CN107082630A - It is a kind of for the novel ceramic tile in kitchen and preparation method thereof - Google Patents

It is a kind of for the novel ceramic tile in kitchen and preparation method thereof Download PDF

Info

Publication number
CN107082630A
CN107082630A CN201710471151.9A CN201710471151A CN107082630A CN 107082630 A CN107082630 A CN 107082630A CN 201710471151 A CN201710471151 A CN 201710471151A CN 107082630 A CN107082630 A CN 107082630A
Authority
CN
China
Prior art keywords
parts
ceramic tile
kitchen
novel ceramic
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710471151.9A
Other languages
Chinese (zh)
Inventor
俞克波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Feixi Bitao Building Material Co Ltd
Original Assignee
Feixi Bitao Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Feixi Bitao Building Material Co Ltd filed Critical Feixi Bitao Building Material Co Ltd
Priority to CN201710471151.9A priority Critical patent/CN107082630A/en
Publication of CN107082630A publication Critical patent/CN107082630A/en
Withdrawn legal-status Critical Current

Abstract

The present invention provides a kind of for the novel ceramic tile in kitchen and preparation method thereof, and its composition includes silica, clay, yellow sand, sodium carbonate, Paris white, graphite powder, adhesive, nicotine, hederin, Herba Asari volatile oil, forsythol, granatum bitter principle, saponarin and strumaroside.Ceramic tile produced by the present invention is compared to common ceramic tile, and its special composition added has the effect of deodorization, deinsectization, and the corrosion resistance of ceramic tile is strong, is particularly suitable for use in environment as kitchen.

