CN107163628A - A kind of construction material based on light matchmaker's decomposing, purifying - Google Patents
A kind of construction material based on light matchmaker's decomposing, purifying Download PDFInfo
- Publication number
- CN107163628A CN107163628A CN201710396976.9A CN201710396976A CN107163628A CN 107163628 A CN107163628 A CN 107163628A CN 201710396976 A CN201710396976 A CN 201710396976A CN 107163628 A CN107163628 A CN 107163628A
- Authority
- CN
- China
- Prior art keywords
- decomposing
- purifying
- construction material
- parts
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of construction material based on light matchmaker's decomposing, purifying, including：50 70 parts of activated carbon, 12 18 parts of montmorillonite, 5 10 parts of modifying titanium dioxide, 29 parts of nanometer silicon carbide, 2 10 parts of mica powder, 24 parts of hydroxypropyl methyl cellulose, 25 parts of styrene-acrylic emulsion, 14 parts of coalescents, 10 15 parts of water nano reinforcing agent, 26 parts of antimitotic agent.The present invention uses modifying titanium dioxide, activated carbon and modifying titanium dioxide synergy, improves the clean-up effect of optically catalytic TiO 2.
Description
Technical field
The present invention relates to building material field, and in particular to a kind of biological construction material based on light matchmaker's decomposing, purifying and its
Preparation method.
Background technology
New Building Materials kind is numerous, and form is different, has the advantages that economical and practical, market is environmentally friendly, disclosure satisfy that existing
For the aesthetic requirement of building decoration.With constantly bringing forth new ideas for construction material, existing frequently-used New Building Materials have：Novel wall
Material, heat preserving and insulating material, waterproof and sealing material etc..With the requirement more and more higher of construction market, the quality of construction material
Also require that more and more higher.
Construction material not only requires, with preferable combination property, to it is also desirable to have environmental-protecting performance now, can reduce ring
Pollute in border.For example, some common building surfacings, can be because aquation drying shrinkage, because the coefficient of expansion of different materials is different, meeting
Produce cracking, face coat and crackle occur, both have impact on the attractive in appearance of building, additionally it is possible to cause rain penetration.Therefore, need now
Want a kind of not only Environmental Safety but also be capable of the construction material of anti-crack.
The content of the invention
It is an object of the invention to overcome the problem above that prior art is present there is provided a kind of based on light matchmaker's decomposing, purifying
Construction material, the intensity of the material preferably, can effectively solve the problem that the problem of material cracking and environmental pollution.
To realize above-mentioned technical purpose and the technique effect, the present invention is achieved through the following technical solutions：
A kind of construction material based on light matchmaker's decomposing, purifying, in parts by weight, including：
Wherein, C element is doped in titanium dioxide by the modifying titanium dioxide is prepared from, titanium dioxide containing C
As presoma, activated carbon as the titanium dioxide containing C carrier.
Further comprise, the activated carbon is 50-300 mesh burgy.
Further comprise, the coalescents are butadiene resin film forming agent.
Further comprise, the water nano reinforcing agent includes nanoscale S2 surfactants, 2- amino 2- methyl isophthalic acids-the third
One or more in alcohol, propane diols, bactericide.
Further comprise, the antimitotic agent includes one kind in slag powders, silica flour, iron powder, aluminium powder, silica flour, swelling agent
Or it is several.
Further comprise, the particle diameter of the nanometer silicon carbide is 10-50nm.
The beneficial effects of the invention are as follows:
The titanium dioxide of the present invention is to use modifying titanium dioxide, activated carbon and modifying titanium dioxide synergy, is improved
The clean-up effect of optically catalytic TiO 2, is a kind of environment-friendly type building material.
Water nano reinforcing agent, antimitotic agent etc. are with the addition of in the material of the present invention, effect of prestressed enhancing, coating passes through heatproof
After denaturation treatment, do not peel off, non-foaming, flawless etc., combination property is preferable.
