CN107474460A - A kind of resin tile on heat-insulating sound-insulating log cabin roof - Google Patents
A kind of resin tile on heat-insulating sound-insulating log cabin roof Download PDFInfo
- Publication number
- CN107474460A CN107474460A CN201710803058.3A CN201710803058A CN107474460A CN 107474460 A CN107474460 A CN 107474460A CN 201710803058 A CN201710803058 A CN 201710803058A CN 107474460 A CN107474460 A CN 107474460A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulating
- resin tile
- poured
- standby
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of resin tile on heat-insulating sound-insulating log cabin roof, the resin tile is by 18 22 parts of acrylonitrile matching in parts by weight, 10 12 parts of styrene, 25 30 parts of ACM, 19 22 parts of dimethyldichlorosilane, 9 11 parts of vinyl ring body, 68 parts of tetramethyl divinyl disiloxane, 14 parts of Octoxinol, 6 10 parts of lead orthoplumbate, 11 13 parts of iron oxide, 8 10 parts of isobutene, 7 11 parts of isoprene, 68 parts of potassium silicate, 46 parts of yittrium oxide, 58 parts of lanthana, 35 parts of silicon nitride, 14 parts of compositions of 68 parts of alchlor and nano zirconium dioxide;There are outstanding heat-insulated and sound insulation capabilities using the heat-insulating sound-insulating log cabin roof of the resin tile.
Description
Technical field
The present invention relates to a kind of resin tile on heat-insulating sound-insulating log cabin roof.
Background technology
Refer to that " log cabin " naturally just expects the romance rural area in Europe.Europe is the continent of ancient mystery, the essence in various countries city
Essence is a splendid legacy, and leaves a good name from generation to generation, the romantic breath distributed everywhere, gives and gets deeply stuck in wherein, sensation so enchanted by the scenery as to forget to return.Europe
The log cabin of the unique style in rural area can be described as the soul of everything --- without reinforcing bar, without concrete, without brick and tile, only mud
The breath of the native fragrance of a flower, the sensation physically and mentally to go back to nature, the gains in depth of comprehension of anxiety have arrived quiet, tired out body and loosened.
Nowadays, show in these countries in Europe, new differentials between town and country.But, it is specifically " rural area is better than city ",
One investigation shows that 89% rural population is reluctant to leave rural area, and 56% urban population wishes firmly to go to the countryside.Why
So more people want to return to rural areaThe indifferent to fame or gain living environment in rural area make us it is charmed, it is to have characteristic also more to attract theirs
The log house of living environment one.The ice-cold breath of steel brick structure has been weary of it, log cabin has rekindled people and lacked in the heart for a long time
Graceful, quiet, natural rural sentiment.
The roof of log cabin will bear to expose to the sun and rain, even the atrocious weather such as hail, in the prior art the roof of log cabin
Typically only with various tiles, but tile, after being persistently exposed to the sun of the sun, heat is slowly delivered on timber, it is difficult to is dropped
Temperature, and influenceed by rainy day and hail, it is difficult to meet the market demand only with the roof soundproof effect of tile.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of heat-insulating sound-insulating wood with outstanding heat-insulated and sound insulation capabilities
The resin tile on room roof.
