CN108221121A - A kind of manufacturing method of Active manganese wall paper - Google Patents

A kind of manufacturing method of Active manganese wall paper Download PDF

Info

Publication number
CN108221121A
CN108221121A CN201810002324.7A CN201810002324A CN108221121A CN 108221121 A CN108221121 A CN 108221121A CN 201810002324 A CN201810002324 A CN 201810002324A CN 108221121 A CN108221121 A CN 108221121A
Authority
CN
China
Prior art keywords
lining cloth
active manganese
cloth layer
wall paper
air
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201810002324.7A
Other languages
Chinese (zh)
Other versions
CN108221121B (en
Inventor
李国兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongtu Lian Network Technology Qinhuangdao Co.,Ltd.
Original Assignee
Shaoxing Xinyu Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaoxing Xinyu Textile Co Ltd filed Critical Shaoxing Xinyu Textile Co Ltd
Priority to CN201810002324.7A priority Critical patent/CN108221121B/en
Publication of CN108221121A publication Critical patent/CN108221121A/en
Application granted granted Critical
Publication of CN108221121B publication Critical patent/CN108221121B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to wall paper manufacturing methods, disclose a kind of manufacturing method of Active manganese wall paper, include the following steps：（1）Jacquard layer weaves：Jacquard layer warp is immersed into the first Active manganese mixed liquor, takes out and air-dries after jacquard layer warp drenches；Jacquard layer weft is immersed into photocatalyst mixed liquor, takes out and air-dries after jacquard layer weft drenches；Jacquard layer warp after air-drying is woven into jacquard layer with jacquard layer weft longitude and latitude；（2）Lining cloth layer weaves：Lining cloth layer warp is immersed into mould inhibitor mixed liquor, takes out and air-dries after lining cloth layer longitude and latitude drenches；Lining cloth layer weft is immersed into the second Active manganese mixed liquor, takes out and air-dries after lining cloth layer weft drenches；Lining cloth layer warp after air-drying is woven into lining cloth layer with lining cloth layer weft longitude and latitude；（3）Compound adhesive is configured；（4）Wall paper is compound.The present invention has the following advantages and effects：It avoids formaldehyde from discharging again and secondary pollution is caused into air by Active manganese decomposing formaldehyde.

Description

A kind of manufacturing method of Active manganese wall paper
Technical field
The present invention relates to wall paper manufacturing method, more particularly to a kind of manufacturing method of Active manganese wall paper.
Background technology
Wall paper is a kind of common inner wall of building decorative material for wall surface, and existing wall paper is generally compound by lining cloth layer and decorative layer It forms, lining cloth layer is with decorative layer in the fabrication process in order to reach the effects that wrinkle resistant, shrinkproof, fire-retardant or in order to keep stamp, dye The durability of color or in order to improve feel, need to just add formaldehyde in auxiliary agent.Formaldehyde has stimulation, formaldehyde to mucocutaneous When reaching a certain concentration indoors, people just has sense of discomfort；More than 0.08m3Concentration of formaldehyde furious, eye can be caused to itch, throat not Suitable or pain, hoarseness, sneeze, uncomfortable in chest, asthma, dermatitis etc..If its content of formaldehyde of house that just finishing has been completed is higher, meeting Induce more diseases.
At present, the Chinese invention patent of Publication No. CN106401102A discloses a kind of wall paper and preparation method thereof, By adding in activated carbon in environmental protection layer, by activated carbon for the absorption of formaldehyde so as to reduce indoor formaldehyde concentration.Activated carbon With stronger adsorptivity, therefore activated carbon being capable of formaldehyde adsorption.But absorption is reversible, when adsorbance reaches a certain level, Absorption will carry out round about, and under natural conditions, gas all can constantly be flowed to the direction of low concentration, and absorption can exist Formaldehyde on activated carbon is discharged into air again, causes secondary pollution.
Invention content
The object of the present invention is to provide a kind of manufacturing methods of Active manganese wall paper, by Active manganese decomposing formaldehyde, avoid Formaldehyde discharges again causes secondary pollution into air.
