CN107267251A - A kind of boiler dirt-resistant additive and its preparation and application - Google Patents
A kind of boiler dirt-resistant additive and its preparation and application Download PDFInfo
- Publication number
- CN107267251A CN107267251A CN201710463393.3A CN201710463393A CN107267251A CN 107267251 A CN107267251 A CN 107267251A CN 201710463393 A CN201710463393 A CN 201710463393A CN 107267251 A CN107267251 A CN 107267251A
- Authority
- CN
- China
- Prior art keywords
- boiler
- dirt
- additive
- parts
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of boiler dirt-resistant additive and its preparation and application, the additive includes the component of following parts by weight:15~25 parts of tungsten ore;10~20 parts of gangue;20~30 parts of bauxite;5~15 parts of chromite;25~35 parts of sandstone.Compared with prior art, the present invention is not on the premise of boiler structure and service condition is changed, it can effectively improve and easily stain fuel ash fusing point, reduce its caking property, substantially reduce slagging, the dust stratification problem for using and easily staiing fuel boiler, strengthen heat exchanger tube heat-transfer effect, reduce the flue gas loss of boiler, improve boiler efficiency;Electrical energy consumption of ventilation is reduced, station service has been saved;Effectively reduce the risk of carbonated drink normal work inside slagging influence heating surface, it is therefore prevented that carbonated drink pipe overheats booster;Reduce corrosion of the slagging to metal pipe-wall.The present invention expands accommodation of the boiler to easily contamination fuel for solving the problems, such as easily to stain fuel slagging, dust stratification.
Description
Technical field
The present invention relates to boiler technology field, and in particular to a kind of boiler dirt-resistant additive and its preparation and application.
Background technology
Many coals, few gas, oil-poor energy resource structure determine that coal is still the leading of China in the future for a long period of time
The energy.Thermal power plant, which is undoubtedly, uses coal rich and influential family, and wherein quite a few is low-order coal, when boiler uses low-order coal, easily causes tight
The dust stratification of weight and slagging.Because grey dirt has the thermal resistance more much bigger than metallic walls, thus heat-transfer effect is reduced, add boiler
Flue gas loss, reduces boiler efficiency, and adds electrical energy consumption of ventilation.Simultaneously as slagging has a locality, thus have influence on by
Carbonated drink normal work inside hot face.Serious slagging will block exhaust gases passes and burner hearth slag-drip opening and carbonated drink pipe is overheated booster,
Destruction equipment is continuously run.Slagging also exacerbates corrosion of metal.To remove slagging, shutdown maintenance of often having to is short by then every 3
Once, long then every 6 months shutdown maintenances once, substantially reduce the time that boiler is continuously run, caused huge individual month shutdown maintenance
Big economic loss.To prevent slagging, some boilers are also forced to run at low load for a long time.Therefore, dust stratification, the serious shadow of slagging
Ring the availability of boiler, exert oneself and security, bring huge economic loss.Therefore, boiler structure and operation are not being changed
On the premise of condition, seek a kind of energy-efficient, inexpensive, strong ecad boiler dirt-resistant additive and be just particularly important.
Current dirt-resistant additive types are various, can be divided into 3 classes according to the main component of additive:Based on kaolin
Dirt-resistant additive, such as 104,371,790 104327903 A of A, CN of A, CN of patent CN 102786998, though effect is good
Consumption is big, freight charges are high, action is slow, fuel tolerance is poor, and kaolinic combination water evaporation heat absorption can reduce boiler efficiency;With
Cr2O3, oxidant, adsorbent be main component chromium base dirt-resistant additive, such as patent CN 104845698 A, CN
104910996 103060051 A of A, CN, though it is fast to work, effect is general, and fuel tolerance is poor, so being difficult to promote;With
Al2O3Pure material and SiO2Oxide dirt-resistant additive based on pure material, such as patent CN 104371789 A, CN
104745270 104164270 A of A, CN, though the good cost of raw material of effect is high, fuel tolerance is poor.Above-mentioned three classes dirt-resistant
Additive is although each advantageous, but consumption is big, freight charges are high, action is slow, the inferior position of fuel tolerance difference causes it to use scope
It is very limited, is extremely difficult to popularization truly.So a kind of energy-efficient, inexpensive, strong ecad pot of research and development
Stove dirt-resistant additive is particularly important.
