CN107058820A - 一种冲压件铝镁合金材料 - Google Patents
一种冲压件铝镁合金材料 Download PDFInfo
- Publication number
- CN107058820A CN107058820A CN201710389232.4A CN201710389232A CN107058820A CN 107058820 A CN107058820 A CN 107058820A CN 201710389232 A CN201710389232 A CN 201710389232A CN 107058820 A CN107058820 A CN 107058820A
- Authority
- CN
- China
- Prior art keywords
- stamping parts
- hydronalium
- mass percent
- magnesium
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种冲压件铝镁合金材料,由以下质量百分比的成分组成:镁≤20%,金≤0.8%,钛≤0.8%,铁≤15%,铂≤0.15%,铜≤5%,余量为铝。本发明的有益效果是:以铝、镁和铁为主要原料,稳定了冲压件的耐磨性,同时采用其它金属元素组成,增强了零件的抗冲蚀性能,延迟了使用寿命,安全性好,稳定性高。
Description
技术领域
本发明涉及一种冲压件,尤其涉及一种冲压件铝镁合金材料。
背景技术
冲压件是靠压力机和模具对板材、带材、管材和型材等施加外力,使之产生塑性变形或分离,从而获得所需形状和尺寸的工件(冲压件)的成形加工方法。冲压和锻造同属塑性加工(或称压力加工),合称锻压。冲压的坯料主要是热轧和冷轧的钢板和钢带。不同行业所指的冲压件一般不同,多用于组配时的称呼。冲压件的制造方法很多,但是目前的制造方法制备的冲压件普遍存在质量一般,易锈蚀,环境适应能力差,使用寿命短;未脱硫处理导致脆性大,易断裂,存在安全隐患;镀层不均匀,镀层易脱落等问题。还有,目前的工艺制造的冲压件普遍存在零件表面耐磨性能差,使用寿命短的问题。
因此,为解决上述问题,特提供一种新的技术方案。
发明内容
本发明提供一种冲压件铝镁合金材料。
本发明采用的技术方案是:
一种冲压件铝镁合金材料,由以下质量百分比的成分组成:镁≤20%,金≤0.8%,钛≤0.8%,铁≤15%,铂≤0.15%,铜≤5%,余量为铝。
进一步的,所述镁的质量百分比为10-20%。
进一步的,所述金的质量百分比为0.3-0.8%。
进一步的,所述钛的质量百分比为0.5-0.8%。
进一步的,所述铁的质量百分比为10-15%。
进一步的,所述铂的质量百分比为0.05-0.15%。
进一步的,所述铜的质量百分比为1-5%。
本发明的有益效果是:以铝、镁和铁为主要原料,稳定了冲压件的耐磨性,同时采用其它金属元素组成,增强了零件的抗冲蚀性能,延迟了使用寿命,安全性好,稳定性高。
具体实施方式
为了加深对本发明的理解,下面将结合实施例对本发明作进一步详述,该实施例仅用于解释本发明,并不构成对本发明的保护范围的限定。
实施例1
一种冲压件铝镁合金材料,由以下质量百分比的成分组成:镁10%,金0.3%,钛0.5%,铁10%,铂0.05%,铜1%,余量为铝。
本发明的有益效果是:以铝、镁和铁为主要原料,稳定了冲压件的耐磨性,同时采用其它金属元素组成,增强了零件的抗冲蚀性能,延迟了使用寿命,安全性好,稳定性高。
实施例2
一种冲压件铝镁合金材料,由以下质量百分比的成分组成:镁15%,金0.5%,钛0.65%,铁12%,铂0.1%,铜3%,余量为铝。
本发明的有益效果是:以铝、镁和铁为主要原料,稳定了冲压件的耐磨性,同时采用其它金属元素组成,增强了零件的抗冲蚀性能,延迟了使用寿命,安全性好,稳定性高。
实施例3
一种冲压件铝镁合金材料,由以下质量百分比的成分组成:镁20%,金0.8%,钛0.8%,铁15%,铂0.15%,铜5%,余量为铝。
本发明的有益效果是:以铝、镁和铁为主要原料,稳定了冲压件的耐磨性,同时采用其它金属元素组成,增强了零件的抗冲蚀性能,延迟了使用寿命,安全性好,稳定性高。
以上所述,仅是本发明的较佳实施例而已,并非是对本发明作任何其他形式的限制,而依据本发明的技术实质所作的任何修改或等同变化,仍属于本发明所要求保护的范围。
Claims (7)
1.一种冲压件铝镁合金材料,其特征在于:由以下质量百分比的成分组成:镁≤20%,金≤0.8%,钛≤0.8%,铁≤15%,铂≤0.15%,铜≤5%,余量为铝。
2.根据权利要求1所述的一种冲压件铝镁合金材料,其特征在于:所述镁的质量百分比为10-20%。
3.根据权利要求1所述的一种冲压件铝镁合金材料,其特征在于:所述金的质量百分比为0.3-0.8%。
4.根据权利要求1所述的一种冲压件铝镁合金材料,其特征在于:所述钛的质量百分比为0.5-0.8%。
5.根据权利要求1所述的一种冲压件铝镁合金材料,其特征在于:所述铁的质量百分比为10-15%。
6.根据权利要求1所述的一种冲压件铝镁合金材料,其特征在于:所述铂的质量百分比为0.05-0.15%。
7.根据权利要求1所述的一种冲压件铝镁合金材料,其特征在于:所述铜的质量百分比为1-5%。