CN102268915A - Implementation process for seamless wallcovering - Google Patents
Implementation process for seamless wallcovering Download PDFInfo
- Publication number
- CN102268915A CN102268915A CN2011101436796A CN201110143679A CN102268915A CN 102268915 A CN102268915 A CN 102268915A CN 2011101436796 A CN2011101436796 A CN 2011101436796A CN 201110143679 A CN201110143679 A CN 201110143679A CN 102268915 A CN102268915 A CN 102268915A
- Authority
- CN
- China
- Prior art keywords
- cloth
- wall cloth
- melt film
- hot melt
- wallcovering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an implementation process for seamless wallcovering. The implement process comprises the following process steps: (1), production of a foundation: adopting a broad textile machine to produce a gray fabric, and dyeing, sizing, finishing, modifying and performing afterfinish on the gray fabric to obtain the foundation; (2), compounding of wallcovering: compounding and combining the foundation with a hot melt film by a compound machine at the temperature of 54-75 DEG C to obtain the wallcovering, and setting base material paper layer on the heat melt film; and (3), adhesion of the wallcovering and a wall surface: flattening and performing dampproof treatment on the wall surface, cutting off wallcovering with the area same as that of the wall surface, tearing off the base material paper, adhering the wallcovering and the wall surface, and melting the hot melt film by heating of a heating roller to adhere the wallcovering and the wall surface together, wherein the heating temperature is 90-130 DEG C. The implementation process for a seamless wallcovering provided by the invention is convenient in construction, simple in procedures, environment-friendly and material-saving.
Description
Technical field
The present invention relates to a kind of implementing process of seamless wall cloth, belong to technical field of construction and decoration materials.
Background technology
Along with the raising day by day of people's living standard and the improvement of dwelling environment, the decoration of indoor wall is more and more paid attention to.Existing indoor wall ornament materials adopts wallpaper usually, because wallpaper is easily damaged, aging and fade, texture is also relatively poor, can not satisfy the needs of high-grade wall fitting.
Simultaneously, because wallpaper does not have tack, must wallpaper be pasted up by elder generation's brushing glue on body of wall before use again, so not only waste time and energy, gluing is inhomogeneous also to be caused being pasted not strongly admittedly easily; In addition, contain harmful chemical composition in the glue, do not meet environmental requirement.
In addition, present wallpaper mostly is 53 centimeters-160 centimeters, has tangible seam between the wallpaper of construction back, plays the limit easily.When wallpaper is constructed,, must cause spillage of material very big, cause certain economic loss to the customer to the colored type picture mosaic case of adjacent wallpaper for attractive in appearance.
Therefore, for solving the problems of the technologies described above, the necessary implementing process that a kind of novel seamless wall cloth is provided is to overcome described defective of the prior art.
Summary of the invention
For addressing the above problem, the object of the present invention is to provide the implementing process of the seamless wall cloth of a kind of decoration grade height, easy to use and environmental protection.
For achieving the above object, the technical scheme that the present invention takes is: a kind of implementing process of seamless wall cloth, and it comprises following processing step,
(1), the production of base cloth: adopt the wide cut weaving loom to produce grey cloth, and to grey cloth dye, finalize the design, arrangement, ornamental processing and back arrangement obtain base cloth;
(2), wall cloth compound: above-mentioned base cloth and a hot melt film are carried out compound by compounding machine under 54 ℃ ~ 75 ℃ condition, base cloth and hot melt film are combined and obtain wall cloth, and a substrate paper is set on hot melt film;
(3), wall cloth and metope are bonding: metope is carried out smooth and moistureproof processing; The wall cloth that cutting is identical with the metope area tears substrate paper and make off wall cloth and metope combination, makes its fusion by a warm-up mill heat hot melt film, makes wall cloth and metope bonding, and the temperature of described heating is 90 ℃ ~ 130 ℃.
The implementing process of seamless wall cloth of the present invention further is set to: the width of described base cloth is 2.7m ~ 3.3m, is specially a kind of fabric.
The implementing process of seamless wall cloth of the present invention further is set to: the temperature during described the typing is 150 ℃ ~ 250 ℃; Temperature when described back is put in order is 150 ℃ ~ 200 ℃, and walking cloth speed is 30 m/min ~ 50 m/min.
The implementing process of seamless wall cloth of the present invention further is set to: described ornamental processing is specially the combination of suede on high sley yarn-dyed jacquard, the polychrome suede, multi color printing, polychrome embroidery or two or more above-mentioned technology.
The implementing process of seamless wall cloth of the present invention further is set to: the specification of described hot melt film is 40g ± 5g/ ㎡, and concrete composition is an ethylene-vinyl acetate copolymer; The specification of described substrate paper is 60g ~ 65g ∕ ㎡, is specially the two silicon paper of Ge Laxin.
