CN106012220A - Washable fabric for shirts - Google Patents
Washable fabric for shirts Download PDFInfo
- Publication number
- CN106012220A CN106012220A CN201610480369.6A CN201610480369A CN106012220A CN 106012220 A CN106012220 A CN 106012220A CN 201610480369 A CN201610480369 A CN 201610480369A CN 106012220 A CN106012220 A CN 106012220A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- fibers
- warp thread
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Washable fabric for shirts is formed by interweaving warp and weft, wherein the warp is prepared from raw materials in parts by weight as follows: 2-4 parts of oxidized graphene, 25-32 parts of cotton fibers, 11-15 parts of wormwood, 5-8 parts of Chinese arborvitae twigs, 5-8 parts of eclipta fibers, 1-2 parts of sodium dodecyl sulfate, 6-10 parts of Chinese pyrola herb fibers, 6-10 parts of hypericum japonicum fibers and 1-2 parts of nano aluminum hydroxide; the weft is prepared from raw materials in parts by weight as follows: 30-38 parts of cotton fibers, 4-8 parts of magnetic therapy fibers, 0.5-2 parts of ethyoxyl laurylamine, 8-13 parts of uncaria fibers, 1-2 parts of 2.3-dibromopropyl, 8-13 parts of bamboo fibers, 5-7 parts of Chinese bastardtoadflax herb fibers, 5-7 parts of cashmere fibers and 5-7 parts of Yunlong mulberry leaf fibers. The fabric is not prone to wrinkle, has good anti-bending performance, sweat volatility, flame retardancy and anti-ultraviolet performance, is soaking resistant and machine-washable, has only few wrinkles after being washed and has good dye attachment.
Description
Technical field
The present invention relates to technical field of textile fabric, be specifically related to a kind of water-fastness shirt fabric.
Background technology
Along with the raising of people's living standard, dress is pursued more and more fastidious by people.Current shirt face
Material be mostly cotton fabric, cotton fabric absorption of perspiration is good, next to the skin wear comfortable, but shirt meat is easy
Fold, needs often flatiron, bothers very much, and easy balling-up of long duration, current shirt is general the most all
Being not suitable for the long-time soaking and water washing of washing machine, laundry machine washing backsight shirt is easily covered with fold.
Summary of the invention
The technical problem to be solved is to provide a kind of water-fastness shirt fabric.
The technical problem to be solved realizes by the following technical solutions:
A kind of water-fastness shirt fabric, is formed by weaving by warp thread and weft yarns, described warp thread include with
The raw material of lower weight portion: graphene oxide 2-4 part, cotton fiber 25-32 part, Wormwood fiber 11-15 part, side
Cacumen Platycladi (Cacumen Biotae) fiber 5-8 part, Herba Ecliptae fiber 5-8 part, dodecyl sodium sulfate 1-2 part, Herba Pyrolae fiber 6-10
Part, Herba Hyperici Japonici fiber 6-10 part, nano-aluminum hydroxide 1-2 part;Described weft yarn includes the former of following weight portion
Material: cotton fiber 30-38 part, magnetic therapy fiber 4-8 part, ethyoxyl Laurel cruel amine 0.5-2 part, Ramulus Uncariae Cum Uncis fiber 8-13
Part, 2,3-dibromopropyl 1-2 part, bamboo fibre 8-13 part, BAIXINCAO fiber 5-7 part, open a meter youngster fiber 5-7
Part, Yunlong Folium Mori fiber 5-7 part.
The preparation method of a kind of water-fastness shirt fabric, comprises the following steps:
(1) each raw material of warp thread is mixed spinning, by each raw material blend spinning of weft yarn;
(2) by warp thread and weft yarn nano titanium oxide solution soaking 25 minutes, it is then placed in-5 DEG C of freezers
Freezing 10 minutes, with hot air drying after taking-up, hot blast temperature was 51 DEG C, and hot blast flow velocity is 2-3m/s;
(3) dried warp thread and weft yarn are sent into Weaving-machine weaving and obtain fabric.
The invention has the beneficial effects as follows: fabric of the present invention is suitable for making shirt and uses, and fabric is difficult to fold,
Buckle resistance is good, and fabric is perspiration wicking good, and fabric also has good fire resistance and anti-ultraviolet property,
The resistance to blister of fabric and washing machine machine washing, only have a small amount of fold after washing, fabric is good to the tack of dyestuff, dye
Not fading after color, fabric of the present invention is worn for a long time certain physiotherapy function to health.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of water-fastness shirt fabric, is formed by weaving by warp thread and weft yarns, described warp thread include with
The raw material of lower weight portion (kilogram): graphene oxide 3 parts, 29 parts of cotton fiber, Wormwood fiber 13 parts, side
Cacumen Platycladi (Cacumen Biotae) fiber 6 parts, Herba Ecliptae fiber 6 parts, dodecyl sodium sulfate 1 part, Herba Pyrolae fiber 8 parts, ear
Grass fiber 8 parts, nano-aluminum hydroxide 1 part;Described weft yarn includes the raw material of following weight portion (kilogram):
34 parts of cotton fiber, magnetic therapy fiber 6 parts, the cruel amine of ethyoxyl Laurel 1 part, Ramulus Uncariae Cum Uncis fiber 11 parts, 2,3-dibromo
Propyl group 1 part, bamboo fibre 11 parts, BAIXINCAO fiber 6 parts, open meter youngster's fiber 6 parts, Yunlong Folium Mori fiber 6 parts.
