CN103103821A - Printing process of polyester fabric - Google Patents
Printing process of polyester fabric Download PDFInfo
- Publication number
- CN103103821A CN103103821A CN2012105396218A CN201210539621A CN103103821A CN 103103821 A CN103103821 A CN 103103821A CN 2012105396218 A CN2012105396218 A CN 2012105396218A CN 201210539621 A CN201210539621 A CN 201210539621A CN 103103821 A CN103103821 A CN 103103821A
- Authority
- CN
- China
- Prior art keywords
- temperature
- printing
- polyester fabric
- printing process
- shaping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a printing process of a polyester fabric. The printing process comprises the steps of printing, evaporating, reduction clearing, and shaping drying, wherein a low-temperature dyeing carrier is added in the printing step, and the quantity of the added dyeing carrier is 1%-7% of the weight of color paste; an evaporation condition of low temperature and constant pressure is adopted in the evaporation step, the temperature is 90-130 DEG C, and the time is 5-10 minutes; a reduction clearing solution comprises the ingredients of 0.5g/L-3g/L sodium hydrosulfite, a 4mL/L-7mL/L sodium hydroxide solution with the mass concentration of 35% and a 3g/L penetrating agent, the temperature in the reduction clearing step is 45-60 DEG C, and the treatment time is 15-20 minutes; and high-temperature width expansion shaping is adopted in the shaping drying step, the temperature is 110-140 DEG C, and the treatment time is 20-50 seconds. The printing process of the polyester fabric can be used for implementing continuous low-temperature evaporation and color fixation of the polyester fabric with low energy, and can effectively overcome the defect of high-temperature evaporation needed by a conventional disperse dye printing process applied to polyester fabric printing.
Description
Technical field
The present invention relates to the textile printing and dyeing field, be specifically related to a kind of printing technology of dacron.
Background technology
Along with people pursue clothes personalization, variation and functionalization, the application of multi-component fibre composite fabric is more extensive in recent years, has all become the focus of current people's research as wool, silk, the long and slender dimension of vinegar etc. and polyster fibre blending or interweave etc.Along with constantly carrying out of science and technology, oneself is not suitable with the demand for development in epoch the traditional dyeing and finishing technique of dacron.And due to the excessive exploitation of the energy, cause lack of energy, and cause the energy supply price more and more higher, traditional dacron dyeing and printing technique is subject to great challenge.
At present, print works generally adopt the high-temperature pressure steam method to carry out vapour steaming colour fixing to DISPERSE DYES, and it is 170 185 ℃ that the high-temperature pressure steam method adopts temperature, need at this temperature to consume sizable energy consumption, reduce the difficult point that required energy consumption just becomes printing technology for this reason.
Summary of the invention
The object of the present invention is to provide a kind of printing technology of dacron, realize low energy consumption dacron continuous low temperature steaming and color fixing, effect has solved existing Disperse Printing process application and has evaporated this deficiency in the required high temperature of dacron stamp.
For achieving the above object, the invention provides a kind of printing technology of dacron, comprise stamp, evaporate, reduction cleaning, shaping and drying operation;
Add the low temperature dyeing carrier in described revenue stamp process, addition is 1% 7% of mill base weight;
Evaporate and adopt the condition of evaporating of low temperature, normal pressure to evaporate in operation, temperature is 90 130 ℃, 5 10 minutes time;
Described reduction cleaning solution comprises following component: sodium dithionite 0.5 3g/L, and mass concentration is 35% sodium hydroxide solution 4 7mL/L, bleeding agent 3g/L;
Described reduction cleaning process temperature is 45 60 ℃, and the processing time is 15 20 minutes; Described shaping and drying operation Bian finalizes the design with the high temperature expanding, and temperature is 110 140 ℃, and the processing time is 20 50 seconds.