Description

It is a kind of for the novel ceramic tile in kitchen and preparation method thereof
Technical field
The invention belongs to building material technical field, and in particular to a kind of novel ceramic tile and its preparation side for kitchen Method.
Background technology
With the raising of ceramic tile production technology, the species of tile product is more and more, including polished bricks, glazed tile, entire body Brick, vitrified tile, ceramic veneer etc., the application of ceramic tile are also increasingly wider, from residential building to office building, from indoor to family Outside, everywhere it can be seen that the use of ceramic tile.
But existing ceramic tile hardness is not high, it is easily damaged in transportation or during installing, and it is existing The high ceramic tile of hardness is mostly heavier, so that cost of transportation is greatly added again, and existing ceramic tile did not also occur Targetedly use scope, it is therefore desirable to which a kind of cost is low and has the ceramic tile of the specific aim scope of application.
The content of the invention
It is with low cost and with pin it is an object of the invention to provide a kind of for the novel ceramic tile in kitchen and preparation method thereof To the property scope of application, hardness is high and quality is light.
The invention provides following technical scheme：
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：10-15 parts of silica, 10-25 parts of clay, yellow sand Native 10-25 parts, 10-23 parts of sodium carbonate, 5-15 parts of Paris white, 5-14 parts of graphite powder, 5-16 parts of adhesive, 10-20 parts of nicotine, 7-15 parts of hederin, 10-18 parts of Herba Asari volatile oil, 8-18 parts of forsythol, 5-10 parts of granatum bitter principle, saponarin 20-30 20-35 parts of part and strumaroside.
It is preferred that, the Ingredients Weight composition number is：12-15 parts of silica, 14-25 parts of clay, yellow sand 16-25 Part, 17-23 parts of sodium carbonate, 7-15 parts of Paris white, 8-14 parts of graphite powder, 9-16 parts of adhesive, 14-20 parts of nicotine, ivy 11-15 parts of glucoside, 12-18 parts of Herba Asari volatile oil, 13-18 parts of forsythol, 7-10 parts of granatum bitter principle, 22-30 parts of saponarin and 26-35 parts of strumaroside.
It is preferred that, the Ingredients Weight composition number is：12 parts of silica, 14 parts of clay, 25 parts of yellow sand, sodium carbonate 23 Part, 7 parts of Paris white, 8 parts of graphite powder, 16 parts of adhesive, 20 parts of nicotine, 11 parts of hederin, 12 parts of Herba Asari volatile oil, the capsule of weeping forsythia 26 parts of 18 parts of phenol, 10 parts of granatum bitter principle, 22 parts of saponarin and strumaroside.
It is preferred that, described adhesive is any of butyl rubber, chlorinated rubber, acrylic resin or shellac.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 20-40Mpa, obtain base substrate；
Step 3: by part drying process, water content control is in 0.5-1.5%；
Step 4: step 3 product is soaked into glaze, 20-40min shapings are fired in 1000-1200 DEG C, then carry out edging, polish i.e. Can.
It is preferred that, the step 2 pressure is 20Mpa.
It is preferred that, the step 3 water content is 0.5%.
It is preferred that, the step 4 firing time is 40min.
The beneficial effects of the invention are as follows：With low cost, obtained ceramic tile is compared to common ceramic tile, and hardness is high, quality is light, tool Targetedly, the special composition of its addition has the effect of deodorization, deinsectization, and the corrosion resistance of ceramic tile is strong, is particularly suitable for use in kitchen Such environment.
Embodiment
Embodiment 1
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：10 parts of silica, 10 parts of clay, 10 parts of yellow sand, 10 parts of sodium carbonate, 5 parts of Paris white, 5 parts of graphite powder, 5 parts of adhesive, 10 parts of nicotine, 7 parts of hederin, Herba Asari volatile oil 10 Part, 8 parts of forsythol, 5 parts of granatum bitter principle, 20 parts of saponarin and 20 parts of strumaroside.
Adhesive is butyl rubber.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 20Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 0.5%；
Step 4: step 3 product is soaked into glaze, 20min shapings are fired in 1000 DEG C, then carry out edging, polishing.
Embodiment 2
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：15 parts of silica, 25 parts of clay, 25 parts of yellow sand, 23 parts of sodium carbonate, 15 parts of Paris white, 14 parts of graphite powder, 16 parts of adhesive, 20 parts of nicotine, 15 parts of hederin, asarum volatilization 35 parts of 18 parts of oil, 18 parts of forsythol, 10 parts of granatum bitter principle, 30 parts of saponarin and strumaroside.
Adhesive is acrylic resin.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 40Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 1.5%；
Step 4: step 3 product is soaked into glaze, 40min shapings are fired in 1200 DEG C, then carry out edging, polishing.
Embodiment 3
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：12 parts of silica, 14 parts of clay, 16 parts of yellow sand, 17 parts of sodium carbonate, 7 parts of Paris white, 8 parts of graphite powder, 9 parts of adhesive, 14 parts of nicotine, 11 parts of hederin, Herba Asari volatile oil 12 Part, 13 parts of forsythol, 7 parts of granatum bitter principle, 22 parts of saponarin and 26 parts of strumaroside.
Adhesive is chlorinated rubber.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 24Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 1%；
Step 4: step 3 product is soaked into glaze, 24min shapings are fired in 1100 DEG C, then carry out edging, polishing.
Embodiment 4
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：12 parts of silica, 14 parts of clay, 25 parts of yellow sand, 23 parts of sodium carbonate, 7 parts of Paris white, 8 parts of graphite powder, 16 parts of adhesive, 20 parts of nicotine, 11 parts of hederin, Herba Asari volatile oil 26 parts of 12 parts, 18 parts of forsythol, 10 parts of granatum bitter principle, 22 parts of saponarin and strumaroside.
Adhesive is shellac.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 20Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 0.5%；
Step 4: step 3 product is soaked into glaze, 40min shapings are fired in 1200 DEG C, then carry out edging, polishing.
Embodiment 5
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：10 parts of silica, 10 parts of clay, 10 parts of yellow sand, 10 parts of sodium carbonate, 5 parts of Paris white, 8 parts of graphite powder, 16 parts of adhesive, 20 parts of nicotine, 11 parts of hederin, Herba Asari volatile oil 26 parts of 12 parts, 18 parts of forsythol, 10 parts of granatum bitter principle, 22 parts of saponarin and strumaroside.
Adhesive is shellac.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 20Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 0.5%；
Step 4: step 3 product is soaked into glaze, 40min shapings are fired in 1200 DEG C, then carry out edging, polishing.
Embodiment 6
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：12 parts of silica, 14 parts of clay, 16 parts of yellow sand, 17 parts of sodium carbonate, 7 parts of Paris white, 8 parts of graphite powder, 16 parts of adhesive, 20 parts of nicotine, 15 parts of hederin, Herba Asari volatile oil 35 parts of 18 parts, 18 parts of forsythol, 10 parts of granatum bitter principle, 30 parts of saponarin and strumaroside.
Adhesive is butyl rubber.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 20Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 0.5%；
Step 4: step 3 product is soaked into glaze, 20min shapings are fired in 1000 DEG C, then carry out edging, polishing.
Embodiment 7
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：12 parts of silica, 14 parts of clay, 25 parts of yellow sand, 23 parts of sodium carbonate, 7 parts of Paris white, 14 parts of graphite powder, 16 parts of adhesive, 20 parts of nicotine, 15 parts of hederin, Herba Asari volatile oil 35 parts of 18 parts, 18 parts of forsythol, 10 parts of granatum bitter principle, 30 parts of saponarin and strumaroside.
Adhesive is acrylic resin.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 40Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 1.5%；
Step 4: step 3 product is soaked into glaze, 40min shapings are fired in 1200 DEG C, then carry out edging, polishing.
Embodiment 8
A kind of novel ceramic tile for kitchen, Ingredients Weight constitutes number and is：12 parts of silica, 14 parts of clay, 16 parts of yellow sand, 17 parts of sodium carbonate, 7 parts of Paris white, 8 parts of graphite powder, 9 parts of adhesive, 14 parts of nicotine, 11 parts of hederin, Herba Asari volatile oil 18 Part, 18 parts of forsythol, 10 parts of granatum bitter principle, 30 parts of saponarin and 35 parts of strumaroside.
Adhesive is shellac.
A kind of preparation method of novel ceramic tile for kitchen, comprises the following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 30Mpa, obtain base substrate；
Step 3: by part drying process, water content control is 0.5%；
Step 4: step 3 product is soaked into glaze, 40min shapings are fired in 1100 DEG C, then carry out edging, polishing.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.

