CN107312216A - 一种直角变径丁腈弯管 - Google Patents
一种直角变径丁腈弯管 Download PDFInfo
- Publication number
- CN107312216A CN107312216A CN201710691010.8A CN201710691010A CN107312216A CN 107312216 A CN107312216 A CN 107312216A CN 201710691010 A CN201710691010 A CN 201710691010A CN 107312216 A CN107312216 A CN 107312216A
- Authority
- CN
- China
- Prior art keywords
- parts
- butyronitrile
- right angle
- bend pipe
- angle reducing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于橡胶管材技术领域。本发明公开了一种直角变径丁腈弯管，其由丁腈胶料制得，丁腈胶料由丁腈橡胶、防老剂、促进剂、氧化镁、硬脂酸、石蜡、凡士林、炭黑、碳酸钙、立德粉、机油、硫黄和八甲基丙烯酸三季戊四醇二己二酸酯等原料制得。本发明中的直角变径丁腈弯管具有较好的断裂韧性，使用过程中不容易发生断裂；本发明中的直角变径丁腈弯管具有良好的抗老化性能，具有更长的使用寿命，减少更换、维护的成本。
Description
技术领域
本发明涉及橡胶管材技术领域，尤其是涉及一种直角变径丁腈弯管。
背景技术
直角变径弯管是一种在管道/管路连接上常用的部件，用于管路之间的变径，也用于管路与相关装置之间的连接，虽然是一个不起眼的小部件，其数量和体积都比管道小很多，但是其具有重要的作用，同时也是对于管路寿命一个重要的影响因素；现实生活中，装置管路的管道部分往往比较受到重视，但是这些管道之间的连接部件变径弯管则往往会被忽视，其出现问题也不容易被察觉，因此也会造成巨大的损失和不必要的麻烦。特别是在汽车中，发动机及附属的变速箱上拥有众多的管路，变径弯管这种连接件往往会被忽视，从而带来不容忽视的隐患，特别是变径弯管处的渗漏等情况不容易被发现，也会造成一系列的危害和危险，因此一种具有较强可靠性的变径弯管成为一种迫切需要。
发明内容
为解决上述问题，本发明提供了一种具有较好断裂韧性，使用过程中形变极小，并且具有良好的抗老化性能的直角变径丁腈弯管。
为实现上述目的，本发明采用的技术方案如下：
一种直角变径丁腈弯管，其由丁腈胶料制得，丁腈胶料包含以下重量份的原料：
丁腈橡胶100份，防老剂0.12～0.17份，促进剂3.1～3.3份，氧化镁2～3份，硬脂酸1.8～2.2份，石蜡0.4～0.6份，凡士林7～8份，炭黑80～100份，碳酸钙40～50份，立德粉10～20份，机油1.5～2.5份，硫黄1.5～2.0份，八甲基丙烯酸三季戊四醇二己二酸酯7～9份。
丁腈橡胶具有较强的可靠性，其抗拉伸强度和抗老化性能都不错，经过多种丁腈橡胶混合炼制后，其性能还能获得巨大的提高，同时加上一些添加剂和助剂改性后，其性能能够满足汽车发动机等领域中，直角变径弯管使用环境的要求，并能够保持较长的使用寿命，减少维护和更换的成本。
作为优选，丁腈胶料包含以下重量份的原料：
丁腈橡胶100份，防老剂0.15份，促进剂3.28份，氧化镁2.5份，硬脂酸2份，石蜡0.5份，凡士林7.5份，炭黑90份，碳酸钙45份，立德粉15份，机油2份，硫黄1.7份，八甲基丙烯酸三季戊四醇二己二酸酯8份。
作为优选，丁腈橡胶由丁腈橡胶26和丁腈橡胶18组成。
作为优选，丁腈橡胶中，丁腈橡胶26和丁腈橡胶18的重量比为1：1。
作为优选，防老剂为N-苯基-2-萘胺。
作为优选，促进剂由2,2′-二硫代二苯并噻唑和N,N′-四甲基二硫双硫羰胺组成。
作为优选，促进剂中，2,2′-二硫代二苯并噻唑和N,N′-四甲基二硫双硫羰胺的重量比为40：1。
作为优选，炭黑为喷雾炭黑。
作为优选，机油为40号机油。
因此，本发明具有以下有益效果：
（1）本发明中的直角变径丁腈弯管具有较好的断裂韧性，使用过程中不容易发生断裂；
（2）本发明中的直角变径丁腈弯管具有良好的抗老化性能，具有更长的使用寿命，减少更换、维护的成本。
具体实施方式
下面结合具体实施方式对本发明的技术方案作进一步的说明。
显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
在本发明中，若非特指，所有的设备和原料均可从市场上购得或是本行业常用的，下述实施例中的方法，如无特别说明，均为本领域常规方法。