The implementing process of seamless wall cloth of the present invention also can be set to: the setting temperature of described step (1) is 180 ℃, and the temperature of back arrangement is 160 ℃, and walking cloth speed is 40 m/min; The combined temp of described step (2) is 60 ℃; The heating-up temperature of described step (3) is 100 ℃.
Compared with prior art, the present invention has following beneficial effect:
1. pass through a compound hot melt film, thereby need not again gluing on the metope in use, easy to use, save operation, harmless, energy-conserving and environment-protective;
2. the thickness of this hot melt film is even, and is bonding firmly with metope, can not produce bulge;
3. this wall cloth is cloth matter structure and imposes ornamental processing, makes its feel better, the decoration grade height;
4. this wall cloth is the wide cut wall cloth, need not composed pattern, and waste of material is few.
[description of drawings]
Fig. 1 is the flow chart of the implementing process of seamless wall cloth of the present invention.
[specific embodiment]
Implementing process below in conjunction with 1 pair of seamless wall cloth of the present invention of accompanying drawing specifies.
Embodiment 1
A kind of implementing process of seamless wall cloth, it comprises following processing step:
(1), the production of base cloth: adopt the wide cut weaving loom to produce grey cloth, and to grey cloth dye, finalize the design, arrangement, ornamental processing and back arrangement obtain base cloth.Wherein, the width of described base cloth is 2.7m ~ 3.3m, is specially a kind of fabric, and this width satisfies the floor height requirement in general house, therefore, need not composed pattern in use, only cutting gets final product need according to wall area, realize real seamless stickup, and make waste of material few, cost is low.Further, the temperature in described when typing is 180 ℃, thereby having increased look firm, make base cloth indeformable, do not fade; Waterproof, antifouling, anti-oil processing are mainly carried out in the arrangement of described back, and concrete technological temperature is 160 ℃, and walking cloth speed is 40m/min, and the base cloth of producing under these technological parameters is the best in quality.Described ornamental processing is specially the combination of suede on high sley yarn-dyed jacquard, the polychrome suede, multi color printing, polychrome embroidery or two or more above-mentioned technology.
(2), wall cloth compound: above-mentioned base cloth and a hot melt film are carried out compound by common compounding machine under 60 ℃ condition, base cloth and hot melt film are combined and obtain wall cloth, and a substrate paper is set on hot melt film.Described hot melt film thickness is even, and its specification is 40g ± 5g/ ㎡, and concrete composition is an ethylene-vinyl acetate copolymer, and this material is harmless to health, environmental protection.The specification of described substrate paper is 60g ~ 65g ∕ ㎡, is specially the two silicon paper of Ge Laxin.
(3), wall cloth and metope are bonding: metope is carried out smooth and moistureproof processing, specifically can adopt cement that metope is flattened, and on metope moisture sealer is set; The cutting wall cloth identical again with the metope area, substrate paper is torn and makes off wall cloth and metope combination, make its fusion, make wall cloth and metope bonding by a warm-up mill heat hot melt film, the temperature of described heating is 100 ℃, can be to greatest extent and the metope combination with hot melt film under this temperature.In this process,, therefore, need not composed pattern in use because the width of wall cloth satisfies the floor height in general house.
Embodiment 2
A kind of implementing process of seamless wall cloth, it comprises following processing step:
(1), the production of base cloth: adopt the wide cut weaving loom to produce grey cloth, and to grey cloth dye, finalize the design, arrangement, ornamental processing and back arrangement obtain base cloth.Wherein, the width of described base cloth is 2.7m ~ 3.3m, is specially a kind of fabric, and this width satisfies the floor height requirement in general house, therefore, need not composed pattern in use, only cutting gets final product need according to wall area, realize real seamless stickup, and make waste of material few, cost is low.Further, the temperature in described when typing is 150 ℃, thereby having increased look firm, make base cloth indeformable, do not fade; Waterproof, fire prevention, anti-greasy dirt processing are mainly carried out in the arrangement of described back, and concrete technological temperature is 150 ℃, and walking cloth speed is 30m/min.Described ornamental processing is specially the combination of suede on high sley yarn-dyed jacquard, the polychrome suede, multi color printing, polychrome embroidery or two or more above-mentioned technology.
(2), wall cloth compound: above-mentioned base cloth and a hot melt film are carried out compound by common compounding machine under 54 ℃ condition, base cloth and hot melt film are combined and obtain wall cloth, and a substrate paper is set on hot melt film.Described hot melt film thickness is even.Its specification is 40g ± 5g/ ㎡, and concrete composition is an ethylene-vinyl acetate copolymer; The specification of described substrate paper is 60g ~ 65g ∕ ㎡, is specially the two silicon paper of Ge Laxin.
