CN107227630A - A kind of printing technology of dacron - Google Patents

A kind of printing technology of dacron Download PDF

Info

Publication number
CN107227630A
CN107227630A CN201710330451.5A CN201710330451A CN107227630A CN 107227630 A CN107227630 A CN 107227630A CN 201710330451 A CN201710330451 A CN 201710330451A CN 107227630 A CN107227630 A CN 107227630A
Authority
CN
China
Prior art keywords
dacron
printing
stamp
parts
printing technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710330451.5A
Other languages
Chinese (zh)
Inventor
秦祥银
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yin Qiao Textile Technology Co Ltd
Original Assignee
Jiangsu Yin Qiao Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Yin Qiao Textile Technology Co Ltd filed Critical Jiangsu Yin Qiao Textile Technology Co Ltd
Priority to CN201710330451.5A priority Critical patent/CN107227630A/en
Publication of CN107227630A publication Critical patent/CN107227630A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of dacron printing technology, by preboarding, the preparation of printing paste, stamp, evaporate, wash and tentering baking step, complete the printing technology of dacron；It the advantage is that：By adding low temperature dyeing carrier in printing paste, reduce dacron stamp and temperature, time and pressure in laking process, low energy consumption dacron continuous low temperature steaming and color fixing is realized, the deficiency that existing Disperse Printing technique is evaporated applied to the HTHP needed for dacron stamp is efficiently solved.

Description

A kind of printing technology of dacron
Technical field
The invention belongs to textile printing and dyeing field, and in particular to a kind of printing technology of dacron.
Background technology
Terylene is hydrophobic thermoplastic fibre, because its hygroscopicity is poor, can not colour it with conventional printing method, So in terylene direct printing technique, it is general that vapour steaming colour fixing, HTHP are carried out to disperse dyes using HTHP steam method Steam method need to consume sizable energy consumption.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to now provide, a kind of temperature is low, the small dacron of energy consumption Printing technology.
In order to solve the above technical problems, the technical solution adopted by the present invention is：A kind of printing technology of dacron, it is created New point is：By pre-setting, the preparation of printing paste, stamp, evaporate, wash and tentering baking step, complete dacron Printing technology；It is described to concretely comprise the following steps：
（1）Pre-setting：Dacron is shaped on forming machine, the pre-setting temperature is 180-200 DEG C, it is described predetermined Type speed is 40-50m/min；
（2）The preparation of printing paste：By the disperse dyes, 1-2 parts of reservehao S, 2-10 parts of low temperature dyeing that parts by weight are 1-3 parts Carrier, 1-3 parts of citric acid and 50-60 parts of printing gum are mixed, and complete the preparation of print paste；
（3）Stamp：Direct printing is carried out to the dacron after pre-setting with printing paste, then it dried, it is described to dry Dry temperature is 60-100 DEG C, and the drying time is 1-3min；
（4）Evaporate：Terylene after stamp is put into cylinder steam box and evaporated；
（5）Washing：Terylene after evaporating is put into the water added with alkaline agent and surfactant and washed 3-5 times；
（6）Tentering is dried：Terylene after washing is subjected to stentering forming on forming machine, the printing technology of dacron is completed, The setting temperature is 150-170 DEG C, and the shaping time is 50-60s.
Further, the step（2）Middle printing gum is one in sodium alginate, carboxymethyl cellulose and emulsion thickening Kind.
Further, the step（4）In evaporate temperature for 80-120 DEG C, evaporate the time for 10-15min, pressure is 95- 105kpa。
Further, the step（5）Middle alkaline agent is one kind in sodium hydroxide, sodium acid carbonate and sodium carbonate, and surface is lived Property agent be stearic acid polyoxyethylene fat and stearic acid polyoxyethylene ether in one kind.
Beneficial effects of the present invention are as follows：The present invention by preboarding, the preparation of printing paste, stamp, evaporate, wash and draw Width baking step, completes the printing technology of dacron；By adding low temperature dyeing carrier in printing paste, dacron is reduced Temperature, time and pressure in stamp and laking process, realize low energy consumption dacron continuous low temperature steaming and color fixing, effectively solve Existing Disperse Printing technique be applied to dacron stamp needed for the deficiency evaporated of HTHP.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation Content disclosed by book understands other advantages and effect of the present invention easily.
Embodiment 1
A kind of dacron printing technology, by pre-setting, the preparation of printing paste, stamp, evaporate, wash and tentering drying walk Suddenly, the printing technology of dacron is completed；Concretely comprise the following steps：
（1）Pre-setting：Dacron is shaped on forming machine, preboarding temperature is 180 DEG C, pre-setting speed is 40m/ min；
（2）The preparation of printing paste：It is 1 part of disperse dyes, 1 part of reservehao S, 2 parts of low temperature dyeing carrier, 1 by parts by weight The citric acid and 50 parts of printing gum of part are mixed, and complete the preparation of print paste；
（3）Stamp：Direct printing is carried out to the dacron after pre-setting with printing paste, then it dried at 60 DEG C Dry, drying time is 1min；
（4）Evaporate：Terylene after stamp is put into cylinder steam box and evaporated at 80 DEG C, the time is evaporated for 10min, pressure For 95KPa；
（5）Washing：Terylene after evaporating is put into the water added with sodium hydroxide and polyoxyethylene stearic acid ester and washed 3 times；
（6）Tentering is dried：Terylene after washing is subjected to stentering forming on forming machine, the printing technology of dacron is completed, Setting temperature is 150 DEG C, and shaping time is 50s.
Embodiment 2
A kind of dacron printing technology, by pre-setting, the preparation of printing paste, stamp, evaporate, wash and tentering drying walk Suddenly, the printing technology of dacron is completed；Concretely comprise the following steps：
（1）Pre-setting：Dacron is subjected to pre-setting on forming machine, preboarding temperature is 200 DEG C, pre-setting speed 50m/ min；
（2）The preparation of printing paste：It is 3 parts of disperse dyes, 2 parts of reservehao S, 10 parts of low temperature dyeing carrier, 3 by parts by weight The citric acid and 60 parts of printing gum of part are mixed, and complete the preparation of print paste；
（3）Stamp：Direct printing is carried out to the dacron after pre-setting with printing paste, then it dried at 100 DEG C Dry, drying time is 3min；
（4）Evaporate：Terylene after stamp is put into cylinder steam box and evaporated at 120 DEG C, the time is evaporated for 15min, pressure Power is 105kpa；
（5）Washing：Dacron is washed 5 times in the water added with sodium acid carbonate and the poly- poplar vinethene of stearic acid；
（6）Tentering is dried：Terylene after washing is subjected to stentering forming on forming machine, the printing technology of dacron is completed, Setting temperature is 170 DEG C, and shaping time is 60s.
Embodiment 3
A kind of dacron printing technology, it is characterised in that:By pre-setting, the preparation of printing paste, stamp, evaporate, wash and Tentering baking step, completes the printing technology of dacron；It is described to concretely comprise the following steps：
（1）Pre-setting：Dacron is subjected to pre-setting on forming machine, pre-setting temperature is 190 DEG C, pre-setting speed 45m/ min；
（2）The preparation of printing paste：It is 2 parts of disperse dyes, 1 part of reservehao S, 6 parts of low temperature dyeing carrier, 2 by parts by weight The citric acid of part and the mixing of 55 parts of printing gum, complete the preparation of print paste；
（3）Stamp：Direct printing is carried out to the dacron after pre-setting with printing paste, then it dried at 80 DEG C, Drying time is 2min；
（4）Evaporate：Terylene after stamp is put into cylinder steam box and evaporated at 100 DEG C, the time is evaporated for 12min, pressure Power is 100kpa；
（5）Washing：Dacron is washed 4 times in the water added with sodium carbonate and the poly- poplar vinethene of stearic acid；
（6）Tentering is dried：Terylene after washing is subjected to stentering forming on forming machine, the printing technology of dacron is completed, Setting temperature is 160 DEG C, and shaping time is 55s.
The present invention by preboarding, the preparation of printing paste, stamp, evaporate, wash and tentering baking step, complete terylene and knit The printing technology of thing；By adding the temperature in low temperature dyeing carrier, reduction dacron stamp and laking process in printing paste Degree, time and pressure, realize low energy consumption dacron continuous low temperature steaming and color fixing, efficiently solve existing Disperse Printing work The deficiency that skill is evaporated applied to the HTHP needed for dacron stamp.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as The technical scheme that can be realized without creative work on the basis of above-described embodiment, is regarded as falling into patent of the present invention In rights protection scope.