The content of the invention
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide one kind it is energy-efficient, low into
Originally, the boiler dirt-resistant additive of strong ecad and its preparation and application.
The purpose of the present invention can be achieved through the following technical solutions:A kind of boiler dirt-resistant additive, its feature exists
In the additive includes the component of following parts by weight:
In above-mentioned ore, MnWO is contained in tungsten ore4, MnWO4Dirt-resistant effect is fabulous, with the part in ash content under high temperature
Inorganic elements combines to form high-melting-point tungsten thing, improves grey component, significantly improves ash content fusing point, and coal adaptability is excellent
It is good;The main component of gangue is Al2O3、SiO2;The main component of bauxite is Al2O3, Al3(SiO3)3;It is main in sandstone
Composition is SiO2;Al2O3、SiO2、Al3(SiO3)3Good alkali metal conversion ratio is shown, alkali metal can be converted into stabilization
Alkali metal aluminosilicate, significantly reduces alkali metal corrosion and alkali metal stains;Contain Cr in chromite2O3, the material plays
Booster action, promote to be changed into crystalline state from glassy state by above-mentioned reacted cinder, further make ash content rapid shaping, prevent
Flowable state cinder stains boiler.
It is preferred that, the sandstone includes the one or more in gneiss, sea sand, river sand or Desert Sand.
It is preferred that, the additive can also include 1~5 part of pyrolusite.There is abundant MnO in pyrolusite2, MnO2
As catalyst, the dirt-resistant reaction of the catalysis above improves reaction rate, and stable dirt-resistant effect improves coal adaptability.
A kind of preparation method of boiler dirt-resistant additive as described above, comprises the following steps:Each component is crushed, so
It is well mixed according to parts by weight afterwards, produce the boiler dirt-resistant additive.
Each component is crushed to particle diameter less than 200 μm.
A kind of application of the boiler dirt-resistant additive obtained using preparation method as described above, the additive is used for coal dust
The dirt-resistant of boiler or fluidized-bed combustion boiler.
When boiler is pulverized-coal fired boiler, the application comprises the following steps:The additive prepared and fire coal are sent in the lump
Enter coal pulverizer to be crushed and mixed, obtained mixture sequentially passes through mill separator, pulverized-coal collector and separated, then
Storage, when in use, pulverized-coal fired boiler is sent into by powder feeding blower fan.
When boiler is fluidized-bed combustion boiler, the application comprises the following steps:By the additive prepared and desulfurizing agent powder
Material mixing storage, then sends into fluidized-bed combustion boiler by powder feeding blower fan.
Using when, the weight ratio of fuel and additive is 100 in the pulverized-coal fired boiler or fluidized-bed combustion boiler:(0.1~3).
Compared with prior art, beneficial effects of the present invention are embodied in following several respects:
(1) formula of the invention is using the ore easily obtained, and cost is low, and with more preferable soil resistant effect and coal
Plant adaptability;
(2) prepare simple, using simple, application prospect is big.
Embodiment
Embodiments of the invention are elaborated below, the present embodiment is carried out lower premised on technical solution of the present invention
Implement, give detailed embodiment and specific operating process, but protection scope of the present invention is not limited to following implementations
Example.
Embodiment 1
Prepare boiler dirt-resistant additive of the present invention:The dirt-resistant additive of the present embodiment presses 20 parts of tungsten ore, gangue
15 parts, 25 parts of bauxite, 10 parts of chromite, 20 parts of gneiss, 10 parts of Desert Sand, 3 parts of pyrolusite mass fraction prepare.
Preparation method:Each component is first crushed to maximum particle diameter less than 200 μm, then again by each component according to mass fraction
It is well mixed.
The application method of this dirt-resistant additive is as follows:
Desulfurizing agent feed bin is stored in after the additive prepared is mixed with desulfurizing agent powder, is finally sent under conveying wind effect
Fluidized bed.
