CN107311533A - A kind of waterproof and the high Polymer Mortar of adhesion strength and preparation method thereof - Google Patents
A kind of waterproof and the high Polymer Mortar of adhesion strength and preparation method thereof Download PDFInfo
- Publication number
- CN107311533A CN107311533A CN201710508643.0A CN201710508643A CN107311533A CN 107311533 A CN107311533 A CN 107311533A CN 201710508643 A CN201710508643 A CN 201710508643A CN 107311533 A CN107311533 A CN 107311533A
- Authority
- CN
- China
- Prior art keywords
- polymer mortar
- adhesion strength
- powder
- high polymer
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of waterproof and the high Polymer Mortar of adhesion strength and preparation method thereof, the Polymer Mortar is according to mass percent, including the following raw material：Ash concrete 40 53%, quartz sand 45 58%, hydroxypropyl methyl cellulose ether 0.04 0.06%, starch ether 0.1 0.12%, polypropylene fibre 0.02 0.04%, butadiene-styrene latex powder 0.1 0.12%, acrylic latex powder 0.72 0.82%, calcium formate 0.4 0.54%, hydrophober 0.1 0.16%, powder defoamer 0.05 0.09%, powder water reducer 0.005 0.06%；Waterproof proposed by the present invention and the high Polymer Mortar of adhesion strength and preparation method thereof, it is while permeability resistance and water resistance is improved, also there is higher adhesion strength and preferable mechanical property, be easy to construction, service life length and production cost is low, preparation technology is simple.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of waterproof and the high Polymer Mortar of adhesion strength
And preparation method thereof.
Background technology
For coming off for building facing brick at present, the problems such as infiltration leak, it often affects the hair of construction industry
Exhibition；And in order to solve these problems, therefore occur in that by using cement-based waterproof high polymer material to be used to bond gap.It is existing
There are exploitation and the waterproof material and structure that use numerous, and traditional water-repellent paint typically each reduces hair using addition cellulose
Pore water imbibition, so as to reach water resistance, but while its water resistance is improved, often lead to its fracture resistance and
Adhesion strength is substantially reduced, therefore exists that its cohesive force is low, the deficiency of mobility and rupture strength difference, it is difficult to moist in basal plane
Or effectively used in the case of having infiltration, service life is short, and cost is high, and difficulty of construction is big, and gravity flowing levelling mortar easily occurs
Pitted skin and the uneven phenomenon of color, so as to largely effect on construction effect.
The content of the invention
It is an object of the invention to propose a kind of waterproof and the high Polymer Mortar of adhesion strength, it is improving impermeabilisation
Property and while water resistance, also with higher adhesion strength and preferable mechanical property, be easy to construction, service life length and
Production cost is low.
It is another object of the present invention to propose a kind of simple waterproof of preparation technology and the high macromolecule of adhesion strength
The preparation method of beneficial clay.
For up to this purpose, the present invention uses following technical scheme：
A kind of waterproof and the high Polymer Mortar of adhesion strength, the Polymer Mortar is according to mass percent, bag
Include the following raw material：Ash concrete 40-53%, quartz sand 45-58%, hydroxypropyl methyl cellulose ether 0.04-0.06%, starch ether
0.1-0.12%, polypropylene fibre 0.02-0.04%, butadiene-styrene latex powder 0.1-0.12%, acrylic latex powder 0.72-
0.82%th, calcium formate 0.4-0.54%, hydrophober 0.1-0.16%, powder defoamer 0.05-0.09%, powder water reducer 0.005-
0.06%.
It is furthermore preferred that the Polymer Mortar is according to mass percent, including the following raw material：Ash concrete 45%, quartz
Sand 53.26%, hydroxypropyl methyl cellulose ether 0.05%, starch ether 0.1%, polypropylene fibre 0.03%, butadiene-styrene latex powder
0.11%th, acrylic latex powder 0.8%, calcium formate 0.5%, hydrophober 0.1%, powder defoamer 0.055%, powder water reducer
0.005%.