Claims (4)

1. a kind of printing technology of dacron, it is characterised in that：By pre-setting, the preparation of printing paste, stamp, evaporate, water Wash and tentering baking step, the printing technology of completion dacron；It is described to concretely comprise the following steps：
（1）Pre-setting：Dacron is shaped on forming machine, the pre-setting temperature is 180-200 DEG C, it is described predetermined Type speed is 40-50m/min；
（2）The preparation of printing paste：By the disperse dyes, 1-2 parts of reservehao S, 2-10 parts of low temperature dyeing that parts by weight are 1-3 parts Carrier, 1-3 parts of citric acid and 50-60 parts of printing gum are mixed, and complete the preparation of print paste；
（3）Stamp：Direct printing is carried out to the terylene after pre-setting with printing paste, then it dried, the drying temperature Spend for 60-100 DEG C, the drying time is 1-3min；
（4）Evaporate：Terylene after stamp is put into cylinder steam box and evaporated；
（5）Washing：Terylene after evaporating is put into the water added with alkaline agent and surfactant and washed 3-5 times；
（6）Tentering is dried：Terylene after washing is subjected to stentering forming on forming machine, the printing technology of dacron is completed, The setting temperature is 150-170 DEG C, and the shaping time is 50-60s.
2. a kind of printing technology of dacron according to claim 1, it is characterised in that：The step（2）Middle stamp Thickener is one kind in sodium alginate, carboxymethyl cellulose and emulsion thickening.
3. a kind of printing technology of dacron according to right will go 1, it is characterised in that：The step（4）In evaporate Temperature is 80-120 DEG C, evaporates the time for 10-15min, pressure is 95-105kpa.
4. a kind of printing technology of dacron according to right will go 1, it is characterised in that：The step（5）Middle alkaline agent For one kind in sodium hydroxide, sodium acid carbonate and sodium carbonate, surfactant is stearic acid polyoxyethylene fat and stearic acid polyoxy One kind in vinethene.
CN201710330451.5A 2017-05-11 2017-05-11 A kind of printing technology of dacron Pending CN107227630A (en)