CN107383981A - A kind of interior wall is incubated antibacterial powder of lacquer putty for use on and its construction method - Google Patents
A kind of interior wall is incubated antibacterial powder of lacquer putty for use on and its construction method Download PDFInfo
- Publication number
- CN107383981A CN107383981A CN201710695297.1A CN201710695297A CN107383981A CN 107383981 A CN107383981 A CN 107383981A CN 201710695297 A CN201710695297 A CN 201710695297A CN 107383981 A CN107383981 A CN 107383981A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- auxiliary agent
- incubated
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of interior wall to be incubated antibacterial powder of lacquer putty for use on and its construction method, including base-material, filler and auxiliary agent, the base-material, filler and auxiliary agent mainly include following component according to parts by weight：Wherein, the base-material includes 10 15 parts of latex powder；The filler includes 10 15 parts of 50 70 parts of calcium carbonate, 10 14 parts of titanium dioxide, 8 10 parts of cellulose and diatomite；The auxiliary agent includes insulation auxiliary agent and antibacterial auxiliary agent, the insulation auxiliary agent includes 9 13 parts of 7 11 parts of sepiolite powder, 20 30 parts of expanded pearlite powder and vermiculite power, and the antibacterial auxiliary agent includes 0.3 0.7 parts of 58 parts of oyster shell whiting, 24 parts of Ground Cloves, 12 parts of African jasmine powder, 46 parts of copper stearate soap powder, 48 parts of bamboo charcoal powder and nano-silver powder.According to component provided by the present invention proportioning make inner wall putty powder can not only insulation, and can bacteria mildew-proof, help for sleep, be advantageous to human body health and live comfortableness.
Description
Technical field
The present invention relates to powder of lacquer putty for use on field, specifically a kind of interior wall is incubated antibacterial powder of lacquer putty for use on and its construction method.
Background technology
A kind of material of decoration property of smooth surface of wall, is a kind of thick slurry coating material during putty, is that coating is whitewashed a wall money
A kind of essential product.Painting is imposed on priming paint or directly applied and imposes on object, for eliminating on coated article surface height not
The defects of flat.
At present, requirement of the internal wall finishing to environmental protection is more and more stricter, the health of the life of this people of this direct relation.And city
Some putty for interior wall powder on field, finishing can not be absorbed caused by pernicious gas, easily human body is damaged, and when long
Between be easy to breed bacteria and mouldy or even cracking phenomenon after use, and traditional inner wall putty powder can not reach
To the effect of insulation, environment in room is in phenomenon cold in winter and hot in summer, reduce the comfortableness of house, people can not be met
Daily demand.
The content of the invention
The present invention provides a kind of fungus-resistant, insulation and purifies the antibacterial powder of lacquer putty for use on of interior wall insulation of air and its apply
Work method.
The present invention solves above-mentioned technical problem and adopted the technical scheme that：A kind of interior wall is incubated antibacterial powder of lacquer putty for use on, including
Base-material, filler and auxiliary agent, the base-material, filler and auxiliary agent mainly include following component according to parts by weight：Wherein, the base-material bag
Include latex powder 10-15 parts；The filler includes calcium carbonate 50-70 parts, titanium dioxide 10-14 parts, cellulose 8-10 parts and diatomite
10-15 parts；The auxiliary agent includes insulation auxiliary agent and antibacterial auxiliary agent, and the insulation auxiliary agent is precious including sepiolite powder 7-11 parts, expansion
Pearl powder 20-30 parts and vermiculite power 9-13 parts, the antibacterial auxiliary agent include oyster shell whiting 5-8 parts, Ground Cloves 2-4 parts, African jasmine powder
1-2 parts, copper stearate soap powder 4-6 parts, bamboo charcoal powder 4-8 parts and nano-silver powder 0.3-0.7 parts.
Further, the particle diameter of the sierozem power is 400-600 mesh.
Further, the titanium dioxide is rutile type titanium white.
Further, the particle diameter of the expanded perlite is 20-40 mesh.
A kind of interior wall is incubated the construction method of antibacterial powder of lacquer putty for use on, mainly includes the following steps that：
(1) base treatment：Include cleaning-repairing-drying successively；
(2) sealing：Caustic soda solution or glue are painted in inner wall surface after treatment；
(3) dispensing：By inner wall putty powder and water according to 1：0.5 ratio is mixed, and then carries out first time stirring-quiet
Put-second stir process；
(4) scratch：First time blade coating-blade coating-drying-the third time of drying-second blade coating-drying is carried out successively；
(5) polish：Inner wall surface is polished using sand paper；
(6) check and accept.
Further, the cleaning is to be removed floating ash, mucilage and the splash of inner wall surface using hairbrush.