To solve the above problems, the present invention adopts the following technical scheme that:
A kind of resin tile on heat-insulating sound-insulating log cabin roof, the resin tile is by the acrylonitrile 18-22 that matches in parts by weight
Part, styrene 10-12 parts, ACM 25-30 parts, dimethyldichlorosilane 19-22 parts, vinyl ring body 9-11 parts,
Tetramethyl divinyl disiloxane 6-8 parts, Octoxinol 1-4 parts, lead orthoplumbate 6-10 parts, iron oxide 11-13 parts, isobutyl
Alkene 8-10 parts, isoprene 7-11 parts, potassium silicate 6-8 parts, yittrium oxide 4-6 parts, lanthana 5-8 parts, silicon nitride 3-5 parts, trichlorine
Change aluminium 6-8 parts and nano zirconium dioxide 1-4 parts composition,
The manufacture method of resin tile, comprises the following steps:
1) dimethyldichlorosilane 19-22 parts are poured into vessel, then add appropriate moisture so that dimethyl two
Fallen after chlorosilane 19-22 part complete hydrolysis with together with vinyl ring body 9-11 parts and tetramethyl divinyl disiloxane 6-8 parts
Enter into reactor, be then heated to 300 DEG C so that vinyl ring body 9-11 parts crack completely, and mixture is made, standby;
2) mixture made from step 1) is poured into distillation equipment and carries out vacuum distillation processing, until mixture becomes
Untill colourless transparent liquid, colourless transparent liquid is made, it is standby;
3) isobutene 8-10 parts and isoprene 7-11 parts are placed in reaction vessel together, then add alchlor 6-
8 parts and it is sufficiently stirred, brings it about catalytic reaction, fully carry out cooling treatment after reaction, rubber is made, it is standby;
4) acrylonitrile 18-22 parts, styrene 10-12 parts, ACM 25-30 parts are poured into emulsification stirring together
In pot, Octoxinol 1-4 parts are added after stirring, carry out emulsification treatment 40 minutes, are taken out, cooling, synthesis modeling is made
Material, it is standby;
5) by rubber one made from colourless transparent liquid made from synthetic plastic made from step 4), step 2) and step 3)
Rise and be poured into boiler and be heated to 450 DEG C so that synthetic plastic and rubber added after being completely dissolved lead orthoplumbate 6-10 parts,
Iron oxide 11-13 parts, potassium silicate 6-8 parts, yittrium oxide 4-6 parts, lanthana 5-8 parts, silicon nitride 3-5 parts and nano zirconium dioxide 1-
4 parts, stir, sticky mixing liquid is made, it is standby;
6) sticky mixing liquid made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Brief description of the drawings
Fig. 1 applies the overall structure diagram on heat-insulating sound-insulating log cabin roof for a kind of resin tile of the present invention.
Embodiment
Embodiment one:
As shown in figure 1, a kind of heat-insulating sound-insulating log cabin roof using the resin tile, including crossbeam 1, solid wood board 2 and resin
Watts 3, curb girder 4 is provided with the crossbeam 1, the curb girder 4 and the mortise-tenon joint of crossbeam 1, the solid wood board 2 are equipped on curb girder 4,
Tap bolt (not shown) is provided with the solid wood board 2, the tap bolt is threadedly coupled with curb girder 4, on the solid wood board 2
Ceramic beaverboard 5 is equipped with, reinforcement adhesive tape 6, the ceramic beaverboard 5 are provided between the solid wood board 2 and ceramic beaverboard 5
On be provided with silica-gel heat-insulating pad 7, the surface of silica-gel heat-insulating pad 7 is that crest shape is set, and is provided with the silica-gel heat-insulating pad 7 light
Steel joist 8, the lightgage steel joist 8 are set to be embedded in ceramic beaverboard 5, and aluminum alloy bar 9 is welded with the lightgage steel joist 8,
The resin tile 3 is installed on aluminum alloy bar 9.
The aluminum alloy bar 9 is hollow setting, can mitigate the overall weight on roof significantly, reduces the burden of crossbeam 1.
Anticorrosive coating (not shown) is scribbled on the aluminum alloy bar 9 and lightgage steel joist 8, aluminum alloy bar 9 can be prevented
It is etched with lightgage steel joist 8, it is durable in use.
The surface of silica-gel heat-insulating pad 7 scribbles lotus leaf emulsion paint (not shown), can be with rainy and self-cleaning, and pollutant can not
The whole surface in silica-gel heat-insulating pad 7 is attached, and can only loosely be gathered in surface, because surface can hardly be stained with wetting, institute
Tumbled with dust-laden rainwater beading, whole surface is chronically at drying regime, prevents microorganism from being attached to the surface of silica-gel heat-insulating pad 7.
