CN107142719B - A kind of textile fabric formaldehyde expellent and its preparation and application - Google Patents
A kind of textile fabric formaldehyde expellent and its preparation and application Download PDFInfo
- Publication number
- CN107142719B CN107142719B CN201710405218.9A CN201710405218A CN107142719B CN 107142719 B CN107142719 B CN 107142719B CN 201710405218 A CN201710405218 A CN 201710405218A CN 107142719 B CN107142719 B CN 107142719B
- Authority
- CN
- China
- Prior art keywords
- parts
- expellent
- textile fabric
- rectorite
- formaldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention proposes a kind of textile fabric formaldehyde expellent and its preparations and application, the textile fabric formaldehyde expellent includes following parts by weight component: 8-14 parts of nano modification rectorite, 2-5 parts of 1- vinyl imidazole, 1-4 parts of methyl guanamines, 0.2-0.7 parts of guanylurea phosphate, 1.2-1.8 parts of antibacterial agent, 0.5-2 parts of aromatic, 0.1-0.4 parts of surfactant, 3-8 parts of polyvinyl alcohol, distill appropriate amount of water, the present invention has high-specific surface area and self-cleaning with textile fabric expellent made from technique to be reasonably formulated, 55% or more is improved compared to conventional adsorbent active carbon porosity, extension of validity 3 times or more, and with excellent antistatic, antibacterial and mouldproof, the effect of radiation protection and softening fabric, except aldehyde rate is up to 99. in 20min 2%, efficiently quickly.
Description
Technical field
The present invention relates to formaldehyde expellent technical fields, and in particular to a kind of textile fabric formaldehyde expellent and its preparation and
Using.
Background technique
Formaldehyde is a kind of colourless, gas of irritant smell, soluble easily in water, alcohol, ether.Formaldehyde has widely in the industry
Purposes.It is usually used in weaving, dyestuff, leather, resin, paint, plastics, rubber, pharmacy, explosive etc..Therefore the pollution master of formaldehyde
Product more than deriving from.Formaldehyde is mainly manifested in following aspect to the harm of human body: formaldehyde can be with the plasm of body cell
In protein combine, change protein interior structure and simultaneously solidify, kill livestock power to have.Initially stimulation eye is glutinous at low concentrations
Film stimulates the upper respiratory tract at high concentrations, causes cough, uncomfortable in chest, while neck has constriction, and mucous membrane is made to fester, Jin Er
Lung causes inflammation.It can cause appetite stimulator, anorexia, weight loss, weak, insomnia after inhaled formaldehyde;If often in contact with
It can generate to quick phenomenon, and skin histology can be caused to fester.Formaldehyde Central nervous system has anesthetic effect, especially to eyesight
There is strong toxic action.Furthermore formaldehyde can also inhereditary material in damaging cells, be suspicious carcinogen.Long Term Contact first
Aldehyde gas can cause headache, it is weak and feeble, perspire irregular, Temperature changing, pulse quickening, fash, eczema, redness etc..Therefore
Formaldehyde is classified as suspicious carcinogen and important environmental contaminants by the World Health Organization (WHO) and Environmental Protection Agency USA.
Due to consideration that the toxicity of formaldehyde, clear stipulaties are forbidden adding formaldehyde into food in China " food hygiene law ".It goes in weaving
Industry China and countries in the world government all define the limitation of formaldehyde, or formulate the environmental protection label method of textile.In recent years due to
People occupy main improvement of terms, and China has promulgated " sanitary standard of formaldehyde in indoor air "
Therefore developing and establishing the method for quick and precisely removing formaldehyde in fabric increasingly seems important.Currently, the prior art
In, such as Chinese patent CN101502748A " deodouring agent for removing formaldehyde ", provide the method and reagent for removing formaldehyde.But by
In the aqueous solution that the formula is based on removing odors, covered by removing odors and being added flavor component.And assistant concentration is not
Height, so to remove the formaldehyde of slow release on solid matter, just relatively difficult, effect will not be too stable.
Summary of the invention
In view of the above problems, the invention proposes a kind of textile fabric formaldehyde expellent and its preparation and application,
There is high-specific surface area and self-cleaning with textile fabric expellent made from technique to be reasonably formulated, compared to conventional adsorbent
Active carbon porosity improves 55% or more, 3 times or more of extension of validity, and with excellent antistatic, antibacterial and mouldproof,
The effect of radiation protection and softening fabric, 20min is interior except aldehyde rate is up to 99.2%, efficiently quickly.
