CN106957517A - 一种用于制作led灯罩的材料及制备方法 - Google Patents
一种用于制作led灯罩的材料及制备方法 Download PDFInfo
- Publication number
- CN106957517A CN106957517A CN201710242804.6A CN201710242804A CN106957517A CN 106957517 A CN106957517 A CN 106957517A CN 201710242804 A CN201710242804 A CN 201710242804A CN 106957517 A CN106957517 A CN 106957517A
- Authority
- CN
- China
- Prior art keywords
- parts
- led lamp
- lamp cover
- adjusted
- reaction vessel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于制作LED灯罩的材料，按照重量份数计包括如下原料：一氧化碳20～30份，氧气25～35份，甲醇15～28份，苯酚10～20份，双酚A20～35份，催化剂0.2～0.5份，驱蚊剂2～5份，阻燃剂1～8份。本发明提供的用于制作LED灯罩的材料由于是采用一氧化碳、氧气和甲醇作为原料进行反应生成碳酸二甲酯，生产过程中不会因为产生有毒有害物质而污染环境，同时也不会对一线工人的身体造成伤害，在原料中加入驱蚊剂和阻燃剂，可以达到驱蚊和阻燃的效果。
Description
技术领域
本发明涉及一种用于制作LED灯罩的材料及制备方法，属于LED灯罩技术领域。
背景技术
LED灯罩的主要材料为聚碳酸酯，传统的聚碳酸酯是以光气法生产的，由于要用到剧毒的光气，生产时对环境污染污染严重，同时也损害了一线生产工的身体健康，传统的LED灯罩不具备驱蚊和阻燃的效果，长时间使用后，蚊虫会聚集在灯旁边，导致灯罩内沉积有大量的蚊虫，影响灯的照明效果，同时灯长时间使用后会由于温度过高而烧掉，万一有火花产生就很容易将灯罩引燃，引起火灾。
发明内容
本发明的主要目的在于提供一种用于制作LED灯罩的材料及制备方法，采用一氧化碳、氧气和甲醇等作为原料，无毒无害，且不会对环境造成污染，在材料中加入驱蚊剂和阻燃剂，可以到达驱蚊和阻燃的效果，可以有效解决背景技术中的问题。
为实现上述目的，本发明采取的技术方案为：
一种用于制作LED灯罩的材料，按照重量份数计包括如下原料：一氧化碳20～30份，氧气25～35份，甲醇15～28份，苯酚10～20份，双酚A20～35份，催化剂0.2～0.5份，驱蚊剂2～5份，阻燃剂1～8份。
优选的，所述催化剂为氯化铜。
优选的，所述驱蚊剂为薰衣草提取物或艾草提取物。
优选的，所述阻燃剂为微胶囊化红磷与氢氧化铝的组合物。
本发明还涉及上述用于制作LED灯罩材料的制备方法，包括以下步骤：
(1)取15～28份甲醇和0.2～0.5份催化剂加入温度为130～200℃，压力为1.5～4.0MPa的反应釜中，再向反应釜中通入20～39份一氧化碳气体和25～35份氧气，并且不断搅拌30～50min，使其充分反应生成碳酸二甲酯；
(2)将上述反应釜的温度调整为160～200℃，压力调整为1.9～5.2MPa，取10～20份苯酚加入上述反应釜中并不断搅拌29～47min，使其与上述步骤所生成的产物进行酯交换生成碳酸二苯酯；
