CN104452046A - Production process of antibacterial knitted fabric - Google Patents
Production process of antibacterial knitted fabric Download PDFInfo
- Publication number
- CN104452046A CN104452046A CN201410743736.8A CN201410743736A CN104452046A CN 104452046 A CN104452046 A CN 104452046A CN 201410743736 A CN201410743736 A CN 201410743736A CN 104452046 A CN104452046 A CN 104452046A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- fiber
- composite fibers
- face fabric
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of antibacterial knitted fabric. The antibacterial knitted fabric is made by taking bamboo charcoal fibers as warp and weft and antibacterial composite fibers as wool yarn for weaving, dyeing, printing and after finishing. The antibacterial composite fibers are made by the following steps: 1), preparing raw materials; 2), preparing cellulose viscose spinning liquid; 3), preparing antibacterial viscose; 4), preparing antibacterial viscose fibers; 5), preparing the antibacterial composite fibers, namely blending the antibacterial viscose fibers obtained in the step 4) with soybean protein fibers and cotton fibers to obtain. By the above mode, the production process is simple in condition and unharsh in process factor, and the antibacterial knitted fabric made by the process has a long-lasting antibacterial function.
Description
Technical field
The present invention relates to fabric production technical field, particularly relate to a kind of production technology of knit fabric.
Background technology
Along with the raising of people's living standard, the requirement of people to clothes is more and more higher, the pursuit of consumer from is warming comfortable to emphasis, attractive in appearance, future development such as grade good for health, function textile also arises at the historic moment, as far back as the World War I time, people have just started the research to antibacterial fabric, to the modern times, the atypical pneumonia that at the beginning of the enteron aisle acute disease and 2003 that Japan in 1996 is caused by 0-157 pathogenic Escherichia coli in the whole country, China causes due to SARS virus, having to, they all cause huge injury to the healthy of the mankind, and people therefrom have also been obtained inspiration: because of concerning natural microorganism, the skin of the mankind is a kind of well nutrition supply persons, some resident bacterium on people's skin play a part protection skin and endanger from pathogenic bacteria, once the flora imbalance in microorganism, a small amount of pathogenic bacteria in them will amount reproduction, and pass through skin, respiratory tract, alimentary canal and genital tract mucosa work the mischief to human body.Antibacterial fabric, as a possible prevention and the product cutting off disease propagation source, will play vital effect in people's disease prevention and cure.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of production technology of antibiosis knitting face fabric, and these process conditions are simple, technical factor is not harsh, and the antibiosis knitting face fabric made has long-acting antibacterial functions.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is:
A kind of production technology of antibiosis knitting face fabric is provided, bamboo-carbon fibre carried out weaving as wool yarn as warp and parallel, antibacterial composite fibers, dyes, obtain antibiosis knitting face fabric after stamp and Final finishing; Wherein, antibacterial composite fibers is prepared from by following step:
1) preparation of raw material, weighs soybean fiber, cotton fiber, cellulose pulp, Nano Silver, titania powder and hydroxyapatite, for subsequent use;
2) preparation of cellulose rayon spinning liquid take cellulose pulp as raw material, through dipping, squeezing, pulverize, experienced, yellow and dissolving step obtain cellulose rayon spinning liquid;
3) preparation of antibacterial viscose glue, adds in alkaline solution by nano-silver ionic, titania powder and hydroxyapatite, stirs 30min, adds stabilizing agent, leaves standstill after again stirring 30min;
4) preparation of antibacterial viscose fiber, antibacterial viscose glue step 3) prepared carries out spinning, obtains antibacterial viscose fiber after coagulation forming;
5) preparation of antibacterial composite fibers, antibacterial viscose fiber step 4) obtained and soybean fiber, cotton fiber carry out blended, obtain antibacterial composite fibers.
In a preferred embodiment of the present invention, the particle diameter of described Nano Silver is less than 50nm.
In a preferred embodiment of the present invention, described Nano Silver accounts for 0.008 ~ 0.015 ‰ of antibacterial composite fibers gross mass.
In a preferred embodiment of the present invention, described titania powder accounts for 0.022 ~ 0.05 ‰ of antibacterial composite fibers gross mass.
In a preferred embodiment of the present invention, the ratio of quality and the number of copies of legumin fiber, cotton fiber, cellulose pulp is 10 ~ 20:25 ~ 40:70 ~ 80.
The invention has the beneficial effects as follows: the production technology of a kind of antibiosis knitting face fabric of the present invention, these process conditions are simple, technical factor is not harsh, and the antibiosis knitting face fabric made has long-acting antibacterial functions.
