CN107083593A - A kind of textile material and preparation method thereof - Google Patents
A kind of textile material and preparation method thereof Download PDFInfo
- Publication number
- CN107083593A CN107083593A CN201710229427.2A CN201710229427A CN107083593A CN 107083593 A CN107083593 A CN 107083593A CN 201710229427 A CN201710229427 A CN 201710229427A CN 107083593 A CN107083593 A CN 107083593A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- textile material
- preparation
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of textile material and preparation method thereof.The textile material is made up of the component comprising following parts by weight：15 20 parts of cotton fiber, 25 40 parts of bamboo-carbon fibre, 10 15 parts of acrylic fibers, 10 20 parts of bark fiber, 10 20 parts of coconut fibre, 10 20 parts of abutilon fibre, 35 parts of tuber of pinellia fiber.The textile material of the present invention is except with the performance that traditional textile material is soft and absorbs water, also there is sterilization, the effect of deinsectization, introduce bark fiber and add toughness and elasticity so that the fabric cleaned easily recovers elasticity, introduce abutilon fibre and tuber of pinellia fiber causes material to have desinsection, degerming effect, the preparation method of the textile material of the present invention is simple, and raw material sources are wide, is adapted to large-scale industrial production.
Description
Technical field
The invention belongs to textile material technical field, and in particular to a kind of warming, moisture absorption, antibacterial, the textile material of insect prevention
And preparation method thereof.
Background technology
With the development and the continuous improvement of human demand of technology, textile technology develops towards personalized direction, weaves
It is very soft that material can be done, and what can also be done is unusually strong, and toughness is strong.Textile material for baby typically requires soft and inhaled
Water, still, soft and water suction the easy breed bacteria of material also easily attract mosquito, are unfavorable for the healthy of baby, weaves
The cotton-wadded quilt that material is made, the problem of in order to solve above-mentioned, the general method using addition anthelmintic drug and antibacterial medicines, baby children
Youngster, which often eats by mistake, causes stomach to damage, the strong cotton-wadded quilt of absorbent material by diaper for baby it is wet after, it is not easy to clean, also do not allow after cleaning
Easily dry, be not easy to recover soft and elasticity after drying, can typically become stone, therefore, the cotton-wadded quilt that such material is made, cotton
The infants such as clothing are relatively low with the general service life of material.
The content of the invention
It is an object of the invention to provide a kind of warming, moisture absorption, antibacterial, the textile material of insect prevention.
The present invention also aims to provide the preparation method of above-mentioned textile material.
A kind of textile material, the textile material is made up of the component comprising following parts by weight：15-20 parts of cotton fiber, bamboo
25-40 parts of Carbon fibe, 10-15 parts of acrylic fibers, 10-20 parts of bark fiber, 10-20 parts of coconut fibre, 10-20 parts of abutilon fibre, half
Fiber 3-5 parts of summer.
The bark fiber is Chinese tamarisk hide fiber, elm bast, Oak Tree hide fiber, acacia hide fiber, paper mulberry hide fiber
In one or more.
The preparation method of the Chinese tamarisk hide fiber or elm bast is：Take Chinese tamarisk skin or elm bark to dry, it is artificial or
Machinery is beaten into silk, is soaked 1-3 days in mass fraction 1-3% buck, plus acetic acid is neutralized to pH=6.5-7.5, pulls out, clearly
Water is rinsed 3-6 times, is dried, is made.
The preparation method of the Oak Tree hide fiber or acacia hide fiber is：Take oak bark or acacia skin to dry, it is artificial or
Machinery is beaten into silk, is soaked 1-3 days in mass fraction 1-3% acetum, plus limewash is neutralized to pH=6.5-7.5,
Pull out, clear water is rinsed 3-6 times, is dried, is made.
The preparation method of the paper mulberry hide fiber is：Tapa is taken, tapa is soaked in 1-2% aqueous tartaric acid solution
Middle immersion 10-30 days, is pulled out, and clear water is rinsed 3-6 times, and artificial or machinery is beaten into silk, is rinsed 3-6 times with clear water again,
Dry, be made.