It is provided with tenon (not shown) on the solid wood board 2, the tenon is set to be embedded in ceramic beaverboard 5, can be with
Lift the stability between solid wood board 2 and ceramic beaverboard 5.
Solid-wood (not shown) is provided with the curb girder 1, multiple stress points can be provided, so as to lift the entirety on roof
Stability.
Another technical problem to be solved by the invention is a kind of manufacture method of resin tile of offer.
To solve the above problems, the present invention adopts the following technical scheme that:
By 25 parts of 10 parts of 18 parts of acrylonitrile, styrene, ACM, the dimethyl dichloro silicon matched in parts by weight
19 parts of alkane, 9 parts of vinyl ring body, 6 parts of tetramethyl divinyl disiloxane, 1 part of Octoxinol, 6 parts of lead orthoplumbate, oxidation
11 parts of iron, 8 parts of isobutene, 7 parts of isoprene, 6 parts of potassium silicate, 4 parts of yittrium oxide, 5 parts of lanthana, 3 parts of silicon nitride, alchlor
6 parts and 1 part of composition of nano zirconium dioxide, comprise the following steps:
1) by dimethyldichlorosilane 19 parts be poured into vessel, then add appropriate moisture so that dimethyl dichloro
After 19 parts of complete hydrolysis of silane reactor is poured into together with 6 parts of 9 parts of vinyl ring body and tetramethyl divinyl disiloxane
In, it is then heated to 300 DEG C so that the cracking completely of 9 parts of vinyl ring body, mixture is made, it is standby;
2) mixture made from step 1) is poured into distillation equipment and carries out vacuum distillation processing, until mixture becomes
Untill colourless transparent liquid, colourless transparent liquid is made, it is standby;
3) 8 parts of isobutene and isoprene 7 are placed in reaction vessel together, then add 6 parts of alchlor simultaneously fully
Stirring, brings it about catalytic reaction, fully carries out cooling treatment after reaction, and rubber is made, standby;
4) 18 parts of acrylonitrile, 10 parts of styrene, 25 parts of ACM are poured into together in emulsification agitated kettle, fully
1 part of Octoxinol is stirring evenly and then adding into, carries out emulsification treatment 40 minutes, is taken out, cooling, synthetic plastic is made, it is standby;
5) by rubber one made from colourless transparent liquid made from synthetic plastic made from step 4), step 2) and step 3)
Rise and be poured into boiler and be heated to 450 DEG C so that synthetic plastic and rubber add 6 parts of lead orthoplumbate, oxygen after being completely dissolved
Change 1 part of 11 parts of iron, 6 parts of potassium silicate, 4 parts of yittrium oxide, 5 parts of lanthana, 3 parts of silicon nitride and nano zirconium dioxide, be sufficiently stirred
It is even, sticky mixing liquid is made, it is standby;
6) sticky mixing liquid made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Embodiment two:
As shown in figure 1, a kind of heat-insulating sound-insulating log cabin roof using the resin tile, including crossbeam 1, solid wood board 2 and resin
Watts 3, curb girder 4 is provided with the crossbeam 1, the curb girder 4 and the mortise-tenon joint of crossbeam 1, the solid wood board 2 are equipped on curb girder 4,
Tap bolt (not shown) is provided with the solid wood board 2, the tap bolt is threadedly coupled with curb girder 4, on the solid wood board 2
Ceramic beaverboard 5 is equipped with, reinforcement adhesive tape 6, the ceramic beaverboard 5 are provided between the solid wood board 2 and ceramic beaverboard 5
On be provided with silica-gel heat-insulating pad 7, the surface of silica-gel heat-insulating pad 7 is that crest shape is set, and is provided with the silica-gel heat-insulating pad 7 light
Steel joist 8, the lightgage steel joist 8 are set to be embedded in ceramic beaverboard 5, and aluminum alloy bar 9 is welded with the lightgage steel joist 8,
The resin tile 3 is installed on aluminum alloy bar 9.