The usage amount of boiler dirt-resistant additive of the present invention is:The mass ratio of this additive and boiler oil is 0.3:
100。
The boiler dirt-resistant additive application that the present embodiment is provided is to certain 135MW bituminous rock circulating fluidized bed boiler of power station
On, monitored, as a result shown under conditions of steam generator system is normally run by long-play:Ash content is with alkali metal aluminosilicate
The ratio that form is present is 90%, measures ash fusion point for 1475 DEG C, reduces the dust stratification as caused by alkali vapor, slagging and heat-transfer surface
Etching problem, improves the utilization ratio of equipment, prolonged boiler life-span.And boiler continuous operating time reaches 258 days, during which pot
Stove items service data normal table.
Embodiment 2
Using formula similar to Example 1 and preparation method and application method, difference is:
(1) parts by weight of each component are as follows:25 parts of tungsten ore, 10 parts of gangue, 30 parts of bauxite, 15 parts of chromite, sea
35 parts of sand, 5 parts of pyrolusite.
(2) mass ratio of additive and boiler oil is 3: 100.
Through actual test, the ratio that ash content is present in alkali metal aluminosilicate form is 92%, and it is 1501 to measure ash fusion point
DEG C, the dust stratification as caused by alkali vapor, slagging and heat-transfer surface etching problem are equally reduced, the utilization ratio of equipment is improved, prolongs
Long boiler life.Boiler continuous operating time reaches 269 days, during which the every service data normal table of boiler.
Embodiment 3
Using formula and preparation method similar to Example 1, difference is:
(1) parts by weight of each component are as follows:15 parts of tungsten ore, 20 parts of gangue, 20 parts of bauxite, 5 parts of chromite, river sand
25 parts, 1 part of pyrolusite.
(2) additive obtained by the present embodiment is used for the mass ratio of certain 350MW boiler using brown coal, additive and boiler oil
For 0.1: 100.
(3) application process:The additive prepared and the coal-fired coal pulverizer of feeding in the lump are crushed and mixed, is obtained
Mixture sequentially passes through mill separator, pulverized-coal collector and separated, and is then store in coal store, when in use, by sending
Powder blower fan sends into pulverized-coal fired boiler.
Through actual test, the ratio that ash content is present in alkali metal aluminosilicate form is 88%, and it is 1463 to measure ash fusion point
DEG C, the dust stratification as caused by alkali vapor, slagging and heat-transfer surface etching problem are equally reduced, the utilization ratio of equipment is improved, prolongs
Long boiler life.Boiler continuous operating time reaches 240 days, during which the every service data normal table of boiler.
Claims (9)
1. a kind of boiler dirt-resistant additive, it is characterised in that the additive includes the component of following parts by weight:
2. a kind of boiler dirt-resistant additive according to claim 1, it is characterised in that the sandstone include gneiss,
One or more in sea sand, river sand or Desert Sand.
3. a kind of boiler dirt-resistant additive according to claim 1, it is characterised in that the additive includes 1~5 part
Pyrolusite.
4. the preparation method of a kind of boiler dirt-resistant additive as described in claims 1 to 3 is any, it is characterised in that described
Preparation method comprises the following steps:Each component is crushed, it is then well mixed according to parts by weight, produce the boiler dirt-resistant and add
Plus agent.
5. the preparation method of a kind of boiler dirt-resistant additive according to claim 4, it is characterised in that each component is crushed
It is less than 200 μm to particle diameter.
6. a kind of application of the additive as described in claims 1 to 3 is any, it is characterised in that the additive is used for pulverized-coal fired boiler
Or the dirt-resistant of fluidized-bed combustion boiler.
7. the application of a kind of boiler dirt-resistant additive according to claim 6, it is characterised in that when boiler is coal dust pot
During stove, the application comprises the following steps:The additive prepared and the coal-fired coal pulverizer of feeding in the lump are crushed with being mixed,
Obtained mixture sequentially passes through mill separator, pulverized-coal collector and separated, and then stores, when in use, passes through powder feeding
Blower fan sends into pulverized-coal fired boiler.
8. the application of a kind of boiler dirt-resistant additive according to claim 6, it is characterised in that when boiler is fluid bed
During boiler, the application comprises the following steps:The additive prepared is mixed into storage with desulfurizing agent powder, then passes through powder feeding
Blower fan sends into fluidized-bed combustion boiler.
9. the application of a kind of boiler dirt-resistant additive according to claim 6, it is characterised in that when applying, the coal
The weight ratio of fuel and additive is 100 in powder boiler or fluidized-bed combustion boiler:(0.1~3).