CN107417175A - A kind of diatom ooze composite - Google Patents
A kind of diatom ooze composite Download PDFInfo
- Publication number
- CN107417175A CN107417175A CN201710741259.5A CN201710741259A CN107417175A CN 107417175 A CN107417175 A CN 107417175A CN 201710741259 A CN201710741259 A CN 201710741259A CN 107417175 A CN107417175 A CN 107417175A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatom ooze
- ooze composite
- triisopropanolamine
- sepiolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of diatom ooze composite, the diatom ooze composite is prepared from the following raw materials in parts by weight：60 85 parts of diatomite, 6 12 parts of expanded perlite, 26 parts of ethylene glycol, 5 12 parts of sepiolite, 15 parts of methylcellulose, 5 15 parts of silica flour, 13 parts of wood fibre, 28 parts of rubber powder, 13 parts of nano titanium oxide, 15 25 parts of coarse whiting, 6 14 parts of modified sodium alginate, 10 20 parts of kaolin, 0.8 2 parts of dispersant, 0.5 1.8 parts of mould inhibitor, 0.6 1.5 parts of surfactant, 15 parts of triisopropanolamine, 13 parts of coalescents, 26 parts of gelling additive, 22 35 parts of water.Diatom ooze composite removal indoor formaldehyde ability in the present invention is strong, and wall can be avoided cracked.
Description
Technical field
The present invention relates to building coating technical field, more particularly to a kind of diatom ooze composite.
Background technology
Wall finiss, also known as emulsion paint, major function are decoration and protection metope, make metope appearance neat and artistic；Wall finiss
Mainly it is formulated by water, film forming matter, coalescents, dispersant, wetting agent, defoamer, coalescents etc..Presently commercially available
Often hardness is low for wall finiss, and film is easy to aging, fades, efflorescence, and weather resistance is poor.At the same time, existing many coating is all
The shortcomings of it is poor to there is rebound performance, and contains various volatile poisonous and harmful substances such as formaldehyde, is good for so as to seriously endanger human body
Health.
The content of the invention
It is an object of the invention to provide a kind of diatom ooze composite, its is safe and pollution-free, and removes indoor formaldehyde energy
Power is strong, and wall can be avoided cracked.
To achieve the above object, the present invention provides following technical scheme：
A kind of diatom ooze composite is prepared from the following raw materials in parts by weight：Diatomite 60-85 parts, expanded perlite 6-
12 parts, ethylene glycol 2-6 parts, sepiolite 5-12 parts, methylcellulose 1-5 parts, silica flour 5-15 parts, wood fibre 1-3 parts, rubber powder
2-8 parts, nano titanium oxide 1-3 parts, coarse whiting 15-25 parts, modified sodium alginate 6-14 parts, kaolin 10-20 parts, dispersant
0.8-2 parts, mould inhibitor 0.5-1.8 parts, surfactant 0.6-1.5 parts, triisopropanolamine 1-5 parts, coalescents 1-3 parts, glue
Solidifying auxiliary agent 2-6 parts, water 22-35 parts.
Preferably, described diatom ooze composite is prepared from the following raw materials in parts by weight：82 parts of diatomite, expansion are precious
9 parts of pearl rock, 3 parts of ethylene glycol, 9 parts of sepiolite, 3 parts of methylcellulose, 11 parts of silica flour, 2 parts of wood fibre, 6 parts of rubber powder, nanometer
1 part of titanium dioxide, 18 parts of coarse whiting, 8 parts of modified sodium alginate, 15 parts of kaolin, 1.2 parts of dispersant, 1 part of mould inhibitor, surface
0.9 part of activating agent, 3 parts of triisopropanolamine, 2 parts of coalescents, 4 parts of gelling additive, 28 parts of water.
Preferably, described diatom ooze composite is prepared from the following raw materials in parts by weight：80 parts of diatomite, expansion are precious
10 parts of pearl rock, 3 parts of ethylene glycol, 6 parts of sepiolite, 4 parts of methylcellulose, 13 parts of silica flour, 3 parts of wood fibre, 7 parts of rubber powder, receive
2.5 parts of titanium dioxide of rice, 22 parts of coarse whiting, 11 parts of modified sodium alginate, 12 parts of kaolin, 1.5 parts of dispersant, 1 part of mould inhibitor,
1 part of surfactant, 3 parts of triisopropanolamine, 2 parts of coalescents, 5 parts of gelling additive, 30 parts of water.