The present invention above-mentioned technical purpose technical scheme is that：A kind of manufacture of Active manganese wall paper Method includes the following steps：
(1) jacquard layer weaves：Jacquard layer warp is immersed into the first Active manganese mixed liquor, after jacquard layer warp drenches It takes out and air-dries；Jacquard layer weft is immersed into photocatalyst mixed liquor, takes out and air-dries after jacquard layer weft drenches；After air-drying Jacquard layer warp with air-dry after jacquard layer weft longitude and latitude be woven into jacquard layer；
(2) lining cloth layer weaves：Lining cloth layer warp is immersed into mould inhibitor mixed liquor, is taken out after lining cloth layer longitude and latitude drenches It air-dries；Lining cloth layer weft is immersed into the second Active manganese mixed liquor, takes out and air-dries after lining cloth layer weft drenches；After air-drying Lining cloth layer warp with air-dry after lining cloth layer weft longitude and latitude be woven into lining cloth layer；
(3) compound adhesive is configured：Coating adhesive, activated carbon and Active manganese are mixed and made into compound adhesive；
(4) wall paper is compound：Jacquard layer is compound by compound adhesive and lining cloth layer.
By using above-mentioned technical proposal, the Active manganese that is adhered on jacquard layer warp can decomposing formaldehyde, lining cloth layer weft The Active manganese of upper adherency also can decomposing formaldehyde, since jacquard layer warp and lining cloth layer weft shift to install to absorb difference The formaldehyde in direction；The photocatalyst adhered on jacquard layer weft generates strong catalytic degradation under the action of ultraviolet light and visible ray Function, toxic and harmful gas in the air that can effectively degrade；The mould inhibitor adhered on lining cloth layer warp can prevent lining cloth layer mould Bacterium grows；Due to being mixed with activated carbon and Active manganese in compound adhesive, activated carbon can formaldehyde adsorption, Active manganese can decompose first Aldehyde can be decomposed the formaldehyde of activated carbon adsorption is reversible by adjacent Active manganese.
The present invention is further arranged to, in step (1) the first Active manganese mixed liquor by following mass percent each component It forms：
By using above-mentioned technical proposal, if the content of Active manganese is higher than 25%, not only increase production cost, but also can shadow The performance that jacquard layer warp has in itself is rung, if the content of Active manganese is less than 15%, causes Active manganese decomposing formaldehyde effect It is undesirable；Dispersant dispersible active manganese prevents the sedimentation and cohesion of particle；Stabilizer can improve the stabilization of Active manganese mixed liquor Property；Antisettling agent can be such that Active manganese is uniformly dispersed in water.
The present invention is further arranged to, and photocatalyst mixed liquor is made of each component of following mass percent in step (1)：
By using above-mentioned technical proposal, if the content of photocatalyst is higher than 30%, not only increase production cost, but also adhere to Photocatalyst can influence the performance that jacquard layer weft has in itself, if the content of photocatalyst be less than 10%, cannot be effectively Toxic and harmful gas in degradation air；The dispersible photocatalyst of dispersant prevents the sedimentation and cohesion of particle；Stabilizer can improve light The stability of catalyst mixed liquor；Antisettling agent can be such that photocatalyst is uniformly dispersed in water.
The present invention is further arranged to, and mould inhibitor mixed liquor is made of each component of following mass percent in step (2)：
By using above-mentioned technical proposal, if the content of mould inhibitor is higher than 35%, not only increase production cost, but also adhere to Mould inhibitor can influence the performance that lining cloth layer warp has in itself, if the content of mould inhibitor be less than 20%, can not prevent Lining cloth layer mould grows；The dispersible mould inhibitor of dispersant prevents the sedimentation and cohesion of particle；Stabilizer can improve mould inhibitor mixing The stability of liquid；Antisettling agent can be such that mould inhibitor is uniformly dispersed in water.
The present invention is further arranged to, in step (2) the second Active manganese mixed liquor by following mass percent each component It forms：
By using above-mentioned technical proposal, lining cloth layer between interior wall and jacquard layer, therefore lining cloth layer weft contact Air area is fewer than the air area that jacquard layer contacts, therefore the Active manganese adhered on lining cloth layer weft on jacquard layer warp than gluing Attached Active manganese can be reduced, and can not only reduce production cost, and can avoid influencing the performance of lining cloth layer weft in itself；Point Powder dispersible active manganese prevents the sedimentation and cohesion of particle；Stabilizer can improve the stability of Active manganese mixed liquor；Anti- precipitation Agent can be such that Active manganese is uniformly dispersed in water.
The present invention is further arranged to, and compound adhesive further includes dispersant, stabilizer, antisettling agent and endures with all one's will in step (3) Agent, compound adhesive are made of each component of following mass percent：
By using above-mentioned technical proposal, the setting of activated carbon can formaldehyde adsorption, the setting of Active manganese can decompose first Aldehyde can be decomposed the formaldehyde of activated carbon adsorption is reversible by adjacent Active manganese；Dispersant dispersible active manganese and activated carbon, Prevent the sedimentation and cohesion of particle；Stabilizer can improve the stability of compound adhesive；Antisettling agent can make Active manganese and activated carbon equal Even is scattered in coating adhesive；Stiffening agent can improve wall paper appearance, increase wall paper elasticity and sense of fullness.
