CN107556854A - A kind of water-and acrylate waterproof and heat-insulating building coating and preparation method thereof - Google Patents
A kind of water-and acrylate waterproof and heat-insulating building coating and preparation method thereof Download PDFInfo
- Publication number
- CN107556854A CN107556854A CN201710968417.0A CN201710968417A CN107556854A CN 107556854 A CN107556854 A CN 107556854A CN 201710968417 A CN201710968417 A CN 201710968417A CN 107556854 A CN107556854 A CN 107556854A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- heat
- building coating
- insulating building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of water-and acrylate waterproof and heat-insulating building coating, and its raw material includes following components by weight:80 120 parts of acrylic acid ester emulsion, 30 50 parts of white cement, 15 30 parts of quartz sand, 20 40 parts of powdered whiting, 5 10 parts of rutile titanium dioxide, 13 parts of hollow glass bead, 9 15 parts of diatomite, 6 10 parts of ceramic hollow microballon, 36 parts of nano far infrared ceramic powder, 36 parts of alumina powder, 0.3 0.9 parts of pH adjusting agent, 0.2 0.5 parts of bactericide, 0.5 1.2 parts of dispersant, 0.2 0.5 parts of defoamer, 1.0 2.5 parts of coalescents, 1.0 1.5 parts of thickener, 0.1 0.3 parts of water reducer, 30 50 parts of distilled water.The present invention also provides its preparation method.This kind of coating has the advantages that preferable elongation percentage, outdoor durable, basic unit's adaptability, green environmental protection, impermeability, high permeability resistant, toughness, insulating refractory.
Description
Technical field
The present invention relates to building coating, and in particular to a kind of water-and acrylate waterproof and heat-insulating building coating and its preparation side
Method.
Background technology
At present, China is in the peak time of building construction, and traditional exterior wall or construction coating for internal wall is mainly emphasized
Anti-corrosion, antifouling, ageing-resistant, self-cleaning is good, but inadequate in the concern of waterproof and heat-insulating aspect of performance.Waterproof and heat-insulating building coating is near
Increasingly paid attention to over year by country, be a kind of building solution very popular in recent years.Therefore, national government is not
But improve waterproof and heat-insulating design standard of the China in the building that will be built build and following, and to build
The transformation of waterproof and heat-insulating is carried out in original building, waterproof and heat-insulating architectural problems turn into one of China's urgent problem to be solved,
Therefore, it is current urgent problem to be solved to prepare a kind of waterproof and heat-insulating building coating.
The content of the invention
It is an object of the invention to provide a kind of water-and acrylate waterproof and heat-insulating building coating, this kind of water-and acrylate is prevented
Water heat insualting building coating has preferable elongation percentage, and outdoor durable, basic unit's adaptability, green environmental protection, impermeability, height are anti-
The advantages that oozing property, toughness, insulating refractory.Another object of the present invention is to provide this kind of water-and acrylate waterproof and heat-insulating and built
Build the preparation method of coating.
The present invention proposes a kind of water-and acrylate waterproof and heat-insulating building coating, and its raw material includes with the following group by weight
Point:Acrylic acid ester emulsion 80-120 parts, white cement 30-50 parts, quartz sand 15-30 parts, powdered whiting 20-40 parts, rutile
Type titanium dioxide 5-10 parts, hollow glass bead 1-3 parts, diatomite 9-15 parts, ceramic hollow microballon 6-10 parts, nanometer are far red
Outer ceramic powder 3-6 parts, alumina powder 3-6 parts, pH conditioning agent 0.3-0.9 parts, bactericide 0.2-0.5 parts, dispersant 0.5-1.2
Part, defoamer 0.2-0.5 parts, coalescents 1.0-2.5 parts, thickener 1.0-1.5 parts, water reducer 0.1-0.3 parts, distillation
Water 30-50 parts.
Further, the pH conditioning agents are the one or more in ammoniacal liquor, sodium hydroxide, potassium hydroxide, triethylamine
Combination.
Further, described dispersant be sodium tripolyphosphate, calgon, sodium pyrophosphate, lauryl sodium sulfate,
One or more in neopelex, methyl anyl alcohol, polyacrylamide.
Further, described defoamer is modified polyether ester DF50.
Further, described coalescents are from polyethylene glycol, ethylene glycol ethyl ether, propane diols phenylate, alcohol ester 12, second
One or more kinds of combinations in glycol butyl ether.
Further, described thickener is methylcellulose, hydroxypropyl methyl cellulose, polyacrylamide, polyethylene
One or more in alcohol, polyvinylpyrrolidone, polyethylene glycol oxide, polyacrylic acid or Sodium Polyacrylate.
Further, described water reducer is polycarboxylate high performance water-reducing agent AF-CA.