Further, the repairing is by the convex of inner wall surface is floating, recess is filled and led up, and controls the flatness of inner wall surface and exists
Less than in 5mm.
Further, the drying is to be removed the moisture of inner wall surface using hair-dryer, keeps the drying of inner wall surface.
Further, the first time speed of agitator is 60-120r/min, mixing time 20-30min, and the standing is
15-20min, second of speed of agitator are 80-150r/min, mixing time 15-20min.
Further, the sand paper is the sand paper of 240-320 mesh.
Above-mentioned material and method are employed, the present invention can obtain a kind of inner wall putty powder of fungus-resistant and insulation.
Due to adding insulation auxiliary agent in the formula of the present invention, the heat insulating effect of metope can be improved, makes to warm up in the winter in house
Xia Liang environment, increase the comfortableness of inhabitation, be incubated in auxiliary agent contain sepiolite powder in addition, the anticorrosive of metope can also be increased
Performance and soundproof effect, expanded perlite can improve apyrous, moisture resistance and the crack resistance of inner wall putty powder；Due to the present invention
Formula in add antibacterial auxiliary agent, the fungus-resistant performance of inner wall putty powder can be improved, and sleep can be adjusted, helped
In health, and the Ground Cloves due to being added in antibacterial auxiliary agent and African jasmine powder, not only with bacteria resistance function, and have
There is sleeping effect, stearic acid Copoloid and Nano Silver have the function of bactericidal, and bamboo charcoal powder has mould proof function, in addition shellfish
Shell powder can absorb pernicious gas, purify air, further help in the health of human body.
Embodiment
In order that present disclosure is easier to be clearly understood, below according to specific embodiment, in the present invention
Wall is described in further detail with the antibacterial powder of lacquer putty for use on of insulation and its construction method.
Embodiment one：
A kind of interior wall is incubated antibacterial powder of lacquer putty for use on, including base-material, filler and auxiliary agent, the base-material, filler and auxiliary agent according to
Parts by weight mainly include following component：Wherein, the base-material includes 10 parts of latex powder；The filler includes 50 parts of calcium carbonate, titanium
10 parts of 10 parts of white powder, 8 parts of cellulose and diatomite；The auxiliary agent includes insulation auxiliary agent and antibacterial auxiliary agent, the insulation auxiliary agent bag
Include 9 parts of 7 parts of sepiolite powder, 20 parts of expanded pearlite powder and vermiculite power, the antibacterial auxiliary agent include 5 parts of oyster shell whiting, 2 parts of Ground Cloves,
0.3 part of African 1 part of jasmine powder, 4 parts of copper stearate soap powder, 4 parts of bamboo charcoal powder and nano-silver powder.
Embodiment two：
A kind of interior wall is incubated antibacterial powder of lacquer putty for use on, including base-material, filler and auxiliary agent, the base-material, filler and auxiliary agent according to
Parts by weight mainly include following component：Wherein, the base-material includes 15 parts of latex powder；The filler includes 70 parts of calcium carbonate, titanium
15 parts of 14 parts of white powder, 10 parts of cellulose and diatomite；The auxiliary agent includes insulation auxiliary agent and antibacterial auxiliary agent, the insulation auxiliary agent bag
13 parts of 11 parts of sepiolite powder, 30 parts of expanded pearlite powder and vermiculite power are included, the antibacterial auxiliary agent includes 8 parts of oyster shell whiting, Ground Cloves 4
Part, 2 parts of African jasmine powder, 6 parts of copper stearate soap powder, 8 parts of bamboo charcoal powder and 0.7 part of nano-silver powder.
Embodiment three：
A kind of interior wall is incubated antibacterial powder of lacquer putty for use on, including base-material, filler and auxiliary agent, the base-material, filler and auxiliary agent according to
Parts by weight mainly include following component：Wherein, the base-material includes 12.5 parts of latex powder；The filler include 60 parts of calcium carbonate,
12.5 parts of 12 parts of titanium dioxide, 9 parts of cellulose and diatomite；The auxiliary agent includes insulation auxiliary agent and antibacterial auxiliary agent, the insulation help
Agent includes 11 parts of 9 parts of sepiolite powder, 25 parts of expanded pearlite powder and vermiculite power, and the antibacterial auxiliary agent includes 6.5 parts of oyster shell whiting, cloves
0.5 part of 3 parts of powder, 1.5 parts of African jasmine powder, 5 parts of copper stearate soap powder, 6 parts of bamboo charcoal powder and nano-silver powder.
