CN106183221A - Metal fabric wall cloth and manufacture method thereof - Google Patents
Metal fabric wall cloth and manufacture method thereof Download PDFInfo
- Publication number
- CN106183221A CN106183221A CN201610537772.8A CN201610537772A CN106183221A CN 106183221 A CN106183221 A CN 106183221A CN 201610537772 A CN201610537772 A CN 201610537772A CN 106183221 A CN106183221 A CN 106183221A
- Authority
- CN
- China
- Prior art keywords
- metal fabric
- wall cloth
- metal
- cloth
- upper strata
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metal fabric wall cloth and manufacture method thereof, metal fabric wall cloth is by upper strata metal fabric, middle level adhesive film and lower layer mix feeding layer up of three layers altogether, upper strata metal fabric is to be formed as radially braiding as broadwise and Duo Gen metallic cable by many wires, and step is to press to be combined with each other under the high temperature of 120 DEG C ± 5 DEG C by upper strata metal fabric, middle level adhesive film and lower layer mix feeding layer to can be prepared by metal fabric wall cloth.The present invention utilizes metal wire to replace traditional paper and weaving cloth, metal wire or metallic cable are compound on the cloth of icon bottom after braiding, there is cycle in service life length, firm and durable, there is the advantages such as metallic luster, there is the lines of three-dimensional skin texture on the surface of wall cloth, also has the performances such as fire protection flame retarding, mildew resistant moistureproof and sound-absorbing breathability.
Description
Technical field
The invention belongs to wall fitting wall cloth and manufacture method technical field thereof, particularly relate to a kind of metal fabric
Wall cloth and manufacture method thereof.
Background technology
Wallpaper is a kind of indoor hardware fitting for papering metope, is widely used in house, office, hotel, hotel
Interior decorations etc., its material is not limited to paper, also comprises other material.Wallpaper because have that color is various, pattern abundant, luxurious
The feature that other house decorative materials multiple such as style, safety and environmental protection, easy construction, affordable are incomparable, therefore in Europe
The developed countries and regions such as beautiful, Japanese obtains considerable degree of universal.Wallpaper is divided into a lot of class, as overlay film wallpaper, coating wallpaper,
Embossing wallpapers etc., generally produce body paper, then the processed through different operations, as being coated with, print, embossing with bleached wood pulp
Or surface covers and mould, dispatching from the factory after the most cut, packaging, usual wallpaper has certain intensity, toughness, appearance attractive in appearance and good
Water repelling property.
In currently available technology, the commonly used patch wall ornament of tradition has wallpaper and wall paper two class, and wallpaper is by bleachingization
Learn wood pulp production body paper, then the processed through different operations, stamp various pattern and form, this pure wood pulp paper wallpaper, easily
The easy alice of mould fugitive color, shrinks wayward, and moisture resistance scrub resistance is poor.Wall paper has multiple base material, and it is resistance to that glass fibre wallhanging is moisture resistance
Clean fire-fighting performance good, but after coating damage, the glass fibre shed is irritant to human body skin；Nonwoven wall paper performance
Good, but fire-fighting poor performance；The magnificent noble quality of damask wall paper, but easily mildew and not preventing fires；Plastics wall paper is ageing-resistant, but in the sun can
Fade yellowing etc..Currently use in glass sandwich is the pattern of the ramie cotton yarn fabric composition of shades of colour and pattern, just makes
Doubling glass product pattern out has beautiful coloration, but must continue over time, and color is gradually decorporated, it has to the most more
Change.And wallpaper traditional in prior art and wall cloth great majority are all paper using and cloth is raw material, paste and be used in after gluing
The material of the surface of decorating objects, wallpaper and wall cloth itself does not possess the performances such as fire protection flame retarding, mildew resistant moistureproof and sound-absorbing are ventilative, from
And make service life of wallpaper or wall cloth relatively low, also can bring various potential safety hazard to field of employment simultaneously.
Summary of the invention
The deficiency that the present invention exists to overcome prior art, it is provided that a kind of metal fabric wall cloth and manufacture method thereof, this
Invention utilizes metal wire to replace traditional paper and weaving cloth, metal wire or metallic cable is compound at the bottom of icon after braiding
A kind of Novel wall cloth material realized on the cloth of layer.
The present invention is achieved by the following technical solutions: a kind of metal fabric wall cloth, its be by upper strata metal fabric, in
Layer adhesive film and lower layer mix feeding layer up of three layers altogether, upper strata metal fabric is as broadwise and Duo Gen metallic cable by many wires
Forming as radially braiding, upper strata metal fabric, middle level adhesive film and lower layer mix feeding layer are combined with each other through high temperature and make metal
Fabric wall cloth, the braiding lines of upper strata metal fabric is divided into rule lines that radial spacing is identical and radial spacing to differ not
Rule lines.
