CN107265973A - 一种墙体保温材料及其制备方法 - Google Patents
一种墙体保温材料及其制备方法 Download PDFInfo
- Publication number
- CN107265973A CN107265973A CN201710471353.3A CN201710471353A CN107265973A CN 107265973 A CN107265973 A CN 107265973A CN 201710471353 A CN201710471353 A CN 201710471353A CN 107265973 A CN107265973 A CN 107265973A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulation
- wall heat
- insulation material
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种墙体保温材料及其制备方法，涉及建筑材料领域，墙体保温材料是由以下重量份的原料制成：改性建材废渣40份、水泥70份、凹凸棒土粉30份、硅藻土粉25份、竹炭粉10份、海泡石25份、二氧化钛3份、轻质碳酸钙70份、滑石粉10份、发泡聚苯板50份、单烷基醚磷酸酯5份、草酸钠2份、甘露醇4份、麦芽糖醇3份、硅丙乳液30份、羟丙基甲基纤维素醚6份；制备方法为(1)将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合搅拌、干燥得活性粉体；(2)将凹凸棒粉和竹炭粉混合煅烧，冷却后加入草酸钠、甘露醇、麦芽糖醇，再加入活性粉体和其余原料；本发明具有节约资源、减少能耗、保护环境和保温隔热效果好的优点。
Description
技术领域
本发明属于建筑材料领域，具体涉及一种墙体保温材料及其制备方法。
背景技术
随着社会的发展，人们对能源的消耗速度越来越快，消耗量也越来越大，在开发新能源的同时，目前就如何减少对能源的损耗显得越来越重要。
房屋建筑在我国的能源消耗比重中占据这重大的比例，而墙体作为房屋建筑的重要组成部分，在很大程度上决定着能源消耗量，研发高性价比的墙体保温材料成为目前迫切需要解决的问题。
墙体保温材料作为影响建筑节能一个重要因素，合理开发墙体保温材料，有效再回收利用建筑工业产生的废渣废料，既能大量节约墙体材料，又能达到节约资源，减少环境污染的目的，符合国家节能环保的政策。
2016年5月18日公告的中国专利文献一种建材废渣生产的墙体保温材料及其制备方法(授权公告号CN104261754B)，其是由下述重量份的原料制得：改性建材废渣5-15，白水泥80-100，浮石70-90，凹凸棒土粉10-15，竹炭粉2-4，单烷基醚磷酸酯1-2，硅丙乳液10-15，草酸钠1-2，甘露醇1-3，麦芽糖醇0.5-1，羟丙基甲基纤维素醚2-4；该发明的墙体保温材料合理回收利用建材废渣生产墙体保温材料，在保证保温隔热效果的前提下，达到节能环保的目的。
在该发明的基础上提出一种墙体保温材料及其制备方法，具有节约资源、减少能耗、保护环境、保温隔热效果好的优点。
发明内容
为了解决现有墙体保温材料存在着不能实现废物再利用、对环境污染大、保温隔热效果差和能耗高的问题，本发明的目的是提供一种墙体保温材料及其制备方法，具有节约资源、减少能耗、保护环境和保温隔热效果好的优点。
本发明提供了如下的技术方案：
一种墙体保温材料，其是由以下重量份的原料制成：
解决了现有墙体保温材料及其制备方法存在着不能实现废物再利用、对环境污染大、保温隔热效果差、能耗高的问题。
优选地，其是由以下重量份的原料制成：
优选地，所述改性建材废渣由以下重量份的原料制成：岩棉板废料15-20份、闭孔珍珠岩废渣10-20份、发泡水泥10-15份、液体石蜡1-3份、油酸0.2-0.4份、酒石酸钠1-3份、硼酸酯偶联剂2-4份，具有实现了废物再利用、保温隔热效果好和能耗低的优点。