The aluminum alloy bar 9 is hollow setting, can mitigate the overall weight on roof significantly, reduces the burden of crossbeam 1.
Anticorrosive coating (not shown) is scribbled on the aluminum alloy bar 9 and lightgage steel joist 8, aluminum alloy bar 9 can be prevented
It is etched with lightgage steel joist 8, it is durable in use.
The surface of silica-gel heat-insulating pad 7 scribbles lotus leaf emulsion paint (not shown), can be with rainy and self-cleaning, and pollutant can not
The whole surface in silica-gel heat-insulating pad 7 is attached, and can only loosely be gathered in surface, because surface can hardly be stained with wetting, institute
Tumbled with dust-laden rainwater beading, whole surface is chronically at drying regime, prevents microorganism from being attached to the surface of silica-gel heat-insulating pad 7.
It is provided with tenon (not shown) on the solid wood board 2, the tenon is set to be embedded in ceramic beaverboard 5, can be with
Lift the stability between solid wood board 2 and ceramic beaverboard 5.
Solid-wood (not shown) is provided with the curb girder 1, multiple stress points can be provided, so as to lift the entirety on roof
Stability.
Another technical problem to be solved by the invention is a kind of manufacture method of resin tile of offer.
To solve the above problems, the present invention adopts the following technical scheme that:
By 28 parts of 11 parts of 20 parts of acrylonitrile, styrene, ACM, the dimethyl dichloro silicon matched in parts by weight
20 parts of alkane, 10 parts of vinyl ring body, 7 parts of tetramethyl divinyl disiloxane, 3 parts of Octoxinol, 8 parts of lead orthoplumbate, oxygen
Change 12 parts of iron, 9 parts of isobutene, 9 parts of isoprene, 7 parts of potassium silicate, 5 parts of yittrium oxide, 7 parts of lanthana, 4 parts of silicon nitride, tri-chlorination
3 parts of compositions of 7 parts of aluminium and nano zirconium dioxide, comprise the following steps:
1) by dimethyldichlorosilane 20 parts be poured into vessel, then add appropriate moisture so that dimethyl dichloro
After 20 parts of complete hydrolysis of silane reactor is poured into together with 7 parts of 10 parts of vinyl ring body and tetramethyl divinyl disiloxane
In, it is then heated to 300 DEG C so that the cracking completely of 10 parts of vinyl ring body, mixture is made, it is standby;
2) mixture made from step 1) is poured into distillation equipment and carries out vacuum distillation processing, until mixture becomes
Untill colourless transparent liquid, colourless transparent liquid is made, it is standby;
3) 9 parts of 9 parts of isobutene and isoprene are placed in reaction vessel together, then add 7 parts of alchlor and fill
Divide stirring, bring it about catalytic reaction, fully carry out cooling treatment after reaction, rubber is made, it is standby;
4) 20 parts of acrylonitrile, 11 parts of styrene, 28 parts of ACM are poured into together in emulsification agitated kettle, fully
3 parts of Octoxinol is stirring evenly and then adding into, carries out emulsification treatment 40 minutes, is taken out, cooling, synthetic plastic is made, it is standby;
5) by rubber one made from colourless transparent liquid made from synthetic plastic made from step 4), step 2) and step 3)
Rise and be poured into boiler and be heated to 450 DEG C so that synthetic plastic and rubber add 8 parts of lead orthoplumbate, oxygen after being completely dissolved
Change 3 parts of 12 parts of iron, 7 parts of potassium silicate, 5 parts of yittrium oxide, 7 parts of lanthana, 4 parts of silicon nitride and nano zirconium dioxide, be sufficiently stirred
It is even, sticky mixing liquid is made, it is standby;
6) sticky mixing liquid made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Embodiment three:
As shown in figure 1, a kind of heat-insulating sound-insulating log cabin roof using the resin tile, including crossbeam 1, solid wood board 2 and resin
Watts 3, curb girder 4 is provided with the crossbeam 1, the curb girder 4 and the mortise-tenon joint of crossbeam 1, the solid wood board 2 are equipped on curb girder 4,
Tap bolt (not shown) is provided with the solid wood board 2, the tap bolt is threadedly coupled with curb girder 4, on the solid wood board 2
Ceramic beaverboard 5 is equipped with, reinforcement adhesive tape 6, the ceramic beaverboard 5 are provided between the solid wood board 2 and ceramic beaverboard 5
On be provided with silica-gel heat-insulating pad 7, the surface of silica-gel heat-insulating pad 7 is that crest shape is set, and is provided with the silica-gel heat-insulating pad 7 light
Steel joist 8, the lightgage steel joist 8 are set to be embedded in ceramic beaverboard 5, and aluminum alloy bar 9 is welded with the lightgage steel joist 8,
The resin tile 3 is installed on aluminum alloy bar 9.