The present invention is further arranged to, and compound adhesive further includes Lavender, and compound adhesive is each by following mass percent Component is formed：
By using above-mentioned technical proposal, the addition of Lavender can not only purify air, and can also play town Quiet hypnosis, the effect of spasmolysis, antibacterial and neuroprotection.
The present invention is further arranged to, and jacquard layer warp is made of china-hemp fibers and silver fiber hybrid woven in step (1), Jacquard layer weft is made of profiled filament and polyester fiber hybrid woven.
By using above-mentioned technical proposal, due to the unique texture of china-hemp fibers, fibrillar center has larger cavity, longitudinal direction There are many crack that is attached thereto and holes, and fiber is made to have more capillary channel, can shift rapidly in diffusing fabric Moisture and steam, so as to which wall paper is avoided to make moist；Silver ion has very high bioactivity in silver fiber so that bacterium Protein coagulating inside and outside cell membrane, so as to block the breathing of bacterial cell and reproductive process；Profiled filament is because section is in special Shape, cohesive force that can be between reinforcing fiber improve the bulkiness and gas permeability of fiber；Polyester fiber is high, wear-resisting, resistance to intensity Corrosion and light resistance.
The present invention is further arranged to, and lining cloth layer warp is made of cotton fiber and bamboo charcoal fiber hybrid woven in step (2), Lining cloth layer weft is made of china-hemp fibers and high water absorption water absorbent fiber hybrid woven.
By using above-mentioned technical proposal, cotton fiber moisture absorption and good permeability are soft and warming；Bamboo charcoal fiber has superpower Adsorption capacity, bamboo Charcoal Adsorption ability is 5 times of charcoal or more, and the harmful substances such as PARA FORMALDEHYDE PRILLS(91,95), benzene, toluene, ammonia and dust can play The effect of peculiar smell and smelly eliminating is absorbed, decomposes, anion emission concentration is high, environmentally protective；The unique texture of china-hemp fibers, in fiber The heart has larger cavity, and longitudinal direction makes fiber have more capillary channel, Neng Gouxun there are many crack and hole that are attached thereto Moisture and steam in speed transfer and diffusing fabric, so as to which wall paper is avoided to make moist；High water absorption water absorbent fiber has very high , there are good gas permeability and heat insulating ability in hygroscopicity and water penetration, and without viscous wet sense, even if after moisture absorption.
In conclusion the invention has the advantages that：
1st, the Active manganese adhered on jacquard layer warp can decomposing formaldehyde, the Active manganese adhered on lining cloth layer weft can also divide Formaldehyde is solved, the formaldehyde so as to absorb different directions is shifted to install due to jacquard layer warp and lining cloth layer weft；Jacquard layer latitude The photocatalyst adhered on line generates strong catalytic degradation function under the action of ultraviolet light and visible ray, and can effectively degrade sky Toxic and harmful gas in gas；The mould inhibitor adhered on lining cloth layer warp can prevent lining cloth layer mould from growing；Due in compound adhesive Be mixed with activated carbon and Active manganese, activated carbon can formaldehyde adsorption, Active manganese can decomposing formaldehyde, even if the first of activated carbon adsorption Aldehyde is reversible also to be decomposed by adjacent Active manganese；
2nd, the addition of Lavender can not only purify air, and can also play tranquilizing soporific, spasmolysis, antibacterial and god Effect through protection；
3rd, due to the unique texture of china-hemp fibers, fibrillar center has larger cavity, and longitudinally there are many what is be attached thereto to split Gap and hole, make fiber have more capillary channel, can shift rapidly with the moisture and steam in diffusing fabric, so as to Enough wall paper is avoided to make moist；Silver ion has very high bioactivity in silver fiber so that the protein inside and outside bacterial cell membrane Solidification, so as to block the breathing of bacterial cell and reproductive process；Profiled filament, can be between reinforcing fiber because section is in special shape Cohesive force improves the bulkiness and gas permeability of fiber；Polyester fiber has that intensity is high, wear-resisting, corrosion-resistant and light resistance；
4th, cotton fiber moisture absorption and good permeability, it is soft and warming；Bamboo charcoal fiber has superpower adsorption capacity, bamboo Charcoal Adsorption energy Power is 5 times of charcoal or more, and the harmful substances such as PARA FORMALDEHYDE PRILLS(91,95), benzene, toluene, ammonia and dust can play absorption, decompose peculiar smell and smelly eliminating Effect, anion emission concentration is high, environmentally protective；The unique texture of china-hemp fibers, fibrillar center have larger cavity, longitudinal direction There are many crack that is attached thereto and holes, and fiber is made to have more capillary channel, can shift rapidly in diffusing fabric Moisture and steam, so as to which wall paper is avoided to make moist；High water absorption water absorbent fiber has very high hygroscopicity and water penetration, and Wet sense is not glued, there are good gas permeability and heat insulating ability in even if after moisture absorption.