(3)将上述反应釜的温度调整为200～260℃，压力调整为3.8～6.0MPa，取20～35份双酚A加入上述反应釜中并不断搅拌90～120min，使其与上述步骤生成的产物进行酯交换并发生缩聚反应生成聚碳酸酯；
(4)将上述反应釜调整为常温常压，待反应釜内的混合物降到常温时取2～5份驱蚊剂和1～8份阻燃剂加入反应釜中，并不断搅拌30～45min使其充分混合后得到用于制作LED灯罩的材料。
本发明提供的用于制作LED灯罩的材料由于是采用一氧化碳、氧气和甲醇作为原料进行反应生成碳酸二甲酯，生产过程中不会因为产生有毒有害物质而污染环境，同时也不会对一线工人的身体造成伤害，在原料中加入驱蚊剂和阻燃剂，可以达到驱蚊和阻燃的效果。由于甲醇、一氧化碳和氧气通过羰化氧化法生成碳酸二甲酯的反应，碳酸二甲酯与苯酚进行酯交换生成碳酸二苯酯的反应以及碳酸二苯酯 与双酚A进行酯交换并缩聚生成聚碳酸酯的反应均为可逆反应，只有在上述个步骤的反应条件下才可达到最大的转化率。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
实施例1
一种用于制作LED灯罩的材料，按照重量份数计包括如下原料：一氧化碳20份，氧气25份，甲醇15份，苯酚10份，双酚A20份，催化剂0.2份，驱蚊剂2份，阻燃剂1份。
优选的，所述催化剂为氯化铜。
优选的，所述驱蚊剂为薰衣草提取物或艾草提取物，可以达到驱蚊的效果，并且无毒无害。
优选的，所述阻燃剂为微胶囊化红磷与氢氧化铝的组合物，微胶囊化红磷与氢氧化铝复配使用，可大幅降低阻燃剂的使用量，从而改善塑料制品的加工性能和物理机械性能，同时采用微胶囊化红磷可以克服红磷本身易燃易爆的缺陷，同时还有在加工中不产生有毒气体，使其分散性、物理、机械性能、热稳定性及阻燃性能均有提高和改善。
本发明还涉及上述用于制作LED灯罩材料的制备方法，包括以下步骤：
(1)取15份甲醇和0.2份催化剂加入温度为130℃，压力为1.5MPa的反应釜中，再向反应釜中通入20份一氧化碳气体和25份氧气，并且不断搅拌30min，使其充分反应生成碳酸二甲酯；
(2)将上述反应釜的温度调整为160℃，压力调整为1.9MPa，取10份苯酚加入上述反应釜中并不断搅拌29min，使其与上述步骤所生成的产物进行酯交换生成碳酸二苯酯；
(3)将上述反应釜的温度调整为200℃，压力调整为3.8～6.0MPa，取20份双酚A加入上述反应釜中并不断搅拌90min，使其与上述步骤生成的产物进行酯交换并发生缩聚反应生成聚碳酸酯；
(4)将上述反应釜调整为常温常压，待反应釜内的混合物降到常温时取2份驱蚊剂和1份阻燃剂加入反应釜中，并不断搅拌30min使其充分混合后得到用于制作LED灯罩的材料。
实施例2
一种用于制作LED灯罩的材料，按照重量份数计包括如下原料：一氧化碳30份，氧气35份，甲醇28份，苯酚20份，双酚A35份，催化剂0.5份，驱蚊剂5份，阻燃剂8份。
优选的，所述催化剂为氯化铜。
优选的，所述驱蚊剂为薰衣草提取物或艾草提取物。
优选的，所述阻燃剂为微胶囊化红磷与氢氧化铝的组合物。
本发明还涉及上述用于制作LED灯罩材料的制备方法，包括以下步骤：
(1)取28份甲醇和0.5份催化剂加入温度为200℃，压力为4.0MPa的反应釜中，再向反应釜中通入39份一氧化碳气体和35份氧气，并且不断搅拌50min，使其充分反应生成碳酸二甲酯；
(2)将上述反应釜的温度调整为200℃，压力调整为5.2MPa，取20份苯酚加入上述反应釜中并不断搅拌47min，使其与上述步骤 所生成的产物进行酯交换生成碳酸二苯酯；
(3)将上述反应釜的温度调整为260℃，压力调整为6.0MPa，取35份双酚A加入上述反应釜中并不断搅拌120min，使其与上述步骤生成的产物进行酯交换并发生缩聚反应生成聚碳酸酯；