Further illustrate, the hydrophober is siloxane polymer；The powder defoamer is mineral oil.
Further illustrate, the powder water reducer is times in polycarboxylate water-reducer, aliphatic water reducing agent or amino water reducer
Meaning is a kind of.
Further illustrate, the ash concrete is the ash concrete of 42.5R grades of intensity.
Further illustrate, the granular size of the quartz sand is 100~250 mesh.
Further illustrate, the fibre length of the polypropylene fibre is 5~6mm.
The preparation method of a kind of waterproof and the high Polymer Mortar of adhesion strength, comprises the following steps：
(1) preparation of masterbatch：Weighed respectively by formula rate hydroxypropyl methyl cellulose ether, starch ether, polypropylene fibre,
Butadiene-styrene latex powder, acrylic latex powder, calcium formate, hydrophober, powder defoamer and powder water reducer are used as masterbatch；And carry out uniform
Mix, obtain agent mixture；
(2) preparation of finished product：Weigh quartz sand and ash concrete respectively by formula rate, and successively in order by quartz sand,
Ash concrete and the agent mixture are uniformly mixed, and obtain waterproof and the high Polymer Mortar of adhesion strength.
Further illustrate, it is 1000r/min that speed is mixed described in step (1), and mixing time is 60s.
Further illustrate, the mixing speed in step (2) is 1000r/min, and mixing time is 5min.
Beneficial effects of the present invention：By being added in its composition of raw materials after a certain amount of multiple fiber element, while using
Two clock latex powders of a certain amount of butadiene-styrene latex powder and acrylic latex powder, effectively reduction pore water imbibition, so as to obtain
More excellent permeability resistance, the Polymer Mortar of water resistance are obtained, while also making Polymer Mortar possess higher
Adhesion strength and preferable mechanical property.Wherein by the hard performance of the butadiene-styrene latex powder, to effectively increase high score
The cohesive force of sub- benefit clay, so as to increase its adhesion strength；And further by the soft performance of the acrylic latex powder,
To make the flexibility of Polymer Mortar higher, make it while possessing high caking ability, possess higher fracture resistance, it flows
Property more preferably, so as to easily facilitate construction, effectively prevent that pitted skin and the uneven phenomenon of color from occurring in gravity flowing levelling mortar, while can drop
The low usage amount of rubber powder and cellulose, so as to greatly save production cost.
Embodiment
Technical scheme is further illustrated below by embodiment.
A kind of waterproof and the high Polymer Mortar of adhesion strength, the Polymer Mortar is according to mass percent, bag
Include the following raw material：Ash concrete 40-53%, quartz sand 45-58%, hydroxypropyl methyl cellulose ether 0.04-0.06%, starch ether
0.1-0.12%, polypropylene fibre 0.02-0.04%, butadiene-styrene latex powder 0.1-0.12%, acrylic latex powder 0.72-
0.82%th, calcium formate 0.4-0.54%, hydrophober 0.1-0.16%, powder defoamer 0.05-0.09%, powder water reducer 0.005-
0.06%.A kind of waterproof proposed by the present invention and the high Polymer Mortar of adhesion strength, by being added in its composition of raw materials
After a certain amount of multiple fiber element, while two clock latex powders of a certain amount of butadiene-styrene latex powder and acrylic latex powder are employed,
Effectively reduction pore water imbibition, so as to obtain more excellent permeability resistance, water resistance Polymer Mortar, and
Polymer Mortar is also set to possess higher adhesion strength and preferable mechanical property simultaneously, service life is longer.Wherein pass through
The hard performance of the butadiene-styrene latex powder, to effectively increase the cohesive force of Polymer Mortar, so as to increase its adhesion strength；
And further by the soft performance of the acrylic latex powder, to make the flexibility of Polymer Mortar higher, make it in tool
While standby high caking ability, possesses higher fracture resistance, its mobility more preferably, so as to easily facilitate construction, is effectively prevented certainly
There is pitted skin and the uneven phenomenon of color in levelling mortar, while the usage amount of rubber powder and cellulose can be reduced, so that significantly
Save production cost.
