CN107298771A - 一种吸音保温建筑装饰材料及制备方法 - Google Patents
一种吸音保温建筑装饰材料及制备方法 Download PDFInfo
- Publication number
- CN107298771A CN107298771A CN201710540720.0A CN201710540720A CN107298771A CN 107298771 A CN107298771 A CN 107298771A CN 201710540720 A CN201710540720 A CN 201710540720A CN 107298771 A CN107298771 A CN 107298771A
- Authority
- CN
- China
- Prior art keywords
- parts
- absorption heat
- ornament materials
- heat preserving
- acoustical absorption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种吸音保温建筑装饰材料及制备方法，所述材料包括原料如下：废旧纸浆、木屑、高粘凹凸棒石粘土、胶黏剂、植物纤维、阻燃剂、轻质碳酸钙、石英粉。制备方法包括：分别将各组分进行混合并充分搅拌均匀，得到混合浆料，然后将混合浆料置于模具中，然后将模具置于平板硫化机中，进行热压成型，然后将成型后的产品进行打磨处理，即制得吸音保温建筑装饰材料。所述装饰材料不仅具有较好的吸音、保温效果，还具有一定的防阻燃性能，且所述制备方法简单易行，适合工业化生产应用。
Description
技术领域
本发明涉及建筑装饰材料技术领域，具体涉及一种吸音保温建筑装饰材料及制备方法。
背景技术
目前建筑市场上采用的屋顶、墙体的建筑材料一般以铝箔、塑料中间层、聚乙烯发泡棉复合形成的保温材料为主。所述的保温材料具有以下缺点：聚乙烯发泡棉是通过物理发泡挤压生成的高泡沫聚乙烯制品，由无数的单个气泡构成,该塑料发泡材料容易燃烧，阻燃效果差，在防火性能方面存在着安全隐患；保温材料的中间层为塑料层，所述塑料层虽然增加了保温材料的拉伸强度，便于施工，但是塑料层使得保温材料的阻燃性能较差；现有的保温材料吸音防噪效果差。
目前市场上用于隔音保温的建筑材料有许多，但基本上是硬质半硬质的材料，这些材料虽可用于墙面的隔音保温，但用作管道等需要弯曲包覆时其适应性较差，因而其使用面窄，市场价值低。
随着技术的进步，也出现了改进型的材料和升级的制造工艺。聚酯纤维毡就是基于原有毛毡类的纤维铺网热烘成型的改进工艺上制造出来的；原有的回收利用纤维更换为粗旦聚酯纤维，原有粘结剂更换为低熔点聚酯纤维；聚酯纤维毡在环保性、斥水性、阻燃性等特性上与毛毡相比大大提高。橡胶发泡材料比聚氨酯发泡在斥水性、阻燃性上有所提高。但两者都在最重要的特性-吸音效率上并没有很大提升。但是，在材料中聚酯短纤维的含量难以再提高，因为抗拉性大幅度下降，造成材料在制造过程中难以成形；由于材料内粗纤维的大量存在，又会造成吸音性能大打折扣。这些都是现有的以熔喷法为基础工艺的吸音保温材料的性能障碍和在制造过程中难于 解决的问题。
因此，研究开发一种既具有较好的吸音、保温效果，又具有简单成型工艺的一种装饰材料的制备方法具有较好的应用价值，也符合目前市场的需求。
发明内容
针对现有技术中的缺陷，本发明的目的是提供一种吸音保温建筑装饰材料及制备方法，所述装饰材料不仅具有较好的吸音、保温效果，还具有一定的防阻燃性能，且所述制备方法简单易行，适合工业化生产应用。
本发明解决技术问题采用如下技术方案：
本发明涉及一种吸音保温建筑装饰材料，包括如下重量份的各原料：废旧纸浆20~35份、木屑10~17份、高粘凹凸棒石粘土6~15份、胶黏剂20~33份、植物纤维10~15份、阻燃剂3~8份、轻质碳酸钙5~9份、石英粉4~7份。
优选地，所述材料包括如下重量份的各原料：废旧纸浆30份、木屑15份、高粘凹凸棒石粘土12份、胶黏剂28份、植物纤维11份、阻燃剂6份、轻质碳酸钙8份、石英粉5份。