Further, its preparation method comprises the following steps:
S10, white cement, quartz sand, powdered whiting, water reducer be put into BJ-100 type blenders according to predetermined number,
5min is mixed, is prepared into powder;
S11, by rutile titanium dioxide, hollow glass bead, diatomite, ceramic hollow microballon, nano far infrared ceramic powder,
The heat insulating function such as alumina powder filler adds mulser, is dispersed with stirring and produces face, filler mill base;
S12, by distilled water, dispersant, part defoamer, coalescents add a mixing bowl in, stirring at low speed disperses 15-20min,
Under conditions of high-speed stirred, by step S10, be prepared into face, filler mill base that powder S11 is prepared and be dispersed with stirring 15-
30min, regulation fineness is then ground to by sand mill, it is standby to obtain slurry;
S13, under conditions of stirring at low speed, by acrylic acid ester emulsion, bactericide, remaining defoamer, thickener, be added to step
In the slurry that S12 is prepared, stirring and adding pH conditioning agents is adjusted to suitable viscosity and pH value, produces required
Water-and acrylate waterproof and heat-insulating building coating.
The technology of the present invention principle:
The present invention is by acrylic acid ester emulsion bactericide, remaining defoamer, thickener and by addition white cement, quartz sand, heavy carbon
The waterproof architectural coating of sour calcium, water reducer composition, its waterproof action principle are:Water is lost based on acrylic acid ester emulsion and turned into
With cohesiveness and successional layers of elastomeric film, cement absorbs the water in emulsion and hardened, so that flexible polymer film
It is mutually communicated with hardening of cement body and coheres into a firm and flexible waterproof layer securely.It is micro- to add glass hollow simultaneously
The reflective insulation color stuffing such as pearl, diatomite, nano titanium oxide, ceramic hollow microballon, nano far infrared ceramic powder, and addition portion
Divide auxiliary agent, a kind of water-and acrylate waterproof and heat-insulating building coating is prepared.Nano titanium oxide and nano-far-infrared ceramics
Powder plays good reflex to solar radiation, reduces the accumulation of heat, hollow ceramic microspheres, hollow glass micropearl have compared with
Low thermal conductivity factor, above-mentioned material is added in coating and plays the effect of heat-insulation and heat-preservation fireproof.The combination of the two, just makes
Flexible polymer-filled in the space of hardening of cement body so that hardening of cement body is finer and close and high resilience, applies
Film has preferable elongation percentage, and hardening of cement body is filled in the polymer again so that polymer have more preferable outdoor durable,
The advantages that basic unit's adaptability, impermeability, high permeability resistant, toughness, thermal insulation.
It is compared with the prior art, the invention has the advantages that:
1st, it is strong that the effect of nano titanium oxide shielding ultraviolet rays is added in the present invention, the infringement of ultraviolet is prevented, improves coating
Service life.Meanwhile its higher hardness, density, dielectric constant and refractive index, be favorably improved coating covering power and
Color power, and have good reflex to the heat radiation in sunlight;
2nd, ceramic hollow microballon, hollow glass bead, diatomite are with the addition of in the present invention, low thermal conductivity, guarantor can be played to building
The heat-insulated effect of temperature, when play the role of thermal source close to when can play heat-insulated, effectively raise the ignition temperature of film, extend
The fire resistance period of film, prevents fire from occurring rapidly;
3rd, the nano far infrared ceramic powder that adds not only heat-insulation and heat-preservation in the present invention, in sunshine(Especially ultraviolet)Under irradiation
OH- is generated, can effectively remove benzene, formaldehyde, sulfide, ammonia and the stink substance of indoor and outdoor, and there is sterilizing function, is green ring
Friendly coating;
4th, a kind of water-and acrylate waterproof and heat-insulating building coating of the present invention.This kind of water-and acrylate waterproof and heat-insulating building coating
With preferable elongation percentage, outdoor durable, basic unit's adaptability, green environmental protection, impermeability, high permeability resistant, toughness, every
The advantages that hot fire resistance.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.The specific embodiments described herein are merely illustrative of the present invention, is not used to limit
The present invention.
Embodiment 1
A kind of water-and acrylate waterproof and heat-insulating building coating, its raw material include following components by weight:Acrylic acid ester emulsion
80 parts, 30 parts of white cement, 15 parts of quartz sand, 20 parts of powdered whiting, 5 parts of rutile titanium dioxide, hollow glass bead 1
Part, 9 parts of diatomite, 6 parts of ceramic hollow microballon, 3 parts of nano far infrared ceramic powder, 3 parts of alumina powder, 0.3 part of pH conditioning agents,
0.2 part of bactericide, 0.5 part of dispersant, 0.2 part of defoamer, 1.0 parts of coalescents, 1.0 parts of thickener, 0.1 part of water reducer, steaming
30 parts of distilled water.
The pH conditioning agents are ammoniacal liquor.
