CN107335463A - 一种用于原油渣油裂解的催化剂制备方法 - Google Patents
一种用于原油渣油裂解的催化剂制备方法 Download PDFInfo
- Publication number
- CN107335463A CN107335463A CN201710634068.9A CN201710634068A CN107335463A CN 107335463 A CN107335463 A CN 107335463A CN 201710634068 A CN201710634068 A CN 201710634068A CN 107335463 A CN107335463 A CN 107335463A
- Authority
- CN
- China
- Prior art keywords
- parts
- crude oil
- stirring
- oil residuum
- mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：将改性膨润土、硅铝胶、水搅拌，调节pH值为1‑1.6，搅拌，调节pH值为6‑6.8，熟化，加入分子筛搅拌，干燥，煅烧，洗涤，干燥得到用于原油渣油裂解的催化剂。改性膨润土采用如下工艺制备：将羧甲基纤维素钠、水搅拌，加入葡萄糖淀粉酶超声处理，减压蒸馏，加入膨润土、乙醇溶液搅拌，过滤，洗涤，真空干燥，粉碎得到改性膨润土。
Description
技术领域
本发明涉及催化剂技术领域，尤其涉及一种用于原油渣油裂解的催化剂制备方法。
背景技术
随着科学技术的进步和经济建设的不断发展，能源危机的问题已经成为阻碍世界各个国家经济发展和建设的首要问题，受资源的影响，我国原油供求矛盾日益突出，从1993年开始，我国成为石油净进口国，每年需要花大量的外汇进口石油及石油产品。
我国大部分原油中渣油含量高，轻质油含量低，加之近年来一些重质油产量不断增长和部分国外重质原油的引进使重油轻质化问题更为突出。重油加工方法常用催化裂化方法，其采用的催化剂的孔容小、烯烃产率低问题一直未得到很好解决。
发明内容
基于背景技术存在的技术问题，本发明提出了一种用于原油渣油裂解的催化剂制备方法，所得催化剂具有大孔容，孔分布集中，有利于油渣大分子进入孔道进行反应，烯烃产率高。
本发明提出的一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：将改性膨润土、硅铝胶、水搅拌，调节pH值为1-1.6，搅拌，调节pH值为6-6.8，熟化，加入分子筛搅拌，干燥，煅烧，洗涤，干燥得到用于原油渣油裂解的催化剂。
优选地，改性膨润土、硅铝胶、分子筛的重量比为60-80：60-100：120-160。
优选地，包括如下步骤：按重量份将60-80份改性膨润土、60-100份硅铝胶、60-80份水搅拌40-60min，搅拌速度为2000-2800r/min，采用浓度为10-20wt％盐酸调节pH值为1-1.6，搅拌20-30min，加入氨水调节pH值为6-6.8，熟化8-14h，加入120-160份分子筛搅拌30-40min，搅拌速度为14000-16000r/min，干燥，800-1000℃煅烧5-10h，去离子水洗涤，干燥得到用于原油渣油裂解的催化剂。
优选地，改性膨润土采用如下工艺制备：将羧甲基纤维素钠、水搅拌，加入葡萄糖淀粉酶超声处理，减压蒸馏，加入膨润土、乙醇溶液搅拌，过滤，洗涤，真空干燥，粉碎得到改性膨润土。
优选地，改性膨润土采用如下工艺制备：按重量份将8-16份羧甲基纤维素钠、50-70份水搅拌，加入0.01-0.015份葡萄糖淀粉酶超声处理，减压蒸馏，加入40-60份膨润土、60-80份浓度为60-70wt％乙醇溶液搅拌，过滤，洗涤，真空干燥，粉碎得到改性膨润土。
