CN107418307A - A kind of sprayed on material and spraying method for timber floor - Google Patents
A kind of sprayed on material and spraying method for timber floor Download PDFInfo
- Publication number
- CN107418307A CN107418307A CN201710566352.7A CN201710566352A CN107418307A CN 107418307 A CN107418307 A CN 107418307A CN 201710566352 A CN201710566352 A CN 201710566352A CN 107418307 A CN107418307 A CN 107418307A
- Authority
- CN
- China
- Prior art keywords
- sprayed
- resin
- timber floor
- plasticizer
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sprayed on material and spraying coating process for timber floor, sprayed on material includes following formula:Resin 60% 80%;Modifying agent 10% 20%;Stabilizer 2% 5%;Levelling agent 1% 5%;Aliphatic acid 1% 5%;Plasticizer 2% 5%;The proportioning is mass ratio.The present invention by resin by replacing prior paraffin; sprayed on material is combined with the notch of the tongue-and-groove on floor by spraying coating process; form one layer of resin protection film; with totally-enclosed, waterproof, prevention Form aldehyde release and spray coated notch due to combining resinous coat; assembled simpler, the smoothness of notch is more preferable.
Description
Technical field
The present invention relates to a kind of sprayed on material and spraying method for timber floor, belong to wood producing technical field.
Background technology
In the prior art, the waterproofing agent as timber floor, most economical is exactly effectively paraffin wax emulsions, at home, paraffin
Emulsion is also applied to the waterproofing agent of timber floor by method, but in process of production, melting point of paraffin wax is low, evaporation is fast, easily makes
Into the pollution of environment and the rising of cost.
The content of the invention
Present invention provides a kind of sprayed on material and spraying method for timber floor, using resin as main spraying
Material, it instead of and be used as the mode of waterproofing agent in traditional handicraft by the use of paraffin.
Technical scheme is as follows:
A kind of sprayed on material for timber floor, sprayed on material include following formula:
Resin 60%-80%
Modifying agent 10%-20%
Stabilizer 2%-5%
Levelling agent 1%-5%
Aliphatic acid 1%-5%
Plasticizer 2%-5%
The proportioning is mass ratio.
Preferably, above-mentioned resin is in PE resins, polyester resin, epoxy resin, polyurethane resin or fluororesin
One or more.
Preferably, above-mentioned modifying agent is paraffin.
Preferably, above-mentioned aliphatic acid is the one or more in oleic acid, stearic acid or laurate.
Preferably, above-mentioned plasticizer is two butyric acid.
A kind of spraying method for timber floor, it is as follows using above-mentioned material, its step:
(1), by resin heating and melting;
(2), under agitation, the good modifying agent of heating and melting is added in the resin solution after melting, then add it is steady
Determine agent, levelling agent, aliphatic acid and plasticizer, heat up and stir to form sprayed on material;
(3), by spraying equipment by step(2)The sprayed on material of middle preparation is sprayed at the notch of the tongue-and-groove of timber floor, is formed
The resin protection film of one layer of closing.
It should be strongly noted that the above method can be used for spraying various types of solid wooden floor boards, laminated flooring, answer
Close floor, combined wall board.
The beneficial effect that the present invention is reached:
The present invention is mutually tied the notch of sprayed on material and the tongue-and-groove on floor by spraying coating process by the way that resin is replaced into prior paraffin
Close, form one layer of resin protection film, there is totally-enclosed, waterproof, prevent Form aldehyde release and spray coated notch is due to combining
Resinous coat, assembled simpler, the smoothness of notch is more preferable.
Embodiment
With reference to embodiment, the invention will be further described.Following examples are only used for clearly illustrating this hair
Bright technical scheme, and can not be limited the scope of the invention with this.
A kind of sprayed on material for timber floor, sprayed on material include following formula:
Resin 60%-80%
Modifying agent 10%-20%
Stabilizer 2%-5%
Levelling agent 1%-5%
Aliphatic acid 1%-5%
Plasticizer 2%-5%
The proportioning is mass ratio.
Preferably, above-mentioned resin is in PE resins, polyester resin, epoxy resin, polyurethane resin or fluororesin
One or more.
Preferably, above-mentioned modifying agent is paraffin.
Preferably, above-mentioned aliphatic acid is the one or more in oleic acid, stearic acid or laurate.
Preferably, above-mentioned plasticizer is two butyric acid.
A kind of spraying method for timber floor, it is as follows using above-mentioned material, its step:
(1), by resin heating and melting;
(2), under agitation, the good modifying agent of heating and melting is added in the resin solution after melting, then add it is steady
Determine agent, levelling agent, aliphatic acid and plasticizer, heat up and stir to form sprayed on material;
(3), by spraying equipment by step(2)The sprayed on material of middle preparation is sprayed at the notch of the tongue-and-groove of timber floor, is formed
The resin protection film of one layer of closing.
It should be strongly noted that the above method can be used for spraying various types of solid wooden floor boards, laminated flooring, answer
Close floor, combined wall board.
Embodiment:
A kind of sprayed on material for timber floor, according to following formula:
PE resins 80%
Paraffin 10%
Stabilizer 5%
Levelling agent 2%
Stearic acid 1%
Two butyric acid 2%,
Above-mentioned is mass ratio.
(1), by PE resin heating and meltings;
(2), under agitation, the good paraffin of heating and melting is added in the PE resin solutions after melting, then add it is steady
Determine agent, levelling agent, stearic acid and two butyric acid, heat up and stir to form sprayed on material;
(3), by spraying equipment by step(2)The sprayed on material of middle preparation is sprayed at the notch of the tongue-and-groove of timber floor, is formed
The resin protection film of one layer of closing.
The timber floor water resistance with resin protection film of finished product is good, and assembly is convenient, prevents Form aldehyde release.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvement and deformation can also be made, these are improved and deformation
Also it should be regarded as protection scope of the present invention.
Claims (7)
- A kind of 1. sprayed on material for timber floor, it is characterised in that:The sprayed on material includes following formula:Resin 60%-80%Modifying agent 10%-20%Stabilizer 2%-5%Levelling agent 1%-5%Aliphatic acid 1%-5%Plasticizer 2%-5%The proportioning is mass ratio.
- A kind of 2. sprayed on material for timber floor according to claim 1, it is characterised in that:The resin is PE trees One or more in fat, polyester resin, epoxy resin, polyurethane resin or fluororesin.
- A kind of 3. sprayed on material for timber floor according to claim 1, it is characterised in that:The modifying agent is stone Wax.
- A kind of 4. sprayed on material for timber floor according to claim 1, it is characterised in that:The aliphatic acid is oil One or more in acid, stearic acid or laurate.
- A kind of 5. sprayed on material for timber floor according to claim 1, it is characterised in that:The plasticizer is two fourths Acid.
- 6. a kind of spraying method for timber floor, it is characterised in that as follows using the material described in claim 1, its step:(1), by resin heating and melting;(2), under agitation, the good modifying agent of heating and melting is added in the resin solution after melting, then add it is steady Determine agent, levelling agent, aliphatic acid and plasticizer, heat up and stir to form sprayed on material;(3), by spraying equipment by step(2)The sprayed on material of middle preparation is sprayed at the notch of the tongue-and-groove of timber floor, is formed The resin protection film of one layer of closing.
- 7. a kind of spraying method for timber floor according to claim 6, it is characterised in that methods described is used to spray respectively Solid wooden floor board, laminated flooring, composite floor board, the combined wall board of type.