Middle level adhesive film is EVA glue-line, and lower layer mix feeding layer selects the yarn weaved fabric with fire protecting performance to make.Braiding upper strata
The radial line of metal fabric and parallel select the spun gold of a diameter of 0.10mm～0.50mm, filamentary silver, aluminium wire, copper wire, iron wire, rustless steel
Silk or B alloy wire material.The color of radial line and parallel select electroplated, enamelling process to process after any color or select not
True qualities with metal material.
The manufacture method of metal fabric wall cloth of the present invention comprises the steps:
A. first braided metal fabric, metal fabric has multiple texture, restrains and irregular two kinds by texture difference divider；B. by gold
Belong to fabric, middle level adhesive film and lower layer mix feeding layer to press together under the high temperature of 120 DEG C ± 5 DEG C and can be prepared by metal fabric wall
Cloth；C, finally cut molding, by detail design requirement, with guillotine, metal fabric wall cloth is cut into the shape of regulation.Then
Making two kinds of forms, a kind of is the form after cutting, another kind be by metal fabric wall cloth and therewith homotype shape sheet material bonding
All-in-one-piece form, finished product notes protecting the regularity of corner, can be made into the packaging being consistent with finished product and put well, and Package casing should be
Duricrust, pressure impact resistance.
Glue to select environment friendly and pollution-free translucent or transparent, can bonding metal fabric and cloth, select E6 glue here, bonding
Melt temperature controls at 120 DEG C ± 5 DEG C, and lower floor is cloth, and cloth selects fire protecting performance to be had, and selects yarn weaved fabric, grammes per square metre
About 300, elastic low, and at a temperature of 130 DEG C, keep 0 contraction, there is extraordinary cementability with E6 glue.Adhesion process is
Such, lower floor is base fabric, and centre is glue-line, is metal fabric on glue-line, and the width of cloth, glue-line and metal fabric is necessary
Ensure consistent.Three, must aligned position before entering pressing machine.After pressing, the most folded over, in order to avoid occurring that injustice is existing
As, the place of the metal fabric wall cloth storage to be lain in after pressing, it is to avoid have the uneven objects such as corner angle to contact.
In step a, the braider of braided metal fabric is the braiding being specifically designed to metal fabric braiding through transformation
Machine, selects the metal wire of a diameter of 0.10mm～0.50mm as latitude according to the performance use of design and the density requirements of lines
Line, the metallic cable of radial line a diameter of 0.10mm～0.50mm of selection, radial line is to be closed by single metal wire rod or multiply metal wire rod
The metallic cable become.
Step a requires metallic cable to be regular or erratic form as arranged radially according to design, by compiling
The Data Control mechanism controls of loom weaves, and knits out the metal fabric of various lines.Metal wire is noted during braiding
Rope does not scratch damage, after having woven, must avoid the shock that collides with, in order to avoid causing the marking in the mobile access course of processing
Or deform and become substandard products.
The invention has the beneficial effects as follows: the present invention relates to a kind of metal fabric wall cloth that can be used for wall fitting and manufacture thereof
Method, the metal fabric wall cloth of the present invention may be used for beautifying constructure wall, furniture surface, screen partition, glass sandwich, window
The various place such as curtain and gift wrap and the decoration of article surface.The present invention utilizes metal wire to replace traditional paper and weaving
Cloth, is compound to a kind of Novel wall cloth material realized on the cloth of icon bottom after braiding by metal wire or metallic cable,
The advantages such as the metal fabric wall cloth of the present invention has cycle in service life length, firm and durable, ageing-resistant, not mildew, pollution-free, gold
Belonging to fabric wall cloth surface and have the effect of metallic luster, decoration is noble magnificent, and texture is strong, has three-dimensional skin texture lines, the gold of the present invention
Belong to fabric wall cloth and also there is the performances such as fire protection flame retarding, mildew resistant moistureproof and sound-absorbing breathability.The present invention by metal wire through special
After metal wire weaving machine presses lines braiding, the various metal braid of formation and become through bonding processing on request with basis cloth
Type, replaces traditional paper and weaving cloth, thus a kind of Novel wall cloth ornament materials realized.
