CN103771331A - Antibacterial healthy cushion - Google Patents
Antibacterial healthy cushion Download PDFInfo
- Publication number
- CN103771331A CN103771331A CN201210400208.3A CN201210400208A CN103771331A CN 103771331 A CN103771331 A CN 103771331A CN 201210400208 A CN201210400208 A CN 201210400208A CN 103771331 A CN103771331 A CN 103771331A
- Authority
- CN
- China
- Prior art keywords
- cushion
- massage
- antibacterial
- granule
- bacterial fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an antibacterial healthy cushion. The cushion is made through blend spinning solution preparation, antibacterial fiber forming, antibacterial woven cloth forming, cushion cutting, massage particle firing and cushion inner core production. The cushion has the advantages of being capable of emitting far infrared rays permanently, improving body microcirculation, relieving body fatigue through acupoint massage, releasing anions, absorbing humidity, resisting bacteria and performing deodorization, good in breathability, anti-abrasion, washable and light and comfortable. The cushion meets human living comfort requirements and is provided with multiple health-care physiotherapeutic functions and can be regarded as one of essential life products of modern living and public service facilities.
Description
technical fieldthe present invention relates to a kind of antibacterial health cushion, by various material such as bamboo-carbon viscose fibre, cotton fiber, aramid fiber, zeolite powder, citric acid, chitin, carbowax, tourmaline powder, wooden fish stone flour, viscosity potter's clay, slow-recovery sponges, through the preparation of blend spinning liquid, anti-bacterial fibre moulding, the antibacterial moulding of weaving cotton cloth, cushion cutting, granule for massage fire, prepared by cushion inner core etc., and processes forms.The present invention makes anti-bacterial fibre fabric and therapeutic massage particle by special process, make cushion there is antibacterial and health-care physical therapy double effects, have permanently releasing far infrared, improve microcirculation in human body, point massage is alleviated human body fatigue, anion releasing, moisture absorption antibacterial and deodouring, good air permeability, rub resistance, can wash, light comfortable feature, both the comfort need that had met people's lives also has the effect of multiple health-care physical therapy, one of indispensable life product of the modern house of therefore can yet be regarded as, public service facility simultaneously.
background technologycushion is the daily necessities that daily life is extensively used, and can make seat for a long time in clean state, general and back cushion is supporting, is indispensable textile article in seat, sofa, compartment, uses comfortable and has an irreplaceable decoration function of other article.Cushion is owing to always directly contacting with coat, served as the protective case of seat, sofa, therefore becomes easily infected by dust and greasy dirt.These dirts are good nutrition sources of various germs, especially under the condition of high temperature humidity, become the good environment of various microbial reproductions, therefore in the breeding and transmittance process of pathogenic bacteria, textiles is an important medium always, and antibacterial fabric not only can avoid textiles because of the erosion of germ impaired, and can block textiles and transmit the approach of pathogenic bacteria, stop breeding and the bacterium of pathogenic bacteria on textiles to decompose the dirt on fabric and produce stink (mostly being organic acid and amine), therefore antibacterial fabric has great significance for the health of human body.Cushion divides according to function and can be divided into antibacterial seat cushion and health-care cushion.General antibacterial seat cushion is on the basis of moulding textiles, to carry out anti-bacterial finish operation, make textiles there is antibacterial action by soaking, spray antiseptic, the Durability of antimicrobial effect of this kind of antibacterial seat cushion is poor, and washing or friction easily weaken antibacterial action, do not have long-term bacteriostasis.What form therewith sharp contrast is the antibacterial fabric that anti-bacterial fibre is made.Opposing and the killing action of anti-bacterial fibre to bacterium is not disposable temporary transient effect, but the long-term efficacy of several thoughtful several years.Why there is this long-term antibiotic property, because it adopts built-in design, make slowly stripping of antiseptic, form inhibition zone at fiber surface, even if antibacterial surface agent is washed off, also have new antiseptic and overflow and form new inhibition zone, so have good washability with the fabric of this fiber making.Health-care cushion normally utilizes natural material itself to have far-infrared transmitting function, makes human body receive far-infrared rays, plays and improves microcirculatory health-care effect, only utilizes its health-care effect of far infrared therapy may be also also not obvious.For this reason we think can invent a kind of have simultaneously antibacterial, health care double action cushion, utilize anti-bacterial fibre to make antibacterial weaving cotton cloth, utilize natural crystal to make health care massage particle, carry out arrangement design according to human acupoint, utilize slow-recovery sponge to make cushion inner core, then make antibacterial health cushion by special sewing process, make it have anion releasing, antibacterial deodourizing, releasing far infrared, improve microcirculation, wear-resisting, press memory effect, alleviate the tired multiple efficacies of human body.