The preparation method of a kind of water-fastness shirt fabric, comprises the following steps:
(1) each raw material of warp thread is mixed spinning, by each raw material blend spinning of weft yarn;
(2) by warp thread and weft yarn nano titanium oxide solution soaking 25 minutes, it is then placed in-5 DEG C of freezers
Freezing 10 minutes, with hot air drying after taking-up, hot blast temperature was 51 DEG C, and hot blast flow velocity is 2-3m/s;
(3) dried warp thread and weft yarn are sent into Weaving-machine weaving and obtain fabric.
Embodiment 2
A kind of water-fastness shirt fabric, is formed by weaving by warp thread and weft yarns, described warp thread include with
The raw material of lower weight portion (kilogram): graphene oxide 2 parts, 25 parts of cotton fiber, Wormwood fiber 11 parts, side
Cacumen Platycladi (Cacumen Biotae) fiber 5 parts, Herba Ecliptae fiber 5 parts, dodecyl sodium sulfate 1 part, Herba Pyrolae fiber 6 parts, ear
Grass fiber 6 parts, nano-aluminum hydroxide 1 part;Described weft yarn includes the raw material of following weight portion (kilogram):
30 parts of cotton fiber, magnetic therapy fiber 4 parts, the cruel amine of ethyoxyl Laurel 0.5 part, Ramulus Uncariae Cum Uncis fiber 8 parts, 2,3-bis-
Bromopropyl 1 part, bamboo fibre 8 parts, BAIXINCAO fiber 5 parts, open meter youngster's fiber 5 parts, Yunlong Folium Mori fiber 5 parts.
The preparation method of a kind of water-fastness shirt fabric, comprises the following steps:
(1) each raw material of warp thread is mixed spinning, by each raw material blend spinning of weft yarn;
(2) by warp thread and weft yarn nano titanium oxide solution soaking 25 minutes, it is then placed in-5 DEG C of freezers
Freezing 10 minutes, with hot air drying after taking-up, hot blast temperature was 51 DEG C, and hot blast flow velocity is 2-3m/s;
(3) dried warp thread and weft yarn are sent into Weaving-machine weaving and obtain fabric.
Embodiment 3
A kind of water-fastness shirt fabric, is formed by weaving by warp thread and weft yarns, described warp thread include with
The raw material of lower weight portion (kilogram): graphene oxide 4 parts, 32 parts of cotton fiber, Wormwood fiber 15 parts, side
Cacumen Platycladi (Cacumen Biotae) fiber 8 parts, Herba Ecliptae fiber 8 parts, dodecyl sodium sulfate 2 parts, Herba Pyrolae fiber 10 parts, ear
Grass fiber 10 parts, nano-aluminum hydroxide 2 parts;Described weft yarn includes the raw material of following weight portion (kilogram):
38 parts of cotton fiber, magnetic therapy fiber 8 parts, the cruel amine of ethyoxyl Laurel 2 parts, Ramulus Uncariae Cum Uncis fiber 13 parts, 2,3-dibromo
Propyl group 2 parts, bamboo fibre 13 parts, BAIXINCAO fiber 7 parts, open meter youngster's fiber 7 parts, Yunlong Folium Mori fiber 7 parts.
The preparation method of a kind of water-fastness shirt fabric, comprises the following steps:
(1) each raw material of warp thread is mixed spinning, by each raw material blend spinning of weft yarn;
(2) by warp thread and weft yarn nano titanium oxide solution soaking 25 minutes, it is then placed in-5 DEG C of freezers
Freezing 10 minutes, with hot air drying after taking-up, hot blast temperature was 51 DEG C, and hot blast flow velocity is 2-3m/s;
(3) dried warp thread and weft yarn are sent into Weaving-machine weaving and obtain fabric.
Test
The fabric of the embodiment of the present invention 1,2,3 and common fabric are as follows through the data of detection:
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Common fabric |
Content of formaldehyde (mg/kg) | 21 | 31 | 27 | 49 |
Tensile strength (N/cm) | 413 | 376 | 355 | 331 |
Tearing brute force (N) | 208 | 183 | 171 | 160 |
Pilling resistance | Not balling-up | Not balling-up | Not balling-up | Balling-up |
Washing machine is machine-washed 1 hour | A small amount of fold | A small amount of fold | A small amount of fold | Fold is many |
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. a water-fastness shirt fabric, is formed by weaving by warp thread and weft yarns, it is characterised in that
Described warp thread includes the raw material of following weight portion: graphene oxide 2-4 part, cotton fiber 25-32 part, Folium Artemisiae Argyi
Fiber 11-15 part, Cacumen Platycladi fiber 5-8 part, Herba Ecliptae fiber 5-8 part, dodecyl sodium sulfate 1-2 part,
Herba Pyrolae fiber 6-10 part, Herba Hyperici Japonici fiber 6-10 part, nano-aluminum hydroxide 1-2 part;Described weft yarn includes
The raw material of following weight portion: cotton fiber 30-38 part, magnetic therapy fiber 4-8 part, ethyoxyl Laurel cruel amine 0.5-2
Part, Ramulus Uncariae Cum Uncis fiber 8-13 part, 2,3-dibromopropyl 1-2 part, bamboo fibre 8-13 part, BAIXINCAO fiber 5-7
Part, open meter youngster's fiber 5-7 part, Yunlong Folium Mori fiber 5-7 part.
2. the preparation method of a water-fastness shirt fabric, it is characterised in that comprise the following steps:
(1) each raw material of warp thread is mixed spinning, by each raw material blend spinning of weft yarn;
(2) by warp thread and weft yarn nano titanium oxide solution soaking 25 minutes, it is then placed in-5 DEG C of freezers
Freezing 10 minutes, with hot air drying after taking-up, hot blast temperature was 51 DEG C, and hot blast flow velocity is 2-3m/s;
(3) dried warp thread and weft yarn are sent into Weaving-machine weaving and obtain fabric.