The preparation method of the abutilon fibre is：Piemarker skin is taken, tapa is soaked in 30% aqueous solution of propylene glycol and soaked
Bubble 10-30 days, is pulled out, and clear water is rinsed 3-6 times, and artificial or machinery is beaten into silk, is rinsed 3-6 times, dried with clear water again,
It is made.
The preparation method of the tuber of pinellia fiber is：Tuber of pinellia cauline leaf is taken, is placed in boiling water and boils 2-4 hours, pull out, manually
Or machinery is beaten into silk, is rinsed 3-6 times with clear water, is dried, be made.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Beneficial effects of the present invention：The textile material of the present invention is except with the property that traditional textile material is soft and absorbs water
Can, also with sterilization, the effect of deinsectization introduces bark fiber and adds toughness and elasticity so that the fabric cleaned is easily extensive
Complex elasticity, introduces abutilon fibre and tuber of pinellia fiber and causes material to have a desinsection, degerming effect, the system of textile material of the invention
Preparation Method is simple, and raw material sources are wide, is adapted to large-scale industrial production.
Embodiment
With reference to specific embodiment, the present invention will be further described.
In following embodiments, the preparation method of the Chinese tamarisk hide fiber or elm bast is：Take Chinese tamarisk skin or elm bark
Dry, artificial or machinery is beaten into silk, is soaked 1-3 days in mass fraction 1-3% buck, plus acetic acid be neutralized to pH=
6.5-7.5, is pulled out, and clear water is rinsed 3-6 times, is dried, is made.
In following embodiments, the preparation method of the Oak Tree hide fiber or acacia hide fiber is：Take oak bark or acacia skin
Dry, artificial or machinery is beaten into silk, is soaked 1-3 days in mass fraction 1-3% acetum, plus limewash is neutralized
To pH=6.5-7.5, pull out, clear water is rinsed 3-6 times, is dried, is made.
In following embodiments, the preparation method of the paper mulberry hide fiber is：Tapa is taken, tapa is soaked in 1-2%'s
Soak 10-30 days, pull out in aqueous tartaric acid solution, clear water is rinsed 3-6 times, artificial or machinery is beaten into silk, again with clear
Water is rinsed 3-6 times, is dried, is made.
In following embodiments, the preparation method of the abutilon fibre is：Piemarker skin is taken, tapa is soaked in the third of 30%
Soak 10-30 days, pull out in two alcohol solutions, clear water is rinsed 3-6 times, artificial or machinery is beaten into silk, and clear water is used again
Rinsing 3-6 times, dries, is made.
In following embodiments, the preparation method of the tuber of pinellia fiber is：Tuber of pinellia cauline leaf is taken, is placed in boiling water and boils 2-4
Hour, pull out, artificial or machinery is beaten into silk, is rinsed 3-6 times with clear water, is dried, be made.
Embodiment 1
A kind of textile material, the textile material is made up of the component comprising following parts by weight：18 parts of cotton fiber, bamboo-carbon fibre 30
Part, 12 parts of acrylic fibers, 15 parts of Chinese tamarisk hide fiber, 15 parts of coconut fibre, 15 parts of abutilon fibre, 4 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, is cleaned 8-10 times, material starts to be hardened, it is impossible to be continuing with, moreover it is possible to anti-
Bacterium（Common pathogen staphylococcus aureus, Escherichia coli O 157, Candida albicans etc.）, moreover it is possible to insect prevention（Acarid, flea, lice
Son, common house centipede, silverfish, tick worm etc. is common to control disease and insect）.
Embodiment 2
A kind of textile material, the textile material is made up of the component comprising following parts by weight：15 parts of cotton fiber, bamboo-carbon fibre 25
Part, 10 parts of acrylic fibers, 10 parts of elm bast, 10 parts of coconut fibre, 10 parts of abutilon fibre, 3 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, is cleaned 8-10 times, material starts to be hardened, it is impossible to be continuing with, moreover it is possible to anti-
Bacterium（Common pathogen staphylococcus aureus, Escherichia coli O 157, Candida albicans etc.）, moreover it is possible to insect prevention（Acarid, flea, lice
Son, common house centipede, silverfish, tick worm etc. is common to control disease and insect）.