The aluminum alloy bar 9 is hollow setting, can mitigate the overall weight on roof significantly, reduces the burden of crossbeam 1.
Anticorrosive coating (not shown) is scribbled on the aluminum alloy bar 9 and lightgage steel joist 8, aluminum alloy bar 9 can be prevented
It is etched with lightgage steel joist 8, it is durable in use.
The surface of silica-gel heat-insulating pad 7 scribbles lotus leaf emulsion paint (not shown), can be with rainy and self-cleaning, and pollutant can not
The whole surface in silica-gel heat-insulating pad 7 is attached, and can only loosely be gathered in surface, because surface can hardly be stained with wetting, institute
Tumbled with dust-laden rainwater beading, whole surface is chronically at drying regime, prevents microorganism from being attached to the surface of silica-gel heat-insulating pad 7.
It is provided with tenon (not shown) on the solid wood board 2, the tenon is set to be embedded in ceramic beaverboard 5, can be with
Lift the stability between solid wood board 2 and ceramic beaverboard 5.
Solid-wood (not shown) is provided with the curb girder 1, multiple stress points can be provided, so as to lift the entirety on roof
Stability.
Another technical problem to be solved by the invention is a kind of manufacture method of resin tile of offer.
To solve the above problems, the present invention adopts the following technical scheme that:
By 30 parts of 12 parts of 22 parts of acrylonitrile, styrene, ACM, the dimethyl dichloro silicon matched in parts by weight
22 parts of alkane, 11 parts of vinyl ring body, 8 parts of tetramethyl divinyl disiloxane, 4 parts of Octoxinol, 10 parts of lead orthoplumbate, oxygen
Change 13 parts of iron, 10 parts of isobutene, 11 parts of isoprene, 8 parts of potassium silicate, 6 parts of yittrium oxide, 8 parts of lanthana, 5 parts of silicon nitride, trichlorine
Change 4 parts of compositions of 8 parts of aluminium and nano zirconium dioxide, comprise the following steps:
1) by dimethyldichlorosilane 22 parts be poured into vessel, then add appropriate moisture so that dimethyl dichloro
After 22 parts of complete hydrolysis of silane reactor is poured into together with 8 parts of 11 parts of vinyl ring body and tetramethyl divinyl disiloxane
In, it is then heated to 300 DEG C so that the cracking completely of 9 parts of vinyl ring body, mixture is made, it is standby;
2) mixture made from step 1) is poured into distillation equipment and carries out vacuum distillation processing, until mixture becomes
Untill colourless transparent liquid, colourless transparent liquid is made, it is standby;
3) 11 parts of 10 parts of isobutene and isoprene are placed in reaction vessel together, then add 8 parts of alchlor simultaneously
It is sufficiently stirred, brings it about catalytic reaction, fully carry out cooling treatment after reaction, rubber is made, it is standby;
4) 22 parts of acrylonitrile, 12 parts of styrene, 30 parts of ACM are poured into together in emulsification agitated kettle, fully
4 parts of Octoxinol is stirring evenly and then adding into, carries out emulsification treatment 40 minutes, is taken out, cooling, synthetic plastic is made, it is standby;
5) by rubber one made from colourless transparent liquid made from synthetic plastic made from step 4), step 2) and step 3)
Rise and be poured into boiler and be heated to 450 DEG C so that synthetic plastic and rubber add 10 parts of lead orthoplumbate, oxygen after being completely dissolved
Change 4 parts of 13 parts of iron, 8 parts of potassium silicate, 6 parts of yittrium oxide, 8 parts of lanthana, 5 parts of silicon nitride and nano zirconium dioxide, be sufficiently stirred