The present invention adds environment-friendly type low temperature dyeing carrier in revenue stamp process, both can promote the dacron expanded level, can strengthen the DISPERSE DYES unimolecule again, can complete on fixation at a lower temperature and dye.The high-temperature pressure method of therefore evaporating in the comparable existing technique of temperature is low, can effectively reduce the deficiency of high energy consumption in technical process.In sum; The present invention can effectively fall existing Disperse Printing process application and evaporate temperature in dacron, thereby reaches energy-saving and cost-reducing effect.
Advantage of the present invention and beneficial effect are: the printing technology that a kind of dacron is provided, realize low energy consumption dacron continuous low temperature steaming and color fixing, effect has solved existing Disperse Printing process application and has evaporated this deficiency in the required high temperature of dacron stamp.
The specific embodiment
Below in conjunction with specific embodiment, the invention will be further described.Following examples only are used for technical scheme of the present invention more clearly is described, and can not limit protection scope of the present invention with this.
Embodiment 1
A kind of printing technology of dacron comprises stamp, evaporates, reduction cleaning, shaping and drying operation;
Add the low temperature dyeing carrier in described revenue stamp process, addition is 5% of mill base weight;
Evaporate and adopt the condition of evaporating of low temperature, normal pressure to evaporate in operation, temperature is 110 ℃, 7 minutes time;
Described reduction cleaning solution comprises following component: sodium dithionite 1.5g/L, and mass concentration is 35% sodium hydroxide solution 6mL/L, bleeding agent 3g/L;
Described reduction cleaning process temperature is 50 ℃, and the processing time is 18 minutes;
Described shaping and drying operation Bian finalizes the design with the high temperature expanding, and temperature is 120 ℃, and the processing time is 40 seconds.
Embodiment 2
A kind of printing technology of dacron comprises stamp, evaporates, reduction cleaning, shaping and drying operation;
Add the low temperature dyeing carrier in described revenue stamp process, addition is 1% of mill base weight;
Evaporate and adopt the condition of evaporating of low temperature, normal pressure to evaporate in operation, temperature is 90 ℃, 5 minutes time;
Described reduction cleaning solution comprises following component: sodium dithionite 0.5g/L, and mass concentration is 35% sodium hydroxide solution 4mL/L, bleeding agent 3g/L;
Described reduction cleaning process temperature is 45 ℃, and the processing time is 15 minutes;
Described shaping and drying operation Bian finalizes the design with the high temperature expanding, and temperature is 110 ℃, and the processing time is 20 seconds.
Embodiment 3
A kind of printing technology of dacron comprises stamp, evaporates, reduction cleaning, shaping and drying operation;
Add the low temperature dyeing carrier in described revenue stamp process, addition is 7% of mill base weight;
Evaporate and adopt the condition of evaporating of low temperature, normal pressure to evaporate in operation, temperature is 130 ℃, 10 minutes time;
Described reduction cleaning solution comprises following component: sodium dithionite 3g/L, and mass concentration is 35% sodium hydroxide solution 7mL/L, bleeding agent 3g/L;
Described reduction cleaning process temperature is 60 ℃, and the processing time is 20 minutes;
Described shaping and drying operation Bian finalizes the design with the high temperature expanding, and temperature is 140 ℃, and the processing time is 50 seconds.
The above is only the preferred embodiment of the present invention; should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the printing technology of a dacron, is characterized in that, comprises stamp, evaporates, reduction cleaning, shaping and drying operation;
Add the low temperature dyeing carrier in described revenue stamp process, addition is 1% 7% of mill base weight;
Evaporate and adopt the condition of evaporating of low temperature, normal pressure to evaporate in operation, temperature is 90 130 ℃, 5 10 minutes time;
Described reduction cleaning solution comprises following component: sodium dithionite 0.5 3g/L, and mass concentration is 35% sodium hydroxide solution 4 7mL/L, bleeding agent 3g/L;
Described reduction cleaning process temperature is 45 60 ℃, and the processing time is 15 20 minutes; Described shaping and drying operation Bian finalizes the design with the high temperature expanding, and temperature is 110 140 ℃, and the processing time is 20 50 seconds.