Claims (8)

1. a kind of novel ceramic tile for kitchen, it is characterised in that the Ingredients Weight constitutes number and is：10-15 parts of silica, 10-25 parts of clay, 10-25 parts of yellow sand, 10-23 parts of sodium carbonate, 5-15 parts of Paris white, 5-14 parts of graphite powder, adhesive 5- 16 parts, 10-20 parts of nicotine, 7-15 parts of hederin, 10-18 parts of Herba Asari volatile oil, 8-18 parts of forsythol, granatum bitter principle 5-10 20-35 parts of part, 20-30 parts of saponarin and strumaroside.
2. a kind of novel ceramic tile for kitchen according to claim 1, it is characterised in that the Ingredients Weight constitutes part Number is：12-15 parts of silica, 14-25 parts of clay, 16-25 parts of yellow sand, 17-23 parts of sodium carbonate, 7-15 parts of Paris white, stone 8-14 parts of ink powder, 9-16 parts of adhesive, 14-20 parts of nicotine, 11-15 parts of hederin, 12-18 parts of Herba Asari volatile oil, forsythol 26-35 parts of 13-18 parts, 7-10 parts of granatum bitter principle, 22-30 parts of saponarin and strumaroside.
3. a kind of novel ceramic tile for kitchen according to claim 1, it is characterised in that the Ingredients Weight constitutes part Number is：12 parts of silica, 14 parts of clay, 25 parts of yellow sand, 23 parts of sodium carbonate, 7 parts of Paris white, 8 parts of graphite powder, adhesive 16 Part, 20 parts of nicotine, 11 parts of hederin, 12 parts of Herba Asari volatile oil, 18 parts of forsythol, 10 parts of granatum bitter principle, saponarin 22 26 parts of part and strumaroside.
4. a kind of novel ceramic tile for kitchen according to claim any one of 1-3, it is characterised in that described adhesive For any of butyl rubber, chlorinated rubber, acrylic resin or shellac.
5. a kind of preparation method of novel ceramic tile for kitchen described in claim any one of 1-3, it is characterised in that including Following steps：
Step 1: raw material are well mixed, dry, grind；
Step 2: step one product is subjected to ball-milling treatment, and it is compressing under 20-40Mpa, obtain base substrate；
Step 3: by part drying process, water content control is in 0.5-1.5%；
Step 4: step 3 product is soaked into glaze, 20-40min shapings are fired in 1000-1200 DEG C, then carry out edging, polish i.e. Can.
6. a kind of preparation method of novel ceramic tile for kitchen according to claim 5, it is characterised in that the step Two pressure are 20Mpa.
7. a kind of preparation method of novel ceramic tile for kitchen according to claim 5, it is characterised in that the step Three water content are 0.5%.
8. a kind of preparation method of novel ceramic tile for kitchen according to claim 5, it is characterised in that the step Four firing times were 40min.
CN201710471151.9A 2017-06-20 2017-06-20 It is a kind of for the novel ceramic tile in kitchen and preparation method thereof Withdrawn CN107082630A (en)