优选地，所述改性建材废渣由以下重量份的原料制成：岩棉板废料15-18份、闭孔珍珠岩废渣10-15份、发泡水泥10-12份、液体石蜡1-2份、油酸0.3-0.4份、酒石酸钠1-2份、硼酸酯偶联剂2-3份，具有实现了废物再利用效果较好、保温隔热效果较好和能耗较低的优点。
优选地，所述改性建材废渣由以下重量份的原料制成：岩棉板废料15份、闭孔珍珠岩废渣15份、发泡水泥12份、液体石蜡2份、油酸0.4份、酒石酸钠2份、硼酸酯偶联剂2份，具有实现了废物再利用效果最好、保温隔热效果最好和能耗最低的优点。
优选地，所述水泥为粉煤灰硅酸盐水泥或复合硅酸盐水泥；粉煤灰硅酸盐水泥由硅酸盐水泥熟料、粉煤灰和适量的石膏混合后磨细而成，实现了废物再利用，成本低，抗裂性好，隔热效果好，耐腐蚀性好；复合硅酸盐水泥具有良好的保温隔热效果。
优选地，所述水泥为粉煤灰硅酸盐水泥，成本低，保温隔热效果好。
一种墙体保温材料的制备方法，包括以下步骤：
(1)将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合后运送到搅拌机搅拌，搅拌速度为900-1100r/min，搅拌时间30-40分钟，喷雾干燥后得到活性粉体；
(2)将凹凸棒粉和竹炭粉混合后在温度为500-550℃环境中煅烧1.5-2h，冷却后加入草酸钠、甘露醇、麦芽糖醇，混合后研磨均匀，过120-150目筛，加入步骤(1)得到的活性粉体和墙体保温材料中的其余原料，搅拌均匀后分装即得。
本发明的有益效果是：
1、本发明解决了现有墙体保温材料存在着不能实现废物再利用、对环境污染大、保温隔热效果差、能耗高的问题。
2、本发明中所述改性建材废渣由以下重量份的原料制成：岩棉板废料15-20份、闭孔珍珠岩废渣10-20份、发泡水泥10-15份、液体石蜡1-3份、油酸0.2-0.4份、酒石酸钠1-3份、硼酸酯偶联剂2-4份，具有实现了废物再利用、保温隔热效果好和能耗低的优点。
3、本发明中所述水泥为粉煤灰硅酸盐水泥或复合硅酸盐水泥；粉煤灰硅酸盐水泥由硅酸盐水泥熟料、粉煤灰和适量的石膏混合后磨细而成，实现了废物再利用，成本低，抗裂性好，隔热效果好，耐腐蚀性好；复合硅酸盐水泥具有良好的保温隔热效果。
具体实施方式
实施例1
一种墙体保温材料，其是由以下重量份的原料制成：
硅藻土粉为特殊多孔的构造，具有良好的红外光反射效果和隔热效果。
海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，具有可塑性好、收缩率低、隔热和抗腐蚀性好。
二氧化钛自身就具有良好的红外光反射效果和隔热效果。
轻质碳酸钙和滑石粉也均具有良好的隔热效果，轻质碳酸钙、滑石粉和二氧化钛三者混合使用使得制造出的墙体保温材料的隔热效果更好。
改性建材废渣由以下重量份的原料制成：岩棉板废料15份、闭孔珍珠岩废渣15份、发泡水泥12份、液体石蜡2份、油酸0.4份、酒石酸钠2份、硼酸酯偶联剂2份，具有实现了废物再利用效果最好、保温隔热效果最好和能耗最低的优点。
岩棉板最为建筑中常见的保温材料，在具有良好的保温隔热的性能的同时，其成本低廉，生活中常见，很容易就地取材，作为墙体保温材料的原料。
闭孔珍珠岩和发泡水泥同样具有很好的隔热效果。
水泥为粉煤灰硅酸盐水泥，成本低，保温隔热效果好。
硼酸酯偶联剂发挥着增强粘接的作用。
一种墙体保温材料的制备方法，包括以下步骤：
(1)将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合后运送到搅拌机搅拌，搅拌速度为900r/min，搅拌时间30分钟，喷雾干燥后得到活性粉体；
(2)将凹凸棒粉和竹炭粉混合后在温度为500℃环境中煅烧1.5h，冷却后加入草酸钠、甘露醇、麦芽糖醇，混合后研磨均匀，过120目筛，加入步骤(1)得到的活性粉体和墙体保温材料中的其余原料，搅拌均匀后分装即得。
依据DB34/T1279-2010进行产品性能测试，上述实施例制得的墙体保温材料的测试结果如下：