In order to achieve the above purpose, the following technical solution is employed by the present invention:
A kind of textile fabric formaldehyde expellent, including following parts by weight component: 8-14 parts of nano modification rectorite, 1- second
2-5 parts of alkenyl imidazoles, 1-4 parts of methyl guanamines, 0.2-0.7 parts of guanylurea phosphate, 1.2-1.8 parts of antibacterial agent, aromatic 0.5-2
Part, 0.1-0.4 parts of surfactant, 3-8 parts of polyvinyl alcohol, distillation appropriate amount of water.
Preferably, the nano modification rectorite is specially nanometer mesoporous aluminas/nanometer Mayan indigo plant property of modified rectorite, system
Standby steps are as follows: rectorite being added in the distilled water of its 10 times of quality, is placed in 75 DEG C of high-speed stirred 5min in dispersion machine, then
It is added thereto and accounts for the octadecyltrimethylammonium chloride of rectorite quality 3% and account for the mixed solution of rectorite quality 5%, after
Continuous high-speed stirred 30-40min, is freeze-dried to obtain powder;Powder, nanometer mesoporous aluminas, nanometer Mayan indigo plant are blended, ball is placed in
Ball milling ball milling 8-10h in grinding machine, after taking out drying.
Preferably, it is counted by weight base unit weight of rectorite, the nanometer mesoporous aluminas additive amount is 1-7%, nanometer Mayan
Blue additive amount is 5-10%.
Preferably, the mixed solution is sodium alginate and sodium carbonate and mixed aqueous solution, wherein sodium alginate quality hundred
Dividing content is 1-3%, and sodium carbonate mass percentage is 2-7%.
Preferably, the antibacterial agent is the monomethyl fumarate of the mass ratio of the material 0.5-0.8:1, methyl carbamate mixing
Object.
Preferably, the aromatic is Rosa Damascana, aloe essential oil, Radix Glycyrrhizae essential oil, Peppermint essential oil, clove oil, silk tree
One of peel essential oil or numerous compositions.
Preferably, the surfactant is the mixture of the lauryl glucosyl of mass ratio 2:1, alkanolamide.
Preferably, textile fabric formaldehyde expellent, preparation step are as follows: by 1- vinyl imidazole, methyl guanamines, amidine phosphate
Base urea is blended, and the distilled water of 6-7 times of three's gross mass is added thereto, then 60 DEG C of stirring 15-20min tire out nano modification
Support stone, surfactant, polyvinyl alcohol are added thereto, constant temperature oscillation 40-60min, then by other surplus stocks be added thereto after
Continuous constant temperature oscillation handles 30-40min, and filtering is drying to obtain textile fabric formaldehyde expellent.
Preferably, textile fabric formaldehyde expellent and distilled water solution is configured to by solid-to-liquid ratio 0.5-1:10 to use.
Due to using above-mentioned technical solution, the beneficial effects of the present invention are:
1) present invention has high-specific surface area and self-cleaning with textile fabric expellent made from technique to be reasonably formulated,
Compared to conventional adsorbent active carbon porosity improve 55% or more, 3 times or more of extension of validity, and have excellent
The effect of antistatic, antibacterial and mouldproof, radiation protection and softening fabric, 20min is interior except aldehyde rate is up to 99.2%, efficiently quickly.
2) with nanometer mesoporous aluminas and the filling-modified rectorite of nanometer Mayan indigo plant intercalation, porous steric configuration is stabilized,
Rectorite uniform pore diameter degree is improved, the persistence of hole absorption is peomoted.Nanometer mesoporous aluminas large specific surface area, into
One step improves adsorbable porosity, enhances the effect of short-term quick adsorption, while having good antistatic, radiation protection
Effect;Nanometer Mayan indigo plant has good self-cleaning, and the service life of expellent can be improved while guaranteeing formaldehyde absorbing.
3) addition antibacterial agent, aromatic are conducive to improve the comprehensive performance of fabric, improve the comfort level and quality of fabric,
And antibacterial agent, aromatic, surfactant help to cooperate 1- vinyl imidazole, the nitrogen-containing heterocycle in methyl guanamines, amino, Asia
Effect is driven away in the decomposition that amino etc. improves PARA FORMALDEHYDE PRILLS(91,95), inherently removes formaldehyde.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described.Based on the embodiment of the present invention, the common skill in this field
Art personnel every other embodiment obtained without creative efforts belongs to the model that the present invention protects
It encloses.