实施例1
一种直角变径丁腈弯管，其由丁腈胶料制得，丁腈胶料包含以下重量份的原料：
丁腈橡胶26 50份，丁腈橡胶18 50份，N-苯基-2-萘胺0.12份，2,2′-二硫代二苯并噻唑3.02份，N,N′-四甲基二硫双硫羰胺0.08份，氧化镁2份，硬脂酸1.8份，石蜡0.4份，凡士林7份，喷雾炭黑80份，碳酸钙40份，立德粉10份，40号机油1.5份，硫黄1.5份，八甲基丙烯酸三季戊四醇二己二酸酯7份。
实施例2
一种直角变径丁腈弯管，其由丁腈胶料制得，丁腈胶料包含以下重量份的原料：
丁腈橡胶26 50份，丁腈橡胶18 50份，N-苯基-2-萘胺0.13份，2,2′-二硫代二苯并噻唑3.2份，N,N′-四甲基二硫双硫羰胺0.08份，氧化镁2.2份，硬脂酸1.9份，石蜡0.45份，凡士林7.5份，喷雾炭黑85份，碳酸钙42份，立德粉15份，40号机油2份，硫黄1.7份，八甲基丙烯酸三季戊四醇二己二酸酯7.5份
实施例3
一种直角变径丁腈弯管，其由丁腈胶料制得，丁腈胶料包含以下重量份的原料：
丁腈橡胶26 50份，丁腈橡胶18 50份， N-苯基-2-萘胺0.15份，2,2′-二硫代二苯并噻唑3.2份，N,N′-四甲基二硫双硫羰胺0.08份，氧化镁2.5份，硬脂酸2份，石蜡0.5份，凡士林7.5份，喷雾炭黑90份，碳酸钙45份，立德粉15份，40号机油2份，硫黄1.7份，八甲基丙烯酸三季戊四醇二己二酸酯8份。
实施例4
一种直角变径丁腈弯管，其由丁腈胶料制得，丁腈胶料包含以下重量份的原料：
丁腈橡胶26 50份，丁腈橡胶18 50份，N-苯基-2-萘胺0.16份，2,2′-二硫代二苯并噻唑3.2份，N,N′-四甲基二硫双硫羰胺0.08份，氧化镁2.8份，硬脂酸2.1份，石蜡0.55份，凡士林7.5份，喷雾炭黑95份，碳酸钙48份，立德粉15份，40号机油2份，硫黄1.8份，八甲基丙烯酸三季戊四醇二己二酸酯8.5份。
实施例5
一种直角变径丁腈弯管，其由丁腈胶料制得，丁腈胶料包含以下重量份的原料：
丁腈橡胶26 50份，丁腈橡胶18 50份，N-苯基-2-萘胺0.17份，2,2′-二硫代二苯并噻唑3.22份，N,N′-四甲基二硫双硫羰胺0.08份，氧化镁3份，硬脂酸2.2份，石蜡0.6份，凡士林8份，喷雾炭黑100份，碳酸钙50份，立德粉20份，40号机油2.5份，硫黄2.0份，八甲基丙烯酸三季戊四醇二己二酸酯9份。
技术指标：
邵氏硬度：76；
拉伸强度：12.9MPa；
扯断伸长率：285%；
永久变形：6%；
老化系数（24h╳90℃）：0.65。
应当理解的是，对于本领域普通技术人员来说，可以根据上述说明加以改进或变换，而所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (9)
1.一种直角变径丁腈弯管，其由丁腈胶料制得，其特征在于所述的丁腈胶料包含以下重量份的原料：
丁腈橡胶100份，防老剂0.12～0.17份，促进剂3.1～3.3份，氧化镁2～3份，硬脂酸1.8～2.2份，石蜡0.4～0.6份，凡士林7～8份，炭黑80～100份，碳酸钙40～50份，立德粉10～20份，机油1.5～2.5份，硫黄1.5～2.0份，八甲基丙烯酸三季戊四醇二己二酸酯7～9份。
2.根据权利要求1所述的一种直角变径丁腈弯管，其特征在于所述的丁腈胶料包含以下重量份的原料：
丁腈橡胶100份，防老剂0.15份，促进剂3.28份，氧化镁2.5份，硬脂酸2份，石蜡0.5份，凡士林7.5份，炭黑90份，碳酸钙45份，立德粉15份，机油2份，硫黄1.7份，八甲基丙烯酸三季戊四醇二己二酸酯8份。
3.根据权利要求1或2所述的一种直角变径丁腈弯管，其特征在于：
所述的丁腈橡胶由丁腈橡胶26和丁腈橡胶18组成。
4.根据权利要求3所述的一种直角变径丁腈弯管，其特征在于：
所述的丁腈橡胶中，丁腈橡胶26和丁腈橡胶18的重量比为1：1。
5.根据权利要求1或2所述的一种直角变径丁腈弯管，其特征在于：
所述的防老剂为N-苯基-2-萘胺。
6.根据权利要求1或2所述的一种直角变径丁腈弯管，其特征在于：
所述的促进剂由2,2′-二硫代二苯并噻唑和N,N′-四甲基二硫双硫羰胺组成。
7.根据权利要求6所述的一种直角变径丁腈弯管，其特征在于：
所述的促进剂中，2,2′-二硫代二苯并噻唑和N,N′ -四甲基二硫双硫羰胺的重量比为40：1。
8.根据权利要求1或2所述的一种直角变径丁腈弯管，其特征在于：
所述的炭黑为喷雾炭黑。
9.根据权利要求1或2所述的一种直角变径丁腈弯管，其特征在于：
所述的机油为40号机油。