CN107435278A - 一种绝缘浆板及其加工工艺 - Google Patents

一种绝缘浆板及其加工工艺 Download PDF

Info

Publication number
CN107435278A
CN107435278A CN201610350580.6A CN201610350580A CN107435278A CN 107435278 A CN107435278 A CN 107435278A CN 201610350580 A CN201610350580 A CN 201610350580A CN 107435278 A CN107435278 A CN 107435278A
Authority
CN
China
Prior art keywords
pulp
paper
insulating slurry
panel
insulating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610350580.6A
Other languages
English (en)
Inventor
徐小芹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610350580.6A priority Critical patent/CN107435278A/zh
Publication of CN107435278A publication Critical patent/CN107435278A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种适于抄造高档电器绝缘用纸的绝缘浆板以及其加工工艺，该绝缘浆板是采用龙须草为原料制作而成；其加工工艺为：备料→蒸煮→洗涤→浆料净化→抄造浆板。由于龙须草纤维细长、均整，柔软性能好，采用龙须草制作的绝缘浆板，恰能满足于抄造高档绝缘纸的要求，适于抄造高档电器绝缘用纸。

Description

一种绝缘浆板及其加工工艺
技术领域
本发明涉及一种适于抄造高档电器绝缘用纸的绝缘浆板及其加工工艺。
背景技术
绝缘浆板主要用于电子行业中电子元件电容器绝缘纸的抄造，在 国内外应用相当广泛，主要以本色木浆绝缘浆板为主。随着这些年电 子信息产业化的飞速发展，对绝缘纸的厚度要求越来越严格，原来广 泛使用的电容纸应用范围越米越小，等超薄型的应用日益广泛，绝缘 纸的超薄型化，对绝缘浆板的性能有了新的要求，原木浆纤维粗短的特点，已不能适应于抄造高档电器绝缘用纸的需要。
发明内容
本发明就是为了提供一种适于抄造高档电器绝缘用纸的绝缘浆 板，以及其加工工艺，该绝缘浆板是采用龙须草为原料制作而成；其 加工工艺为：备料→蒸煮→洗涤→浆料净化→抄造浆板。 由于龙须草 纤维细长、均整，柔软性能好，采用龙须草制作的绝缘浆板，恰能满 足于抄造高档绝缘纸的要求，适于抄造高档电器绝缘用纸。
下面结合实施例进一步说明本发明。
采用龙须草作为生产原料，并采用以下工艺：(一)、备料：对原 料进行选择，除去一切杂草、杂物，经过切麻机切碎；(二)、在25m3蒸球中蒸煮：用浓度为30％的NaOH碱液，按绝干草量16～18％的用 草量、液比在3.2～3.5∶1条件下，将水、碱、龙须草置入蒸球中，不 加蒸汽空转30min，均匀升温至150℃，保温时间为1～2.5h；然后升 压至0.5～0.65mpa，温度至160～165℃，再保温6～7h；蒸后粗浆硬度 达：KMnO4值9左右，残碱8～12g/l，纤维平均长1.7～2mm；然后进 入80m3喷放仓再经过3～6m2斜筛、2SK-2型跳筛后进入洗涤过程； (三)、ZNC-2型4.5m2侧压浓缩机串联2台，进行洗涤：先在温度为 50-100℃、洗涤水硬度为200-300ppm，浆层厚度为3～62mm，适当增 加压力差的条件下洗涤，再进入第二台在温度为80-120℃、洗涤水硬 度为200-300ppm，浆层厚度为3～6mm，适当增加压力差的条件下进 行第二次洗涤，并保证设备洗涤能力达到20～30m2，洗涤后PH值呈 中性；(四)、进行浆料的净化：洗涤后浆板进入1.6m2ZSL离心筛再 经过606型二级二段除砂系统，通过多级多段净化，除去尘埃、细砂， 然后经过8m2ZNW-3型圆网浓缩机达到造纸储浆池，再次通过600型 除砂系统进入纸机抄造浆板过程；(五)、浆板抄造机抄造浆板，经分 切机分切计量打包后入库。入库产品质量达到以下标准：在每1800cm2中铁微粒子数平均≤100个，纤维铁数平均≤100个，铜微粒子数为0， 其硬度值KMnO4值≥12，夹杂物量≤30000mm2/kg。

Claims (3)

1.一种绝缘浆板，其特征在于：所述绝缘浆板是采用龙须草为原 料制作而成。
2. 如权利要求1所述的绝缘浆板，其加工工艺为：备料→蒸煮→ 洗涤→浆料净化→抄造纸浆。
3. 如权利要求2所述的绝缘浆板，其特征在于：所述蒸煮工艺是 将水、碱、龙须草在用浓度为30％的NaOH碱液、按绝干草量16～18％ 的用草量、液比在3.2～3.5∶1条件下置入蒸球中转30min，均匀升温 至150℃后保温1～2.5小时；然后升压至0.5～0.65mpa，温度至160～165 ℃再保温6～7小时。
CN201610350580.6A 2016-05-25 2016-05-25 一种绝缘浆板及其加工工艺 Pending CN107435278A (zh)