干表观密度(kg/m3):291；
线性收缩率(％)：0.34；
抗压强度(Mpa)：1.35；
粘结强度(Kpa)：94；
导热系数(w/m﹒k)：0.026。
实施例2
一种墙体保温材料，其是由以下重量份的原料制成：
硅藻土粉为特殊多孔的构造，具有良好的红外光反射效果和隔热效果。
海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，具有可塑性好、收缩率低、隔热和抗腐蚀性好。
二氧化钛自身就具有良好的红外光反射效果和隔热效果。
轻质碳酸钙和滑石粉也均具有良好的隔热效果，轻质碳酸钙、滑石粉和二氧化钛三者混合使用使得制造出的墙体保温材料的隔热效果更好。
改性建材废渣由以下重量份的原料制成：岩棉板废料15份、闭孔珍珠岩废渣15份、发泡水泥12份、液体石蜡2份、油酸0.4份、酒石酸钠2份、硼酸酯偶联剂2份，具有实现了废物再利用效果最好、保温隔热效果最好和能耗最低的优点。
岩棉板最为建筑中常见的保温材料，在具有良好的保温隔热的性能的同时，其成本低廉，生活中常见，很容易就地取材，作为墙体保温材料的原料。
闭孔珍珠岩和发泡水泥同样具有很好的隔热效果。
水泥为粉煤灰硅酸盐水泥，成本低，保温隔热效果好。
硼酸酯偶联剂发挥着增强粘接的作用。
一种墙体保温材料的制备方法，包括以下步骤：
(1)将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合后运送到搅拌机搅拌，搅拌速度为1100r/min，搅拌时间40分钟，喷雾干燥后得到活性粉体；
(2)将凹凸棒粉和竹炭粉混合后在温度为550℃环境中煅烧2h，冷却后加入草酸钠、甘露醇、麦芽糖醇，混合后研磨均匀，过150目筛，加入步骤(1)得到的活性粉体和墙体保温材料中的其余原料，搅拌均匀后分装即得。
依据DB34/T1279-2010进行产品性能测试，上述实施例制得的墙体保温材料的测试结果如下：
干表观密度(kg/m3):296；
线性收缩率(％)：0.33；
抗压强度(Mpa)：1.45；
粘结强度(Kpa)：96；
导热系数(w/m﹒k)：0.024。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种墙体保温材料，其特征在于，其是由以下重量份的原料制成：
2.根据权利要求1所述的墙体保温材料，其特征在于，其是由以下重量份的原料制成：
3.根据权利要求1所述的墙体保温材料，其特征在于：所述改性建材废渣由以下重量份的原料制成：岩棉板废料15-20份、闭孔珍珠岩废渣10-20份、发泡水泥10-15份、液体石蜡1-3份、油酸0.2-0.4份、酒石酸钠1-3份、硼酸酯偶联剂2-4份。
4.根据权利要求3所述的墙体保温材料，其特征在于：所述改性建材废渣由以下重量份的原料制成：岩棉板废料15-18份、闭孔珍珠岩废渣10-15份、发泡水泥10-12份、液体石蜡1-2份、油酸0.3-0.4份、酒石酸钠1-2份、硼酸酯偶联剂2-3份。
5.根据权利要求4所述的墙体保温材料，其特征在于：所述改性建材废渣由以下重量份的原料制成：岩棉板废料15份、闭孔珍珠岩废渣15份、发泡水泥12份、液体石蜡2份、油酸0.4份、酒石酸钠2份、硼酸酯偶联剂2份。
6.根据权利要求1所述的墙体保温材料，其特征在于：所述水泥为粉煤灰硅酸盐水泥或复合硅酸盐水泥。
7.根据权利要求6所述的墙体保温材料，其特征在于：所述水泥为粉煤灰硅酸盐水泥。
8.一种如权利要求1所述的墙体保温材料的制备方法，其特征在于，包括以下步骤：
(1)将硅丙乳液、单烷基醚磷酸酯和羟丙基甲基纤维素醚混合后运送到搅拌机搅拌，搅拌速度为900-1100r/min，搅拌时间30-40分钟，喷雾干燥后得到活性粉体；
(2)将凹凸棒粉和竹炭粉混合后在温度为500-550℃环境中煅烧1.5-2h，冷却后加入草酸钠、甘露醇、麦芽糖醇，混合后研磨均匀，过120-150目筛，加入步骤(1)得到的活性粉体和墙体保温材料中的其余原料，搅拌均匀后分装即得。