Described dispersant is sodium tripolyphosphate.
Described defoamer is modified polyether ester DF50.
Described coalescents select polyethylene glycol.
Described thickener is methylcellulose.
Described water reducer is polycarboxylate high performance water-reducing agent AF-CA.
Its preparation method comprises the following steps:
S10, white cement, quartz sand, powdered whiting, water reducer be put into BJ-100 type blenders according to predetermined number,
5min is mixed, is prepared into powder;
S11, by rutile titanium dioxide, hollow glass bead, diatomite, ceramic hollow microballon, nano far infrared ceramic powder,
The heat insulating function such as alumina powder filler adds mulser, is dispersed with stirring and produces face, filler mill base;
S12, by distilled water, dispersant, part defoamer, coalescents add a mixing bowl in, stirring at low speed disperses 15min,
Under conditions of high-speed stirred, by step S10, be prepared into face, filler mill base that powder S11 is prepared and be dispersed with stirring 15min,
Then regulation fineness is ground to by sand mill, it is standby obtains slurry;
S13, under conditions of stirring at low speed, by acrylic acid ester emulsion, bactericide, remaining defoamer, thickener, be added to step
In the slurry that S12 is prepared, stirring and adding pH conditioning agents is adjusted to suitable viscosity and pH value, produces required
Water-and acrylate waterproof and heat-insulating building coating.
Embodiment 2
A kind of water-and acrylate waterproof and heat-insulating building coating, its raw material include following components by weight:Acrylic acid ester emulsion
120 parts, 50 parts of white cement, 30 parts of quartz sand, 40 parts of powdered whiting, 10 parts of rutile titanium dioxide, glass hollow it is micro-
3 parts of pearl, 15 parts of diatomite, 10 parts of ceramic hollow microballon, 6 parts of nano far infrared ceramic powder, 6 parts of alumina powder, pH conditioning agents
0.9 part, 0.5 part of bactericide, 1.2 parts of dispersant, 0.5 part of defoamer, 2.5 parts of coalescents, 1.5 parts of thickener, diminishing
0.3 part of agent, 50 parts of distilled water.
The combination that the pH conditioning agents are ammoniacal liquor, sodium hydroxide arbitrarily matches.
The combination that described dispersant is sodium tripolyphosphate, calgon arbitrarily matches.
Described defoamer is modified polyether ester DF50.
The combination that described coalescents are arbitrarily matched from polyethylene glycol, ethylene glycol ethyl ether.
Described thickener is hydroxypropyl methyl cellulose.
Described water reducer is polycarboxylate high performance water-reducing agent AF-CA.
Its preparation method comprises the following steps:
S10, white cement, quartz sand, powdered whiting, water reducer be put into BJ-100 type blenders according to predetermined number,
5min is mixed, is prepared into powder;
S11, by rutile titanium dioxide, hollow glass bead, diatomite, ceramic hollow microballon, nano far infrared ceramic powder,
The heat insulating function such as alumina powder filler adds mulser, is dispersed with stirring and produces face, filler mill base;
S12, by distilled water, dispersant, part defoamer, coalescents add a mixing bowl in, stirring at low speed disperses 20min,
Under conditions of high-speed stirred, by step S10, be prepared into face, filler mill base that powder S11 is prepared and be dispersed with stirring 30min,
Then regulation fineness is ground to by sand mill, it is standby obtains slurry;
S13, under conditions of stirring at low speed, by acrylic acid ester emulsion, bactericide, remaining defoamer, thickener, be added to step
In the slurry that S12 is prepared, stirring and adding pH conditioning agents is adjusted to suitable viscosity and pH value, produces required
Water-and acrylate waterproof and heat-insulating building coating.
Embodiment 3
A kind of water-and acrylate waterproof and heat-insulating building coating, its raw material include following components by weight:Acrylic acid ester emulsion
100 parts, 40 parts of white cement, 20 parts of quartz sand, 30 parts of powdered whiting, 6 parts of rutile titanium dioxide, hollow glass bead 2
Part, 12 parts of diatomite, 8 parts of ceramic hollow microballon, 5 parts of nano far infrared ceramic powder, 5 parts of alumina powder, 0.6 part of pH conditioning agents,
0.3 part of bactericide, 0.9 part of dispersant, 0.4 part of defoamer, 1.6 parts of coalescents, 1.2 parts of thickener, 0.2 part of water reducer,
35 parts of distilled water.
The combination that the pH conditioning agents are ammoniacal liquor, sodium hydroxide, potassium hydroxide arbitrarily match.
Further, described dispersant is sodium tripolyphosphate, calgon, sodium pyrophosphate, lauryl sodium sulfate
The combination arbitrarily matched.
Described defoamer is modified polyether ester DF50.
Described coalescents select ethylene glycol ethyl ether.