Accompanying drawing explanation
Fig. 1 is the structural representation of rule A lines metal fabric wall cloth of the present invention；
Fig. 2 is the cross-sectional view of rule A lines metal fabric wall cloth of the present invention；
Fig. 3 is the side structure schematic diagram of rule A lines metal fabric wall cloth of the present invention；
Fig. 4 is the structural representation of the present invention irregular B lines metal fabric wall cloth；
Fig. 5 is the cross-sectional view of the present invention irregular B lines metal fabric wall cloth；
Fig. 6 is the cross-sectional view of the present invention irregular C lines metal fabric wall cloth；
Fig. 7 is the cross-sectional view of rule D lines metal fabric wall cloth of the present invention；
Fig. 8 is the cross-sectional view of the present invention irregular E lines metal fabric wall cloth；
Fig. 9 is the cross-sectional view of rule F lines metal fabric wall cloth of the present invention；
Figure 10 is the cross-sectional view of the present invention irregular G lines metal fabric wall cloth；
In figure: 1-metallic cable；2-metal wire；3-middle level adhesive film；4-lower layer mix feeding layer.
Irregular B and irregular C is the metal wall cloth of irregular weaving method, and 1 is the metallic cable of synthesis, single or bifilar
And with can；2 is metal wire, monochromatic by design alternative or select shades of colour alternately to weave, it is possible to mariages is also used.
Irregular E and irregular G is the metal wall cloth of another kind of irregular weaving method, and 1 is the metallic cable of synthesis, Dan Shuan
Stock can, 2 is metal wire, monochromatic by design alternative or select shades of colour alternately to weave, can mariages using.
Rule A, rule D and rule F are the metal wall cloths of rule weaving method, and 1 is the metallic cable of synthesis, can want by lines
Seek the distance adjusted each other, it is also possible to mariages is also used；Rule F is another rule that have adjusted metallic cable spacing and obtain
The metal wall cloth of type lines；2 is metal wire, by design menu color or select shades of colour alternately to weave, and can mariages using.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the invention will be further described.
Embodiment 1: a kind of metal fabric wall cloth, it is by upper strata metal fabric, middle level adhesive film 3 and lower layer mix feeding layer 4
Up of three layers altogether, upper strata metal fabric is to be formed as radially braiding as broadwise and Duo Gen metallic cable 1 by many wires 2,
Upper strata metal fabric, middle level adhesive film 3 and lower layer mix feeding layer 4 are combined with each other through high temperature and make metal fabric wall cloth, upper strata gold
The braiding lines belonging to fabric is the rule lines that radial spacing is identical.Middle level adhesive film 3 is EVA glue-line, and lower layer mix feeding layer 4 selects
The yarn weaved fabric with fire protecting performance is made.Weave the optional monochrome of metal wire 2 of upper strata metal fabric or select shades of colour alternately
Weave.
Embodiment 2: a kind of metal fabric wall cloth, it is by upper strata metal fabric, middle level adhesive film 3 and lower layer mix feeding layer 4
Up of three layers altogether, upper strata metal fabric is to be formed as radially braiding as broadwise and Duo Gen metallic cable 1 by many wires 2,
Upper strata metal fabric, middle level adhesive film 3 and lower layer mix feeding layer 4 are combined with each other through high temperature and make metal fabric wall cloth, upper strata gold
The braiding lines belonging to fabric is the irregular lines that radial spacing differs.Middle level adhesive film 3 is EVA glue-line, lower layer mix feeding layer 4
The yarn weaved fabric with fire protecting performance is selected to make.Weave the metal wire 2 menu color of upper strata metal fabric or select shades of colour to hand over
For weaving.
The manufacture method of metal fabric wall cloth of the present invention comprises the steps: a. elder generation braided metal fabric, and metal fabric has
Multiple texture, is restrained and irregular two kinds by texture difference divider；B. metal fabric, middle level adhesive film and lower layer mix feeding layer are existed
Press together under the high temperature of 120 DEG C ± 5 DEG C and can be prepared by metal fabric wall cloth；C, finally cut molding, want by detail design
Ask, with guillotine, metal fabric wall cloth is cut into the shape of regulation.D, finally cut molding, by detail design requirement, by sanction
Metal fabric wall cloth is cut into the shape of regulation by machine of cutting.Then making two kinds of forms, a kind of is the form after cutting, another kind of
Being the form being bonded into one by the sheet material of metal fabric wall cloth and homotype shape therewith, finished product notes protecting the regularity of corner,
Can be made into the packaging being consistent with finished product to put well, Package casing should be duricrust, pressure impact resistance.
Glue selects environment friendly and pollution-free translucent or transparent, can bonding metal fabric and cloth, the present invention selects E6 glue, viscous
Closing melt temperature to control at 120 DEG C ± 5 DEG C, lower floor is cloth, and cloth selects fire protecting performance to be had, and selects yarn weaved fabric, gram
Focusing on about 300, elasticity is low, and keeps 0 contraction at a temperature of 130 DEG C, has extraordinary cementability with E6 glue.Adhesion process
Being such, lower floor is base fabric, and centre is glue-line, is metal fabric on glue-line, and the width of cloth, glue-line and metal fabric must
Must ensure consistent.Three, must aligned position before entering pressing machine.It is after pressing, the most folded over, in order to avoid injustice occurs
Phenomenon, the place of the metal fabric wall cloth storage to be lain in after pressing, it is to avoid have the uneven objects such as corner angle to contact.
