CN107021631A - 一种磨砂质感橘黄色陶瓷釉料及其制备方法 - Google Patents

一种磨砂质感橘黄色陶瓷釉料及其制备方法 Download PDF

Info

Publication number
CN107021631A
CN107021631A CN201710350746.9A CN201710350746A CN107021631A CN 107021631 A CN107021631 A CN 107021631A CN 201710350746 A CN201710350746 A CN 201710350746A CN 107021631 A CN107021631 A CN 107021631A
Authority
CN
China
Prior art keywords
parts
crocus
ceramic glaze
frosted texture
glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710350746.9A
Other languages
English (en)
Inventor
黄菲
闫莹灿
黎永丽
张志彬
孟林
王道恒
安佰高
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Northeastern University China
Original Assignee
Northeastern University China
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Northeastern University China filed Critical Northeastern University China
Priority to CN201710350746.9A priority Critical patent/CN107021631A/zh
Publication of CN107021631A publication Critical patent/CN107021631A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种釉料，具体涉及一种磨砂质感橘黄色陶瓷釉料及其制备方法。本发明的技术方案如下：一种磨砂质感橘黄色陶瓷釉料，其原料配方为：按重量份数比计，Q矿8‑10份，钾长石3‑5份，绿泥石5‑7份，滑石粉3‑5份，粘土4‑6份，硼砂2‑4份，石英粉3‑5份，氧化铝粉1‑3份。本发明提供的磨砂质感橘黄色陶瓷釉料及其制备方法，烧制出的釉面呈橘黄色，手感坚硬粗糙，使用方便，可以批量快速生产，应用前景广泛。

Description

一种磨砂质感橘黄色陶瓷釉料及其制备方法
技术领域
本发明涉及一种釉料，具体涉及一种磨砂质感橘黄色陶瓷釉料及其制备方法。
背景技术
众所周知，釉可以改善陶瓷制品的表面性能，大多数釉可以使制品变得平滑，光亮，不吸水，对提高制品的强度，改善制品的热稳定性和化学稳定性也是有利的。陶瓷行业非常注重采用先进的釉料技术，目前陶瓷产品中所用的釉料也越来越丰富多样，但要使制品具有磨砂质感以及防滑功能，目前绝大多数方法都需要采用特殊的材料或者复杂的工艺制作过程，成本较高。
发明内容
本发明提供一种磨砂质感橘黄色陶瓷釉料及其制备方法，烧制出的釉面呈橘黄色，手感坚硬粗糙，使用方便，可以批量快速生产，应用前景广泛。
本发明的技术方案如下：
一种磨砂质感橘黄色陶瓷釉料，其原料配方为：按重量份数比计，Q矿8-10份，钾长石3-5份，绿泥石5-7份，滑石粉3-5份，粘土4-6份，硼砂2-4份，石英粉3-5份，氧化铝粉1-3份。
上述的磨砂质感橘黄色陶瓷釉料的制备方法，包括如下步骤：
(1)将原料粉碎，按配方所述重量份数比，称取各组分；
(2)将Q矿、粘土、硼砂、滑石粉混合后，加入重量份数为8-10份的热水浸泡2小时，热水温度为50-70℃，过200目筛去粗，得到浆料A；
(3)将钾长石、绿泥石进行粉碎处理，粉碎30min，过200目筛处理，然后加入石英粉、氧化铝粉以及重量份数为8-10份的水充分搅拌，得到浆料B；
(4)将所得浆料A与浆料B充分混合，即可制得磨砂质感橘黄色陶瓷釉料。
本发明的有益效果为：利用本发明制备的磨砂质感橘黄色陶瓷釉料，烧制出的釉面呈橘黄色，手感坚硬粗糙，使用方便，可以批量快速生产，采用原料易得，成本低，应用前景广泛。
具体实施方式
一种磨砂质感橘黄色陶瓷釉料，其原料配方为：按重量份数比计，Q矿9份，钾长石4份，绿泥石6份，滑石粉4份，粘土5份，硼砂3份，石英粉4份，氧化铝粉2份。
上述的磨砂质感橘黄色陶瓷釉料的制备方法，包括如下步骤：
(1)将原料粉碎，按配方所述重量份数比，称取各组分；
(2)将Q矿、粘土、硼砂、滑石粉混合后，加入重量份数为8-109份的热水浸泡2小时，热水温度为60℃，过200目筛去粗，得到浆料A；
(3)将钾长石、绿泥石进行粉碎处理，粉碎30min，过200目筛处理，然后加入石英粉、氧化铝粉以及重量份数为10份的水充分搅拌，得到浆料B；
(4)将所得浆料A与浆料B充分混合，即可制得磨砂质感橘黄色陶瓷釉料。
上述磨砂质感橘黄色陶瓷釉料的施釉方法为喷釉法。

Claims (2)

1.一种磨砂质感橘黄色陶瓷釉料，其特征在于，其原料配方为：按重量份数比计，Q矿8-10份，钾长石3-5份，绿泥石5-7份，滑石粉3-5份，粘土4-6份，硼砂2-4份，石英粉3-5份，氧化铝粉1-3份。
2.一种如权利要求1所述的磨砂质感橘黄色陶瓷釉料的制备方法，其特征在于，包括如下步骤：
(1)将原料粉碎，按配方所述重量份数比，称取各组分；
(2)将Q矿、粘土、硼砂、滑石粉混合后，加入重量份数为8-10份的热水浸泡2小时，热水温度为50-70℃，过200目筛去粗，得到浆料A；
(3)将钾长石、绿泥石进行粉碎处理，粉碎30min，过200目筛处理，然后加入石英粉、氧化铝粉以及重量份数为8-10份的水充分搅拌，得到浆料B；
(4)将所得浆料A与浆料B充分混合，即可制得磨砂质感橘黄色陶瓷釉料。
CN201710350746.9A 2017-05-18 2017-05-18 一种磨砂质感橘黄色陶瓷釉料及其制备方法 Pending CN107021631A (zh)