优选地，所述胶黏剂为EVA胶水、环氧树脂胶黏剂、聚乙烯醇胶黏剂中的任一种。
优选地，所述植物纤维为棉麻纤维或者竹纤维。
优选地，所述阻燃剂为三氧化二锑或者有机硅系阻燃剂。
本发明还涉及一种制备吸音保温建筑装饰材料的方法，包括如下步骤：
（1）按照配比分别称取废旧纸浆、木屑、植物纤维粉碎，并过50~80目筛，备用；
（2）按照配比分别称取胶黏剂、轻质碳酸钙、石英粉混合搅拌均匀，然后加入步骤（1）得到的混合物、高粘凹凸棒石粘土和阻燃剂，充分混合均匀，得到混合浆料；
（3）将制备得到的混合浆料置于模具中，然后将模具置于平板硫化机中，进行热压成型，然后将成型后的产品进行打磨处理，即制得吸音保温建筑装饰材料。
优选地，所述步骤（3）中热压成型温度为170~180℃。
优选地，所述步骤（3）中热压成型的压力控制在20~23MPa。
与现有技术相比，本发明具有如下的有益效果：
（1）本发明所述的吸音保温建筑装饰材料，采用废旧纸浆及纤维材料作为主材，不仅具有较好的吸音、保温效果，还大大降低了装饰材料的制作成本，且对废弃物的处理提供了条件，实现了废弃物的资源化利用，具有较好的应用价值。
（2）本发明所述的吸音保温建筑装饰材料中添加有高粘凹凸棒石粘土，大大增加了制备过程各原料之间的粘结性能，且由于凹凸棒石粘土独特的层链状结构，能够对声波进行无数次反射、相互叠加、碰撞，最终使得声波转化为热能，声波强度减弱，声音消失，实现消音的作用。
（3）本发明所述的吸音保温建筑装饰材料的中添加阻燃剂，使得制备得到的装饰材料具有一定的阻燃效果，在保证材料吸音、保温功能的同时提高了材料的使用安全性。
（4）本发明所述吸音保温建筑装饰材料的制备工艺简单、条件温和、设备投资少，且生产过程安全、无污染，适合工业化推广生产，具有较好的应用前景。
具体实施方式
下面结合具体实施例，进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。下列实施例中未注明具体条件的实验方法，通常按照常规条件，例如Sambrook等分子克隆：实验室手册（New York:Cold Spring Harbor Laboratory Press,1989）中所述的条件，或按照制造厂商所建议的条件。
实施例1：
本发明优选实施例的一种吸音保温建筑装饰材料及制备方法；
所述吸音保温建筑装饰材料，由如下重量份的各原料制备而成：
废旧纸浆 30份；
木屑 15份；
高粘凹凸棒石粘土 12份；
胶黏剂 28份；
植物纤维 11份；
阻燃剂 6份；
轻质碳酸钙 8份；
石英粉 5份。
所述胶黏剂为EVA胶水。
所述植物纤维为棉麻纤维。
所述阻燃剂为三氧化二锑。
本发明制备吸音保温建筑装饰材料的方法，包括如下步骤：
（1）按照配比分别称取废旧纸浆、木屑、植物纤维粉碎，并过50~80目筛，备用；
（2）按照配比分别称取胶黏剂、轻质碳酸钙、石英粉混合搅拌均匀，然后加入步骤（1）得到的混合物、高粘凹凸棒石粘土和阻燃剂，充分混合均匀，得到混合浆料；
（3）将制备得到的混合浆料置于模具中，然后将模具置于平板硫化机中，于175℃、压力为20MPa的条件下进行热压成型，然后将成型后的产品进行打磨处理，即制得吸音保温建筑装饰材料。
实施例2：
本发明优选实施例的一种吸音保温建筑装饰材料及制备方法；
所述吸音保温建筑装饰材料，由如下重量份的各原料制备而成：
废旧纸浆 20份；
木屑 10份；
高粘凹凸棒石粘土 6份；
胶黏剂 20份；
植物纤维 10份；
阻燃剂 3份；
轻质碳酸钙 5份；
石英粉 4份。
所述胶黏剂为环氧树脂胶黏剂。
所述植物纤维为者竹纤维。
所述阻燃剂为有机硅系阻燃剂。
本发明制备吸音保温建筑装饰材料的方法，包括如下步骤：
（1）按照配比分别称取废旧纸浆、木屑、植物纤维粉碎，并过50~80目筛，备用；
（2）按照配比分别称取胶黏剂、轻质碳酸钙、石英粉混合搅拌均匀，然后加入步骤（1）得到的混合物、高粘凹凸棒石粘土和阻燃剂，充分混合均匀，得到混合浆料；
（3）将制备得到的混合浆料置于模具中，然后将模具置于平板硫化机中，于170℃、压力为20MPa的条件下进行热压成型，然后将成型后的产品进行打磨处理，即制得吸音保温建筑装饰材料。
实施例3：
