CN107417216A - A kind of corrosion-resistant water-permeable brick - Google Patents
A kind of corrosion-resistant water-permeable brick Download PDFInfo
- Publication number
- CN107417216A CN107417216A CN201710870533.9A CN201710870533A CN107417216A CN 107417216 A CN107417216 A CN 107417216A CN 201710870533 A CN201710870533 A CN 201710870533A CN 107417216 A CN107417216 A CN 107417216A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- permeable brick
- corrosion
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of corrosion-resistant water-permeable brick, fraction proportioning by weight is made up of following components:34 42 parts of portland cement, 8 10 parts of black cement, 23 parts of anhydrite powder, 0.5 1 parts of iron oxide red, 33 42 parts of coagulated sludge powder, 8 10 parts of mine tailing, 46 parts of terpene resin powder, 15 20 parts of fine sand, 11 14 parts of slag powders, 15 20 parts of stone of rice, 10 12 parts of cenosphere, 15 20 parts of cement, 22 26 parts of waterglass, 14 16 parts of alkyl phenol ether sulfosuccinate, 16 19 parts of lignosulfonates, 35 parts of isocyanuric acid three-glycidyl ester, 23 34 parts of quartz sand.The advantage of the invention is that:Water-permeable brick surface layer of the present invention is prepared by quartz sand, black cement, iron oxide red, and bottom is relatively good by mine tailing, fine sand, rice stone and cement production systD, quality, it is hardly damaged, service life is also just long, and due to containing iron oxide red in surface layer, therefore the appearance of water-permeable brick then better appearance.
Description
Technical field
The present invention relates to building material field, more particularly to a kind of corrosion-resistant water-permeable brick.
Background technology
City Route for pedestrians is equipped with fragment of brick mostly, to maintain attractive in appearance and planarization, the brick laid on existing Route for pedestrians
Block is mostly molded using direct sintering after clay compacting, and its water permeability is poor, and its one side has blocked rainwater to underground water
Supplement, on the other hand, because rain drainage is not smooth, also easily cause urban waterlogging.
In order to solve the above problems, permeable brick product is proposed in the prior art.Water-permeable brick in the market substantially may be used
It is divided into ceramic water-permeable brick, cement base water-permeable brick and resin-bonded water-permeable brick three basic forms of it.Although ceramic water-permeable brick has hard
Degree is high, intensity is big, pattern is abundant and the advantage of size specification, and still, complex manufacturing, resource consumption is big, and production cost is high;
Resin-bonded water-permeable brick then causes poor durability due to the aging of resin;Cement base water-permeable brick production cost is low, but pressure resistance
Spend low, and wear no resistance.And for common water-permeable brick, because its porosity is higher, its Salt corrosion corrosion is poor, so as to cause
Durability differs larger, it is necessary to frequent maintenance and replacement operation with common clay brick.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of good corrosion-resistant water-permeable brick of anticorrosion effect.
In order to solve the above technical problems, the technical scheme is that:A kind of corrosion-resistant water-permeable brick, its innovative point are:
Fraction proportioning by weight is made up of following components:
Portland cement 34-42 parts, black cement 8-10 parts, anhydrite powder 2-3 parts, iron oxide red 0.5-1 parts, coagulated sludge powder
33-42 parts, mine tailing 8-10 parts, terpene resin powder 4-6 parts, fine sand 15-20 parts, slag powders 11-14 parts, rice stone 15-20 parts are empty
Heart microballon 10-12 parts, cement 15-20 parts, waterglass 22-26 parts, alkyl phenol ether sulfosuccinate 14-16 parts, sulfomethylated lignin
Hydrochlorate 16-19 parts, isocyanuric acid three-glycidyl ester 3-5 parts, quartz sand 23-34 parts.
Further, the portland cement is P.O42.5 cement or P.O.52.5 cement.
Further, the fineness of the anhydrite powder is below 0.074mm, than surface >=400m2/kg.
Further, the density of the cenosphere is 1.8-2.3g/cm3, and particle diameter is less than 100 μm.
The advantage of the invention is that:Water-permeable brick surface layer of the present invention is prepared by quartz sand, black cement, iron oxide red, bottom by
Mine tailing, fine sand, rice stone and cement production systD, quality is relatively good, is hardly damaged, and service life is also just long, and due to
Contain iron oxide red in surface layer, therefore the appearance of water-permeable brick then better appearance.