Embodiment 1:
A kind of textile fabric formaldehyde expellent, including following parts by weight component: 12 parts of nano modification rectorite, 1- ethylene
4 parts of base imidazoles, 2 parts of methyl guanamines, 0.6 part of guanylurea phosphate, 1.6 parts of antibacterial agent, 2 parts of aromatic, 0.3 part of surfactant,
5 parts of polyvinyl alcohol, distillation appropriate amount of water.
Wherein, nano modification rectorite is specially nanometer mesoporous aluminas/nanometer Mayan indigo plant property of modified rectorite, preparation step
It is as follows: rectorite to be added in the distilled water of its 10 times of quality, be placed in 75 DEG C of high-speed stirred 5min in dispersion machine, then thereto
Addition accounts for the octadecyltrimethylammonium chloride of rectorite quality 3% and accounts for the mixed solution of rectorite quality 5%, continues high speed
30-40min is stirred, powder is freeze-dried to obtain;Powder, nanometer mesoporous aluminas, nanometer Mayan indigo plant are blended, are placed in ball mill
Ball milling ball milling 8-10h, after taking out drying.It is counted by weight base unit weight of rectorite, the nanometer mesoporous aluminas additive amount is
4%, nanometer Mayan indigo plant additive amount is 10%;Mixed solution is sodium alginate and sodium carbonate and mixed aqueous solution, wherein alginic acid
Sodium mass percentage is 2%, and sodium carbonate mass percentage is 5%.
Wherein, antibacterial agent is monomethyl fumarate, the methyl carbamate mixture of the mass ratio of the material 0.6:1;Aromatic
For Rosa Damascana, cortex albiziae essential oil composition;Surfactant is lauryl glucosyl, the alkanolamide of mass ratio 2:1
Mixture.
Textile fabric formaldehyde expellent preparation step is as follows: 1- vinyl imidazole, methyl guanamines, guanylurea phosphate is total
It is mixed, the distilled water of 6-7 times of three's gross mass, 60 DEG C of stirring 15-20min, then by nano modification rectorite, table are added thereto
Face activating agent, polyvinyl alcohol are added thereto, constant temperature oscillation 40-60min, then other surplus stocks are added thereto and continue constant temperature vibration
Processing 30-40min is swung, filtering is drying to obtain textile fabric formaldehyde expellent.
Embodiment 2:
A kind of textile fabric formaldehyde expellent, including following parts by weight component: 10 parts of nano modification rectorite, 1- ethylene
3 parts of base imidazoles, 1 part of methyl guanamines, 0.2 part of guanylurea phosphate, 1.2 parts of antibacterial agent, 1.5 parts of aromatic, surfactant 0.4
Part, 8 parts of polyvinyl alcohol, distillation appropriate amount of water.
Wherein, nano modification rectorite is specially nanometer mesoporous aluminas/nanometer Mayan indigo plant property of modified rectorite, preparation step
It is as follows: rectorite to be added in the distilled water of its 10 times of quality, be placed in 75 DEG C of high-speed stirred 5min in dispersion machine, then thereto
Addition accounts for the octadecyltrimethylammonium chloride of rectorite quality 3% and accounts for the mixed solution of rectorite quality 5%, continues high speed
30-40min is stirred, powder is freeze-dried to obtain;Powder, nanometer mesoporous aluminas, nanometer Mayan indigo plant are blended, are placed in ball mill
Ball milling ball milling 8-10h, after taking out drying.It is counted by weight base unit weight of rectorite, the nanometer mesoporous aluminas additive amount is
7%, nanometer Mayan indigo plant additive amount is 8%;Mixed solution is sodium alginate and sodium carbonate and mixed aqueous solution, wherein sodium alginate
Mass percentage is 3%, and sodium carbonate mass percentage is 6%.
Wherein, antibacterial agent is monomethyl fumarate, the methyl carbamate mixture of the mass ratio of the material 0.8:1;Aromatic
For Rosa Damascana, aloe essential oil composition;Surfactant is the lauryl glucosyl of mass ratio 2:1, alkanolamide
Mixture.
Textile fabric formaldehyde expellent preparation step is as follows: 1- vinyl imidazole, methyl guanamines, guanylurea phosphate is total
It is mixed, the distilled water of 6-7 times of three's gross mass, 60 DEG C of stirring 15-20min, then by nano modification rectorite, table are added thereto
Face activating agent, polyvinyl alcohol are added thereto, constant temperature oscillation 40-60min, then other surplus stocks are added thereto and continue constant temperature vibration
Processing 30-40min is swung, filtering is drying to obtain textile fabric formaldehyde expellent.