summary of the inventionthe invention provides a kind of antibacterial health cushion, main points are to be made up of anti-bacterial fibre fabric and granule for massage, wherein anti-bacterial fibre fabric is prepared from by blend spinning solution, through anti-bacterial fibre moulding, the antibacterial moulding of weaving cotton cloth, cushion cutting, granule for massage fire, the technique final molding such as prepared by cushion inner core.The formula following (component and percentage by weight %) of blend spinning solution: bamboo-carbon viscose fibre 20-35, cotton fiber 20-40, aramid fiber 10-20, zeolite powder 3-7, citric acid 2-5, chitin 1-4, carbowax 3-8, deionized water add to 100; The formula following (component and percentage by weight %) of granule for massage: tourmaline powder 12-28, wooden fish stone flour 8-14, viscosity potter's clay 36-50, deionized water add to 100.
Bamboo-carbon viscose fibre is that to get mao bamboon be raw material, adopt pure oxygen pyrometer nitrogen to intercept the calcine technology of time delay, more refinement and the honeycomb of micropore that bamboo charcoal is innately had, and then make with thering is the polyester modification section melt spinning of honeycomb microporous structure trend.Bamboo-carbon viscose fibre includes bamboo charcoal micropowder, because bamboo charcoal has the feature such as super large specific surface area, superelevation absorption, thus fiber fully demonstrate absorption peculiar smell that bamboo charcoal has, distribute simple and elegant delicate fragrance, antibacterial and bacteriostatic, block electromagenetic wave radiation, emitting far-infrared, regulate the effects such as humiture, beauty and skin care.
Cotton fiber is the fiber of coating on the seed of Malvaceae cotton, is the important source material of textile industry, and the moisture absorption of cotton fiber goods and good permeability are soft and warming.The Main Ingredients and Appearance of cotton fiber is cellulose, and cellulose is natural polymer, and cellulosic chemical structural formula is that basic structural unit repeats to form by α glucose, and its element set becomes carbon 44.44%, hydrogen 6.17%, oxygen 49.39%.The polymeric level of cotton fiber is at 6000～11000.In addition, cotton fiber also, with other materials of 5% left and right, is called accompaniment, and accompaniment is on spinning process and float white silk, dyeing and printing process all has impact.Adipocere matter is contained on the surface of cotton fiber, is commonly called as cotton wax, and cotton wax has protective effect to cotton fiber, is that cotton fiber has one of reason of good spinning performance, but in the time of high temperature, the easy melting of cotton wax, so cotton easily around roller, around rubber roll.Through ungrease treatment, raw cotton hygroscopic property increases, and water injectivity can reach 23～24 times of own weight.
Aramid fiber, be a kind of novel high-tech syntheticfibres, have superhigh intensity, high-modulus and high temperature resistant, acid-fast alkali-proof, the premium properties such as lightweight, its intensity is 5～6 times of steel wire, modulus is steel wire or glass fibre 2～3 times, toughness is 2 times of steel wire, and weight is only 1/5 left and right of steel wire, at the temperature of 560 ℃, do not decompose, do not melt, there is good insulativity and ageing resistance, there is very long life cycle.Aramid fiber is a kind of flexible macromolecule, disruption characteristic is higher than ordinary polyester, cotton, nylon etc., percentage elongation is larger, soft, good spinnability, can be produced into chopped fiber and the long filament of different fiber numbers, length, makes yarn with different be made into fabric, nonwoven fabrics at general textile machine, through arranging later, meet the requirement of the protective clothes of different field.Aramid fiber has good rub resistance and chemical resistance, after 100 washings, still can reach the more than 85% of former brute force with the cloth tearing brute force of aramid fiber processing.
Zeolite is the aluminium silicate mineral of a kind of shape structure of slag formation, and zeolite powder is that natural zeolite grinding forms, and color is white.There is unique adsorbability, catalytic, ion exchangeable, selectivity, resistance to acids, heat stability, biologically active and the antibiotic property of ion.Its anti-microbial property is superior, and the main antiseptic of Chang Zuowei syntheticfibres blending and modifying plays a role.
Chitin, is i.e. poly-(the Isosorbide-5-Nitrae)-2-acetamido-2-deoxidation-β-D-Glucose of policapram base glucose, and its chemical constitution and cellulose family are seemingly.Chitin is almost to exist with strip or powdery, due in molecule, intermolecular extremely strong hydrogen bond action, chitin is crystalline structure closely, is only dissolved in minority organic solvent.Chitin with positive electricity with bacterium with negative charge, by Van der Waals force mutually absorption, cause membranolysis, slurries are excessive and dead.Can also induce bacterium to produce chitinase by chitin fiber, can impel cell membrane to decompose and the evil life of anti-bacteria, accelerate phosphoric acid redox system, upset the normal growth metabolism of cell.