Specific embodiment
Embodiment 1
A kind of manufacturing method of Active manganese wall paper, includes the following steps：
(1) jacquard layer weaves：Jacquard layer warp is immersed into the first Active manganese mixed liquor, after jacquard layer warp drenches It takes out and air-dries；Jacquard layer weft is immersed into photocatalyst mixed liquor, takes out and air-dries after jacquard layer weft drenches；After air-drying Jacquard layer warp with air-dry after jacquard layer weft longitude and latitude be woven into jacquard layer.
First Active manganese mixed liquor is made of each component of following mass percent：
Photocatalyst mixed liquor is made of each component of following mass percent：
Jacquard layer warp is made of china-hemp fibers and silver fiber hybrid woven, and jacquard layer weft is fine by profiled filament and terylene Dimension hybrid woven is made.
(2) lining cloth layer weaves：Lining cloth layer warp is immersed into mould inhibitor mixed liquor, is taken out after lining cloth layer longitude and latitude drenches It air-dries；Lining cloth layer weft is immersed into the second Active manganese mixed liquor, takes out and air-dries after lining cloth layer weft drenches；After air-drying Lining cloth layer warp with air-dry after lining cloth layer weft longitude and latitude be woven into lining cloth layer；
Mould inhibitor mixed liquor is made of each component of following mass percent：
Second Active manganese mixed liquor is made of each component of following mass percent：
Lining cloth layer warp is made of cotton fiber and bamboo charcoal fiber hybrid woven, and lining cloth layer weft is by china-hemp fibers and high water absorption Water absorbent fiber hybrid woven is made.
(3) compound adhesive is configured：By dispersant, stabilizer, antisettling agent and stiffening agent, coating adhesive, activated carbon and Active manganese It is mixed and made into compound adhesive；Compound adhesive is made of each component of following mass percent：
(4) wall paper is compound：Jacquard layer is compound by compound adhesive and lining cloth layer.
Embodiment 2
By the manufacturing method of 1 wall paper of embodiment, it is in the difference of embodiment 1 in the first Active manganese mixed liquor by following matter The each component for measuring percentage is formed：
Photocatalyst mixed liquor is made of each component of following mass percent：
Mould inhibitor mixed liquor is made of each component of following mass percent：
Second Active manganese mixed liquor is made of each component of following mass percent：
Compound adhesive is made of each component of following mass percent：
Embodiment 3
By the manufacturing method of 1 wall paper of embodiment, it is in the difference of embodiment 1 in the first Active manganese mixed liquor by following matter The each component for measuring percentage is formed：
Photocatalyst mixed liquor is made of each component of following mass percent：
Mould inhibitor mixed liquor is made of each component of following mass percent：
Second Active manganese mixed liquor is made of each component of following mass percent：
Compound adhesive is made of each component of following mass percent：
Embodiment 4
By the manufacturing method of 1 wall paper of embodiment, it is in the difference of embodiment 1 in by Lavender, dispersant, stabilization Agent, antisettling agent and stiffening agent, coating adhesive, activated carbon and Active manganese are mixed and made into compound adhesive；Compound adhesive is by following quality percentage The each component of ratio is formed：
Embodiment 5
By the manufacturing method of 1 wall paper of embodiment, it is in the difference of embodiment 1 in by Lavender, dispersant, stabilization Agent, antisettling agent and stiffening agent, coating adhesive, activated carbon and Active manganese are mixed and made into compound adhesive；Compound adhesive is by following quality percentage The each component of ratio is formed：
Embodiment 6
By the manufacturing method of 1 wall paper of embodiment, it is in the difference of embodiment 1 in by Lavender, dispersant, stabilization Agent, antisettling agent and stiffening agent, coating adhesive, activated carbon and Active manganese are mixed and made into compound adhesive；Compound adhesive is by following quality percentage The each component of ratio is formed：
Wall paper of the present invention is with being addition activated carbon wall paper Experimental comparison：
Concentration of formaldehyde, original indoor formaldehyde concentration are detected in the confined chamber of same space and in the case that temperature is identical For：0.2mg/m3, comparing result such as table 1：
Product Time Concentration of formaldehyde Product Time Concentration of formaldehyde
Embodiment 1 12h 0.11mg/m3 Activated carbon wall paper 12h 0.14mg/m3
Embodiment 2 24h 0.05mg/m3 Activated carbon wall paper 24h 0.09mg/m3
Embodiment 3 36h 0.02mg/m3 Activated carbon wall paper 36h 0.05mg/m3
Embodiment 4 48h 0.01mg/m3 Activated carbon wall paper 48h 0.04mg/m3
Embodiment 5 60h 0 Activated carbon wall paper 60h 0.06mg/m3
Embodiment 6 72h 0 Activated carbon wall paper 72h 0.06mg/m3
Found out by table, the formaldehyde that the present invention can be in fast decoupled air, and be not in reversible；Containing activated carbon Wall paper can also adsorb formaldehyde in air, but the efficiency adsorbed is significantly lower than the present invention, and interior was checked again at 60 hours There is reversible in its value of concentration of formaldehyde, and in 72 hours rear chambers still with the presence of formaldehyde.