Corrosion-resistant water-permeable brick of the present invention on the premise of porosity, coefficient of permeability are significantly higher than conventional water-permeable brick,
Its compression strength remains above conventional water-permeable brick, and has good decay resistance, significantly improves service life.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Embodiment 1
The corrosion-resistant water-permeable brick of present invention fraction proportioning by weight is made up of following components:
Fraction proportioning by weight is made up of following components:
34 parts of portland cement, 8 parts of black cement, 2 parts of anhydrite powder, 0.5 part of iron oxide red, 33 parts of coagulated sludge powder, mine tailing 8
Part, 4 parts of terpene resin powder, 15 parts of fine sand, 11 parts of slag powders, 15 parts of rice stone, 10 parts of cenosphere, 15 parts of cement, waterglass 22
Part, 14 parts of alkyl phenol ether sulfosuccinate, 16 parts of lignosulfonates, 3 parts of isocyanuric acid three-glycidyl ester, quartz sand 23
Part.
In above-mentioned formula, portland cement is P.O42.5 cement or P.O.52.5 cement, and the fineness of anhydrite powder is
Below 0.074mm, than surface >=400m2/kg, the density of cenosphere is 1.8-2.3g/cm3, and particle diameter is less than 100 μm.
Embodiment 2
The corrosion-resistant water-permeable brick of present invention fraction proportioning by weight is made up of following components:
Fraction proportioning by weight is made up of following components:
42 parts of portland cement, 10 parts of black cement, 3 parts of anhydrite powder, 1 part of iron oxide red, 42 parts of coagulated sludge powder, mine tailing 10
Part, 6 parts of terpene resin powder, 20 parts of fine sand, 14 parts of slag powders, 20 parts of rice stone, 12 parts of cenosphere, 20 parts of cement, waterglass 26
Part, 16 parts of alkyl phenol ether sulfosuccinate, 19 parts of lignosulfonates, 5 parts of isocyanuric acid three-glycidyl ester, quartz sand 34
Part.
In above-mentioned formula, portland cement is P.O42.5 cement or P.O.52.5 cement, and the fineness of anhydrite powder is
Below 0.074mm, than surface >=400m2/kg, the density of cenosphere is 1.8-2.3g/cm3, and particle diameter is less than 100 μm.
Embodiment 3
The corrosion-resistant water-permeable brick of present invention fraction proportioning by weight is made up of following components:
Fraction proportioning by weight is made up of following components:
38 parts of portland cement, 9 parts of black cement, 2 parts of anhydrite powder, 0.8 part of iron oxide red, 38 parts of coagulated sludge powder, mine tailing 9
Part, 5 parts of terpene resin powder, 17 parts of fine sand, 12 parts of slag powders, 18 parts of rice stone, 11 parts of cenosphere, 17 parts of cement, waterglass 24
Part, 15 parts of alkyl phenol ether sulfosuccinate, 17 parts of lignosulfonates, 4 parts of isocyanuric acid three-glycidyl ester, quartz sand 29
Part.
In above-mentioned formula, portland cement is P.O42.5 cement or P.O.52.5 cement, and the fineness of anhydrite powder is
Below 0.074mm, than surface >=400m2/kg, the density of cenosphere is 1.8-2.3g/cm3, and particle diameter is less than 100 μm.
Water-permeable brick surface layer of the present invention is prepared by quartz sand, black cement, iron oxide red, bottom by mine tailing, fine sand, meter Shi with
And cement production systD, quality is relatively good, is hardly damaged, and service life is also just long, and due to containing iron oxide red in surface layer, therefore
The appearance of water-permeable brick then better appearance.
Corrosion-resistant water-permeable brick of the present invention on the premise of porosity, coefficient of permeability are significantly higher than conventional water-permeable brick,
Its compression strength remains above conventional water-permeable brick, and has good decay resistance, significantly improves service life.
It should be understood by those skilled in the art that the present invention is not limited to the above embodiments, above-described embodiment and explanation
Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also have
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
By appended claims and its equivalent thereof.
Claims (4)
- A kind of 1. corrosion-resistant water-permeable brick, it is characterised in that:Fraction proportioning by weight is made up of following components:Portland cement 34-42 parts, black cement 8-10 parts, anhydrite powder 2-3 parts, iron oxide red 0.5-1 parts, coagulated sludge powder 33-42 parts, mine tailing 8-10 parts, terpene resin powder 4-6 parts, fine sand 15-20 parts, slag powders 11-14 parts, rice stone 15-20 parts are empty Heart microballon 10-12 parts, cement 15-20 parts, waterglass 22-26 parts, alkyl phenol ether sulfosuccinate 14-16 parts, sulfomethylated lignin Hydrochlorate 16-19 parts, isocyanuric acid three-glycidyl ester 3-5 parts, quartz sand 23-34 parts.
- 2. corrosion-resistant water-permeable brick according to claim 1, it is characterised in that:The portland cement is P.O42.5 cement Or P.O.52.5 cement.
- 3. corrosion-resistant water-permeable brick according to claim 1, it is characterised in that:The fineness of the anhydrite powder is 0.074mm Hereinafter, than surface >=400m2/kg.
- 4. corrosion-resistant water-permeable brick according to claim 1, it is characterised in that:The density of the cenosphere is 1.8- 2.3g/cm3 particle diameter is less than 100 μm.