Preferably, described diatom ooze composite is prepared from the following raw materials in parts by weight：75 parts of diatomite, expansion are precious
7 parts of pearl rock, 5 parts of ethylene glycol, 10 parts of sepiolite, 3 parts of methylcellulose, 10 parts of silica flour, 2 parts of wood fibre, 5 parts of rubber powder, receive
2 parts of titanium dioxide of rice, 24 parts of coarse whiting, 10 parts of modified sodium alginate, 16 parts of kaolin, 1.6 parts of dispersant, 1.2 parts of mould inhibitor,
1.3 parts of surfactant, 5 parts of triisopropanolamine, 2 parts of coalescents, 5 parts of gelling additive, 25 parts of water.
Compared with prior art, the beneficial effects of the invention are as follows：
Diatom ooze composite in the present invention is a kind of pollution-free and environmentally friendly finishing material, will not be produced any harmful
In the material of health, it is painted has good water resistance, resistance to acids and bases after metope, and removes indoor formaldehyde ability
By force, wall can be avoided cracked.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
A kind of diatom ooze composite is prepared from the following raw materials in parts by weight：70 parts of diatomite, 10 parts of expanded perlite,
3 parts of ethylene glycol, 7 parts of sepiolite, 3 parts of methylcellulose, 10 parts of silica flour, 1.5 parts of wood fibre, 5 parts of rubber powder, nanometer titanium dioxide
2 parts of titanium, 20 parts of coarse whiting, 13 parts of modified sodium alginate, 12 parts of kaolin, 1.4 parts of dispersant, 1.5 parts of mould inhibitor, surface-active
1 part of agent, 3 parts of triisopropanolamine, 2 parts of coalescents, 5 parts of gelling additive, 30 parts of water.
Embodiment two：
A kind of diatom ooze composite is to be prepared from the following raw materials in parts by weight：82 parts of diatomite, expanded perlite 9
Part, 3 parts of ethylene glycol, 9 parts of sepiolite, 3 parts of methylcellulose, 11 parts of silica flour, 2 parts of wood fibre, 6 parts of rubber powder, nano-silica
Change 1 part of titanium, 18 parts of coarse whiting, 8 parts of modified sodium alginate, 15 parts of kaolin, 1.2 parts of dispersant, 1 part of mould inhibitor, surface-active
0.9 part of agent, 3 parts of triisopropanolamine, 2 parts of coalescents, 4 parts of gelling additive, 28 parts of water.
Embodiment three：
A kind of diatom ooze composite is to be prepared from the following raw materials in parts by weight：80 parts of diatomite, expanded perlite 10
Part, 3 parts of ethylene glycol, 6 parts of sepiolite, 4 parts of methylcellulose, 13 parts of silica flour, 3 parts of wood fibre, 7 parts of rubber powder, nano-silica
Change 2.5 parts of titanium, 22 parts of coarse whiting, 11 parts of modified sodium alginate, 12 parts of kaolin, 1.5 parts of dispersant, 1 part of mould inhibitor, surface is lived
1 part of agent of property, 3 parts of triisopropanolamine, 2 parts of coalescents, 5 parts of gelling additive, 30 parts of water.
Example IV:
A kind of diatom ooze composite is to be prepared from the following raw materials in parts by weight：75 parts of diatomite, expanded perlite 7
Part, 5 parts of ethylene glycol, 10 parts of sepiolite, 3 parts of methylcellulose, 10 parts of silica flour, 2 parts of wood fibre, 5 parts of rubber powder, nano-silica
Change 2 parts of titanium, 24 parts of coarse whiting, 10 parts of modified sodium alginate, 16 parts of kaolin, 1.6 parts of dispersant, 1.2 parts of mould inhibitor, surface is lived
1.3 parts of agent of property, 5 parts of triisopropanolamine, 2 parts of coalescents, 5 parts of gelling additive, 25 parts of water.
