CN105753323B - A kind of your porcelain preparation method of emerald green glaze - Google Patents

A kind of your porcelain preparation method of emerald green glaze Download PDF

Info

Publication number
CN105753323B
CN105753323B CN201610187865.2A CN201610187865A CN105753323B CN 105753323 B CN105753323 B CN 105753323B CN 201610187865 A CN201610187865 A CN 201610187865A CN 105753323 B CN105753323 B CN 105753323B
Authority
CN
China
Prior art keywords
glaze
green
raw
parts
kiln
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201610187865.2A
Other languages
Chinese (zh)
Other versions
CN105753323A (en
Inventor
杨云超
仝利军
Original Assignee
杨云超
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 杨云超 filed Critical 杨云超
Priority to CN201610187865.2A priority Critical patent/CN105753323B/en
Publication of CN105753323A publication Critical patent/CN105753323A/en
Application granted granted Critical
Publication of CN105753323B publication Critical patent/CN105753323B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of your porcelain preparation method of emerald green glaze, the emerald green glaze is matched by the following raw material and made:Tang's ditch soil 30%, half way up the mountain soil 30%, kaolin 40%, the glaze raw material tremolite 30%, feldspar 28%, dark stone 23%, calcite 2%, lamb bone meal 3%, in a word the present invention have the advantages that glaze layer it is transparent it is beautiful, workable, market prospects are good.

Description

A kind of your porcelain preparation method of emerald green glaze
Technical field
The invention belongs to ceramic preparation method fields, and in particular to a kind of your porcelain preparation method of emerald green glaze.
Background technology
The color matching of ceramics on current market is mostly using sky blue, the pure colors such as red or dark blue, this tradition Color matching increasingly can not meet the more and more personalized market demand, in Chinese civilization development history, Song Dynasty culture occupies pole Its important historical role, your culture of porcelain are an important component of Song Dynasty culture again, it is with its exquisite workmanship, moulding show U.S., glaze paint Yun Run, graceful plain charm and unique elegance are an epoch-making important marks in China's celadon development history Will, Ruyao porcelain tire is canescence, and the depth is different, all similar to the incense ashes after burning, thus be commonly called as " ash colour body " this be identification One of main points of Ruyao porcelain, Ruyao enamel key colour are a kind of light Celestes, are commonly called as " Ovum Anas domestica putamina cyan ", glaze layer is not Thickness with the transition variation of moulding, is presented the layer variability of the deep or light depth, exploration is carried out to your porcelain using the material of Ruzhou locality Innovation will be played the role of greatly facilitating to the development of your culture of porcelain.
The content of the invention
The object of the present invention is achieved like this:A kind of your porcelain preparation method of emerald green glaze, the emerald green glaze is by following former Material proportioning makes:Tang's ditch soil 30%, half way up the mountain soil 30%, kaolin 40%, the glaze raw material tremolite 30%, feldspar 28%, black stone First 23%, calcite 2%, lamb bone meal 3%.
The preparation process of the emerald green glaze is as follows:
Step 1: after the glaze raw material is crushed, it is mixed according to the above mentioned proportion to be put into ball crusher, it is total to add in mixed raw material The water of the 27%-35% of raw material gross weight, when start wet-milling 22-30 is small, wet-grinded slurry crosses 300 mesh sieves, and static 12 is small When, water content is detected using moisture teller, and water content is adjusted to 56%-62%, it is spare;
Step 2: carrying out wiping dedusting to biscuit with water, wiping is simultaneously by slurry obtained by step 1 by the clockwise or inverse time Pin direction is stirred, and during stirring since the center of slurry, and is gradually moved to circumference, and mixing time is 20 minutes, stirring Biscuit is put into glaze slurry after finishing, leaching glaze is carried out to biscuit outer surface, after the completion of soaking glaze, modifies green body;
Step 3: the green body trimmed in step 2 is put into kiln, divulges information in kiln, green body is made to be burnt in oxidizing atmosphere System controls the firing temperature in kiln, makes temperature interior ventilation for being ramped up 1200 ° -1300 °, reducing kiln when 7-8 is small Amount, makes combustion atmosphere in kiln gradually switch to reducing atmosphere, and green body keeps the temperature 40-50 minutes under 1250 ° -1320 °, controls kiln Interior firing temperature is gradually heated up with every 3 minutes 1 ° of temperature, and green body keeps the temperature firing 30 minutes under conditions of 1350 ° -1365 °, Truce is taken out after being cooled to room temperature to get to your porcelain of emerald green glaze.
The tremolite raw material is derived from the tremolite of Ruzhou City of Henan Province locality.
Beneficial effects of the present invention:The present invention has good excellent of transparent beautiful, the workable, market prospects of glaze layer in a word Point.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of your porcelain preparation method of emerald green glaze, the emerald green glaze is matched by the following raw material and made: Tang's ditch soil 30%, half way up the mountain soil 30%, kaolin 40%, the glaze raw material tremolite 30%, feldspar 28%, dark stone 23%, Fang Xie Stone 2%, lamb bone meal 3%.
Embodiment 2
Present embodiment discloses a kind of your porcelain preparation method of emerald green glaze, the emerald green glaze is matched by the following raw material and made: Tang's ditch soil 30%, half way up the mountain soil 30%, kaolin 40%, the glaze raw material tremolite 30%, feldspar 28%, dark stone 23%, Fang Xie Stone 2%, lamb bone meal 3%.
The preparation process of the emerald green glaze is as follows:
Step 1: after the glaze raw material is crushed, it is mixed according to the above mentioned proportion to be put into ball crusher, it is total to add in mixed raw material The water of the 27%-35% of raw material gross weight, when start wet-milling 22-30 is small, wet-grinded slurry crosses 300 mesh sieves, and static 12 is small When, water content is detected using moisture teller, and water content is adjusted to 56%-62%, it is spare;
Step 2: carrying out wiping dedusting to biscuit with water, wiping is simultaneously by slurry obtained by step 1 by the clockwise or inverse time Pin direction is stirred, and during stirring since the center of slurry, and is gradually moved to circumference, and mixing time is 20 minutes, stirring Biscuit is put into glaze slurry after finishing, leaching glaze is carried out to biscuit outer surface, after the completion of soaking glaze, modifies green body;
Step 3: the green body trimmed in step 2 is put into kiln, divulges information in kiln, green body is made to be burnt in oxidizing atmosphere System controls the firing temperature in kiln, makes temperature interior ventilation for being ramped up 1200 ° -1300 °, reducing kiln when 7-8 is small Amount, makes combustion atmosphere in kiln gradually switch to reducing atmosphere, and green body keeps the temperature 40-50 minutes under 1250 ° -1320 °, controls kiln Interior firing temperature is gradually heated up with every 3 minutes 1 ° of temperature, and green body keeps the temperature firing 30 minutes under conditions of 1350 ° -1365 °, Truce is taken out after being cooled to room temperature to get to your porcelain of emerald green glaze.
The tremolite raw material is derived from the tremolite of Ruzhou City of Henan Province locality.
In a word the present invention have the advantages that glaze layer it is transparent it is beautiful, workable, market prospects are good.