本发明优选实施例的一种吸音保温建筑装饰材料及制备方法；
所述吸音保温建筑装饰材料，由如下重量份的各原料制备而成：
废旧纸浆 35份；
木屑 17份；
高粘凹凸棒石粘土 15份；
胶黏剂 33份；
植物纤维 15份；
阻燃剂 8份；
轻质碳酸钙 9份；
石英粉 7份。
所述胶黏剂为聚乙烯醇胶黏剂。
所述植物纤维为棉麻纤维。
所述阻燃剂为三氧化二锑。
本发明制备吸音保温建筑装饰材料的方法，包括如下步骤：
（1）按照配比分别称取废旧纸浆、木屑、植物纤维粉碎，并过50~80目筛，备用；
（2）按照配比分别称取胶黏剂、轻质碳酸钙、石英粉混合搅拌均匀，然后加入步骤（1）得到的混合物、高粘凹凸棒石粘土和阻燃剂，充分混合均匀，得到混合浆料；
（3）将制备得到的混合浆料置于模具中，然后将模具置于平板硫化机中，于180℃、压力为23MPa的条件下进行热压成型，然后将成型后的产品进行打磨处理，即制得吸音保温建筑装饰材料。
实施例4：
本发明优选实施例的一种吸音保温建筑装饰材料及制备方法；
所述吸音保温建筑装饰材料，由如下重量份的各原料制备而成：
废旧纸浆 22份；
木屑 15份；
高粘凹凸棒石粘土 10份；
胶黏剂 26份；
植物纤维 10份；
阻燃剂 5份；
轻质碳酸钙 6份；
石英粉 7份。
所述胶黏剂为EVA胶水。
所述植物纤维为棉麻纤维。
所述阻燃剂为三氧化二锑。
本发明制备吸音保温建筑装饰材料的方法，包括如下步骤：
（1）按照配比分别称取废旧纸浆、木屑、植物纤维粉碎，并过50~80目筛，备用；
（2）按照配比分别称取胶黏剂、轻质碳酸钙、石英粉混合搅拌均匀，然后加入步骤（1）得到的混合物、高粘凹凸棒石粘土和阻燃剂，充分混合均匀，得到混合浆料；
（3）将制备得到的混合浆料置于模具中，然后将模具置于平板硫化机中，于178℃、压力为22MPa的条件下进行热压成型，然后将成型后的产品进行打磨处理，即制得吸音保温建筑装饰材料。
综上所述，本发明所述的吸音保温建筑装饰材料，采用废旧纸浆及纤维材料作为主材，不仅具有较好的吸音、保温效果，还大大降低了装饰材料的制作成本，且对废弃物的处理提供了条件，实现了废弃物的资源化利用，具有较好的应用价值。
本发明所述吸音保温建筑装饰材料的制备工艺简单、条件温和、设备投资少，且生产过程安全、无污染，适合工业化推广生产，具有较好的应用前景。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (8)
1.一种吸音保温建筑装饰材料，其特征在于：包括如下重量份的各原料：废旧纸浆20~35份、木屑10~17份、高粘凹凸棒石粘土6~15份、胶黏剂20~33份、植物纤维10~15份、阻燃剂3~8份、轻质碳酸钙5~9份、石英粉4~7份。
2.根据权利要求1所述的吸音保温建筑装饰材料，其特征在于：所述材料包括如下重量份的各原料：废旧纸浆30份、木屑15份、高粘凹凸棒石粘土12份、胶黏剂28份、植物纤维11份、阻燃剂6份、轻质碳酸钙8份、石英粉5份。
3.根据权利要求1所述的吸音保温建筑装饰材料，其特征在于：所述胶黏剂为EVA胶水、环氧树脂胶黏剂、聚乙烯醇胶黏剂中的任一种。
4.根据权利要求1所述的吸音保温建筑装饰材料，其特征在于：所述植物纤维为棉麻纤维或者竹纤维。
5.根据权利要求1所述的吸音保温建筑装饰材料，其特征在于：所述阻燃剂为三氧化二锑或者有机硅系阻燃剂。
6.一种制备如权利要求1~5任一项所述的吸音保温建筑装饰材料的方法，其特征在于：包括如下步骤：
（1）按照配比分别称取废旧纸浆、木屑、植物纤维粉碎，并过50~80目筛，备用；
（2）按照配比分别称取胶黏剂、轻质碳酸钙、石英粉混合搅拌均匀，然后加入步骤（1）得到的混合物、高粘凹凸棒石粘土和阻燃剂，充分混合均匀，得到混合浆料；
（3）将制备得到的混合浆料置于模具中，然后将模具置于平板硫化机中，进行热压成型，然后将成型后的产品进行打磨处理，即制得吸音保温建筑装饰材料。
7.根据权利要求6所述的吸音保温建筑装饰材料的制备方法，其特征在于：所述步骤（3）中热压成型温度为170~180℃。
8.根据权利要求6所述的吸音保温建筑装饰材料的制备方法，其特征在于：所述步骤（3）中热压成型的压力控制在20~23MPa。