Example IV：
A kind of interior wall is incubated antibacterial powder of lacquer putty for use on, including base-material, filler and auxiliary agent, the base-material, filler and auxiliary agent according to
Parts by weight mainly include following component：Wherein, the base-material includes 13 parts of latex powder；The filler includes 65 parts of calcium carbonate, titanium
13 parts of 13 parts of white powder, 9.3 parts of cellulose and diatomite；The auxiliary agent includes insulation auxiliary agent and antibacterial auxiliary agent, the insulation auxiliary agent
Including 12 parts of 10 parts of sepiolite powder, 27 parts of expanded pearlite powder and vermiculite power, the antibacterial auxiliary agent includes 7 parts of oyster shell whiting, Ground Cloves
0.6 part of 3.4 parts, 1.7 parts of African jasmine powder, 5.3 parts of copper stearate soap powder, 7 parts of bamboo charcoal powder and nano-silver powder.
In embodiment one, two, three and four, the particle diameter of sierozem power is 400-600 mesh, is ensureing the exquisiteness of inner wall putty powder
On the basis of property, the levelability and feel of film can be improved.
The titanium dioxide is rutile type titanium white, can further improve the intensity of inner wall putty powder.
The particle diameter of the expanded perlite is 20-40 mesh, and the distribution of expanded perlite can be made more uniform, improves putty
The fire protecting performance and security performance of powder, the moisture-resistant hot property and heat-insulating property of powder of lacquer putty for use on are further improved, and green, peace
Good perfection.
In addition, the titanium dioxide added in the component of inner wall putty powder, its heat endurance is good, and density and hardness is high, can be with
Prevent powder of lacquer putty for use on applies from cracking afterwards on the wall, and can prevent ultraviolet and moisture from passing through, extend making for inner wall putty powder
Use the life-span.
Cellulose can prevent inner wall putty powder from cracking.
Diatomite can eliminate formaldehyde, purify air, adjust humidity, releasing negative oxygen ion, fire protection flame retarding, and can
With the good security of comfortableness of deodorization and sterilization, further raising living environment.
Wherein, matched according to the component of embodiment one, two, three and four, inner wall putty can be fabricated to by the following method
Powder：Step 1：Feedstock treating, component grinds and is filtered using sieve respectively, impurity therein is removed, can be with
Increase the quality of powder of lacquer putty for use on；
Step 2：Filler is mixed with base-material using mixer first；
Step 3：Insulation auxiliary agent is mixed, then added in the mixture in step 2；
Step 4：Antibacterial auxiliary agent is mixed, then adds in the mixture in step 3, stirs；
Step 5：Product inspection, packaging of weighing.
Embodiment five：
A kind of interior wall is incubated the construction method of antibacterial powder of lacquer putty for use on, mainly includes the following steps that：
(1) base treatment：Include cleaning-repairing-drying successively；
The base treatment of step (1) can increase the adhesion of inner wall surface and putty, make its dry after it is not easy to crack and
Come off.
(2) sealing：Caustic soda solution or glue are painted in inner wall surface after treatment；
Step (2) sealing is to remove the greasy dirt of inner wall surface, ensures the adhesive force of powder of lacquer putty for use on.
(3) dispensing：By inner wall putty powder and water according to 1：0.5 ratio is mixed, and then carries out first time stirring-quiet
Put-second stir process；
Step (3) reclaimed water and the mixed proportion of inner wall putty powder can increase the mobility and tack of powder of lacquer putty for use on, prevent
Powder of lacquer putty for use on comes off from metope.
(4) scratch：First time blade coating-blade coating-drying-the third time of drying-second blade coating-drying is carried out successively；
Powder of lacquer putty for use on can prevent powder of lacquer putty for use on from ftractureing, avoid producing sky by blade coating more than twice and drying in step (4)
Bulging phenomenon, improve the quality of its blade coating.
(5) polish：Inner wall surface is polished using sand paper；
Step (5) polishing can be floating by the flash on powder of lacquer putty for use on surface and projection, ensures the flatness of metope, and be easy to
The progress of next step mopping work.
(6) check and accept.
The cleaning is to be removed floating ash, mucilage and the splash of inner wall surface using hairbrush, it is ensured that the cleaning of metope,
So as to increase the adhesive force of powder of lacquer putty for use on.
The repairing is by the convex of inner wall surface is floating, recess is filled and led up, and the flatness of inner wall surface is controlled less than 5mm
It is interior, increase the flatness and aesthetic property of metope, reduce the dosage of powder of lacquer putty for use on, reduce cost.
The drying is to be removed the moisture of inner wall surface using hair-dryer, keeps the drying of inner wall surface, and artificial drying can be with
Dry efficiency and the effect dried are improved, shortens the whole finishing duration.