In step a, the braider of braided metal fabric is the braiding being specifically designed to metal fabric braiding through transformation
Machine, selects the metal wire 2 of a diameter of 0.10mm～0.50mm as latitude according to the performance use of design and the density requirements of lines
Line, the metallic cable 1 of radial line a diameter of 0.10mm～0.50mm of selection, radial line is by single strand wire 2 material or multiply metal wire 2 material
The metallic cable 1 of synthesis.Radial line and parallel select spun gold, filamentary silver, aluminium wire, copper wire, iron wire, stainless steel silk or B alloy wire material, face
Color the most electroplated, the enamelling process of choosing process after any color or select the true qualities of different metal materials.According to design in step a
Require metallic cable 1 to be regular or erratic form as arranged radially, by the Data Control mechanism controls of braider
Weave, knit out the metal fabric of various lines.Notice during braiding that metal wire 2 is restricted and do not scratch damage, woven
Cheng Hou, must avoid the shock that collides with, in order to avoid causing the marking or deformation and becoming substandard products in the mobile access course of processing.
Metal fabric wall cloth in the present invention can be used in building interior and exterior wall decoration, can be also used in screen cut off,
The various places such as glass sandwich, curtain and gift wrap, it is possible to make the decoration on top-grade furniture surface, it is also possible to by the gold of the present invention
Belong to fabric wall cloth to be used in method of laminating glass, form the product of a kind of glass clamp colors metal pattern lines.
Last it should be noted that, above content is only in order to illustrate technical scheme, rather than the present invention is protected
The restriction of scope, simple modification that technical scheme is carried out by those of ordinary skill in the art or equivalent,
Spirit and scope all without departing from technical solution of the present invention.
Claims (7)
1. a metal fabric wall cloth, it is characterised in that: described metal fabric wall cloth is by upper strata metal fabric, middle level adhesive film
With lower layer mix feeding layer up of three layers altogether, described upper strata metal fabric is as broadwise and Duo Gen metallic cable conduct by many wires
Radially braiding forms, described upper strata metal fabric, middle level adhesive film and lower layer mix feeding layer through high temperature be combined with each other make described
Metal fabric wall cloth, the braiding lines of described upper strata metal fabric is divided into rule lines that radial spacing is identical and radial spacing not
Identical irregular lines.
Metal fabric wall cloth the most according to claim 1, it is characterised in that: described middle level adhesive film is EVA glue-line, described
Lower layer mix feeding layer selects the yarn weaved fabric with fire protecting performance to make.
Metal fabric wall cloth the most according to claim 1 and 2, it is characterised in that: weave the footpath of described upper strata metal fabric
Line and parallel select the spun gold of a diameter of 0.10mm～0.50mm, filamentary silver, aluminium wire, copper wire, iron wire, stainless steel silk or alloy wire
Material.
Metal fabric wall cloth the most according to claim 1 and 2, it is characterised in that: the color of described radial line and parallel is selected
Electroplated, enamelling process process after any color or select the true qualities of different metal materials.
The manufacture method of metal fabric wall cloth the most according to claim 1, it is characterised in that: described metal fabric wall cloth
Manufacture method comprises the steps:
A. first braided metal fabric, metal fabric has multiple texture, restrains and irregular two kinds by texture difference divider；
B. metal fabric, middle level adhesive film and lower layer mix feeding layer are pressed together under the high temperature of 120 DEG C ± 5 DEG C and can be prepared by
Metal fabric wall cloth；
C, finally cut molding, by detail design requirement, with guillotine, metal fabric wall cloth is cut into the shape of regulation.
The manufacture method of metal fabric wall cloth the most according to claim 5, it is characterised in that: in step a, braided metal is knitted
The braider of thing is the braider being specifically designed to metal fabric braiding through transformation, according to performance use and the lines of design
Density requirements select the metal wire of a diameter of 0.10mm～0.50mm as parallel, radial line select a diameter of 0.10mm～
The metallic cable of 0.50mm, radial line is the metallic cable synthesized by single metal wire rod or multiply metal wire rod.
The manufacture method of metal fabric wall cloth the most according to claim 5, it is characterised in that: step a is wanted according to design
Asking metallic cable as arranged radially is regular or erratic form, is carried out by the Data Control mechanism controls of braider
Braiding, knits out the metal fabric of various lines.