Contain substantial amounts of activated carbon in the material of the present invention, with higher adsorption capacity, meet wanting for ep-type material
Ask；Wood fibre, the weight of lightening material are added in the material；Polyurethane rubber is with the addition of in the material so that material wear-resistant
Better performances, and with the good good characteristic of ageing-resistant, air-tightness.
The present invention is improved by introducing nano level component to construction material, and the fire prevention for improving construction material is protected
Warm nature energy.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of specification, described in detail below with presently preferred embodiments of the present invention as after.The tool of the present invention
Body embodiment is shown in detail by following examples.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
Embodiment 1
A kind of construction material based on light matchmaker's decomposing, purifying is disclosed in embodiment 1, in parts by weight, including：
Embodiment 2
A kind of construction material based on light matchmaker's decomposing, purifying is disclosed in embodiment 2, in parts by weight, including：
Embodiment 3
A kind of construction material based on light matchmaker's decomposing, purifying is disclosed in embodiment 3, in parts by weight, including：
Wherein, C element is doped in titanium dioxide by the modifying titanium dioxide is prepared from, titanium dioxide containing C
As presoma, activated carbon as the titanium dioxide containing C carrier.
The activated carbon is 50-300 mesh burgy.
The coalescents are butadiene resin film forming agent.
The water nano reinforcing agent include nanoscale S2 surfactants, 2- amino 2- methyl isophthalic acids-propyl alcohol, propane diols,
One or more in bactericide.
The antimitotic agent includes the one or more in slag powders, silica flour, iron powder, aluminium powder, silica flour, swelling agent.
The particle diameter of the nanometer silicon carbide is 10-50nm.
Above-mentioned titanium dioxide is to use modifying titanium dioxide, activated carbon and modifying titanium dioxide synergy, improves two
The clean-up effect of titanium oxide photochemical catalyst.
Water nano reinforcing agent, antimitotic agent etc. are with the addition of in material, effect of prestressed enhancing, coating is handled by temperature-change resistance
Afterwards, do not peel off, non-foaming, flawless etc., combination property is preferable.
Contain substantial amounts of activated carbon in material, with higher adsorption capacity, meet the requirement of ep-type material；In material
Middle addition wood fibre, the weight of lightening material；Polyurethane rubber is with the addition of in the material so that material wear-resistant performance is preferable,
And with the good good characteristic of ageing-resistant, air-tightness.
Nano level component is introduced, construction material is improved, the fireproof heat insulating performance of construction material is improved.
The foregoing description of the disclosed embodiments, enables professional and technical personnel in the field to realize or using the present invention.
A variety of modifications to these embodiments will be apparent for those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, it is of the invention
The embodiments shown herein is not intended to be limited to, and is to fit to and principles disclosed herein and features of novelty phase one
The most wide scope caused.
Claims (6)
1. a kind of construction material based on light matchmaker's decomposing, purifying, it is characterised in that in parts by weight, including：
Wherein, C element is doped in titanium dioxide by the modifying titanium dioxide is prepared from, the conduct of titanium dioxide containing C
Presoma, activated carbon as the titanium dioxide containing C carrier.
2. the construction material according to claim 1 based on light matchmaker's decomposing, purifying, it is characterised in that the activated carbon is
50-300 mesh burgy.
3. the construction material according to claim 1 based on light matchmaker's decomposing, purifying, it is characterised in that the coalescents are
Butadiene resin film forming agent.
4. the construction material according to claim 1 based on light matchmaker's decomposing, purifying, it is characterised in that the water nano increases
Strong agent includes the one or more in nanoscale S2 surfactants, 2- amino 2- methyl isophthalic acids-propyl alcohol, propane diols, bactericide.
5. the construction material according to claim 1 based on light matchmaker's decomposing, purifying, it is characterised in that the antimitotic agent includes
One or more in slag powders, silica flour, iron powder, aluminium powder, silica flour, swelling agent.
6. the construction material according to claim 1 based on light matchmaker's decomposing, purifying, it is characterised in that the nanometer silicon carbide
Particle diameter be 10-50nm.