The first time speed of agitator is 60-120r/min, and mixing time 20-30min, the standing is 15-
20min, second of speed of agitator are 80-150r/min, mixing time 15-20min, can be abundant with water by powder of lacquer putty for use on
Mixing, avoid producing the phenomenon lumpd, improve smoothness during powder of lacquer putty for use on blade coating.
The sand paper is the sand paper of 240-320 mesh, can increase the planarization of metope.
According to inner wall putty powder made of component proportioning in above-described embodiment one, two, three and four according to being applied in embodiment five
Work method is constructed, and after testing, institute's inspection project meets《Architecture indoor putty》JG/T3049-1998 standards and《Paint film resists
Bacterium fungus-proof test method》The requirement of HG/T3950-2007 standards, it is qualified.
Wherein Detection results are as follows：
The inner wall putty powder made according to component provided by the present invention proportioning can not only insulation, and can press down
Bacterium is mould proof, helps for sleep, the comfortableness for being advantageous to the health of human body and living.And utilize the construction work provided in the present invention
Skill, the adhesive force and planarization of inner wall putty powder can be increased, prevent from ftractureing, extend the service life of powder of lacquer putty for use on.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effect carry out
It is further described, should be understood that the specific embodiment that the foregoing is only the present invention, is not limited to this
Invention, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc., should be included in this hair
Within bright protection domain.
Claims (10)
1. a kind of interior wall is incubated antibacterial powder of lacquer putty for use on, it is characterised in that：Including base-material, filler and auxiliary agent, the base-material, filler and
Auxiliary agent mainly includes following component according to parts by weight：Wherein,
The base-material includes latex powder 10-15 parts；
The filler includes calcium carbonate 50-70 parts, titanium dioxide 10-14 parts, cellulose 8-10 parts and diatomite 10-15 parts；
The auxiliary agent includes insulation auxiliary agent and antibacterial auxiliary agent, and the insulation auxiliary agent includes sepiolite powder 7-11 parts, expanded pearlite powder
20-30 parts and vermiculite power 9-13 parts, the antibacterial auxiliary agent include oyster shell whiting 5-8 parts, Ground Cloves 2-4 parts, African jasmine powder 1-2
Part, copper stearate soap powder 4-6 parts, bamboo charcoal powder 4-8 parts and nano-silver powder 0.3-0.7 parts.
2. interior wall according to claim 1 is incubated antibacterial powder of lacquer putty for use on, it is characterised in that：The particle diameter of the sierozem power is
400-600 mesh.
3. interior wall according to claim 1 is incubated antibacterial powder of lacquer putty for use on, it is characterised in that：The titanium dioxide is rutile-type
Titanium dioxide.
4. interior wall according to claim 1 is incubated antibacterial powder of lacquer putty for use on, it is characterised in that：The particle diameter of the expanded perlite
For 20-40 mesh.
5. a kind of interior wall is incubated the construction method of antibacterial powder of lacquer putty for use on, it is characterised in that：Mainly include the following steps that：
（1）Base treatment：Include cleaning-repairing-drying successively；
（2）Sealing：Caustic soda solution or glue are painted in inner wall surface after treatment；
（3）Dispensing：By inner wall putty powder and water according to 1：0.5 ratio is mixed, and then carries out first time stirring-standing-
Second of stir process；
（4）Blade coating：First time blade coating-blade coating-drying-the third time of drying-second blade coating-drying is carried out successively；
（5）Polishing：Inner wall surface is polished using sand paper；
（6）Check and accept.
6. interior wall according to claim 5 is incubated the construction method of antibacterial powder of lacquer putty for use on, it is characterised in that：The cleaning is
Floating ash, mucilage and the splash of inner wall surface are removed using hairbrush.
7. interior wall according to claim 5 is incubated the construction method of antibacterial powder of lacquer putty for use on, it is characterised in that：The repairing is
By the convex of inner wall surface is floating, recess is filled and led up, the flatness of inner wall surface is set to control in less than 5mm.
8. interior wall according to claim 5 is incubated the construction method of antibacterial powder of lacquer putty for use on, it is characterised in that：The drying is
The moisture of inner wall surface is removed using hair-dryer, keeps the drying of inner wall surface.
9. interior wall according to claim 5 is incubated the construction method of antibacterial powder of lacquer putty for use on, it is characterised in that：The first time
Speed of agitator is 60-120r/min, and mixing time 20-30min, the standing is 15-20min, and second of stirring turns
Speed is 80-150r/min, mixing time 15-20min.
10. interior wall according to claim 5 is incubated the construction method of antibacterial powder of lacquer putty for use on, it is characterised in that：The sand paper
For the sand paper of 240-320 mesh.