric is weaved;It is selected in the present embodiment to be woven next obtained by woven or knitting
High intensity embroidery fabric is made, the raw material for fabric of embroidering is to use high strength polyester filament yarn as raw material, and the thickness for fabric of embroidering is
0.25mm;The fineness of used high strength polyester filament yarn is 50D;The weight per square meter of described embroidery fabric is 200 grams.
Step B, the embroidery fabric that step A is obtained is compound with fire retardant nonwoven fabric, obtains base fabric of embroidering;Described fire-retardant nonwoven
Cloth is fire-retardant spunlace non-woven cloth or fire-retardant spun-bonded non-woven fabrics, and weight per square meter is 80 grams;Described fire retardant nonwoven fabric passes through PU glue
It is compound with embroidery fabric.From the fire-retardant spun-bonded non-woven fabrics that are in the present embodiment, selected raw material be PET spun-bonded non-woven fabrics,
PE spun-bonded non-woven fabrics, PA spun-bonded non-woven fabrics, PP spun-bonded non-woven fabrics, when producing fire-retardant spunbond nonwoven, flame-retardant color master batch grain is mixed into
Into spun-bonded non-woven fabrics fused raw material, the raw material for being mixed into flame-retardant color master batch grain is made by the spinning with flame-retardant nature by extruder
Bonded non-woven fabrics.
Step C, to the embroidery fabric obtained by step B, computerized embroidery is carried out, obtains embroidered cloth;Computerized embroidery be successively by
Following steps, successively as follows:
Step C1, embroidery computer printing is carried out according to pattern, designed pattern typing computer, computer printing is carried out according to pattern
Programming.Required embroidery flower pattern is carried out to retouch original text design, then carries out embroidery version plate-making, first by designed pattern typing electricity
Brain, film-making is carried out according to pattern computer, and embroidered by examination, test run determines suitable embroidery program.
Step C2, computerized emboridering machine is embroidered:The qualified embroidery program entry computerized emboridering machine that will be completed, needs
Embroidered embroidered cloth fabric stretches tight on framework, opens embroidery machine and carries out continuously repeating embroidery, until whole cloth cloth is completed.
Step D, to the embroidered cloth obtained by step C, nano antifouling coating treatment is carried out in the pattern side of embroidery;Nanometer is anti-
Dirty coating treatment, successively as follows:
In its embroidery pattern side, the TPU membrane progress thick with 0.3 mm is compound.
Brushing nano zine oxide treatment fluid in TPU membrane, obtains the anti-of 90nm thickness in TPU membrane on institute is compound after drying
Dirty nano coating.
Step E, the embroidered cloth fire retardant nonwoven fabric side flame retardant type wall paper body paper after step D processing is carried out compound;First have to
EVA glued membranes are combined on the wallpaper base stock with flame retardant effect by hot pressing, then stereotyped embroidered cloth and surface recombination
The wallpaper base stock of EVA glued membranes is compound, selected EVA glued membranes for thickness between 0.01-0.1mm fusing point 70 DEG C with
On, with selecting 3.2 meters according to the breadth of production on-site environment temperature appropriate adjustment recombination time and film thickness, wallpaper base stock;
The surface with glue of wallpaper base stock and the back side fitting of embroidered cloth are placed in parallel alignment selvedge and trimming, it is compound using hot press heating,
Hot pressing temperature is in the range of 90-110 DEG C, and hot pressing time heated compound tense between 50 seconds, and the embroidery of embroidered cloth is face-up, heat
Pressing plate to embroidery front heating, hot press heating breadth breadth be 3.5 meters, the length heated every time be 1 meter to 1.5 meters it
Between, segmented heat pressure adhesive is used to embroidered cloth and wallpaper base stock by hot press, whole process embroidered cloth and wallpaper base stock are continuously multiple
Not severing among closing.
Step F, the compound one layer of release liners of adhesive layer are passed through in body paper side.So that when pasting, release liners can be taken off, just
It can be attached on front cover, the engineering time can be saved, improve effect, and the pollution in room is reduced without using coating.
Step G, embroidery wall cloth is examined, storage through cutting edge clot.
Preferred embodiment of the invention described in detail above.It should be appreciated that one of ordinary skill in the art without
Creative work can is needed to make many modifications and variations according to the design of the present invention.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical scheme, all should be in the protection domain being defined in the patent claims.
Claims (6)
- A kind of 1. antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming, it is characterised in that in turn include the following steps,Step A, high intensity embroidery fabric is weaved;Step B, the embroidery fabric that step A is obtained is compound with fire retardant nonwoven fabric, obtains base fabric of embroidering;Step C, to the embroidery fabric obtained by step B, computerized embroidery is carried out, obtains embroidered cloth;Step D, to the embroidered cloth obtained by step C, nano antifouling coating treatment is carried out in the pattern side of embroidery;Step E, the embroidered cloth fire retardant nonwoven fabric side flame retardant type wall paper body paper after step D processing is carried out compound;Step F, the compound one layer of release liners of adhesive layer are passed through in body paper side;In step A, the raw material of described embroidery fabric is to use high strength polyester filament yarn as raw material, and the thickness for fabric of embroidering is 0.2-0.25mm;The fineness of used high strength polyester filament yarn is 30-50D;The weight per square meter of described embroidery fabric is 90-200 grams.
- 2. the antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming as claimed in claim 1, it is characterised in that in step A, Described embroidery fabric is using obtained by woven or knitting.
- 3. the antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming as claimed in claim 1, it is characterised in that in step B, Described fire retardant nonwoven fabric is fire-retardant spunlace non-woven cloth or fire-retardant spun-bonded non-woven fabrics, and weight per square meter is 60-150 grams;Described Fire retardant nonwoven fabric is compound by PU glue and embroidery fabric.
- 4. the antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming as claimed in claim 1, it is characterised in that in step C, Described computerized embroidery is successively as follows, successively as follows:Step C1, the designed pattern typing computer of embroidery computer printing is carried out according to pattern, computer printing is carried out according to pattern Programming;Step C2, computerized emboridering machine is embroidered:The qualified embroidery program entry computerized emboridering machine that will be completed, it is embroidered needing Embroidered cloth fabric stretch tight on framework, open embroidery machine carry out continuously repeating embroidery.
- 5. the antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming as claimed in claim 1, it is characterised in that step D, institute The nano antifouling coating treatment stated, successively as follows:Step D1, the embroidered cloth obtained by step C, in its embroidery pattern side, the TPU membrane progress thick with 0.1-0.3mm is compound;Step D2, brushing nano zine oxide treatment fluid in TPU membrane, 55- is obtained after drying in TPU membrane on step D1 institutes are compound The antifouling nano coating of 90nm thickness.
- 6. the antifouling embroidery seamless wall cloth production technology of high-strength anti-flaming as claimed in claim 1, it is characterised in that also include:Step H, embroidery wall cloth is examined, storage through cutting edge clot.