Embodiment 3
A kind of textile material, the textile material is made up of the component comprising following parts by weight：20 parts of cotton fiber, bamboo-carbon fibre 40
Part, 15 parts of acrylic fibers, 20 parts of Oak Tree hide fiber, 20 parts of coconut fibre, 20 parts of abutilon fibre, 5 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, is cleaned 8-10 times, material starts to be hardened, it is impossible to be continuing with, moreover it is possible to anti-
Bacterium（Common pathogen staphylococcus aureus, Escherichia coli O 157, Candida albicans etc.）, moreover it is possible to insect prevention（Acarid, flea, lice
Son, common house centipede, silverfish, tick worm etc. is common to control disease and insect）.
Embodiment 4
A kind of textile material, the textile material is made up of the component comprising following parts by weight：16 parts of cotton fiber, bamboo-carbon fibre 28
Part, 13 parts of acrylic fibers, 17 parts of acacia hide fiber, 15 parts of coconut fibre, 18 parts of abutilon fibre, 4 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, is cleaned 8-10 times, material starts to be hardened, it is impossible to be continuing with, moreover it is possible to anti-
Bacterium（Common pathogen staphylococcus aureus, Escherichia coli O 157, Candida albicans etc.）, moreover it is possible to insect prevention（Acarid, flea, lice
Son, common house centipede, silverfish, tick worm etc. is common to control disease and insect）.
Embodiment 5
A kind of textile material, the textile material is made up of the component comprising following parts by weight：18 parts of cotton fiber, bamboo-carbon fibre 25
Part, 13 parts of acrylic fibers, 15 parts of paper mulberry hide fiber, 18 parts of coconut fibre, 12 parts of abutilon fibre, 4 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, is cleaned 8-10 times, material starts to be hardened, it is impossible to be continuing with, moreover it is possible to anti-
Bacterium（Common pathogen staphylococcus aureus, Escherichia coli O 157, Candida albicans etc.）, moreover it is possible to insect prevention（Acarid, flea, lice
Son, common house centipede, silverfish, tick worm etc. is common to control disease and insect）.
Embodiment 5
A kind of textile material, the textile material is made up of the component comprising following parts by weight：18 parts of cotton fiber, bamboo-carbon fibre 25
Part, 13 parts of acrylic fibers, 15 parts of paper mulberry hide fiber, 18 parts of coconut fibre, 12 parts of abutilon fibre, 4 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out add 0.5 part of lapis lazuli powder and 0.5 part of glycerine, knead and be sufficiently mixed,
Then mix, and be twisted together with other components of formula ratio；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, is cleaned 28 times, material softness, and 50 materials of cleaning start to be hardened, it is impossible to
It is continuing with, moreover it is possible to antibacterial（Common pathogen staphylococcus aureus, Escherichia coli O 157, Candida albicans etc.）, moreover it is possible to it is anti-
Worm（Acarid, flea, louse, common house centipede, silverfish, tick worm etc. is common to control disease and insect）.
Comparative example 1
A kind of textile material, the textile material is made up of the component comprising following parts by weight：18 parts of cotton fiber, bamboo-carbon fibre 30
Part, 12 parts of acrylic fibers, 15 parts of coconut fibre, 15 parts of abutilon fibre, 4 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, but cleaned material after 1 time and be hardened, it is impossible to it is continuing with, moreover it is possible to anti-
Bacterium（Common pathogen staphylococcus aureus, Escherichia coli O 157, Candida albicans etc.）, moreover it is possible to insect prevention（Acarid, flea, lice
Son, common house centipede, silverfish, tick worm etc. is common to control disease and insect）.