(4)将上述反应釜调整为常温常压，待反应釜内的混合物降到常温时取5份驱蚊剂和8份阻燃剂加入反应釜中，并不断搅拌45min使其充分混合后得到用于制作LED灯罩的材料。
实施例3
一种用于制作LED灯罩的材料，按照重量份数计包括如下原料：一氧化碳26份，氧气32份，甲醇19份，苯酚14份，双酚A31份，催化剂0.4份，驱蚊剂3份，阻燃剂5份。
优选的，所述催化剂为氯化铜。
优选的，所述驱蚊剂为薰衣草提取物或艾草提取物。
优选的，所述阻燃剂为微胶囊化红磷与氢氧化铝的组合物。
本发明还涉及上述用于制作LED灯罩材料的制备方法，包括以下步骤：
(1)取19份甲醇和0.4份催化剂加入温度为150℃，压力为2.9MPa的反应釜中，再向反应釜中通入26份一氧化碳气体和32份氧气，并且不断搅拌45min，使其充分反应生成碳酸二甲酯；
(2)将上述反应釜的温度调整为180℃，压力调整为4.1MPa，取14份苯酚加入上述反应釜中并不断搅拌40min，使其与上述步骤所生成的产物进行酯交换生成碳酸二苯酯；
(3)将上述反应釜的温度调整为240℃，压力调整为5.4MPa， 取31份双酚A加入上述反应釜中并不断搅拌100min，使其与上述步骤生成的产物进行酯交换并发生缩聚反应生成聚碳酸酯；
(4)将上述反应釜调整为常温常压，待反应釜内的混合物降到常温时取3份驱蚊剂和5份阻燃剂加入反应釜中，并不断搅拌40min使其充分混合后得到用于制作LED灯罩的材料。
以上只通过说明的方式描述了本发明的某些示范性实施例，毋庸置疑，对于本领域的普通技术人员，在不偏离本发明的精神和范围的情况下，可以用各种不同的方式对所描述的实施例进行修正。因此，上述描述在本质上是说明性的，不应理解为对本发明权利要求保护范围的限制。
Claims (5)
1.一种用于制作LED灯罩的材料，其特征在于：按照重量份数计包括如下原料：一氧化碳20～30份，氧气25～35份，甲醇15～28份，苯酚10～20份，双酚A20～35份，催化剂0.2～0.5份，驱蚊剂2～5份，阻燃剂1～8份。
2.根据权利要求1所述的一种用于制作LED灯罩的材料，其特征在于：所述催化剂为氯化铜。
3.根据权利要求1所述的一种用于制作LED灯罩的材料，其特征在于：所述驱蚊剂为薰衣草提取物或艾草提取物。
4.根据权利要求1所述的一种用于制作LED灯罩的材料，其特征在于：所述阻燃剂为微胶囊化红磷与氢氧化铝的组合物。
5.一种用于上述任一权利要求所述的用于制作LED灯罩的材料，其特征在于：所述用于制作LED灯罩材料的制备方法包括以下步骤：
(1)取15～28份甲醇和0.2～0.5份催化剂加入温度为130～200℃，压力为1.5～4.0MPa的反应釜中，再向反应釜中通入20～39份一氧化碳气体和25～35份氧气，并且不断搅拌30～50min，使其充分反应生成碳酸二甲酯；
(2)将上述反应釜的温度调整为160～200℃，压力调整为1.9～5.2MPa，取10～20份苯酚加入上述反应釜中并不断搅拌29～47min，使其与上述步骤所生成的产物进行酯交换生成碳酸二苯酯；
(3)将上述反应釜的温度调整为200～260℃，压力调整为3.8～6.0MPa，取20～35份双酚A加入上述反应釜中并不断搅拌90～120min，使其与上述步骤生成的产物进行酯交换并发生缩聚反应生成聚碳酸酯；
(4)将上述反应釜调整为常温常压，待反应釜内的混合物降到常温时取2～5份驱蚊剂和1～8份阻燃剂加入反应釜中，并不断搅拌30～45min使其充分混合后得到用于制作LED灯罩的材料。