Embodiment 3:
A kind of textile fabric formaldehyde expellent, including following parts by weight component: 8 parts of nano modification rectorite, 1- ethylene
2 parts of base imidazoles, 4 parts of methyl guanamines, 0.7 part of guanylurea phosphate, 1.5 parts of antibacterial agent, 0.5 part of aromatic, surfactant 0.2
Part, 3 parts of polyvinyl alcohol, distillation appropriate amount of water.
Wherein, nano modification rectorite is specially nanometer mesoporous aluminas/nanometer Mayan indigo plant property of modified rectorite, preparation step
It is as follows: rectorite to be added in the distilled water of its 10 times of quality, be placed in 75 DEG C of high-speed stirred 5min in dispersion machine, then thereto
Addition accounts for the octadecyltrimethylammonium chloride of rectorite quality 3% and accounts for the mixed solution of rectorite quality 5%, continues high speed
30-40min is stirred, powder is freeze-dried to obtain;Powder, nanometer mesoporous aluminas, nanometer Mayan indigo plant are blended, are placed in ball mill
Ball milling ball milling 8-10h, after taking out drying.It is counted by weight base unit weight of rectorite, the nanometer mesoporous aluminas additive amount is
5%, nanometer Mayan indigo plant additive amount is 5%;Mixed solution is sodium alginate and sodium carbonate and mixed aqueous solution, wherein sodium alginate
Mass percentage is 1%, and sodium carbonate mass percentage is 2%.
Wherein, antibacterial agent is monomethyl fumarate, the methyl carbamate mixture of the mass ratio of the material 0.5:1;Aromatic
For aloe essential oil;Surfactant is the mixture of the lauryl glucosyl of mass ratio 2:1, alkanolamide.
Textile fabric formaldehyde expellent preparation step is as follows: 1- vinyl imidazole, methyl guanamines, guanylurea phosphate is total
It is mixed, the distilled water of 6-7 times of three's gross mass, 60 DEG C of stirring 15-20min, then by nano modification rectorite, table are added thereto
Face activating agent, polyvinyl alcohol are added thereto, constant temperature oscillation 40-60min, then other surplus stocks are added thereto and continue constant temperature vibration
Processing 30-40min is swung, filtering is drying to obtain textile fabric formaldehyde expellent.
Embodiment 4:
A kind of textile fabric formaldehyde expellent, including following parts by weight component: 14 parts of nano modification rectorite, 1- ethylene
5 parts of base imidazoles, 3 parts of methyl guanamines, 0.5 part of guanylurea phosphate, 1.8 parts of antibacterial agent, 1.7 parts of aromatic, surfactant 0.1
Part, 6 parts of polyvinyl alcohol, distillation appropriate amount of water.
Wherein, nano modification rectorite is specially nanometer mesoporous aluminas/nanometer Mayan indigo plant property of modified rectorite, preparation step
It is as follows: rectorite to be added in the distilled water of its 10 times of quality, be placed in 75 DEG C of high-speed stirred 5min in dispersion machine, then thereto
Addition accounts for the octadecyltrimethylammonium chloride of rectorite quality 3% and accounts for the mixed solution of rectorite quality 5%, continues high speed
30-40min is stirred, powder is freeze-dried to obtain;Powder, nanometer mesoporous aluminas, nanometer Mayan indigo plant are blended, are placed in ball mill
Ball milling ball milling 8-10h, after taking out drying.It is counted by weight base unit weight of rectorite, the nanometer mesoporous aluminas additive amount is
1%, nanometer Mayan indigo plant additive amount is 6%;Mixed solution is sodium alginate and sodium carbonate and mixed aqueous solution, wherein sodium alginate
Mass percentage is 2%, and sodium carbonate mass percentage is 7%.
Wherein, antibacterial agent is monomethyl fumarate, the methyl carbamate mixture of the mass ratio of the material 0.6:1;Aromatic
For Rosa Damascana, Peppermint essential oil, clove oil composition;Surfactant is lauryl glucosyl, the alkane of mass ratio 2:1
The mixture of alkylolamides.