(3), wall cloth and metope are bonding: metope is carried out smooth and moistureproof processing, specifically can adopt cement that metope is flattened, and on metope moisture sealer is set; The cutting wall cloth identical with the metope area tears substrate paper and make off wall cloth and metope combination again, makes its fusion by a warm-up mill heat hot melt film, makes wall cloth and metope bonding, and the temperature of described heating is 90 ℃.
Embodiment 3
A kind of implementing process of seamless wall cloth, it comprises following processing step:
(1), the production of base cloth: adopt the wide cut weaving loom to produce grey cloth, and to grey cloth dye, finalize the design, arrangement, ornamental processing and back arrangement obtain base cloth.Wherein, the width of described base cloth is 2.7m ~ 3.3m, is specially a kind of fabric, and this width satisfies the floor height requirement in general house, therefore, need not composed pattern in use, only cutting gets final product need according to wall area, realize real seamless stickup, and make waste of material few, cost is low.Further, the temperature in described when typing is 250 ℃, thereby having increased look firm, make base cloth indeformable, do not fade; Waterproof, fire prevention, anti-greasy dirt processing are mainly carried out in the arrangement of described back, and concrete technological temperature is 200 ℃, and walking cloth speed is 50m/min.Described ornamental processing is specially the combination of suede on high sley yarn-dyed jacquard, the polychrome suede, multi color printing, polychrome embroidery or two or more above-mentioned technology.
(2), wall cloth compound: above-mentioned base cloth and a hot melt film are carried out compound by common compounding machine under 75 ℃ condition, base cloth and hot melt film are combined and obtain wall cloth, and a substrate paper is set on hot melt film.Described hot melt film thickness is even.Its specification is 40g ± 5g/ ㎡, and concrete composition is an ethylene-vinyl acetate copolymer; The specification of described substrate paper is 60g ~ 65g ∕ ㎡, is specially the two silicon paper of Ge Laxin.
(3), wall cloth and metope are bonding: metope is carried out smooth and moistureproof processing, specifically can adopt cement that metope is flattened, and on metope moisture sealer is set; The cutting wall cloth identical with the metope area tears substrate paper and make off wall cloth and metope combination again, makes its fusion by a warm-up mill heat hot melt film, makes wall cloth and metope bonding, and the temperature of described heating is 130 ℃.
The above specific embodiment only is the preferred embodiment of this creation, not in order to limiting this creation, all in this creation spirit and principle within made any modification, be equal to replacement, improvement etc., all should be included within the protection domain of this creation.
Claims (6)
1. the implementing process of a seamless wall cloth is characterized in that: comprise following processing step,
(1), the production of base cloth: adopt the wide cut weaving loom to produce grey cloth, and to grey cloth dye, finalize the design, arrangement, ornamental processing and back arrangement obtain base cloth;
(2), wall cloth compound: above-mentioned base cloth and a hot melt film are carried out compound by compounding machine under 54 ℃ ~ 75 ℃ condition, base cloth and hot melt film are combined and obtain wall cloth, and a substrate paper is set on hot melt film;
(3), wall cloth and metope are bonding: metope is carried out smooth and moistureproof processing; The wall cloth that cutting is identical with the metope area tears substrate paper and make off wall cloth and metope combination, makes its fusion by a warm-up mill heat hot melt film, makes wall cloth and metope bonding, and the temperature of described heating is 90 ℃ ~ 130 ℃.
2. the implementing process of seamless wall cloth as claimed in claim 1, it is characterized in that: the width of described base cloth is 2.7m ~ 3.3m, is specially a kind of fabric.
3. the implementing process of seamless wall cloth as claimed in claim 2 is characterized in that: the temperature during described typing is 150 ℃ ~ 250 ℃; Temperature when described back is put in order is 150 ℃ ~ 200 ℃, and walking cloth speed is 30 m/min ~ 50 m/min.
4. the implementing process of seamless wall cloth as claimed in claim 3 is characterized in that: described ornamental processing is specially the combination of suede on high sley yarn-dyed jacquard, the polychrome suede, multi color printing, polychrome embroidery or two or more above-mentioned technology.
5. the implementing process of seamless wall cloth as claimed in claim 1, it is characterized in that: the specification of described hot melt film is 40g ± 5g/ ㎡, concrete composition is an ethylene-vinyl acetate copolymer; The specification of described substrate paper is 60g ~ 65g ∕ ㎡, is specially the two silicon paper of Ge Laxin.
6. the implementing process of seamless wall cloth as claimed in claim 1, it is characterized in that: the setting temperature of described step (1) is 180 ℃, and the temperature of back arrangement is 160 ℃, and walking cloth speed is 40 m/min; The combined temp of described step (2) is 60 ℃; The heating-up temperature of described step (3) is 100 ℃.