It is furthermore preferred that the Polymer Mortar is according to mass percent, including the following raw material：Ash concrete 45%, quartz
Sand 53.26%, hydroxypropyl methyl cellulose ether 0.05%, starch ether 0.1%, polypropylene fibre 0.03%, butadiene-styrene latex powder
0.11%th, acrylic latex powder 0.8%, calcium formate 0.5%, hydrophober 0.1%, powder defoamer 0.055%, powder water reducer
0.005%.
Further illustrate, the hydrophober is siloxane polymer；The powder defoamer is mineral oil.
Further illustrate, the powder water reducer is times in polycarboxylate water-reducer, aliphatic water reducing agent or amino water reducer
Meaning is a kind of.By adding a certain amount of powder water reducer, and combine acrylic latex powder and butadiene-styrene latex powder so that certain
While forming high cohesive force under cohesive force effect, the Polymer Mortar dispersiveness and mobility are further increased.
Further illustrate, the ash concrete is the ash concrete of 42.5R grades of intensity.
Further illustrate, the granular size of the quartz sand is 100~250 mesh.It is 100~250 mesh from granular size
Quartz sand and the ash concrete of 42.5R grades of intensity form the base-material of even density so that the bonding of Polymer Mortar is strong
Degree is more uniform, and its water resistance is also more stablized.
Further illustrate, the fibre length of the polypropylene fibre is 5~6mm.It is 5~6mm by using fibre length
Polypropylene fibre and a certain amount of butadiene-styrene latex powder and acrylic latex powder two clock latex powders, make the Polymer Mortar
Adhesion strength it is higher while, its water resistance more stablize.
The preparation method of a kind of waterproof and the high Polymer Mortar of adhesion strength, comprises the following steps：
(1) preparation of masterbatch：Weighed respectively by formula rate hydroxypropyl methyl cellulose ether, starch ether, polypropylene fibre,
Butadiene-styrene latex powder, acrylic latex powder, calcium formate, hydrophober, powder defoamer and powder water reducer are used as masterbatch；And carry out uniform
Mix, obtain agent mixture；
(2) preparation of finished product：Weigh quartz sand and ash concrete respectively by formula rate, and successively in order by quartz sand,
Ash concrete and the agent mixture are uniformly mixed, and obtain waterproof and the high Polymer Mortar of adhesion strength.
The preparation method of a kind of waterproof proposed by the present invention and the high Polymer Mortar of adhesion strength, wherein first by recipe ratio system
It is standby to obtain masterbatch, its raw material is mixed and possesses that high caking ability, fold resistance and permeability resistance be good and mobility with acquisition
More preferable agent mixture；Quartz sand, ash concrete and agent mixture are stirred mixing again, you can obtain the beneficial glue of macromolecule
Mud, its preparation technology is simple, and its overall water resistance is more preferably, adhesion strength is higher and possesses more preferable mechanical property, applies
Work is convenient and uniform in effect, stability are good.
Further illustrate, it is 1000r/min that speed is mixed described in step (1), and mixing time is 60s.Pass through control
The mixing speed of masterbatch processed, while making to be sufficiently mixed uniform between each raw material, with avoid damage to cellulose, butadiene-styrene latex powder and
Acrylic latex powder performance, so as to obtain more stable agent mixture.
Further illustrate, the mixing speed in step (2) is 1000r/min, and mixing time is 5min.Pass through
Certain mixing speed between the quartz sand, ash concrete and agent mixture is controlled, so that its mixing is more uniform, dispersiveness
With mobility more preferably, so as to form more stable mixed system.