Citric acid is mainly used in dissolving chitin, and it is fully dissolved in spinning solution, also has in addition cross-linking properties, makes various fibre compositions closely crosslinked.Carbowax is organic solvent, and hydrophile-lipophile balance performance is fabulous, has splendid coupling.It has good water-soluble, and has good intermiscibility with many organic constituentses, and in textile industry, Chang Zuowei hand modifier and antistatic additive use.
Tourmaline has forever electrically and far infrared effect, in the time being heated, can bring electric charge, has pyroelectric effect, can be releasing far infrared, negative ion and several kinds of mineral elements.Japan scientific research personnel confirmation, when tourmaline is pulverized, energy increases on year-on-year basis.Thinner all to pieces, energy is larger.Tourmaline powder forever electrically can produce a large amount of negative oxygen ions, there is the effect of the human body of adjusting ionic equilibrium, can make body and mind loosen, activating cell, improves the effects such as nature cure rate; Detect through national authority mechanism, the nano particle of tourmaline powder can efficiently be launched the far-infrared rays of needed by human body, and in its band emission rate of 8-15 micron, up to 88%, it is the light of the life of human body that scientist names this wave band.Far-infrared rays can be penetrated into health deep layer position, and warm cell, stimulates circulation, and makes metabolism smooth and easy.Tourmaline far-infrared rays emissivity nearly 98%, numerical value is high compared with other mineral.
Mineral composition in limonite is ironstone, Fe
2o
3content from 20% to 78% not etc., other impurity is often phosphate, also has a small amount of melasilicate, and strontium, molybdenum, lithium, zinc, selenium and other trace elements; Viscosity potter's clay mineral composition complexity, is mainly made up of ancudite, hydromuscovite, montmorillonite, quartz and feldspar.Grain size is inconsistent, often containing sand grains, flour sand and clay etc.Viscosity potter's clay tool hygroscopic character and adsorbability, have plasticity after adding water, and is raw MAT'L important in granule for massage manufacture craft.
Slow-recovery sponge is called again inertia sponge, memory foam.That NASA is a kind of hitech materials that space program is designed and developed at first, help to alleviate the pressure that cosmonaut bears in landing and flight course, due to its unique stress reduction feature, can allow health naturally be had a rest without pressure position at one.This kind of material has unique temperature-sensitive characteristic, meeting deliquescing while being heated, meeting hardening while catching a cold, when touching body temperature, the particle on surface is softening, and the particle softening along with body wt is evenly distributed compression area, can mould buman body type, eliminate spot pressure, impel the blood in body can be oppressed in no instance.After human body leaves, it is reinstatement again.In addition, slow-recovery sponge also has impayable endurance ability, highdensity material guarantees that it has powerful endurance ability and powerful bearing capacity, this attribute of releasing the pressure has been avoided bounce pressure or the self-built pain causing of gravity and discomfort, highdensity material also has actv. and resists sweat and stink infiltration, guarantee to meet personal hygiene, be harmful to human health.
Preparation technology of the present invention is:
(1) described component zeolite powder, chitin, citric acid, carbowax are dissolved in deionized water, add cotton fiber, bamboo-carbon viscose fibre, aramid fiber after stirring, continuous stirring 30min obtains blend spinning solution;
(2), by the above-mentioned blend spinning solution making after filtration after deaeration, stoste is sprayed in coagulating bath from the aperture of extrusion nozzle with pressure;
(3) sodium hydroxide of coagulating bath employing 10% and the mixed liquor of ethanol, the fiber solidifying washs with warm water, stretches 1125 times and reels afterwards, and under tension state, at 70 ℃, dry 1h, obtains mixing anti-bacterial fibre;
(4) by above-mentioned mixing anti-bacterial fibre through comb and parallel cotton fibers prior to spinning, silver lap, drafting, rove, spun yarn, winder, twist thread, reeling, warping, sizing, pass, weave, the operation such as arrangement makes anti-bacterial fibre cloth;
(5) above-mentioned anti-bacterial fibre cloth is carried out to cutting, be processed into the cushion cover of various model specifications;
(6) granule for massage is made: described component zeolite powder, tourmaline powder, wooden fish stone flour, viscosity potter's clay, according to formula rate, are uniformly mixed, add deionized water furnishing pasty state, after basic mediation evenly, be processed into oblate particle through molding; Put in the cool and be dried, after being dried, fetalism is repaired level and smooth with instrument again; Then put into high temperature furnace (800-1200 ℃) and carry out double roasting, cooling after;
(7) inner core is made: slow-recovery sponge upper epidermis is distributed and places granule for massage according to human acupoint, apply and make fixing with terylene cloth;
(8) the above-mentioned inner core making is packed into the cushion cover of moulding, detect qualified after, packing warehouse-in.
