CN107164869A - A kind of diatom ooze window curtain fabric and preparation method thereof - Google Patents
A kind of diatom ooze window curtain fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107164869A CN107164869A CN201710401027.5A CN201710401027A CN107164869A CN 107164869 A CN107164869 A CN 107164869A CN 201710401027 A CN201710401027 A CN 201710401027A CN 107164869 A CN107164869 A CN 107164869A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- fabric
- window curtain
- fiber
- curtain fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to window curtain fabric field, and in particular to a kind of diatom ooze window curtain fabric and preparation method thereof, include the component of following mass parts：40 50 parts of diatom ooze textile fabric, 40 50 parts of cotton fiber, 30 40 parts of flax fiber, 20 30 parts of chitin fiber；Preparation method is：Using diatom ooze textile fabric, flax fiber as warp, chitin fiber, cotton fiber are parallel, and fiber is manufactured into fabric；Gained fabric is carried out to go formaldehyde to arrange, two leachings two are rolled, infiltration rate is 70 80%, washing and drying sizing obtains diatom ooze window curtain fabric；The present invention provides a kind of diatom ooze window curtain fabric and preparation method thereof, and diatom ooze window curtain fabric made from this method not only has that shading performance is good, sun-resistant, wash resistant, is difficult the advantage decolourized, and also eliminates formaldehyde with excellent, purifies the effect of air.
Description
Technical field
The invention belongs to window curtain fabric field, and in particular to a kind of diatom ooze window curtain fabric and preparation method thereof.
Background technology
With the development of science and technology the transformation and the gradually reinforcement of environmental consciousness of consumers' aesthetic, curtain not only embody one
The expression in room, also reflects life taste and the temperament and interest of owner, a natural and graceful, brief graceful curtain can be residence
Make something perfect even more perfect room.In addition to decoration functions, material, function, the comfort level of curtain are also closely bound up with our healthy, life.
But in the production process of window curtain fabric, in order to reach it is wrinkle resistant, shrinkproof, fire-retardant etc. effect, or in order to keep stamp, dyeing
Durability, or in order to improve feel, formaldehyde need to be just added in auxiliary agent, with formaldehyde printing and dyeing assistant it is more be that pure cotton is weaved
Product, because pure cotton textile easily wrinkles, the stiffness of cotton can be improved using the auxiliary agent containing formaldehyde.Weaving containing formaldehyde
Product, during people's use, can gradually disengage free formaldehyde, and respiratory inflammation is triggered by human respiratory tract and skin contact
And scytitis, can also stimulation be produced to eyes.Formaldehyde can trigger allergy, can also induce cancer.Producer uses the dye containing formaldehyde
Color auxiliary agent, particularly some factories are extremely harmful to human body using the high inexpensive aids of content of formaldehyde to reduce cost.
Diatom ooze have eliminate formaldehyde, purification air, regulation humidity, releasing negative oxygen ion, fire protection flame retarding, metope it is self-cleaning,
The functions such as deodorization and sterilization；Diatom ooze health environment-friendly, it is only not ornamental very well, also with feature, but in the prior art, silicon
Algal gel is more as indoor hardware fitting, is seldom used in field of textiles at present.
The content of the invention
In order to overcome deficiency of the prior art, the present invention provides a kind of diatom ooze window curtain fabric and preparation method thereof, should
Diatom ooze window curtain fabric made from method not only has that shading performance is good, sun-resistant, wash resistant, is difficult the advantage decolourized, also has
There are excellent elimination formaldehyde, purification air.
In order to realize foregoing invention purpose, present invention employs following technical scheme：
A kind of diatom ooze window curtain fabric, includes the component of following mass parts：40-50 parts of diatom ooze textile fabric, cotton fiber
40-50 parts, 30-40 parts of flax fiber, 20-30 parts of chitin fiber.
Preferably, the preparation method of the diatom ooze textile fabric is：Nanometer diatom ooze powder, solubilizer, surface are lived
Property agent is kneaded in terylene magma, ultrasonically treated 1-2 hours, and diatom ooze textile fabric is made by spinning cotton technology.
Preferably, the nanometer diatom ooze powder, solubilizer, surfactant qualities ratio are 5：2：1.
Preferably, the nanometer diatom ooze powder diameter is 3-5nm.
A kind of preparation method of diatom ooze window curtain fabric, it is characterised in that comprise the following steps：Weaved with diatom ooze fine
Dimension, flax fiber are warp, and chitin fiber, cotton fiber are parallel, and fiber is manufactured into fabric；Gained fabric is carried out to go first
Aldehyde is arranged, and two leachings two are rolled, and infiltration rate is 70-80%, and washing and drying sizing obtains diatom ooze window curtain fabric.
Beneficial effect：Diatom ooze textile fabric is made by ultrasonic technique in diatom ooze, the diatom ooze textile fabric is made
Window curtain fabric have and excellent eliminate formaldehyde, purification air, regulation humidity, the function of releasing negative oxygen ion；Chitin fiber
It can play a part of level dyeing and assisting-dyeing for fabric, fabric can be made to adsorb direct dyes, the ability of reactive dye is improved, contracting
Short dyeing time, reduces production cost；The fabric of the present invention has also carried out going formaldehyde to arrange, and effectively eliminates in weaving process
The formaldehyde of generation, diatom ooze window curtain fabric made from this method not only has that shading performance is good, sun-resistant, wash resistant, is difficult to take off
The advantage of color, also with the excellent effect for eliminating formaldehyde, purification air.