Detailed description of the invention
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
Embodiment 1:
A kind of antibiosis knitting face fabric, by warp thread, weft yarn and wool yarn interlacing, one is had at least for bamboo-carbon fibre in described warp thread and weft yarn, described wool yarn is antibacterial composite fibers, described antibacterial composite fibers is by soybean fiber, cotton fiber, cellulose pulp, Nano Silver, titania powder and hydroxyapatite carry out blending and make, wherein, soybean fiber, cotton fiber, the ratio of quality and the number of copies of cellulose pulp is 15:35:75, described Nano Silver accounts for 0.01 ‰ of total fiber mass, described titania powder accounts for 0.03 ‰ of total fiber mass, the particle diameter of described Nano Silver is less than 50nm.
Above-mentioned this antibiosis knitting face fabric is carried out weaving as wool yarn as warp and parallel, antibacterial composite fibers by bamboo-carbon fibre, dyes, obtains antibiosis knitting face fabric after stamp and Final finishing; Wherein, antibacterial composite fibers is prepared from by following step:
1) preparation of raw material, weighs soybean fiber, cotton fiber, cellulose pulp, Nano Silver, titania powder and hydroxyapatite, for subsequent use;
2) preparation of cellulose rayon spinning liquid take cellulose pulp as raw material, through dipping, squeezing, pulverize, experienced, yellow and dissolving step obtain cellulose rayon spinning liquid;
3) preparation of antibacterial viscose glue, adds in alkaline solution by nano-silver ionic, titania powder and hydroxyapatite, stirs 30min, adds stabilizing agent, leaves standstill after again stirring 30min;
4) preparation of antibacterial viscose fiber, antibacterial viscose glue step 3) prepared carries out spinning, obtains antibacterial viscose fiber after coagulation forming;
5) preparation of antibacterial composite fibers, antibacterial viscose fiber step 4) obtained and soybean fiber, cotton fiber carry out blended, obtain antibacterial composite fibers.
Embodiment 2:
A kind of antibiosis knitting face fabric, wherein, the ratio of quality and the number of copies of soybean fiber, cotton fiber, dimension element pulp is 12:32:75, wherein, described Nano Silver accounts for 0.012 ‰ of total fiber mass, and described titania powder accounts for 0.025 ‰ of total fiber mass, and all the other are identical with embodiment 1.
The preparation method of the present embodiment is also with embodiment 1.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. a production technology for antibiosis knitting face fabric, is characterized in that, is carried out weaving by bamboo-carbon fibre, dyes, obtains antibiosis knitting face fabric after stamp and Final finishing as warp and parallel, antibacterial composite fibers as wool yarn; Wherein, antibacterial composite fibers is prepared from by following step:
1) preparation of raw material, weighs soybean fiber, cotton fiber, cellulose pulp, Nano Silver, titania powder and hydroxyapatite, for subsequent use;
2) preparation of cellulose rayon spinning liquid take cellulose pulp as raw material, through dipping, squeezing, pulverize, experienced, yellow and dissolving step obtain cellulose rayon spinning liquid;
3) preparation of antibacterial viscose glue, adds in alkaline solution by nano-silver ionic, titania powder and hydroxyapatite, stirs 30min, adds stabilizing agent, leaves standstill after again stirring 30min;
4) preparation of antibacterial viscose fiber, antibacterial viscose glue step 3) prepared carries out spinning, obtains antibacterial viscose fiber after coagulation forming;
5) preparation of antibacterial composite fibers, antibacterial viscose fiber step 4) obtained and soybean fiber, cotton fiber carry out blended, obtain antibacterial composite fibers.
2. the production technology of antibiosis knitting face fabric according to claim 1, is characterized in that, the particle diameter of described Nano Silver is less than 50nm.
3. the production technology of antibiosis knitting face fabric according to claim 1, is characterized in that, described Nano Silver accounts for 0.008 ~ 0.015 ‰ of antibacterial composite fibers gross mass.
4. the production technology of antibiosis knitting face fabric according to claim 1, is characterized in that, described titania powder accounts for 0.022 ~ 0.05 ‰ of antibacterial composite fibers gross mass.
5. the production technology of antibiosis knitting face fabric according to claim 1, is characterized in that, the ratio of quality and the number of copies of legumin fiber, cotton fiber, cellulose pulp is 10 ~ 20:25 ~ 40:70 ~ 80.