The invention has the beneficial effects as follows: (1) is permanently releasing far infrared, form hot penetration, make Marjoram Extract, improve microcirculation in human body; (2) anti-microbial property is good, strong to the pathogenic microorganism such as bacterium, fungi bacteriostasis; (3) built-in granule for massage is arranged according to human acupoint, plays the health care massage effect of relaxing through invigorating blood circulation when use, alleviates human body fatigue and myalgia; (4) good air permeability, can wash; (5) adsorption power is powerful, decomposes and eliminates peculiar smell; (6) rub resistance, antiskid capability are superior; (7) preparation is simple, easy to use; (8) soft, light comfortable; (9) press memory effect, eliminate spot pressure, human body is thoroughly loosened.
the specific embodimentbelow in conjunction with embodiment, the present invention is described in further detail:
1, be configured according to following table institute column data (percentage by weight %) and described step thereof:
Formula one:
The formula following (component and percentage by weight %) of blend spinning solution: bamboo-carbon viscose fibre 24-35, cotton fiber 25-40, aramid fiber 12-20, zeolite powder 4-7, citric acid 3-5, chitin 2-4, carbowax 5-8, deionized water add to 100; The formula following (component and percentage by weight %) of granule for massage: tourmaline powder 15-28, wooden fish stone flour 9-14, viscosity potter's clay 38-50, deionized water add to 100.
Formula two:
The formula following (component and percentage by weight %) of blend spinning solution: bamboo-carbon viscose fibre 20-35, cotton fiber 20-40, aramid fiber 10-20, zeolite powder 3-7, citric acid 2-5, chitin 1-4, carbowax 3-8, deionized water add to 100; The formula following (component and percentage by weight %) of granule for massage: tourmaline powder 12-28, wooden fish stone flour 8-14, viscosity potter's clay 36-50, deionized water add to 100.
Formula three:
The formula following (component and percentage by weight %) of blend spinning solution: bamboo-carbon viscose fibre 20-35, cotton fiber 20-40, aramid fiber 10-18, zeolite powder 3-6, citric acid 2-4, chitin 1-3, carbowax 3-6, deionized water add to 100; The formula following (component and percentage by weight %) of granule for massage: tourmaline powder 12-25, wooden fish stone flour 8-12, viscosity potter's clay 36-48, deionized water add to 100.
Claims (2)
1. the present invention relates to a kind of antibacterial health cushion, it is characterized in that jointly being formed by anti-bacterial fibre fabric and granule for massage, wherein anti-bacterial fibre fabric is prepared from by blend spinning solution, the formula following (component and percentage by weight %) of blend spinning solution: bamboo-carbon viscose fibre 20-35, cotton fiber 20-40, aramid fiber 10-20, zeolite powder 3-7, citric acid 2-5, chitin 1-4, carbowax 3-8, deionized water add to 100; The formula following (component and percentage by weight %) of granule for massage: tourmaline powder 12-28, wooden fish stone flour 8-14, viscosity potter's clay 36-50, deionized water add to 100.
2. antibacterial health cushion according to claim 1, is characterized in that having the technique of being prepared as follows:
(1) described component zeolite powder, chitin, citric acid, carbowax are dissolved in deionized water, add cotton fiber, bamboo-carbon viscose fibre, aramid fiber after stirring, continuous stirring 30min obtains blend spinning solution;
(2), by the above-mentioned blend spinning solution making after filtration after deaeration, stoste is sprayed in coagulating bath from the aperture of extrusion nozzle with pressure;
(3) sodium hydroxide of coagulating bath employing 10% and the mixed liquor of ethanol, the fiber solidifying washs with warm water, stretches 1125 times and reels afterwards, and under tension state, at 70 ℃, dry 1h, obtains mixing anti-bacterial fibre;
(4) by above-mentioned mixing anti-bacterial fibre through comb and parallel cotton fibers prior to spinning, silver lap, drafting, rove, spun yarn, winder, twist thread, reeling, warping, sizing, pass, weave, the operation such as arrangement makes anti-bacterial fibre cloth;
(5) above-mentioned anti-bacterial fibre cloth is carried out to cutting, be processed into the cushion cover of various model specifications;
(6) granule for massage is made: described component zeolite powder, tourmaline powder, wooden fish stone flour, viscosity potter's clay, according to formula rate, are uniformly mixed, add deionized water furnishing pasty state, after basic mediation evenly, be processed into oblate particle through molding; Put in the cool and be dried, after being dried, fetalism is repaired level and smooth with instrument again; Then put into high temperature furnace (800-1200 ℃) and carry out double roasting, cooling after;
(7) inner core is made: slow-recovery sponge upper epidermis is distributed and places granule for massage according to human acupoint, apply and make fixing with terylene cloth;
(8) the above-mentioned inner core making is packed into the cushion cover of moulding, detect qualified after, packing warehouse-in.