Embodiment
The present invention is further described in detail with reference to specific embodiment, but is not limited to this.
Embodiment 1
A kind of diatom ooze window curtain fabric, includes the component of following mass parts：40 parts of diatom ooze textile fabric, cotton fiber 50
Part, 40 parts of flax fiber, 20 parts of chitin fiber.
The preparation method of the diatom ooze textile fabric is：By nanometer diatom ooze powder, solubilizer, surfactant mixing
In terylene magma, ultrasonically treated 1 hour, diatom ooze textile fabric is made by spinning cotton technology.
The nanometer diatom ooze powder, solubilizer, surfactant qualities ratio are 5：2：1.
The nanometer diatom ooze powder diameter is 3nm.
A kind of preparation method of diatom ooze window curtain fabric, it is characterised in that comprise the following steps：Weaved with diatom ooze fine
Dimension, flax fiber are warp, and chitin fiber, cotton fiber are parallel, and fiber is manufactured into fabric；Gained fabric is carried out to go first
Aldehyde is arranged, and two leachings two are rolled, and infiltration rate is 70%, and washing and drying sizing obtains diatom ooze window curtain fabric.
Embodiment 2
A kind of diatom ooze window curtain fabric, includes the component of following mass parts：50 parts of diatom ooze textile fabric, cotton fiber 40
Part, 30 parts of flax fiber, 30 parts of chitin fiber.
The preparation method of the diatom ooze textile fabric is：By nanometer diatom ooze powder, solubilizer, surfactant mixing
In terylene magma, ultrasonically treated 2 hours, diatom ooze textile fabric is made by spinning cotton technology.
The nanometer diatom ooze powder, solubilizer, surfactant qualities ratio are 5：2：1.
The nanometer diatom ooze powder diameter is 5nm.
A kind of preparation method of diatom ooze window curtain fabric, it is characterised in that comprise the following steps：Weaved with diatom ooze fine
Dimension, flax fiber are warp, and chitin fiber, cotton fiber are parallel, and fiber is manufactured into fabric；Gained fabric is carried out to go first
Aldehyde is arranged, and two leachings two are rolled, and infiltration rate is 80%, and washing and drying sizing obtains diatom ooze window curtain fabric.
Embodiment 3
A kind of diatom ooze window curtain fabric, includes the component of following mass parts：45 parts of diatom ooze textile fabric, cotton fiber 45
Part, 35 parts of flax fiber, 25 parts of chitin fiber.
The preparation method of the diatom ooze textile fabric is：By nanometer diatom ooze powder, solubilizer, surfactant mixing
In terylene magma, ultrasonically treated 1.5 hours, diatom ooze textile fabric is made by spinning cotton technology.
The nanometer diatom ooze powder, solubilizer, surfactant qualities ratio are 5：2：1.
The nanometer diatom ooze powder diameter is 4nm.
A kind of preparation method of diatom ooze window curtain fabric, it is characterised in that comprise the following steps：Weaved with diatom ooze fine
Dimension, flax fiber are warp, and chitin fiber, cotton fiber are parallel, and fiber is manufactured into fabric；Gained fabric is carried out to go first
Aldehyde is arranged, and two leachings two are rolled, and infiltration rate is 76%, and washing and drying sizing obtains diatom ooze window curtain fabric.
Diatom ooze window curtain fabric obtained by embodiment 1-3 is placed in closed new renovated room, the initial first in room
Aldehyde is 3mg/L, and PM2.5 is 90mg/m3, diatom ooze window curtain fabric place one month, measurement indoor formaldehyde content and
PM2.5, acquired results are as shown in the table：
| Embodiment 1 | Embodiment 2 | Embodiment 3 | |
| Indoor formaldehyde content (mg/L) | 0.4 | 0.4 | 0.3 |
| PM2.5(mg/m3) | 30 | 31 | 28 |
As a result show：The diatom ooze window curtain fabric of the present invention has excellent elimination formaldehyde, purifies the effect of air.
Claims (5)
1. a kind of diatom ooze window curtain fabric, it is characterised in that include the component of following mass parts：Diatom ooze textile fabric 40-50
Part, 40-50 parts of cotton fiber, 30-40 parts of flax fiber, 20-30 parts of chitin fiber.
2. a kind of diatom ooze window curtain fabric according to claim 1, it is characterised in that the system of the diatom ooze textile fabric
Preparation Method is：Nanometer diatom ooze powder, solubilizer, surfactant are kneaded in terylene magma, it is ultrasonically treated 1-2 hours,
Diatom ooze textile fabric is made by spinning cotton technology.
3. a kind of diatom ooze window curtain fabric according to claim 2, it is characterised in that the nanometer diatom ooze powder, increasing
Solvent, surfactant qualities ratio are 5：2：1.
4. a kind of diatom ooze window curtain fabric according to Claims 2 or 3, it is characterised in that the nanometer diatom ooze powder
Particle diameter is 3-5nm.
5. the preparation method of a kind of diatom ooze window curtain fabric described in claim 1, it is characterised in that comprise the following steps：With
Diatom ooze textile fabric, flax fiber are warp, and chitin fiber, cotton fiber are parallel, and fiber is manufactured into fabric；By gained
Fabric is carried out going formaldehyde to arrange, and two leachings two are rolled, and infiltration rate is 70-80%, and washing and drying sizing obtains diatom ooze window curtain fabric.