The preparation method of a kind of waterproofs of embodiment 1- and the high Polymer Mortar of adhesion strength, comprises the following steps：
(1) preparation of masterbatch：Weighed respectively by formula rate hydroxypropyl methyl cellulose ether, starch ether, polypropylene fibre,
Butadiene-styrene latex powder, acrylic latex powder, calcium formate, hydrophober, powder defoamer and powder water reducer are used as masterbatch；And carry out uniform
Mix, the mixing speed is 1000r/min, and mixing time is 60s, obtains agent mixture；
(2) preparation of finished product：Weigh quartz sand and ash concrete respectively by formula rate, and successively in order by quartz sand,
Ash concrete and the agent mixture are uniformly mixed, and the mixing speed is 1000r/min, mixing time
For 5min, waterproof and the high Polymer Mortar 1 of adhesion strength are obtained.
Its each raw material components proportioning is as shown in the table：
The preparation method of a kind of waterproofs of embodiment 2- and the high Polymer Mortar of adhesion strength, comprises the following steps：
(1) preparation of masterbatch：Weighed respectively by formula rate hydroxypropyl methyl cellulose ether, starch ether, polypropylene fibre,
Butadiene-styrene latex powder, acrylic latex powder, calcium formate, hydrophober, powder defoamer and powder water reducer are used as masterbatch；And carry out uniform
Mix, the mixing speed is 1000r/min, and mixing time is 60s, obtains agent mixture；
(2) preparation of finished product：Weigh quartz sand and ash concrete respectively by formula rate, and successively in order by quartz sand,
Ash concrete and the agent mixture are uniformly mixed, and the mixing speed is 1000r/min, mixing time
For 5min, waterproof and the high Polymer Mortar 2 of adhesion strength are obtained.
Its each raw material components proportioning is as shown in the table：
The preparation method of a kind of waterproofs of embodiment 3- and the high Polymer Mortar of adhesion strength, comprises the following steps：
(1) preparation of masterbatch：Weighed respectively by formula rate hydroxypropyl methyl cellulose ether, starch ether, polypropylene fibre,
Butadiene-styrene latex powder, acrylic latex powder, calcium formate, hydrophober, powder defoamer and powder water reducer are used as masterbatch；And carry out uniform
Mix, the mixing speed is 1000r/min, and mixing time is 60s, obtains agent mixture；
(2) preparation of finished product：Weigh quartz sand and ash concrete respectively by formula rate, and successively in order by quartz sand,
Ash concrete and the agent mixture are uniformly mixed, and the mixing speed is 1000r/min, mixing time
For 5min, waterproof and the high Polymer Mortar 3 of adhesion strength are obtained.
Its each raw material components proportioning is as shown in the table：
The preparation method of a kind of comparative example-waterproof and the high Polymer Mortar of adhesion strength, comprises the following steps：
(1) hydroxypropyl methyl cellulose ether and powder water reducer are weighed respectively by formula rate, and carries out uniform mixing and is stirred
Mix, the mixing speed is 1000r/min, and mixing time is 60s, obtains agent mixture；
(2) preparation of finished product：Weigh quartz sand and ash concrete respectively by formula rate, and successively in order by quartz sand,
Ash concrete and the agent mixture are uniformly mixed, and the mixing speed is 1000r/min, mixing time
For 5min, waterproof and the high Polymer Mortar 4 of adhesion strength are obtained.
Its each raw material components proportioning is as shown in the table：
| Material name | Percentage % |
| Ash concrete (42.5R) | 42.07% |
| Quartz sand (100#) | 57.36% |
| Hydroxypropyl methyl cellulose ether | 0.03% |
| Polycarboxylate water-reducer (powder water reducer) | 0.54% |
The Polymer Mortar that the Polymer Mortar prepared by embodiment 1~3 is obtained with comparative example is adopted
Performance test is carried out after sample, and carries out comparative result such as table 1 below：
Table 1：The performance detection table of different technologies parameter
As shown in Table 1, the Polymer Mortar obtained as prepared by embodiment 1~3 and comparative example, wherein embodiment
Polymer Mortar in 1~3, can meet the requirement of the technical parameter of execution standard, its compression strength, rupture strength, anti-
The performance of penetration and adhesion strength is above comparative example, therefore the Polymer Mortar prepared by inventive formulation ratio
The more excellent existing Polymer Mortar of various aspects of performance preparation technology；And it can also be seen that and obtained by embodiment 2
The compression strength of Polymer Mortar, rupture strength, the performance of impermeabilisation power and adhesion strength is obviously higher than the and of embodiment 1
Implement 3；Therefore, the various aspects of performance of the Polymer Mortar prepared by the formula rate of embodiment 2 is more excellent.