Comparative example 2
A kind of textile material, the textile material is made up of the component comprising following parts by weight：18 parts of cotton fiber, bamboo-carbon fibre 30
Part, 12 parts of acrylic fibers, 15 parts of Chinese tamarisk hide fiber, 15 parts of coconut fibre, 4 parts of tuber of pinellia fiber.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, it is impossible to antibacterial, can insect prevention（Acarid, flea, louse, common house centipede, silverfish, tick
Worm etc. is common to control disease and insect）.
Comparative example 3
A kind of textile material, the textile material is made up of the component comprising following parts by weight：18 parts of cotton fiber, bamboo-carbon fibre 30
Part, 12 parts of acrylic fibers, 15 parts of Chinese tamarisk hide fiber, 15 parts of coconut fibre, 15 parts of abutilon fibre.
The preparation method of above-mentioned textile material, is carried out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.
Prepared textile material flexible absorbent, moreover it is possible to antibacterial（Common pathogen staphylococcus aureus, Escherichia coli
O157, Candida albicans etc.）, it is impossible to insect prevention.
Claims (8)
1. a kind of textile material, it is characterised in that the textile material is made up of the component comprising following parts by weight：Cotton fiber
15-20 parts, 25-40 parts of bamboo-carbon fibre, 10-15 parts of acrylic fibers, 10-20 parts of bark fiber, 10-20 parts of coconut fibre, abutilon fibre
10-20 parts, 3-5 parts of tuber of pinellia fiber.
2. a kind of textile material according to claim 1, it is characterised in that the bark fiber is Chinese tamarisk hide fiber, elm
One or more in hide fiber, Oak Tree hide fiber, acacia hide fiber, paper mulberry hide fiber.
3. a kind of textile material according to claim 2, it is characterised in that the system of the Chinese tamarisk hide fiber or elm bast
Preparation Method is：Chinese tamarisk skin or elm bark is taken to dry, artificial or machinery is beaten into silk, is soaked in mass fraction 1-3% buck
Bubble 1-3 days, plus acetic acid are neutralized to pH=6.5-7.5, pull out, and clear water is rinsed 3-6 times, is dried, is made.
4. a kind of textile material according to claim 2, it is characterised in that the system of the Oak Tree hide fiber or acacia hide fiber
Preparation Method is：Oak bark or acacia skin is taken to dry, artificial or machinery is beaten into silk, in mass fraction 1-3% acetum
Middle immersion 1-3 days, plus limewash are neutralized to pH=6.5-7.5, pull out, and clear water is rinsed 3-6 times, is dried, is made.
5. a kind of textile material according to claim 2, it is characterised in that the preparation method of the paper mulberry hide fiber is：Take
Tapa, tapa is soaked in 1-2% aqueous tartaric acid solution and soaked 10-30 days, pulled out, clear water rinsing 3-6 times, manually
Or machinery is beaten into silk, is rinsed 3-6 times with clear water again, is dried, be made.
6. a kind of textile material according to claim 1, it is characterised in that the preparation method of the abutilon fibre is：Take piemarker
Hemp skin, tapa is soaked in 30% aqueous solution of propylene glycol soak 10-30 days, pull out, clear water rinse 3-6 times, manually or
Machinery is beaten into silk, is rinsed 3-6 times with clear water again, is dried, be made.
7. a kind of textile material according to claim 1, it is characterised in that the preparation method of the tuber of pinellia fiber is：Take half
Summer cauline leaf, is placed in boiling water and boils 2-4 hours, pull out, and artificial or machinery is beaten into silk, is rinsed 3-6 times with clear water, is shone
It is dry, it is made.
8. the preparation method of textile material described in claim 1, it is characterised in that carry out in accordance with the following steps：
1) by cotton fiber, fiber-spinnable is made in bamboo-carbon fibre and acrylic fibers；
2) by cotton fiber, bamboo-carbon fibre and acrylic fibers cut-out, and mixed with other components of formula ratio, and be twisted together；
3) compound strip can be spun by being combed into the yarn component twisted with the fingers with after using carding machine, and drafting；
4) the compound strip after drafting is combed into after combed sliver, then through rove-spun yarn-winder is into yarn, then pass through spiral
It is twisted together on core.