Claims (3)

1. a kind of your porcelain preparation method of emerald green glaze, it is characterised in that:The emerald green glaze is matched by the following raw material and made:Tang's ditch soil 30 parts, half way up the mountain soil 30 parts, 40 parts of kaolin, 30 parts of the glaze raw material tremolite, 28 parts of feldspar, 23 parts of dark stone, 2 parts of calcite, 3 parts of lamb bone meal.
2. a kind of your porcelain preparation method of emerald green glaze as described in claim 1, it is characterised in that:The preparation step of the emerald green glaze It is rapid as follows:
Step 1: after the glaze raw material is crushed, it is mixed according to the above mentioned proportion to be put into ball crusher, add in mixed raw material total raw material The water of the 27%-35% of total weight, when start wet-milling 22-30 is small, wet-grinded slurry crosses 300 mesh sieves, it is static 12 it is small when, make Water content is detected with moisture teller, and water content is adjusted to 56%-62%, it is spare;
Step 2: carrying out wiping dedusting to biscuit with water, wiping is simultaneously by slurry obtained by step 1 by side clockwise or counterclockwise To being stirred, during stirring since the center of slurry, and gradually moved to circumference, mixing time is 20 minutes, and stirring is completed Biscuit is put into glaze slurry afterwards, leaching glaze is carried out to biscuit outer surface, after the completion of soaking glaze, modifies green body;
Step 3: the green body trimmed in step 2 is put into kiln, divulges information in kiln, green body made to be fired in oxidizing atmosphere, The firing temperature in kiln is controlled, makes temperature interior ventilation quantity for being ramped up 1200 ° -1300 °, reducing kiln when 7-8 is small, makes Combustion atmosphere gradually switchs to reducing atmosphere in kiln, and green body keeps the temperature 40-50 minutes under 1250 ° -1320 °, controls in kiln Firing temperature is gradually heated up with every 3 minutes 1 ° of temperature, and green body keeps the temperature firing 30 minutes under conditions of 1350 ° -1365 °, is ceased fire It is taken out after being cooled to room temperature to get to your porcelain of emerald green glaze.
3. a kind of your porcelain preparation method of emerald green glaze as described in claim 1, it is characterised in that:The tremolite raw material is derived from The tremolite of Ruzhou City of Henan Province locality.
CN201610187865.2A 2016-03-23 2016-03-23 A kind of your porcelain preparation method of emerald green glaze Expired - Fee Related CN105753323B (en)