Embodiment five：
A kind of diatom ooze composite is prepared from the following raw materials in parts by weight：60 parts of diatomite, 6 parts of expanded perlite,
2 parts of ethylene glycol, 5 parts of sepiolite, 1 part of methylcellulose, 5 parts of silica flour, 1 part of wood fibre, 2 parts of rubber powder, nano titanium oxide 1
Part, 15 parts of coarse whiting, 6 parts of modified sodium alginate, 10 parts of kaolin, 0.8 part of dispersant, 0.5 part of mould inhibitor, surfactant
0.6 part, 1 part of triisopropanolamine, 1 part of coalescents, 2 parts of gelling additive, 22 parts of water.
Embodiment six：
A kind of diatom ooze composite is prepared from the following raw materials in parts by weight：85 parts of diatomite, 12 parts of expanded perlite,
6 parts of ethylene glycol, 12 parts of sepiolite, 5 parts of methylcellulose, 15 parts of silica flour, 3 parts of wood fibre, 8 parts of rubber powder, nanometer titanium dioxide
3 parts of titanium, 25 parts of coarse whiting, 14 parts of modified sodium alginate, 20 parts of kaolin, 2 parts of dispersant, 1.8 parts of mould inhibitor, surfactant
1.5 parts, 5 parts of triisopropanolamine, 3 parts of coalescents, 6 parts of gelling additive, 35 parts of water.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (4)
1. a kind of diatom ooze composite, it is characterised in that be prepared from the following raw materials in parts by weight：Diatomite 60-85 parts are swollen
Swollen perlite 6-12 parts, ethylene glycol 2-6 parts, sepiolite 5-12 parts, methylcellulose 1-5 parts, silica flour 5-15 parts, wood fibre
1-3 parts, rubber powder 2-8 parts, nano titanium oxide 1-3 parts, coarse whiting 15-25 parts, modified sodium alginate 6-14 parts, kaolin 10-
20 parts, dispersant 0.8-2 parts, mould inhibitor 0.5-1.8 parts, surfactant 0.6-1.5 parts, triisopropanolamine 1-5 parts, film forming helps
Agent 1-3 parts, gelling additive 2-6 parts, water 22-35 parts.
2. a kind of diatom ooze composite according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into：82 parts of diatomite, 9 parts of expanded perlite, 3 parts of ethylene glycol, 9 parts of sepiolite, 3 parts of methylcellulose, 11 parts of silica flour are wooden
2 parts of fiber, 6 parts of rubber powder, 1 part of nano titanium oxide, 18 parts of coarse whiting, 8 parts of modified sodium alginate, 15 parts of kaolin, dispersant
1.2 parts, 1 part of mould inhibitor, 0.9 part of surfactant, 3 parts of triisopropanolamine, 2 parts of coalescents, 4 parts of gelling additive, 28 parts of water.
3. a kind of diatom ooze composite according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into：80 parts of diatomite, 10 parts of expanded perlite, 3 parts of ethylene glycol, 6 parts of sepiolite, 4 parts of methylcellulose, 13 parts of silica flour, wood
3 parts of matter fiber, 7 parts of rubber powder, 2.5 parts of nano titanium oxide, 22 parts of coarse whiting, 11 parts of modified sodium alginate, 12 parts of kaolin, point
1.5 parts of powder, 1 part of mould inhibitor, 1 part of surfactant, 3 parts of triisopropanolamine, 2 parts of coalescents, 5 parts of gelling additive, water 30
Part.
4. a kind of diatom ooze composite according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into：75 parts of diatomite, 7 parts of expanded perlite, 5 parts of ethylene glycol, 10 parts of sepiolite, 3 parts of methylcellulose, 10 parts of silica flour, wood
2 parts of matter fiber, 5 parts of rubber powder, 2 parts of nano titanium oxide, 24 parts of coarse whiting, 10 parts of modified sodium alginate, 16 parts of kaolin, disperse
1.6 parts of agent, 1.2 parts of mould inhibitor, 1.3 parts of surfactant, 5 parts of triisopropanolamine, 2 parts of coalescents, 5 parts of gelling additive, water
25 parts.