优选地，改性膨润土采用如下工艺制备：按重量份将8-16份羧甲基纤维素钠、50-70份水搅拌40-60min，加入0.01-0.015份葡萄糖淀粉酶超声处理80-120min，超声温度为45-55℃，超声功率为100-200W，减压蒸馏，加入40-60份膨润土、60-80份浓度为60-70wt％乙醇溶液搅拌15-25min，过滤，洗涤，65-75℃真空干燥，粉碎得到改性膨润土。
本发明采用羧甲基纤维素钠在葡萄糖淀粉酶与超声协同作用下，适度酶解导致化学键断裂，而且通过合理控制超声条件，体系温度升高至一定程度，制品化学键断裂适中，表面张力降低明显，与膨润土的分散性极好，与硅铝胶配合，在高速搅拌下，不仅相互间分散程度极高，而且堵塞微孔的杂质被清除，部分微孔孔壁被破坏或者转变为过渡孔，用盐酸处理后既能增加催化剂的酸性中心，又能使催化剂的孔径向大孔偏移，有利于油渣大分子进入孔道进行反应，从而使烯烃产率提高，进一步配合加入分子筛，并合理控制配比，大孔容、孔分布集中，烯烃产率高。
具体实施方式
下面，通过具体实施例对本发明的技术方案进行详细说明。
实施例1
一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：将改性膨润土、硅铝胶、水搅拌，调节pH值为1-1.6，搅拌，调节pH值为6-6.8，熟化，加入分子筛搅拌，干燥，煅烧，洗涤，干燥得到用于原油渣油裂解的催化剂。
实施例2
一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：按重量份将60份改性膨润土、100份硅铝胶、60份水搅拌60min，搅拌速度为2000r/min，采用浓度为20wt％盐酸调节pH值为1-1.6，搅拌20min，加入氨水调节pH值为6-6.8，熟化14h，加入120份分子筛搅拌40min，搅拌速度为14000r/min，干燥，1000℃煅烧5h，去离子水洗涤，干燥得到用于原油渣油裂解的催化剂。
实施例3
一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：按重量份将80份改性膨润土、60份硅铝胶、80份水搅拌40min，搅拌速度为2800r/min，采用浓度为10wt％盐酸调节pH值为1-1.6，搅拌30min，加入氨水调节pH值为6-6.8，熟化8h，加入160份分子筛搅拌30min，搅拌速度为16000r/min，干燥，800℃煅烧10h，去离子水洗涤，干燥得到用于原油渣油裂解的催化剂。
改性膨润土采用如下工艺制备：将羧甲基纤维素钠、水搅拌，加入葡萄糖淀粉酶超声处理，减压蒸馏，加入膨润土、乙醇溶液搅拌，过滤，洗涤，真空干燥，粉碎得到改性膨润土。
实施例4
一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：按重量份将65份改性膨润土、90份硅铝胶、65份水搅拌55min，搅拌速度为2200r/min，采用浓度为18wt％盐酸调节pH值为1-1.6，搅拌22min，加入氨水调节pH值为6-6.8，熟化12h，加入130份分子筛搅拌38min，搅拌速度为14500r/min，干燥，950℃煅烧6h，去离子水洗涤，干燥得到用于原油渣油裂解的催化剂。
改性膨润土采用如下工艺制备：按重量份将12份羧甲基纤维素钠、60份水搅拌，加入0.012份葡萄糖淀粉酶超声处理，减压蒸馏，加入50份膨润土、70份浓度为65wt％乙醇溶液搅拌，过滤，洗涤，真空干燥，粉碎得到改性膨润土。
实施例5
一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：按重量份将75份改性膨润土、70份硅铝胶、75份水搅拌45min，搅拌速度为2600r/min，采用浓度为12wt％盐酸调节pH值为1-1.6，搅拌28min，加入氨水调节pH值为6-6.8，熟化10h，加入150份分子筛搅拌32min，搅拌速度为15500r/min，干燥，850℃煅烧8h，去离子水洗涤，干燥得到用于原油渣油裂解的催化剂。