The combination that described thickener is methylcellulose, hydroxypropyl methyl cellulose, polyacrylamide arbitrarily match.
Described water reducer is polycarboxylate high performance water-reducing agent AF-CA.
Its preparation method comprises the following steps:
S10, white cement, quartz sand, powdered whiting, water reducer be put into BJ-100 type blenders according to predetermined number,
5min is mixed, is prepared into powder;
S11, by rutile titanium dioxide, hollow glass bead, diatomite, ceramic hollow microballon, nano far infrared ceramic powder,
The heat insulating function such as alumina powder filler adds mulser, is dispersed with stirring and produces face, filler mill base;
S12, by distilled water, dispersant, part defoamer, coalescents add a mixing bowl in, stirring at low speed disperses 18min,
Under conditions of high-speed stirred, by step S10, be prepared into face, filler mill base that powder S11 is prepared and be dispersed with stirring 25min,
Then regulation fineness is ground to by sand mill, it is standby obtains slurry;
S13, under conditions of stirring at low speed, by acrylic acid ester emulsion, bactericide, remaining defoamer, thickener, be added to step
In the slurry that S12 is prepared, stirring and adding pH conditioning agents is adjusted to suitable viscosity and pH value, produces required
Water-and acrylate waterproof and heat-insulating building coating.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (8)
1. a kind of water-and acrylate waterproof and heat-insulating building coating, it is characterised in that its raw material includes following components by weight:
Acrylic acid ester emulsion 80-120 parts, white cement 30-50 parts, quartz sand 15-30 parts, powdered whiting 20-40 parts, rutile-type
Titanium dioxide 5-10 parts, hollow glass bead 1-3 parts, diatomite 9-15 parts, ceramic hollow microballon 6-10 parts, nano-far-infrared
Ceramic powder 3-6 parts, alumina powder 3-6 parts, pH conditioning agent 0.3-0.9 parts, bactericide 0.2-0.5 parts, dispersant 0.5-1.2
Part, defoamer 0.2-0.5 parts, coalescents 1.0-2.5 parts, thickener 1.0-1.5 parts, water reducer 0.1-0.3 parts, distillation
Water 30-50 parts.
A kind of 2. water-and acrylate waterproof and heat-insulating building coating according to claim 1, it is characterised in that:The pH
Conditioning agent is one or more kinds of combinations in ammoniacal liquor, sodium hydroxide, potassium hydroxide, triethylamine.
A kind of 3. water-and acrylate waterproof and heat-insulating building coating according to claim 1, it is characterised in that:Described
Dispersant is sodium tripolyphosphate, calgon, sodium pyrophosphate, lauryl sodium sulfate, neopelex, methylpent
One or more in alcohol, polyacrylamide.
A kind of 4. water-and acrylate waterproof and heat-insulating building coating according to claim 1, it is characterised in that:Described
Defoamer is modified polyether ester DF50.
A kind of 5. water-and acrylate waterproof and heat-insulating building coating according to claim 1, it is characterised in that:Described
Coalescents are from a kind of or more in polyethylene glycol, ethylene glycol ethyl ether, propane diols phenylate, alcohol ester 12, butyl glycol ether
The combination of kind.
A kind of 6. water-and acrylate waterproof and heat-insulating building coating according to claim 1, it is characterised in that:Described
Thickener is methylcellulose, hydroxypropyl methyl cellulose, polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, polyoxygenated
One or more in ethene, polyacrylic acid or Sodium Polyacrylate.
A kind of 7. water-and acrylate waterproof and heat-insulating building coating according to claim 1, it is characterised in that:Described
Water reducer is polycarboxylate high performance water-reducing agent AF-CA.
A kind of 8. water-and acrylate waterproof and heat-insulating building coating according to claim 1, it is characterised in that:It is prepared
Method comprises the following steps:
S10, white cement, quartz sand, powdered whiting, water reducer be put into BJ-100 type blenders according to predetermined number,
5min is mixed, is prepared into powder;
S11, by rutile titanium dioxide, hollow glass bead, diatomite, ceramic hollow microballon, nano far infrared ceramic powder,
The heat insulating function such as alumina powder filler adds mulser, is dispersed with stirring and produces face, filler mill base;
S12, by distilled water, dispersant, part defoamer, coalescents add a mixing bowl in, stirring at low speed disperses 15-20min,
Under conditions of high-speed stirred, by step S10, be prepared into face, filler mill base that powder S11 is prepared and be dispersed with stirring 15-
30min, regulation fineness is then ground to by sand mill, it is standby to obtain slurry;
S13, under conditions of stirring at low speed, by acrylic acid ester emulsion, bactericide, remaining defoamer, thickener, be added to step
In the slurry that S12 is prepared, stirring and adding pH conditioning agents is adjusted to suitable viscosity and pH value, produces required
Water-and acrylate waterproof and heat-insulating building coating.