The technical principle of the present invention is described above in association with specific embodiment.These descriptions are intended merely to explain the present invention's
Principle, and limiting the scope of the invention can not be construed in any way.Based on explanation herein, the technology of this area
Personnel, which would not require any inventive effort, can associate other embodiments of the present invention, and these modes are fallen within
Within protection scope of the present invention.
Claims (10)
1. a kind of waterproof and the high Polymer Mortar of adhesion strength, it is characterised in that：The Polymer Mortar is according to quality
Percentage, including the following raw material：Ash concrete 40-53%, quartz sand 45-58%, hydroxypropyl methyl cellulose ether 0.04-
0.06%th, starch ether 0.1-0.12%, polypropylene fibre 0.02-0.04%, butadiene-styrene latex powder 0.1-0.12%, acrylic based emulsion
Powder 0.72-0.82%, calcium formate 0.4-0.54%, hydrophober 0.1-0.16%, powder defoamer 0.05-0.09%, powder water reducer
0.005-0.06%.
2. a kind of waterproof according to claim 1 and the high Polymer Mortar of adhesion strength, it is characterised in that：The height
Molecule benefit clay is according to mass percent, including the following raw material：Ash concrete 45%, quartz sand 53.26%, hydroxypropyl methyl fiber
Plain ether 0.05%, starch ether 0.1%, polypropylene fibre 0.03%, butadiene-styrene latex powder 0.11%, acrylic latex powder 0.8%, first
Sour calcium 0.5%, hydrophober 0.1%, powder defoamer 0.055%, powder water reducer 0.005%.
3. a kind of waterproof according to claim 1 and the high Polymer Mortar of adhesion strength, it is characterised in that：It is described to hate
Aqua is siloxane polymer；The powder defoamer is mineral oil.
4. a kind of waterproof according to claim 1 and the high Polymer Mortar of adhesion strength, it is characterised in that：The powder
Water reducer is any one in polycarboxylate water-reducer, aliphatic water reducing agent or amino water reducer.
5. a kind of waterproof according to claim 1 and the high Polymer Mortar of adhesion strength, it is characterised in that：The ash
Cement is the ash concrete of 42.5R grades of intensity.
6. a kind of waterproof according to claim 1 and the high Polymer Mortar of adhesion strength, it is characterised in that：The stone
The granular size of sand is 100~250 mesh.
7. a kind of waterproof according to claim 1 and the high Polymer Mortar of adhesion strength, it is characterised in that：It is described poly-
The fibre length of tacryl is 5~6mm.
8. a kind of preparation side of the high Polymer Mortar of waterproof and adhesion strength as described in claim 1~7 any one
Method, it is characterised in that：Comprise the following steps：
(1) preparation of masterbatch：Weigh hydroxypropyl methyl cellulose ether, starch ether, polypropylene fibre, butylbenzene respectively by formula rate
Latex powder, acrylic latex powder, calcium formate, hydrophober, powder defoamer and powder water reducer are used as masterbatch；And uniformly mixed
Stirring, obtains agent mixture；
(2) preparation of finished product：Quartz sand and ash concrete are weighed respectively by formula rate, and successively in order by quartz sand, buck
Mud and the agent mixture are uniformly mixed, and obtain waterproof and the high Polymer Mortar of adhesion strength.
9. the preparation method of a kind of waterproof according to claim 8 and the high Polymer Mortar of adhesion strength, its feature
It is：It is 1000r/min that speed is mixed described in step (1), and mixing time is 60s.
10. the preparation method of a kind of waterproof according to claim 8 and the high Polymer Mortar of adhesion strength, its feature
It is：The mixing speed in step (2) is 1000r/min, and mixing time is 5min.