改性膨润土采用如下工艺制备：按重量份将16份羧甲基纤维素钠、50份水搅拌60min，加入0.01份葡萄糖淀粉酶超声处理120min，超声温度为45℃，超声功率为200W，减压蒸馏，加入40份膨润土、80份浓度为60wt％乙醇溶液搅拌25min，过滤，洗涤，65℃真空干燥，粉碎得到改性膨润土。
实施例6
一种用于原油渣油裂解的催化剂制备方法，包括如下步骤：按重量份将70份改性膨润土、80份硅铝胶、70份水搅拌50min，搅拌速度为2400r/min，采用浓度为15wt％盐酸调节pH值为1-1.6，搅拌25min，加入氨水调节pH值为6-6.8，熟化11h，加入140份分子筛搅拌35min，搅拌速度为15000r/min，干燥，900℃煅烧7h，去离子水洗涤，干燥得到用于原油渣油裂解的催化剂。
改性膨润土采用如下工艺制备：按重量份将8份羧甲基纤维素钠、70份水搅拌40min，加入0.015份葡萄糖淀粉酶超声处理80min，超声温度为55℃，超声功率为100W，减压蒸馏，加入60份膨润土、60份浓度为70wt％乙醇溶液搅拌15min，过滤，洗涤，75℃真空干燥，粉碎得到改性膨润土。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (6)
1.一种用于原油渣油裂解的催化剂制备方法，其特征在于，包括如下步骤：将改性膨润土、硅铝胶、水搅拌，调节pH值为1-1.6，搅拌，调节pH值为6-6.8，熟化，加入分子筛搅拌，干燥，煅烧，洗涤，干燥得到用于原油渣油裂解的催化剂。
2.根据权利要求1所述用于原油渣油裂解的催化剂制备方法，其特征在于，改性膨润土、硅铝胶、分子筛的重量比为60-80：60-100：120-160。
3.根据权利要求1或2所述用于原油渣油裂解的催化剂制备方法，其特征在于，包括如下步骤：按重量份将60-80份改性膨润土、60-100份硅铝胶、60-80份水搅拌40-60min，搅拌速度为2000-2800r/min，采用浓度为10-20wt％盐酸调节pH值为1-1.6，搅拌20-30min，加入氨水调节pH值为6-6.8，熟化8-14h，加入120-160份分子筛搅拌30-40min，搅拌速度为14000-16000r/min，干燥，800-1000℃煅烧5-10h，去离子水洗涤，干燥得到用于原油渣油裂解的催化剂。
4.根据权利要求1-3任一项所述用于原油渣油裂解的催化剂制备方法，其特征在于，改性膨润土采用如下工艺制备：将羧甲基纤维素钠、水搅拌，加入葡萄糖淀粉酶超声处理，减压蒸馏，加入膨润土、乙醇溶液搅拌，过滤，洗涤，真空干燥，粉碎得到改性膨润土。
5.根据权利要求1-4任一项所述用于原油渣油裂解的催化剂制备方法，其特征在于，改性膨润土采用如下工艺制备：按重量份将8-16份羧甲基纤维素钠、50-70份水搅拌，加入0.01-0.015份葡萄糖淀粉酶超声处理，减压蒸馏，加入40-60份膨润土、60-80份浓度为60-70wt％乙醇溶液搅拌，过滤，洗涤，真空干燥，粉碎得到改性膨润土。
6.根据权利要求1-5任一项所述用于原油渣油裂解的催化剂制备方法，其特征在于，改性膨润土采用如下工艺制备：按重量份将8-16份羧甲基纤维素钠、50-70份水搅拌40-60min，加入0.01-0.015份葡萄糖淀粉酶超声处理80-120min，超声温度为45-55℃，超声功率为100-200W，减压蒸馏，加入40-60份膨润土、60-80份浓度为60-70wt％乙醇溶液搅拌15-25min，过滤，洗涤，65-75℃真空干燥，粉碎得到改性膨润土。