CN107474614A - 一种抗反射膜的底漆配方及制备方法 - Google Patents

一种抗反射膜的底漆配方及制备方法 Download PDF

Info

Publication number
CN107474614A
CN107474614A CN201710660726.1A CN201710660726A CN107474614A CN 107474614 A CN107474614 A CN 107474614A CN 201710660726 A CN201710660726 A CN 201710660726A CN 107474614 A CN107474614 A CN 107474614A
Authority
CN
China
Prior art keywords
reflective film
base paint
paint formulation
structural
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710660726.1A
Other languages
English (en)
Other versions
CN107474614B (zh
Inventor
胡好荣
庄敬国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yingtan Laiqi Technology Co ltd
Original Assignee
ACTIF POLARIZERS(CHINA) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ACTIF POLARIZERS(CHINA) Co Ltd filed Critical ACTIF POLARIZERS(CHINA) Co Ltd
Priority to CN201710660726.1A priority Critical patent/CN107474614B/zh
Publication of CN107474614A publication Critical patent/CN107474614A/zh
Application granted granted Critical
Publication of CN107474614B publication Critical patent/CN107474614B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种抗反射膜的底漆配方，其包括按质量比计的75%异丙醇、22%正丁醇、1%醋酸和2%硅烷。采用本发明的配方形成的底漆粘合性好，使得该底漆应用于抗反射膜中能够使得抗反射膜的TAC主体层和微结构哑光层结合牢度好，保证抗反射膜的质量。

Description

一种抗反射膜的底漆配方及制备方法
技术领域
本发明属于光学材料领域，具体涉及一种抗反射膜的底漆配方及制备方法。
背景技术
光污染是继废气、废水、废渣和噪声等污染之后的一种新的环境污染源，其主要包括白亮污染、人工白昼污染和彩光污染等镜面反射污染和发光污染，霓虹灯、广告牌灯、LED灯、荧光灯、旋转灯等人工白昼光和彩色光污染，以及商店的大块镜面或铝合金装饰门面、建筑物的钢化玻璃、大理石、衣服镜面装饰、眼镜等镜面反射光污染。
据研究，当光的单位反射强度达到一定的值时，光污染不仅伤害人眼的眼角和虹膜，引起视力下降，增加白内障的发病率；同时也扰乱人们正常的生物节律，使人体生物钟混乱，导致食欲不振、精神低迷等身心健康。
由此产生了一种能有效分散单位强光反射强度，降低反射能量的抗反射膜，如图1所示，该抗反射膜由TAC主体层1、底漆层2、微结构哑光层3和电镀层4构成，其中底漆层2是基材与微结构哑光层3粘合的架桥，如果粘合效果不好，在微结构膜层与基材复合时牢度不合格，无法应用，微结构膜层无法实现内置的目的。
现有技术的底漆一般采用甲醇10%与二氯甲烷90%形成的混合溶液，或者采用85.7%二氯乙烷、9.5%甲醇和4.8%丙酮形成的混合溶液。现有底漆的粘合性较差，导致将该底漆应用于抗反射膜时，抗反射膜的TAC主体层与微结构哑光层之间的接合牢度差，影响抗反射膜的质量。
发明内容
本发明的目的在于提供一种扛反射膜的底漆配方,该配方形成的底漆粘合性好。
为实现上述目的，本发明采用的技术方案是：
一种抗反射膜的底漆配方，其包括按质量比计的75%异丙醇、22%正丁醇、1%醋酸和2%硅烷。
一种抗反射膜的底漆制备方法，首先将75%的异丙醇和22%的正丁醇混合,然后加入1%的醋酸,混合均匀后加入2%硅烷进行搅拌，搅拌均匀后静置2小时即制得抗反射膜的底漆。
与现有技术相比，采用本发明底漆配方制得的底漆粘合性好，将该底漆应用于抗反射膜中能够使得抗反射膜的TAC主体层和微结构哑光层结合牢度好，保证抗反射膜的质量。
附图说明
图1为抗反射膜的结构示意图。
具体实施方式
本发明揭示了一种抗反射膜的底漆配方，其包括按质量比计的75%异丙醇、22%正丁醇、1%醋酸和2%硅烷。
按照上述配方中的配比，首先将异丙醇和正丁醇混合,然后加入醋酸,混合均匀后加入硅烷进行搅拌，搅拌均匀后静置2小时，即制得抗反射膜的底漆。
以下表格为实验配方比例的部分实验数据结果：
上述表格中的第1组和第2组底漆配方为现有技术中的底漆配方，从表格中可以得出：
第1组和第2组提供的现有底漆配方制得的底漆应用于抗反射膜时，抗反射膜的TAC主体层1与微结构哑光层3的结合牢度差；
第3组底漆配方制得的底漆应用于抗反射膜时，抗反射膜的TAC主体层1与微结构哑光层3的结合牢度差；
第4组底漆配方制得的底漆应用于抗反射膜时，抗反射膜的TAC主体层1与微结构哑光层3的结合牢度较佳；
第5组底漆配方制得的底漆应用于抗反射膜时，抗反射膜的TAC主体层1与微结构哑光层3的结合牢度最佳。
所以，与现有技术相比，采用本发明底漆配方制得的底漆粘合性好，将该底漆应用于抗反射膜中能够使得抗反射膜的TAC主体层1和微结构哑光层3结合牢度好，保证抗反射膜的质量。

Claims (2)

1.一种抗反射膜的底漆配方，其特征在于：其包括按质量比计的75%异丙醇、22%正丁醇、1%醋酸和2%硅烷。
2.一种抗反射膜的底漆制备方法，其特征在于：首先将75%的异丙醇和22%的正丁醇混合,然后加入1%的醋酸,混合均匀后加入2%硅烷进行搅拌，搅拌均匀后静置2小时即制得抗反射膜的底漆。
CN201710660726.1A 2017-08-04 2017-08-04 一种抗反射膜的底漆配方及制备方法 Active CN107474614B (zh)