It is even, sticky mixing liquid is made, it is standby;
6) sticky mixing liquid made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Beneficial effects of the present invention are:By the way that resin tile is arranged into aerial, it is possible to reduce resin tile and aluminum alloy bar
Contact area, the transmission efficiency of heat and sound is reduced, by being provided with silica-gel heat-insulating pad and ceramic beaverboard, both coordinate tool
There is outstanding heat-insulating capability, and silica-gel heat-insulating pad surface is set for crest shape, has good buffering vibration effect, makes silica gel
Heat insulating mattress is very strong to the absorbability of high frequency, silica-gel heat-insulating pad is had outstanding sound insulation and noise reduction effect.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
The change or replacement expected without creative work, it should all be included within the scope of the present invention.
Claims (2)
- A kind of 1. resin tile on heat-insulating sound-insulating log cabin roof, it is characterised in that:The resin tile by match in parts by weight third Alkene nitrile 18-22 parts, styrene 10-12 parts, ACM 25-30 parts, dimethyldichlorosilane 19-22 parts, ethene basic ring Body 9-11 parts, tetramethyl divinyl disiloxane 6-8 parts, Octoxinol 1-4 parts, lead orthoplumbate 6-10 parts, iron oxide 11- 13 parts, isobutene 8-10 parts, isoprene 7-11 parts, potassium silicate 6-8 parts, yittrium oxide 4-6 parts, lanthana 5-8 parts, silicon nitride 3- 5 parts, alchlor 6-8 parts and nano zirconium dioxide 1-4 parts composition.
- 2. the resin tile on heat-insulating sound-insulating log cabin roof according to claim 1, it is characterised in that:The manufacturer of resin tile Method, include following steps:1) dimethyldichlorosilane 19-22 parts are poured into vessel, then add appropriate moisture so that dimethyl dichloro silicon It is poured into after alkane 19-22 part complete hydrolysis with together with vinyl ring body 9-11 parts and tetramethyl divinyl disiloxane 6-8 parts In reactor, 300 DEG C are then heated to so that vinyl ring body 9-11 parts crack completely, and mixture is made, standby;2) mixture made from step 1) is poured into distillation equipment and carries out vacuum distillation processing, until mixture becomes colourless Untill transparency liquid, colourless transparent liquid is made, it is standby;3) isobutene 8-10 parts and isoprene 7-11 parts are placed in reaction vessel together, then add alchlor 6-8 parts And be sufficiently stirred, catalytic reaction is brought it about, fully carries out cooling treatment after reaction, rubber is made, it is standby;4) acrylonitrile 18-22 parts, styrene 10-12 parts, ACM 25-30 parts are poured into emulsification agitated kettle together In, Octoxinol 1-4 parts are added after stirring, carry out emulsification treatment 40 minutes, takes out, cooling, synthetic plastic is made, It is standby;5) rubber made from colourless transparent liquid made from synthetic plastic made from step 4), step 2) and step 3) is fallen together Enter into boiler and be heated to 450 DEG C so that synthetic plastic and rubber add lead orthoplumbate 6-10 parts, oxidation after being completely dissolved Iron 11-13 parts, potassium silicate 6-8 parts, yittrium oxide 4-6 parts, lanthana 5-8 parts, silicon nitride 3-5 parts and nano zirconium dioxide 1-4 parts, Stir, sticky mixing liquid is made, it is standby;6) sticky mixing liquid made from step 5) is poured into injection mold, then through cooling treatment, you can use.