Textile fabric formaldehyde expellent preparation step is as follows: 1- vinyl imidazole, methyl guanamines, guanylurea phosphate is total
It is mixed, the distilled water of 6-7 times of three's gross mass, 60 DEG C of stirring 15-20min, then by nano modification rectorite, table are added thereto
Face activating agent, polyvinyl alcohol are added thereto, constant temperature oscillation 40-60min, then other surplus stocks are added thereto and continue constant temperature vibration
Processing 30-40min is swung, filtering is drying to obtain textile fabric formaldehyde expellent.
Formaldehyde expellent made from the embodiment of the present invention 1 is configured to solution (solid-to-liquid ratio 1:10), is then added
In the formaldehyde standard solution of 0.1mg/ml, under confined conditions, sufficiently oscillation mixing detects through spectrophotometer, aldehyde is removed after 10min
Rate up to after 80%, 20min remove aldehyde rate up to 99%.
Formaldehyde expellent made from the embodiment of the present invention 1 is configured to solution (solid-to-liquid ratio 1:10), by fabric to be processed
(content of formaldehyde 476.6-512.7mg/kg) is placed in solution, is cleaned fabric with clear water after immersion 20min under room temperature, is surveyed
Obtaining content of formaldehyde on fabric is 48.7-62.4mg/kg, meets national standard, and fabric carries out tracking and monitoring, 2- to treated
Content of formaldehyde is less than 5mg/kg on fabric after 2.5h.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features;And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (8)
1. a kind of textile fabric formaldehyde expellent, which is characterized in that including following parts by weight component: nano modification rectorite 8-
14 parts, 2-5 parts of 1- vinyl imidazole, 1-4 parts of methyl guanamines, 0.2-0.7 parts of guanylurea phosphate, 1.2-1.8 parts of antibacterial agent, fragrance
0.5-2 parts of agent, 0.1-0.4 parts of surfactant, 3-8 parts of polyvinyl alcohol, distillation appropriate amount of water;The nano modification rectorite is specific
For nanometer mesoporous aluminas/nanometer Mayan indigo plant property of modified rectorite, preparation step is as follows: rectorite is added to the steaming of its 10 times of quality
In distilled water, 75 DEG C of high-speed stirred 5min in dispersion machine are placed in, the octadecyl three for accounting for rectorite quality 3% is then added thereto
Ammonio methacrylate and the mixed solution for accounting for rectorite quality 5% continue high-speed stirred 30-40min, are freeze-dried to obtain powder;It will
Powder, nanometer mesoporous aluminas, nanometer Mayan indigo plant are blended, and are placed in ball milling ball milling 8-10h in ball mill, after taking out drying.
2. textile fabric formaldehyde expellent according to claim 1, it is characterised in that: it is counted by weight base unit weight of rectorite,
The nanometer mesoporous aluminas additive amount is 1-7%, and nanometer Mayan indigo plant additive amount is 5-10%.
3. textile fabric formaldehyde expellent according to claim 1, it is characterised in that: the mixed solution is sodium alginate
With the mixed aqueous solution of sodium carbonate, wherein sodium alginate mass percentage is 1-3%, and sodium carbonate mass percentage is 2-
7%.
4. textile fabric formaldehyde expellent according to claim 1, it is characterised in that: the antibacterial agent is the mass ratio of the material
Monomethyl fumarate, the methyl carbamate mixture of 0.5-0.8:1.
5. textile fabric formaldehyde expellent according to claim 1, it is characterised in that: the aromatic be Rosa Damascana,
One of aloe essential oil, Radix Glycyrrhizae essential oil, Peppermint essential oil, clove oil, silk tree peel essential oil or numerous compositions.
6. textile fabric formaldehyde expellent according to claim 1, it is characterised in that: the surfactant is mass ratio
The mixture of the lauryl glucosyl of 2:1, alkanolamide.
7. textile fabric formaldehyde expellent according to claim 1-6, which is characterized in that preparation step is as follows:
1- vinyl imidazole, methyl guanamines, guanylurea phosphate are blended, thereto the distilled water of 6-7 times of three's gross mass of addition, 60 DEG C
15-20min is stirred, is then added thereto nano modification rectorite, surfactant, polyvinyl alcohol, constant temperature oscillation 40-
60min, then other surplus stocks are added thereto and continue constant temperature oscillation processing 30-40min, filtering is drying to obtain textile fabric
Formaldehyde expellent.
8. the application of the textile fabric formaldehyde expellent as made from claim 7, it is characterised in that: by textile fabric formaldehyde
Expellent and distilled water are configured to solution by solid-to-liquid ratio 0.5-1:10 and use.