This specific embodiment is only explanation of the invention, is not limitation of the present invention, people in the art Member can as needed make the present embodiment the modification of no creative contribution after this specification is read, but as long as at this It is all protected in the right of invention by Patent Law.

Claims (9)

1. a kind of manufacturing method of Active manganese wall paper, it is characterized in that including the following steps：
(1) jacquard layer weaves：Jacquard layer warp is immersed into the first Active manganese mixed liquor, is taken out after jacquard layer warp drenches It air-dries；Jacquard layer weft is immersed into photocatalyst mixed liquor, takes out and air-dries after jacquard layer weft drenches；Carrying after air-drying Flower layer warp is woven into jacquard layer with the jacquard layer weft longitude and latitude after air-drying；
(2) lining cloth layer weaves：Lining cloth layer warp is immersed into mould inhibitor mixed liquor, wind is taken out after lining cloth layer longitude and latitude drenches It is dry；Lining cloth layer weft is immersed into the second Active manganese mixed liquor, takes out and air-dries after lining cloth layer weft drenches；After air-drying Lining cloth layer warp is woven into lining cloth layer with the lining cloth layer weft longitude and latitude after air-drying；
(3) compound adhesive is configured：Coating adhesive, activated carbon and Active manganese are mixed and made into compound adhesive；
(4) wall paper is compound：Jacquard layer is compound by compound adhesive and lining cloth layer.
2. a kind of manufacturing method of Active manganese wall paper according to claim 1, it is characterized in that：
The first Active manganese mixed liquor is made of each component of following mass percent in step (1)：
3. a kind of manufacturing method of Active manganese wall paper according to claim 1, it is characterized in that：
Photocatalyst mixed liquor is made of each component of following mass percent in step (1)：
4. a kind of manufacturing method of Active manganese wall paper according to claim 1, it is characterized in that：
Mould inhibitor mixed liquor is made of each component of following mass percent in step (2)：
5. a kind of manufacturing method of Active manganese wall paper according to claim 1, it is characterized in that：
The second Active manganese mixed liquor is made of each component of following mass percent in step (2)：
6. a kind of manufacturing method of Active manganese wall paper according to claim 1, it is characterized in that：
Compound adhesive further includes dispersant, stabilizer, antisettling agent and stiffening agent in step (3), and compound adhesive is by following quality percentage The each component of ratio is formed：
7. a kind of manufacturing method of Active manganese wall paper according to claim 6, it is characterized in that：
Compound adhesive further includes Lavender, and compound adhesive is made of each component of following mass percent：
8. a kind of manufacturing method of Active manganese wall paper according to claim 1, it is characterized in that：
Jacquard layer warp is made of china-hemp fibers and silver fiber hybrid woven in step (1), jacquard layer weft by profiled filament and Polyester fiber hybrid woven is made.
9. a kind of manufacturing method of Active manganese wall paper according to claim 1, it is characterized in that：
Lining cloth layer warp is made of cotton fiber and bamboo charcoal fiber hybrid woven in step (2), lining cloth layer weft by china-hemp fibers and High water absorption water absorbent fiber hybrid woven is made.
CN201810002324.7A 2018-01-02 2018-01-02 Method for manufacturing active manganese wall cloth Active CN108221121B (en)